CN102603229A - Resin floor material and process for constructing circular arc angle of floor on scene - Google Patents
Resin floor material and process for constructing circular arc angle of floor on scene Download PDFInfo
- Publication number
- CN102603229A CN102603229A CN2012100716633A CN201210071663A CN102603229A CN 102603229 A CN102603229 A CN 102603229A CN 2012100716633 A CN2012100716633 A CN 2012100716633A CN 201210071663 A CN201210071663 A CN 201210071663A CN 102603229 A CN102603229 A CN 102603229A
- Authority
- CN
- China
- Prior art keywords
- component
- resin
- orders
- dry
- mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a resin floor material and a process for constructing a circular arc angle of a floor on the scene. The resin floor material and the process for constructing the circular arc angle of the floor on the scene comprise main raw materials of a component A, a component B and a component C, wherein the component A comprises 90%-99% of resin and 1%-10% of diluent, the component B comprises a curing agent, the component C comprises dry mortar, and the weight ratio of component A to component B to component C is 2:1:24. A main construction tool is a circular-arc cutter or a pressing object with the radian being 30 degrees to 90 degrees. The components A, B and C are mixed uniformly firstly, and then the material is paved at a corner, the circular-arc cutter or the pressing object with proper angle is selected to compact the material, after the material is cured, finish paint is coated by a rotary drum or a screeding cutter, and after being cured, the material can be used. The resin material manufactured on the scene has the advantages that the attractiveness is achieved, cleaning dead angle does not exist when the floor is cleaned, bacteria can be prevented from growing, and the like, can be widely used for family decoration, and is particularly suitable for occasions such as food and medical systems which have higher requirements on cleanliness.
Description
Technical field
The present invention relates to floor material and construction technology thereof, the resin floor material of concrete a kind of field fabrication and the technology of using this floor material that arc chord angle is constructed thereof.
Background technology
Advantages such as that the resin material terrace of field fabrication has is attractive in appearance, wear-resisting, dustproof, shock resistance; But during cleaning ground; There is the corner or spot as yet untouched by a clean-up campaign to cause bacteria breed easily; Especially food, medical system etc. to the occasion that cleanliness factor is had relatively high expectations, all can be brought some harm and loss thereof in case infectation of bacteria occurs.
Summary of the invention
The present invention provides a kind of according to the deficiency of prior art and adopts the floor material that solvent-free system or water-based system material process and use this material the terrace arc chord angle to be carried out the technology of site operation; The resin material terrace that solves present field fabrication is not easy cleaning and has the corner or spot as yet untouched by a clean-up campaign, is prone to cause problems such as bacteria breed.
The invention provides a kind of resin material terrace arc chord angle construction technology of field fabrication, purpose is.
Terrace arc chord angle construction technology that a kind of resin material of field fabrication is seamless comprises A, B, C component, it is characterized in that the composition of each component and weight percent are following:
The A component
Resin 90%-99%
Thinner 1%-10%
B component solidifying agent 100%
C component dry-mix 100%
The weight ratio of said A, B, C component is 2: 1: 24
Wherein resin is any one among epoxy E51 resin (grand prosperous 128), vinyl resin (Jiangsu three wooden BS8170), the water-borne acrylic resin (Opel enlightening AC27401);
AGE reactive thinner (the broad chemical industry in Shanghai) or deionized water;
Solidifying agent is any one among polyetheramine solidifying agent (the deep HB2114 of nation in Guangzhou), aliphatic cyclic amine solidifying agent (gas 1784), fatty amine curing agent (Jia Dida EC130), polyamide curing agent (monarch river, Shanghai D0115), the aqueous polyurethane solidifying agent (sieve ground HDI);
Dry-mix is that silica sand, colorful quartz sands, building are husky, any one or among them several kinds among the oven dry river sand, natural river sand, silica powder, water-ground limestone, talcum powder, ordinary Portland cement mix.
Silica sand, colorful quartz sands, building particle diameter husky, that dry river sand and natural river sand are 20-40 order or 40-60 order or 60-80 order or 80-120 order in the said dry-mix; The particle diameter of silica powder is 260 orders or 325 orders or 400 orders; The particle diameter of water-ground limestone is 260 orders or 325 orders or 400 orders; Talcous particle diameter is 260 orders or 325 orders or 400 orders.
