CN104844087A - 一种环保电气石蒸压砖 - Google Patents
一种环保电气石蒸压砖 Download PDFInfo
- Publication number
- CN104844087A CN104844087A CN201510201318.0A CN201510201318A CN104844087A CN 104844087 A CN104844087 A CN 104844087A CN 201510201318 A CN201510201318 A CN 201510201318A CN 104844087 A CN104844087 A CN 104844087A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- autoclaved brick
- tourmaline
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保电气石蒸压砖,其是由下述重量份的原料制得:水泥8-12、电气石粉5-7、膨胀蛭石粉4-8、铁矿尾渣1-3、粉煤灰4-8、苛化白泥6-8、河砂5-10,二氧化钛2-4、硝酸铝1-2、硝酸镁1-2、偶氮二甲酰胺0.2-0.3、过硫酸铵0.1-0.2,卡波姆0.2-0.4、聚丙烯酸0.1-0.2、硬脂酸0.1-0.3、去离子水适量。
Description
技术领域
本发明涉及蒸压砖领域,确切地说是一种环保电气石蒸压砖。
背景技术
蒸压砖为利用粉煤灰、煤渣、煤矸石、尾矿渣、化工渣或者天然砂、海涂泥等(以上原料的一种或数种)作为主要原料,不经高温煅烧而制造的一种新型墙体材料。
发明内容
本发明的目的在于提供一种环保电气石蒸压砖。
上述目的通过以下方案实现:
一种环保电气石蒸压砖,其特征在于:其是由下述重量份的原料制得:水泥8-12、电气石粉5-7、膨胀蛭石粉4-8、铁矿尾渣1-3、粉煤灰4-8、苛化白泥6-8、河砂5-10,二氧化钛2-4、硝酸铝1-2、硝酸镁1-2、偶氮二甲酰胺0.2-0.3、过硫酸铵0.1-0.2,卡波姆0.2-0.4、聚丙烯酸0.1-0.2、硬脂酸0.1-0.3、去离子水适量。
所述的一种环保电气石蒸压砖,其特征在于:制备方法包括以下步骤:
(1)将电气石粉、膨胀蛭石粉、铁矿尾渣、硬脂酸混匀后,加入适量水,搅拌均匀后,静置2-4小时,干燥,过100-120目筛得复配矿物粉备用;
(2)将二氧化钛、硝酸镁、硝酸铝加入到适量去离子水中,搅拌均匀后,再将卡波姆、聚丙烯酸加入其中,45-50℃下搅拌均匀,得到凝胶溶液;
(3)将复配矿物粉加入到凝胶溶液中,球磨混合均匀得到浆料,加入偶氮二甲酰胺、过硫酸铵,常温下反应50-60min,60-65℃下干燥15-25h,后在500-550℃下煅烧10-20min,得到包覆粉体;
(4)将包覆粉体与适量去离子水、以及其余原料搅拌均匀,成型,制得蒸压砖坯料;
(5)将蒸压砖坯料静置10-12h后,放入高压釜进行高压蒸压养护,190-205℃下、蒸汽压力1-1.5MPa下保温10-12h,然后出釜,即得。
本发明的有益效果为:本发明使用电气石和铁矿尾渣,能够增加本发明的强度;本发明通过将二氧化钛包覆在矿物粉表面,能够对铁矿尾渣起到一定的杀菌、消毒作用,通过提高所得蒸压砖的强度以及抗冻性能,通过凝胶溶液使得包覆二氧化钛更均匀,所得蒸压砖抗折强度更高。
具体实施方式
一种环保电气石蒸压砖,其是由下述重量(kg)的原料制得:水泥8、电气石粉5、膨胀蛭石粉4、铁矿尾渣1、粉煤灰4、苛化白泥6、河砂5,二氧化钛4、硝酸铝1、硝酸镁1、偶氮二甲酰胺0.2、过硫酸铵0.1,卡波姆0.2、聚丙烯酸0.2、硬脂酸0.1、去离子水适量。
所述的一种环保电气石蒸压砖,制备方法包括以下步骤:
(1)将电气石粉、膨胀蛭石粉、铁矿尾渣、硬脂酸混匀后,加入适量水,搅拌均匀后,静置4小时,干燥,过100-120目筛得复配矿物粉备用;
(2)将二氧化钛、硝酸镁、硝酸铝加入到适量去离子水中,搅拌均匀后,再将卡波姆、聚丙烯酸加入其中,50℃下搅拌均匀,得到凝胶溶液;
(3)将复配矿物粉加入到凝胶溶液中,球磨混合均匀得到浆料,加入偶氮二甲酰胺、过硫酸铵,常温下反应60min,65℃下干燥25h,后在550℃下煅烧20min,得到包覆粉体;
(4)将包覆粉体与适量去离子水、以及其余原料搅拌均匀,成型,制得蒸压砖坯料;
(5)将蒸压砖坯料静置12h后,放入高压釜进行高压蒸压养护,190-205℃下、蒸汽压力1-1.5MPa下保温12h,然后出釜,即得。
制得的 80 份蒸压砖送检测试, 得出 :平均抗压强度为 20. 85Mpa, 平均抗折强 度为 5. 34Mpa, 冻融试验后平均抗压强度为 17.6Mpa, 干质量损失为 0. 2-0.8%, 抗冻性符合 GB11945-1999《蒸压灰砂砖》 中 MU15C 优等品的要求。
Claims (2)
1.一种环保电气石蒸压砖,其特征在于:其是由下述重量份的原料制得:水泥8-12、电气石粉5-7、膨胀蛭石粉4-8、铁矿尾渣1-3、粉煤灰4-8、苛化白泥6-8、河砂5-10,二氧化钛2-4、硝酸铝1-2、硝酸镁1-2、偶氮二甲酰胺0.2-0.3、过硫酸铵0.1-0.2,卡波姆0.2-0.4、聚丙烯酸0.1-0.2、硬脂酸0.1-0.3、去离子水适量。
2. 根据权利要求1所述的一种环保电气石蒸压砖,其特征在于:制备方法包括以下步骤:
(1)将电气石粉、膨胀蛭石粉、铁矿尾渣、硬脂酸混匀后,加入适量水,搅拌均匀后,静置2-4小时,干燥,过100-120目筛得复配矿物粉备用;
(2)将二氧化钛、硝酸镁、硝酸铝加入到适量去离子水中,搅拌均匀后,再将卡波姆、聚丙烯酸加入其中,45-50℃下搅拌均匀,得到凝胶溶液;
(3)将复配矿物粉加入到凝胶溶液中,球磨混合均匀得到浆料,加入偶氮二甲酰胺、过硫酸铵,常温下反应50-60min,60-65℃下干燥15-25h,后在500-550℃下煅烧10-20min,得到包覆粉体;
(4)将包覆粉体与适量去离子水、以及其余原料搅拌均匀,成型,制得蒸压砖坯料;
(5)将蒸压砖坯料静置10-12h后,放入高压釜进行高压蒸压养护,190-205℃下、蒸汽压力1-1.5MPa下保温10-12h,然后出釜,即得。