CN104829249A - 一种高铝耐火砖的制备方法 - Google Patents

一种高铝耐火砖的制备方法 Download PDF

Info

Publication number
CN104829249A
CN104829249A CN201510169847.7A CN201510169847A CN104829249A CN 104829249 A CN104829249 A CN 104829249A CN 201510169847 A CN201510169847 A CN 201510169847A CN 104829249 A CN104829249 A CN 104829249A
Authority
CN
China
Prior art keywords
powder
alumina
preparation
raw material
refractory brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510169847.7A
Other languages
English (en)
Inventor
高寿林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Li Xin High-Temperature Refractory Co Ltd
Original Assignee
Zhejiang Li Xin High-Temperature Refractory Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Li Xin High-Temperature Refractory Co Ltd filed Critical Zhejiang Li Xin High-Temperature Refractory Co Ltd
Priority to CN201510169847.7A priority Critical patent/CN104829249A/zh
Publication of CN104829249A publication Critical patent/CN104829249A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种高铝耐火砖的制备方法，可以延长耐火砖的使用寿命，所述高铝耐火砖包括下述重量份数的原料：电熔刚玉粉20-30％、板状刚玉15-20％、氧化铝微粉20-25％、镁砂细粉5-8％、二氧化锆粉5-10％、硅酸钠5-10％、红柱石粉5-8％、硼化钛添加剂2-3％，上述原料总量为100％；制备方法包括以下步骤：步骤一、按重量百分比称取上述原料后加水混合，原料与水的质量比为5-8：1，然后均匀搅拌30-45min；步骤二、向模具中加入搅拌后的混合料并锤捣5-8min，并使表面平整，自然放置2-3h后脱模在阴凉处晾置2-3天得待烧品；步骤三、将所述待烧品在1700-1750℃的温度下烧结得到高铝耐火砖。

Description

一种高铝耐火砖的制备方法
技术领域
本发明涉及一种玻璃窑炉内壁上使用的耐火砖，具体涉及一种高铝耐火砖的制备方法。
背景技术
现有的玻璃窑炉通道上使用的高铝耐火砖多存在易腐蚀、抗性差的问题，这大大影响了耐火砖的使用寿命，同时还降低了所生产出来的玻璃的质量。
发明内容
本发明所要解决的技术问题在于提供一种高铝耐火砖的制备方法，可以延长该高铝耐火砖的使用寿命。
为解决上述现有的技术问题，本发明采用如下方案：一种高铝耐火砖的制备方法，所述高铝耐火砖包括下述重量份数的原料：电熔刚玉粉20-30％、板状刚玉15-20％、氧化铝微粉20-25％、镁砂细粉5-8％、二氧化锆粉5-10％、硅酸钠5-10％、红柱石粉5-8％、硼化钛添加剂2-3％，上述原料总量为100％；所述高铝耐火砖的制备方法包括以下步骤：步骤一、按重量百分比称取上述原料后加水混合，原料与水的质量比为5-8：1，然后均匀搅拌30-45min；步骤二、向模具中加入搅拌后的混合料并锤捣5-8min，并使表面平整，自然放置2-3h后脱模在阴凉处晾置2-3天得待烧品；步骤三、将所述待烧品在1700-1750℃的温度下烧结得到高铝耐火砖。
作为优选，所述电熔刚玉粉中Al2O3的质量含量为90％以上，所述电熔刚玉粉、硅酸钠、镁砂细粉的粒度均在3mm以下，所述氧化铝微粉的粒度为2mm以下，所述二氧化锆粉、红柱石粉的粒度为1mm以下。
作为优选，所述耐火砖包括下述重量份数的原料：电熔刚玉粉30％、板状刚玉20％、氧化铝微粉20％、镁砂细粉6％、二氧化锆粉5％、硅酸钠10％、红柱石粉7％、硼化钛添加剂2％。
有益效果：
本发明采用上述技术方案以后，通过对耐火砖的组分、配比和工艺进行优化，可以达到延长耐火砖的使用寿命的目的。
具体实施方式
一种高铝耐火砖的制备方法，所述高铝耐火砖包括下述重量份数的原料：电熔刚玉粉20-30％、板状刚玉15-20％、氧化铝微粉20-25％、镁砂细粉5-8％、二氧化锆粉5-10％、硅酸钠5-10％、红柱石粉5-8％、硼化钛添加剂2-3％，上述原料总量为100％；其特征在于，所述高铝耐火砖的制备方法包括以下步骤：步骤一、按重量百分比称取上述原料后加水混合，原料与水的质量比为5-8：1，然后均匀搅拌30-45min；步骤二、向模具中加入搅拌后的混合料并锤捣5-8min，并使表面平整，自然放置2-3h后脱模在阴凉处晾置2-3天得待烧品；步骤三、将所述待烧品在1700-1750℃的温度下烧结得到高铝耐火砖。
该实施例中，所述电熔刚玉粉中Al2O3的质量含量为90％以上，所述电熔刚玉粉、硅酸钠、镁砂细粉的粒度均在3mm以下，所述氧化铝微粉的粒度为2mm以下，所述二氧化锆粉、红柱石粉的粒度为1mm以下。
该实施例中，优选所述耐火砖包括下述重量份数的原料：电熔刚玉粉30％、板状刚玉20％、氧化铝微粉20％、镁砂细粉6％、二氧化锆粉5％、硅酸钠10％、红柱石粉7％、硼化钛添加剂2％。

Claims (3)

1.一种高铝耐火砖的制备方法，所述高铝耐火砖包括下述重量份数的原料：电熔刚玉粉20-30％、板状刚玉15-20％、氧化铝微粉20-25％、镁砂细粉5-8％、二氧化锆粉5-10％、硅酸钠5-10％、红柱石粉5-8％、硼化钛添加剂2-3％，上述原料总量为100％；其特征在于，所述高铝耐火砖的制备方法包括以下步骤：步骤一、按重量百分比称取上述原料后加水混合，原料与水的质量比为5-8：1，然后均匀搅拌30-45min；步骤二、向模具中加入搅拌后的混合料并锤捣5-8min，并使表面平整，自然放置2-3h后脱模在阴凉处晾置2-3天得待烧品；步骤三、将所述待烧品在1700-1750℃的温度下烧结得到高铝耐火砖。
2.根据权利要求1所述的一种高铝耐火砖的制备方法，其特征在于：所述电熔刚玉粉中Al2O3的质量含量为90％以上，所述电熔刚玉粉、硅酸钠、镁砂细粉的粒度均在3mm以下，所述氧化铝微粉的粒度为2mm以下，所述二氧化锆粉、红柱石粉的粒度为1mm以下。
3.根据权利要求1或2所述的一种高铝耐火砖的制备方法，其特征在于：所述耐火砖包括下述重量份数的原料：电熔刚玉粉30％、板状刚玉20％、氧化铝微粉20％、镁砂细粉6％、二氧化锆粉5％、硅酸钠10％、红柱石粉7％、硼化钛添加剂2％。
CN201510169847.7A 2015-04-10 2015-04-10 一种高铝耐火砖的制备方法 Pending CN104829249A (zh)