A kind of resin floor material of field fabrication described in the claim 1 that adopts carries out the technology that the terrace arc chord angle is constructed, and containing radian is 30 degree-90 degree round tools or pressing object, it is characterized in that according to following procedure:
(1). resin and the thinner prepared are stirred, be mixed with the A component, the weight percent of each material is in its mixed solution: resin 90%-99% thinner 1%-10%;
(2). take by weighing the B component, the weight of B component is 1/2 of A component gross weight, and A component and B component are mixed;
(3). take by weighing the C component dry-mix of 8 times of gross weights after the mixing of A, B component, the C component dry-mix that takes by weighing is added in the mixed solution of A, B component, it is stirred;
(4). the particle loaded fluid after A, B, C component mixed paves in the corner equably, selects the round tool that is complementary with the corner angle or flattens the object compacting, treats its curing;
(5). after the curing,, treat can use after finish paint solidifies at its external coating finish paint with steamed bun cutter or cylinder, wherein steamed bun cutter and cylinder all are the common instrument of building trade.
The material that resin floor material of the present invention adopts is solvent-free system or water-based system, good environmental protection; Through the terrace arc chord angle good looking appearance of resin floor material provided by the invention through round tool or the field fabrication of pressing object; And when cleaning ground, there is not the corner or spot as yet untouched by a clean-up campaign; And can prevent bacteria breed; Meet to the higher food of environmental requirement, medical system the occasion that can have relatively high expectations to cleanliness factor adaptable across food and medical system etc.
Embodiment
Below in conjunction with embodiment the present invention is done further detailed description.
Embodiment one:
A kind of resin floor material comprises A, B, C component, it is characterized in that the composition of each component and weight percent are following:
The component aqueous vinyl resin of A (Opel enlightening AC27401) 90%
Deionized water 10%
B component waterborne polyurethane solidifying agent (the inferior HDI in sieve ground) 100%
C component
The weight ratio of said A, B, C component is 2: 1: 24
The technology of constructing to the terrace arc chord angle in the resin floor material scene that a kind of above-mentioned composition is formed is characterized in that according to following procedure:
(1). 90% water-borne acrylic resin (Opel enlightening AC27401) and 10% deionized water and stirring is even, be mixed with the A component;
(2). take by weighing B component aqueous polyurethane solidifying agent (the inferior HDI in sieve ground), the B composition weight is 1/2 of an A component gross weight;
(3). take by weighing that the C of gross weight octuple forms dry-mix after the mixing of A, B component, wherein the composition of C component dry-mix and weight percent that each is formed are: particle diameter 40 orders-60 order silica sand 20%, particle diameter 60 orders-80 purpose natural river sand 20%, 80 orders-120 order colorful quartz sands 35%, 325 order water-ground limestones 10% and 425 ordinary Portland cements, 15% uniform mixing form.
(4). the C component dry-mix that will take by weighing is added in the mixed solution of A, B component; It is stirred; Particle loaded fluid after A, B, C component mixed paves in the corner equably, selects the round tool that is complementary with the corner angle or flattens object with its compacting, treats its curing;
(5) solidify after,, treat can use after the finish paint curing at its external coating finish paint with steamed bun cutter or cylinder
Embodiment two:
A kind of resin floor material comprises A, B, C component, it is characterized in that the composition of each component and weight percent are following:
A component epoxy E51 resin (grand prosperous 128) 90%
AGE reactive thinner (the broad chemical industry in Shanghai) 10%
B component aliphatic cyclic amine solidifying agent (gas 1784) 100%
C component
The weight ratio of said A, B, C component is 2: 1: 24
The technology of constructing to the terrace arc chord angle in a kind of resin floor material scene of using above-mentioned substance to form is characterized in that according to following procedure:
(1). with weight ratio is that 90% epoxy E51 resin (grand prosperous 128) and 10% AGE reactive thinner (the broad chemical industry in Shanghai) are even, is mixed with the A component;
(2). take by weighing B component aliphatic cyclic amine solidifying agent (gas 1784), the weight of B component is 1/2 of A component gross weight, then itself and the A component that configures is mixed A in the mixed solution: B=2: 1;
(3). take by weighing the C component dry-mix of gross weight octuple after the mixing of A, B component; Wherein C forms dry-mix by 40 orders-60 order colorful quartz sands 20%, 60 orders-80 order colorful quartz sands 30%, 80 orders-120 order colorful quartz sands 35%, 325 order silica powders 15%; The C component dry-mix that takes by weighing is added in the mixed solution of A, B component; It is stirred
(4) particle loaded fluid after A, B, C component are mixed paves in the corner equably, selects the round tool that is complementary with the corner angle or flattens object with its compacting, treats its curing;
(5). after the curing, at its external coating finish paint, treat can use after finish paint solidifies with steamed bun cutter or cylinder.
