CN104788043A - 老旧建筑墙修复用环氧砂浆 - Google Patents
老旧建筑墙修复用环氧砂浆 Download PDFInfo
- Publication number
- CN104788043A CN104788043A CN201510153664.6A CN201510153664A CN104788043A CN 104788043 A CN104788043 A CN 104788043A CN 201510153664 A CN201510153664 A CN 201510153664A CN 104788043 A CN104788043 A CN 104788043A
- Authority
- CN
- China
- Prior art keywords
- building wall
- sand
- old building
- epoxy mortar
- particle diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种老旧建筑墙修复用环氧砂浆。所述老旧建筑墙修复用环氧砂浆，包括以下重量份数的组分：环氧树脂：90-140重量份；固化剂：10-30重量份；邻苯二甲酸二丁酯：10-20重量份；水泥：150-200重量份；石英砂：500-600重量份。本发明所述组分的环氧砂浆用于老旧建筑墙时，其粘结力优良。
Description
技术领域
本发明属于建筑材料领域，具体地，涉及老旧建筑墙修复用环氧砂浆。
背景技术
老旧建筑墙由于年代久远，表皮酥散起泡，灰尘污垢将砌体内部的水分封闭在砖与面膜之间，长此以往，水分和砖砌体表面产生物理和化学反应，表面变质霉烂。
为了避免老旧建筑墙的进一步劣化，对其的修复成为迫切需要解决的问题。环氧砂浆作为一种新型的建筑用修补材料，因其施工性、抗渗性、抗剥落性、抗冻融性、抗碳化性、抗裂性等性能均良好而被受到广泛应用。环氧砂浆通常包括环氧树脂、固化剂、水泥、沙子等，但是其应用于老旧建筑墙修复时的粘结能力仍不够理想。
发明内容
本发明所要解决的技术问题是提供一种粘结力好的老旧建筑墙修复用的环氧砂浆。
本发明解决上述问题所采用的技术方案是：
老旧建筑墙修复用环氧砂浆，包括以下重量份数的组分：
环氧树脂：90-140重量份；
固化剂：10-30重量份；
邻苯二甲酸二丁酯：10-20重量份；
水泥：150-200重量份；
石英砂：500-600重量份。
其中，所述固化剂选自以下物质中的至少一种：乙二胺、己二胺、二乙烯三胺、三乙烯四胺、二乙氨基丙胺。
其中，所述石英砂由粒径为0.3-0.6mm的细砂、粒径为1-2mm的中砂以及粒径为2-3mm的粗砂组成的。
其中，所述细砂、中砂、粗砂的质量比为3:2:1。
综上，本发明所述组分的环氧砂浆用于老旧建筑墙时，其粘结力优良。
具体实施方式
下面结合实施例，对本发明作进一步的详细说明，但本发明的实施方式不限于此。
实施例1
老旧建筑墙修复用环氧砂浆，组分如下：
环氧树脂：90重量份；
二乙烯三胺：10重量份；
邻苯二甲酸二丁酯：10重量份；
水泥：150重量份；
石英砂：500重量份；
其中，所述石英砂由粒径为0.3-0.6mm的细砂、粒径为1-2mm的中砂以及粒径为2-3mm的粗砂组成的；且所述细砂、中砂、粗砂的质量比为3:2:1。
实施例2
老旧建筑墙修复用环氧砂浆，组分如下：
环氧树脂：140重量份；
二乙氨基丙胺：30重量份；
邻苯二甲酸二丁酯：20重量份；
水泥：200重量份；
石英砂：600重量份；
其中，所述石英砂由粒径为0.3-0.6mm的细砂、粒径为1-2mm的中砂以及粒径为2-3mm的粗砂组成的；且所述细砂、中砂、粗砂的质量比为3:2:1。
实施例3
老旧建筑墙修复用环氧砂浆，组分如下：
环氧树脂：100重量份；
二乙烯三胺：20重量份；
邻苯二甲酸二丁酯：15重量份；
水泥：180重量份；
石英砂：550重量份；
其中，所述石英砂由粒径为0.3-0.6mm的细砂、粒径为1-2mm的中砂以及粒径为2-3mm的粗砂组成的；且所述细砂、中砂、粗砂的质量比为3:2:1。
使用本发明所述的组分的环氧砂浆，修复老旧建筑墙时，其粘结性能优良，具有广泛应用。
如上所述，可较好的实现本发明。
以上所述，仅是本发明的较佳实施例而已，并非对本发明作任何形式上的限制，依据本发明的技术实质，在本发明的精神和原则之内，对以上实施例所作的任何简单的修改、等同替换与改进等，均仍属于本发明技术方案的保护范围之内。
Claims (4)
1.老旧建筑墙修复用环氧砂浆，其特征在于，包括以下重量份数的组分：
环氧树脂：90-140重量份；
固化剂：10-30重量份；
邻苯二甲酸二丁酯：10-20重量份；
水泥：150-200重量份；
石英砂：500-600重量份。
2.根据权利要求1所述的老旧建筑墙修复用环氧砂浆，其特征在于，所述固化剂选自以下物质中的至少一种：乙二胺、己二胺、二乙烯三胺、三乙烯四胺、二乙氨基丙胺。
3.根据权利要求1所述的老旧建筑墙修复用环氧砂浆，其特征在于，所述石英砂由粒径为0.3-0.6mm的细砂、粒径为1-2mm的中砂以及粒径为2-3mm的粗砂组成的。
4.根据权利要求3所述的老旧建筑墙修复用环氧砂浆，其特征在于，所述细砂、中砂、粗砂的质量比为3:2:1。