CN104673031B - Coating material for inorganic non-metallic or metallic surfaces - Google Patents
Coating material for inorganic non-metallic or metallic surfaces Download PDFInfo
- Publication number
- CN104673031B CN104673031B CN201510058034.0A CN201510058034A CN104673031B CN 104673031 B CN104673031 B CN 104673031B CN 201510058034 A CN201510058034 A CN 201510058034A CN 104673031 B CN104673031 B CN 104673031B
- Authority
- CN
- China
- Prior art keywords
- agent
- mass ratio
- linan
- global
- dispersant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a coating material for inorganic non-metallic or metallic surfaces. The coating material comprises a priming material and a facing material, wherein the priming material is prepared from the following raw materials in percentage by weight: 20-50% of a water-based resin emulsion, 10-40% of an inorganic heat insulating micropowder or mineral micropowder, 0.1-5% of an additive and the balance of water, and the facing material is prepared from the following raw materials in percentage by weight: 5-20% of hollow beads, 5-20% of nano titanium dioxide, 5-20% of a mineral micropowder or metal micropowder, 0.1-10% of silica aerogel, 5-50% of a mixed aqueous polymer emulsion, 0.1-10% of an additive, 0-10% of a pigment or color paste and the balance of water. The coating material provided by the invention is an environment-friendly aqueous emulsion, has multiple functions of reflecting, insulating heat, self-cleaning, resisting corrosion, weathering, acids, alkalis and water and thoroughly overcomes the defects of the existing facing protection coatings which are poor in functions of reflecting, heat insulating, secondary heat insulating, self-cleaning and corrosion, weathering, acid, alkali and water resisting.
Description
Technical field
The present invention relates to a kind of coating material for inorganic non-metallic surface or metal surface, belong to chemical material neck
Domain.
Background technology
With scientific and technical progress, various energy-saving materials emerge in an endless stream, and wherein, heat insulating coatings are as power saving function
The typical case of coating, by the common concern of insider and obtain obvious development.The Main Function of heat insulating coatings is resistance
The only intrusion that is lost and stoping extraneous solar energy of self heat.Especially southern area illumination is strong, temperature is high, and rainwater is many,
It is thus desirable to the coating of good heat-insulation effect, to stop the invasion of extraneous solar energy intercept heat transmission.
Reflective insulation is mainly reflected sunlight heat, and the transmission of sunlight heat and radiation typically can be divided into four by wavelength
Point, wherein, 10~400 μm of ultraviolet region wavelength, account for the 5% of sunlight heat;400~720 μm of visible region wavelength, accounts for too
The 45% of solar heat;720~2500 μm of far red light area, accounts for more than 2500 μm of the 45% mid and far infrared light area of sunlight heat,
Account for the 5% of sunlight heat.Therefore, any reflection heat resistant material can reflect away more than 85% sunlight heat, intercept simultaneously
Transmitting and having long-term weatherability of sunlight heat remainder heat energy is exactly to be worth using for reference the quality product promoted.
Existing reflective insulation class coating or patent, including there being fluorine-containing cf key in the material molecule of disposal of pollutants to environment
Solvent material, substantially disclosure satisfy that requirement in terms of sunlight heat reflection, but for penetrating and absorbed sunlight heat
Lack enough obstructing capacities, especially in material molecule, the compound coat of not fluorine-containing cf key is easily aging, some are deficient for weatherability
Lack, color is single, increased many uncertain maintenance costs and potential safety hazard.
Content of the invention
The technical problem to be solved is to provide a kind of coating for inorganic non-metallic surface or metal surface
Material, this coating material is a kind of aqueous emulsion ep-type material, has reflection, adiabatic, anti-corrosion, acid and alkali-resistance, waterproof, self-cleaning, resistance to
Hou Xing etc. is multi-functional, thoroughly solve the reflective insulation of existing facing protective coating, secondary adiabatic, anti-corrosion, acid and alkali-resistance, waterproof,
Self-cleaning, weather-proof sex chromosome mosaicism.