Embodiment three:
A kind of resin floor material comprises A, B, C component, it is characterized in that the composition of each component and weight percent are following:
A component epoxy E51 resin (grand prosperous 128) 95%
AGE reactive thinner (the broad chemical industry in Shanghai) 5%
B component fatty amine curing agent (Jia Dida EC130) 100%
C component silica sand 80-120 order 100%
The weight ratio of said A, B, C component is 2: 1: 24
The technology of constructing to the terrace arc chord angle in a kind of resin floor material scene of using above-mentioned substance to form is characterized in that according to following procedure:
(1). with weight ratio is that 95% epoxy E51 resin (grand prosperous 128) and 10% AGE reactive thinner (the broad chemical industry in Shanghai) are even, is mixed with the A component;
(2). take by weighing B component fatty amine curing agent (Jia Dida EC130), the weight of B component is 1/2 of A component gross weight, then itself and the A component that configures is mixed A in the mixed solution: B=2: 1;
(3). take by weighing that the C component particle diameter of gross weight octuple is a 80-120 purpose silica sand after the mixing of A, B component, the C component silica sand that takes by weighing is added in the mixed solution of A, B component, it is stirred;
(4). the particle loaded fluid after A, B, C component mixed paves in the corner equably, selects the round tool that is complementary with the corner angle or flattens object with its compacting, treats its curing;
(5). after the curing, at its external coating finish paint, treat can use after finish paint solidifies with steamed bun cutter or cylinder.
Claims (3)
1. a resin floor material comprises A, B, C component, it is characterized in that the composition of each component and weight percent are following:
The A component
Resin 90%-99%
Thinner 1%-10%
B component solidifying agent 100%
C component dry-mix 100%
The weight ratio of said A, B, C component is 2: 1: 24
Wherein resin is any one among epoxy E51 resin, vinyl resin, the water-borne acrylic resin;
Thinner is AGE reactive thinner or deionized water;
Solidifying agent is any one among polyetheramine solidifying agent, aliphatic cyclic amine solidifying agent, fatty amine curing agent, polyamide curing agent, the aqueous polyurethane solidifying agent;
Dry-mix is that silica sand, colorful quartz sands, building are husky, any one or among them several kinds in the oven dry river sand, natural river sand, silica powder, water-ground limestone, talcum powder, ordinary Portland cement mix.
2. a kind of resin floor material according to claim 1 is characterized in that: silica sand, colorful quartz sands, building particle diameter husky, that dry river sand and natural river sand are 20-40 order or 40-60 order or 60-80 order or 80-120 order in the said dry-mix; The particle diameter of silica powder is 260 orders or 325 orders or 400 orders; The particle diameter of water-ground limestone is 260 orders or 325 orders or 400 orders; Talcous particle diameter is 260 orders or 325 orders or 400 orders.
3. technology that adopts the resin floor material scene described in the claim 1 that the terrace arc chord angle is constructed, to contain radian be 30 degree-90 degree round tools or flatten object, it is characterized in that according to procedure down:
(1) resin and the thinner prepared are stirred, be mixed with the A component, the weight percent of each material is in its mixed solution: resin 90%-99% thinner 1%-10%;
(2) take by weighing the B component, the weight of B component is 1/2 of A component gross weight, and A component and B component are mixed;
(3) take by weighing the C component dry-mix of 8 times of gross weights after the mixing of A, B component, the C component dry-mix that takes by weighing is added in the mixed solution of A, B component, it is stirred;
(4) particle loaded fluid after A, B, C component are mixed paves in the corner equably, selects the round tool that is complementary with the corner angle or flattens object with its compacting, treats its curing;
(5) solidify after,, treat can use after the finish paint curing at its external coating finish paint with steamed bun cutter or cylinder.