CN104889599A - 多元铜基钎料 - Google Patents
多元铜基钎料 Download PDFInfo
- Publication number
- CN104889599A CN104889599A CN201510255270.1A CN201510255270A CN104889599A CN 104889599 A CN104889599 A CN 104889599A CN 201510255270 A CN201510255270 A CN 201510255270A CN 104889599 A CN104889599 A CN 104889599A
- Authority
- CN
- China
- Prior art keywords
- brazing filler
- filler
- element copper
- low
- solder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了多元铜基钎料,是由Mn、Ni、Sn、Si、Al和CuZn组成。本发明成本低、熔点低,且通过加入适量Mn和Sn,进一步提高了钎料的润湿性能和钎缝剪切强度。
Description
技术领域
本发明涉及一种钎料,具体涉及一种多元铜基钎料。
背景技术
白口铸铁价格低廉,具有较高的耐磨性,但韧性低,一般认为钎焊没有意义,常用堆焊方法或者复合方法(白口铸铁与钢浇复合锭或白口铸铁与韧性钢板镶嵌)在钢表面获得一耐磨层。在基体材料钢表面通过堆焊白口铸铁形成耐磨层,由于焊接温度高,易使部件产生变形,并形成裂纹,甚至开焊,复合材料在结构形状和锻压、机加工等工序中又受到一定的限制。
近几年研究结果表明:钎焊是有希望用于上述双金属材料连接的一种焊接方法,可获得牢固的钎缝。因此,焊接技术是制造低廉、高硬度、耐磨性优良的白口铸铁部件的优选方法,CuZn系合金是常用的一种价格低廉的硬钎料,对钢的润湿性和填满间隙的能力很好,广泛应用于钎焊低温碳、低合金钢的焊补铸铁。CuZn钎料由于熔点高,以致钎焊温度也高,因而对白口铸铁组织和性能影响较大,界面溶蚀严重,需对其进行解决。
发明内容
本发明所要解决的技术问题在于提供一种成本低、润湿性能好、钎缝剪切强度高、熔点低的多元铜基钎料。
本发明所要解决的技术问题采用以下技术方案来实现:
多元铜基钎料,是由以下质量百分比的组分组成:
Mn: 8.5-9.5%
Ni: 1.5-2.5%
Sn: 0.3-0.8%
Si: 0.3-0.8%
Al: 0.5-1%
余量为CuZn。
各组分的较佳质量百分比为:
Mn: 8.6%
Ni: 1.5%
Sn: 0.4%
Si: 0.5%
Al: 0.8%
余量为CuZn。
本发明的有益效果是:本发明熔点低,且通过加入适量Mn和Sn,进一步提高了钎料的润湿性能和钎缝剪切强度。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
多元铜基钎料,是由以下质量百分比的组分组成:
Mn: 8.5-9.5%
Ni: 1.5-2.5%
Sn: 0.3-0.8%
Si: 0.3-0.8%
Al: 0.5-1%
余量为CuZn。
各组分的较佳质量百分比为:
Mn: 8.6%
Ni: 1.5%
Sn: 0.4%
Si: 0.5%
Al: 0.8%
余量为CuZn。
多元铜基钎料, 其成本低,熔点低,且通过加入适量Mn和Sn,进一步提高了钎料的润湿性能和钎缝剪切强度。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.多元铜基钎料,其特征在于,是由以下质量百分比的组分组成:
Mn: 8.5-9.5%
Ni: 1.5-2.5%
Sn: 0.3-0.8%
Si: 0.3-0.8%
Al: 0.5-1%
余量为CuZn。
2.根据权利要求1所述的多元铜基钎料,其特征在于,是由以下质量百分比的组分组成:
Mn: 8.6%
Ni: 1.5%
Sn: 0.4%
Si: 0.5%
Al: 0.8%
余量为CuZn。