The technical scheme is that a kind of be used for inorganic non-metallic surface or metal surface
Coating material, including facing primer and facing layer material, wherein,
Based on the percentage composition of facing primer raw material gross weight, it is made up of the following raw material:
Resin aqueous emulsion 20~50%, inorganic thermal insulation micropowder and mineral micro powder 10~40%, additive 0.1~5%, remaining
Measure as tap water,
Based on the percentage composition of facing layer material raw material gross weight, it is made up of the following raw material:
Hollow beads 5~20%, nano titanium oxide 5~20%, mineral micro powder and metal fine powder 5~20%, silicon airsetting
Glue 0.1~10%, polymer mixed aqueous emulsion 5~50%, auxiliary agent 0.1~10%, pigment or mill base 0~10%, clout is water.
On the basis of technique scheme, the present invention can also do following improvement.
Further, in the raw material of facing primer forms, described resin aqueous emulsion is pure-acrylic emulsion, silicone acrylic emulsion
One of or two kinds of mixture;
Further, in the raw material of facing primer forms, described inorganic thermal insulation micropowder and breeze micropowder are aluminium powder, weigh
The mixture of one or more of spar, cordierite, mica powder, kieselguhr, particle diameter is 100nm~20 μm;
Further, in the raw material of facing primer forms, described additive is dispersant, levelling agent, preservative, anti-
The mixture of one or more of water preparation.
Further, in the raw material of facing layer material forms, described hollow beads are floating bead, glass microballoon, ceramic fine bead
One or more of mixture;
Further, in the raw material of facing layer material forms, described mineral micro powder and metal fine powder are barite, violet is blue or green
The mixture of one or more of stone, aluminium powder, particle diameter is 100nm~20 μm.
Further, in the raw material of facing layer material forms, described silica aerogel is that German hoechst company produces;
Further, facing layer material raw material form in, described polymer mixed aqueous emulsion be polymer pure-acrylic emulsion,
The mixture of one or more of silicone acrylic emulsion, polymerization fluorine emulsion;
Further, in the raw material of facing layer material forms, described auxiliary agent is dispersant, levelling agent, rheological agent, defoamer
One or more of mixture.
The invention has the beneficial effects as follows:
The facing primer that the present invention provides is with the heat-insulated micropowder of resin aqueous emulsion composite inorganic, breeze micropowder, interpolation
Agent and water composition, through brushing construction form auxiliary reflective insulation layer, this auxiliary reflective insulation layer, have auxiliary reflection, heat-insulated, anti-
Corruption, acid and alkali-resistance, water-proof function, can be bondd with basic unit and finish coat in perfection;
Facing layer material with hollow beads, nano titanium oxide, mineral micro powder and metal fine powder for reflected radiation material, with
Silica aerogel is adiabator, with polymer mixed aqueous emulsion as film former, adds colorant or pigment, is aided with auxiliary agent, through brushing
Construction form heat reflecting and insulating layer, this coating have suppression solar radiant heat, infrared radiant heat, cut-off heat conduction reflection exhausted
Hot merit energy, has the multi-functional ring of anti-corrosion, acid and alkali-resistance, splendid resistance to water, overlength weatherability, self-cleaning and contaminated resistance simultaneously
Water-retaining property coating.
Brief description
Fig. 1 is a kind of composite coating structure schematic diagram for inorganic non-metallic surface or metal surface;
In accompanying drawing, the list of parts representated by each label is as follows:
1st, basic unit, 2, facing bottom, 3, finish coat.
Specific embodiment
Hereinafter the principle and feature of the present invention is described, example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
In example below, silica aerogel used is that German hoechst company produces;
The raw material composition of 13 embodiment facing bottoms of table and performance test
Wherein, resin aqueous emulsion is made up of with silicone acrylic emulsion 1:1 in mass ratio pure-acrylic emulsion;
Inorganic thermal insulation micropowder and mineral micro powder are by aluminium powder, barite, cordierite, mica powder, kieselguhr 1:1 in mass ratio:
1:1:1 forms, particle diameter 100nm~20 μm;
Additive is made up of dispersant, levelling agent, preservative, waterproofing agent 4:3:2:1 in mass ratio, and dispersant is Linan ring
Space dispersant 300, levelling agent is Linan global non-organic silicon levelling agent 358, and preservative is Linan global preservative tm-8, waterproof
Agent is German watt gram waterproofing agent of organosilicon.
