CN104692710A - Epoxy resin terrazzo mixing proportion - Google Patents
Epoxy resin terrazzo mixing proportion Download PDFInfo
- Publication number
- CN104692710A CN104692710A CN201510060330.4A CN201510060330A CN104692710A CN 104692710 A CN104692710 A CN 104692710A CN 201510060330 A CN201510060330 A CN 201510060330A CN 104692710 A CN104692710 A CN 104692710A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- terrazzo
- glass
- stone
- flour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an epoxy resin terrazzo which is characterized by being prepared by evenly blending the following raw materials according to the specific weight: 6.0-6.5 kg/m<3> of epoxy resin, 1.2-1.3 kg/m<3> of curing agent, 0.5-1.0 kg/m<3> of flour, 100-160 kg/m<3> of industrial salt, 1320-1640 kg/m<3> of stones, 10-30 kg/m<3> quartz sand, 450-670 kg/m<3> glass, and 10-30 kg/m<3> of luminous powder. Compared with the prior art, the epoxy resin terrazzo has the advantages that the quality of terrace is obviously improved, and the construction process is more environment-friendly. The epoxy resin terrazzo has good application prospects at the places of supermarkets and the like which lay emphasis on the decoration effect.
Description
Technical field
The present invention relates to a kind of raw material counterweight of decorating terrace, its proterties is applicable to the floor construction that decorative effect is focused in market etc., is not suitable for the non-decoration terrace that the wearing and tearing such as factory, storehouse are larger; A kind of material fiting ratio weight of epoxy resin terrazzo specifically.
Background technology
Along with Economic development, quality of the life improves constantly, and the requirement of high-grade place to fine fitment constantly promotes.For meeting ground gloss, the demand such as withstand voltage, wear-resisting, terrazzo terrace progressively pours in construction market.But traditional terrazzo exists following defect: 1. construction process needs water seasoning, working-yard ponding is many; 2. affect by soundness of cement, as improper in process maintenance, easily occur hollowing, cracking, or make finished product plasticity deficiency, fragility excessive, impact uses; 3. traditional terrazzo dull coloring, decorative effect can not meet the requirement in high-grade place; 4. bruting process still needs to water in a large number, and pollute site operation environment, other operations can not be constructed simultaneously.
Summary of the invention
The object of the invention is to overcome above deficiency, a kind of finished product not easily hollowing, cracking is provided, construction process environmental protection and do not affect other operations, the Waterstones proportioning that decorative effect is various.
In order to achieve the above object, the present invention relates to a kind of Waterstones proportioning, it is characterized in that adopting the following even mix of raw material of proportion that coordinates to form, the terrazzo density of configuration is 2100 kg/ m
3-2300kg/ m
3.Form by coordinating the even mix of the raw material of proportion as follows:
Epoxy resin 6.0-6.5kg/m
3;
Solidifying agent 1.2-1.3kg/ m
3;
Flour 0.5-1.0kg/ m
3;
Industrial Salt 100-160kg/ m
3;
Stone 1320-1640kg/ m
3;
Quartz sand 10-30kg/ m
3;
Glass 450-670kg/ m
3;
Light powder 10-30kg/ m
3.
Described epoxy resin terrazzo, by above-mentioned cooperation proportion, weight and the 86%-94% accounting for gross weight of stone and glass, wherein stone quality accounts for 70% ~ 80%, requires clean no-sundries, and diameter is 4mm-10mm; Glass quality accounts for 25% ~ 30%: glass can by identical other non-aggressives of hardness and not with the material substitution of epoxy resin generation chemical reaction.
In described epoxy resin terrazzo raw material, what play adhesive effect is the mixture of epoxy resin, solidifying agent and flour, and the mass ratio of its epoxy resin and solidifying agent is 5:1, and during weighing, quality permissible variation is 100g, flour can by above-mentioned proportion admixture, also can not admixture; The color of epoxy resin is determined according to the pattern of design requirements.
Described epoxy resin terrazzo, the even mix of raw material, the final slurry forming denseness and be about 60mm.
Compare with traditional terrazzo, tool of the present invention has the following advantages:
(1) wear resistance and elasticity is had concurrently; The terrazzo being mixed with glass has wear resistance, the material behavior of coupling collar epoxy resins, makes this terrazzo finished product have certain elasticity and toughness; Because hardness is little compared with the terrazzo of traditional full stone formula, so the decoration of the inapplicable terrace such as warehouse, factory larger with wearing and tearing;
(2) quality of finished product good; Rated epoxy, solidifying agent, flour replace cement to do matrix material, and avoid the quality problems such as finished product hollowing, cracking produced by soundness of cement affects, final product quality is good;
(3) construction process environmental protection; Not containing hydraulic material in formula, without the need to watering in a large number when maintenance and construction, construction process environmental protection;
(4) duration is saved; Because construction process produces without a large amount of ponding, mud, other operations on-the-spot do not affect construction, can the same period, the construction that interts, save the whole duration.
The present invention is highly suitable for the construction of the decoration terraces such as market.
Embodiment
Now in conjunction with example, the present invention will be further described.
Embodiment one:
Design a kind of epoxy resin terrazzo material fiting ratio as follows:
。
Embodiment two:
Design a kind of epoxy resin terrazzo material fiting ratio as follows:
。
Innovative point:
(1) use epoxy resin and solidifying agent to replace traditional cement material to make tamanori, avoid the quality problems of the finished product cracking caused by soundness of cement affects;
(2) epoxy resin is on-hydraulic material, without the need to adding water during maintenance, is conducive to on-the-spot civilized construction, saves the duration.
Claims (2)
1. an epoxy resin terrazzo, is characterized in that adopting the following even mix of raw material of proportion that coordinates to form:
Epoxy resin 6.0-6.5kg/m
3;
Solidifying agent 1.2-1.3kg/ m
3;
Flour 0.5-1.0kg/ m
3;
Industrial Salt 100-160kg/ m
3;
Stone 1320-1640kg/ m
3;
Quartz sand 10-30kg/ m
3;
Glass 450-670kg/ m
3;
Light powder 10-30kg/ m
3.
2. proportion according to claim 1, is characterized in that: the mass ratio of epoxy resin and solidifying agent is 5:1; Weight and the 86%-94% accounting for gross weight of stone and glass, wherein stone quality accounts for 70% ~ 80%, requires clean no-sundries, and diameter is 4mm-10mm; Glass quality accounts for 25% ~ 30%.