CN104353938A - 一种铝硅钎料 - Google Patents
一种铝硅钎料 Download PDFInfo
- Publication number
- CN104353938A CN104353938A CN201410486678.5A CN201410486678A CN104353938A CN 104353938 A CN104353938 A CN 104353938A CN 201410486678 A CN201410486678 A CN 201410486678A CN 104353938 A CN104353938 A CN 104353938A
- Authority
- CN
- China
- Prior art keywords
- filler metal
- brazing filler
- aluminum
- silicon brazing
- good
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种焊接材料,尤其是一种铝硅钎料。其组成成分包括:Al、Si、Ni、Ag、Cu、Mn。它熔化温度低,润湿性能和流动性能好,还具有良好的镀覆性、可加工性、耐腐蚀性能,而且焊接接头强度高、塑性好、耐腐蚀性强,还有优良的抗热裂性能,是一种性能优良的铝硅钎料。
Description
技术领域
本发明涉及一种焊接材料,尤其是一种铝硅钎料。
背景技术
随着科学技术的发展,航空、航天、汽车、电子、生活用品方面以铝代铜、以铝代钢的发展在很大程度上推动了铝合金钎焊技术的发展。Al-Si系钎料具有良好的钎焊性、和母材色泽一致性、镀覆性和抗腐蚀性能而且该系钎料可以进行变质处理,大大增加了钎料和焊缝的韧性和折弯性能,加之成本低廉,因此应用广泛。但是此系钎料的液相线在577℃左右,而一般铝合金的熔点在600℃左右,过高的钎焊温度容易使母材晶粒长大,从而影响接头的力学性能。作为钎焊技术的重要组成部分,国内外铝硅钎料的发展趋势主要集中在通过添加合金元素、改变生产工艺来改善钎料性能等方面。
发明内容
本发明旨在解决上述问题,提供了一种铝硅钎料,它在单纯铝硅钎料的基础上增加了银、铜、镍、锰元素,克服了普通铝硅基钎料熔点高,接头强度低的弊端,其采用的技术方案如下:
一种铝硅钎料,其特征在于,所述的钎料包括以下成分,各组合成分按重量百分比依次为:
在上述技术方案中,所述钎料熔化温度为500~535℃,属铝钎焊用高温硬钎料。
Si能够降低Al的熔点,提高焊缝的强度,而且由于Si可作变质处理,从而使得焊缝的韧性好,折弯性能较强;另外,在Al-Si二元相图的亚共晶区域的合金具有良好的流动性、润湿性和耐腐蚀性;添加Cu元素能降低Al的熔点,提高钎料的流动性,而且Cu可以与Al形成固溶体,从而使合金得到固溶强化,提高焊缝的强度;Ni的加入会提高钎料的填缝性能,改善接头焊缝及基体组织的分布,从而提高接头的剪切强度;添加少量Ag、Mn可降低钎料的温度,改善铺展性,提高钎料的强度。
本发明具有如下优点:熔化温度低,润湿性能和流动性能好,还具有良好的镀覆性、可加工性、耐腐蚀性能,而且焊接接头强度高、塑性好、耐腐蚀性强,还有优良的抗热裂性能,是一种性能优良的铝硅钎料。
具体实施方式
实施例1
一种铝硅钎料,其特征在于,所述的钎料包括以下成分,各组合成分按重量百分比依次为:
在上述技术方案中,该组成元素的钎料熔化温度约为525℃。
实施例2
一种铝硅钎料,其特征在于,所述的钎料包括以下成分,各组合成分按重量百分比依次为:
在上述技术方案中,该组成元素的钎料熔化温度约为518℃。
上面以举例方式对本发明进行了说明,但本发明不限于上述具体实施例,凡基于本发明所做的任何改动或变型均属于本发明要求保护的范围。
Claims (2)
1.一种铝硅钎料,其特征在于,所述的钎料包括以下成分,各组合成分按重量百分比依次为:
。
2.根据权利要求1所述的一种铝硅钎料,其特征在于:所述钎料熔化温度为500~535℃,属铝钎焊用高温硬钎料。