By the raw material mix homogeneously in table 1, form auxiliary reflective insulation layer through brushing construction, measure auxiliary reflective insulation layer
Performance indications as shown in table 1.
The raw material composition of 23 embodiment finish coats of table and performance test
Hollow beads are made up of floating bead, glass microballoon, ceramic fine bead 1:1:1 in mass ratio;
Mineral micro powder and metal fine powder are made up of barite, cordierite, aluminium powder 3:3:4 in mass ratio;
Aqueous polymer dispersion is by polymer pure-acrylic emulsion, silicone acrylic emulsion, polymerization fluorine emulsion 3.5:3.5:3 group in mass ratio
Become;
Auxiliary agent is made up of dispersant, levelling agent, rheological agent, defoamer 4:3:2:1 in mass ratio, and dispersant is that Linan is global
Dispersant 300, levelling agent is Linan global non-organic silicon levelling agent 358, and rheological agent is organobentonite, and defoamer is Linan ring
Space defoamer ac-202.
By the raw material mix homogeneously in table 2, form heat reflecting and insulating layer through brushing construction, measure the property of heat reflecting and insulating layer
Energy index is as shown in table 2.
As shown in figure 1, a kind of composite coating structure for inorganic non-metallic surface or metal surface, by basic unit 1, facing
Bottom 2 and finish coat 3 form, wherein,
Basic unit 1 is Inorganic Non-metallic Materials or metal material, basic unit should be cleared up during construction,
Facing bottom 2, takes the facing primer of above-described embodiment preparation, electric stirring, batch extension or roller coating construction, coating
Surface in basic unit.
Finish coat 3, when facing bottom moisture content is less than 5%, takes the facing layer material of above-described embodiment preparation, electric mixing
Mix, carry out roller coating construction, be coated on facing bottom.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement made etc., should be included within the scope of the present invention.
Claims (3)
1. a kind of coating material for inorganic non-metallic surface or metal surface is it is characterised in that include facing primer
And facing layer material, wherein,
Based on the percentage composition of facing primer raw material gross weight, it is made up of the following raw material:
Resin aqueous emulsion 33%, inorganic thermal insulation micropowder and mineral micro powder 46%, additive 4.5%, water surplus from the beginning, wherein,
Resin aqueous emulsion is made up of with silicone acrylic emulsion 1:1 in mass ratio pure-acrylic emulsion, inorganic thermal insulation micropowder and mineral micro powder by aluminium powder,
Barite, cordierite, mica powder, kieselguhr 1:1:1:1:1 in mass ratio forms, particle diameter 100nm~20 μm, and additive is by disperseing
Agent, levelling agent, preservative, waterproofing agent 4:3:2:1 in mass ratio forms, and dispersant is the global dispersant in Linan 300, and levelling agent is
Linan global non-organic silicon levelling agent 358, preservative is Linan global preservative tm-8, and waterproofing agent is that German watt gram organosilicon is prevented
Water preparation;
Based on the percentage composition of facing layer material raw material gross weight, it is made up of the following raw material:
Hollow beads 7.5%, nanometer tio221%, mineral micro powder and metal fine powder 24%, silica aerogel 4.5%, polymer water and milk
Liquid 36%, auxiliary agent 0.5%, water surplus, wherein, hollow beads are by floating bead, glass microballoon, ceramic fine bead 1:1:1 group in mass ratio
Become, mineral micro powder and metal fine powder are made up of barite, cordierite, aluminium powder 3:3:4 in mass ratio, aqueous polymer dispersion is by being polymerized
Thing pure-acrylic emulsion, silicone acrylic emulsion, polymerization fluorine emulsion 3.5:3.5:3 in mass ratio composition, auxiliary agent is by dispersant, levelling agent, rheology
Agent, defoamer 4:3:2:1 in mass ratio forms, and dispersant is the global dispersant in Linan 300, and levelling agent is the global non-organic in Linan
Silicon levelling agent 358, rheological agent is organobentonite, and defoamer is Linan global defoamer ac-202, and silica aerogel used is moral
Hoechst company of state produces.
2. a kind of coating material for inorganic non-metallic surface or metal surface is it is characterised in that include facing primer
And facing layer material, wherein,
Based on the percentage composition of facing primer raw material gross weight, it is made up of the following raw material:
Resin aqueous emulsion 42%, inorganic thermal insulation micropowder and mineral micro powder 43%, additive 4%, water surplus from the beginning, wherein, water
Property resin emulsion be made up of with silicone acrylic emulsion 1:1 in mass ratio pure-acrylic emulsion, inorganic thermal insulation micropowder and mineral micro powder are by aluminium powder, weight
Spar, cordierite, mica powder, kieselguhr 1:1:1:1:1 in mass ratio forms, particle diameter 100nm~20 μm, and additive is by disperseing
Agent, levelling agent, preservative, waterproofing agent 4:3:2:1 in mass ratio forms, and dispersant is the global dispersant in Linan 300, and levelling agent is
Linan global non-organic silicon levelling agent 358, preservative is Linan global preservative tm-8, and waterproofing agent is that German watt gram organosilicon is prevented
Water preparation;
Based on the percentage composition of facing layer material raw material gross weight, it is made up of the following raw material:
Hollow beads 9.8%, nanometer tio214%, mineral micro powder and metal fine powder 21%, silica aerogel 6.2%, polymer water and milk
Liquid 40%, auxiliary agent 0.5%, pigment or mill base 2%, water surplus, wherein, hollow beads are pressed by floating bead, glass microballoon, ceramic fine bead
Mass ratio 1:1:1 forms, and mineral micro powder and metal fine powder are made up of barite, cordierite, aluminium powder 3:3:4 in mass ratio, polymerization
Thing aqueous emulsion is made up of polymer pure-acrylic emulsion, silicone acrylic emulsion, polymerization fluorine emulsion 3.5:3.5:3 in mass ratio, and auxiliary agent is by disperseing
Agent, levelling agent, rheological agent, defoamer 4:3:2:1 in mass ratio forms, and dispersant is the global dispersant in Linan 300, and levelling agent is
Linan global non-organic silicon levelling agent 358, rheological agent is organobentonite, and defoamer is Linan global defoamer ac-202, institute
It is that German hoechst company produces with silica aerogel.
3. a kind of coating material for inorganic non-metallic surface or metal surface is it is characterised in that include facing primer
And facing layer material, wherein,
Based on the percentage composition of facing primer raw material gross weight, it is made up of the following raw material:
Resin aqueous emulsion 47%, inorganic thermal insulation micropowder and mineral micro powder 40%, additive 3.5%, water surplus from the beginning, wherein,
Resin aqueous emulsion is made up of with silicone acrylic emulsion 1:1 in mass ratio pure-acrylic emulsion, inorganic thermal insulation micropowder and mineral micro powder by aluminium powder,
Barite, cordierite, mica powder, kieselguhr 1:1:1:1:1 in mass ratio forms, particle diameter 100nm~20 μm, and additive is by disperseing
Agent, levelling agent, preservative, waterproofing agent 4:3:2:1 in mass ratio forms, and dispersant is the global dispersant in Linan 300, and levelling agent is
Linan global non-organic silicon levelling agent 358, preservative is Linan global preservative tm-8, and waterproofing agent is that German watt gram organosilicon is prevented
Water preparation;
Based on the percentage composition of facing layer material raw material gross weight, it is made up of the following raw material:
Hollow beads 12%, nanometer tio210.5%, mineral micro powder and metal fine powder 15%, silica aerogel 7.5%, polymer water
Emulsion 44%, auxiliary agent 0.5%, pigment or mill base 5%, water surplus, hollow beads press matter by floating bead, glass microballoon, ceramic fine bead
Than 1:1:1 composition, mineral micro powder and metal fine powder are made up of amount barite, cordierite, aluminium powder 3:3:4 in mass ratio, polymer
Aqueous emulsion by polymer pure-acrylic emulsion, silicone acrylic emulsion, polymerization fluorine emulsion 3.5:3.5:3 in mass ratio form, auxiliary agent by dispersant,
Levelling agent, rheological agent, defoamer 4:3:2:1 in mass ratio forms, and dispersant is the global dispersant in Linan 300, and levelling agent is to face
Pacify global non-organic silicon levelling agent 358, rheological agent is organobentonite, defoamer is Linan global defoamer ac-202, used
Silica aerogel is that German hoechst company produces.