CN104559475A - 一种印刷油墨 - Google Patents
一种印刷油墨 Download PDFInfo
- Publication number
- CN104559475A CN104559475A CN201410763913.9A CN201410763913A CN104559475A CN 104559475 A CN104559475 A CN 104559475A CN 201410763913 A CN201410763913 A CN 201410763913A CN 104559475 A CN104559475 A CN 104559475A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing
- ink
- minute
- ethyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种印刷油墨,包括如下重量份数的组分:钛白份1-3份、异丙醇2-4份、乙酸乙酯1-3份、树脂1-3份、无机微粒2-4份、聚烯烃蜡3-5份、阳离子光引发剂2-4份和着色剂1-3份。本发明提供的一种印刷油墨,印刷效果好,并且对人体无危害。
Description
技术领域
本发明涉及印刷领域,具体涉及一种印刷油墨。
背景技术
油墨的颜色(色相)、身骨(稀稠、流动度等流变性能)和干燥性能是油墨的三个最重要的性能。它们的种类很多,物理性质亦不一样,有的很稠、很粘;而有的却相当稀。有的以植物油作连结料;有的用树脂和溶剂或水等作连结料。这些都是根据印刷的对象即承印物、印刷方法、印刷版材的类型和干燥方法等来决定。
油墨的干燥速度、触变性、骨架性能对生产效率、产品质量有着巨大的影响,而且油墨的成分对人体有影响,如何研究对人体危害尽量小、生产效率高、环境友好、成本低的油墨有着深远的意义。
发明内容
综上所述,本发明所要解决的技术问题是提供一种印刷油墨。
本发明解决上述技术问题的技术方案如下:一种印刷油墨,包括如下重量份数的组分:钛白份1-3份、异丙醇2-4份、乙酸乙酯1-3份、树脂1-3份、无机微粒2-4份、聚烯烃蜡3-5份、阳离子光引发剂2-4份和着色剂1-3份。
一种印刷油墨的制作方法,包括如下的步骤:
(1)按如下重量份数分别取得各组分:钛白份1-3份、异丙醇2-4份、乙酸乙酯1-3份、树脂1-3份、无机微粒2-4份、聚烯烃蜡3-5份、阳离子光引发剂2-4份和着色剂1-3份;
(2)将钛白粉、异丙醇、乙酸乙酯、树脂、无机微粒、聚烯烃蜡混合搅拌10-15分钟;
(3)加热到70℃后,加入离子光引发剂和着色剂反应5-10分钟;
(4)继续搅拌3-5分钟,研磨分散成浆料,即得。
进一步,步骤(2)的搅拌速度为400-800转/分。
进一步,步骤(3)的加热速度为2-4℃/分。
本发明的有益效果是:本发明提供的一种印刷油墨,印刷效果好,并且对人体无危害。
具体实施方式
以下结合具体实例对本发明的原理和特征进行描述,所举实例只用于解释本发明,并非用于限定本发明的范围。
实施例1
一种印刷油墨的制作方法,包括如下的步骤:
(1)按如下重量份数分别取得各组分:钛白粉1份、异丙醇2份、乙酸乙酯1份、树脂1份、无机微粒2份、聚烯烃蜡3份、阳离子光引发剂2份和着色剂1份;
(2)将钛白粉、异丙醇、乙酸乙酯、树脂、无机微粒、聚烯烃蜡混合搅拌10分钟,搅拌速度为400转/分;
(3)以加热速度为2℃/分加热到70℃后,加入离子光引发剂和着色剂反应5分钟;
(4)继续搅拌3分钟,研磨分散成浆料,即得。
实施例2
一种印刷油墨的制作方法,包括如下的步骤:
(1)按如下重量份数分别取得各组分:钛白粉2份、异丙醇3份、乙酸乙酯2份、树脂2份、无机微粒3份、聚烯烃蜡4份、阳离子光引发剂3份和着色剂2份;
(2)将钛白粉、异丙醇、乙酸乙酯、树脂、无机微粒、聚烯烃蜡混合搅拌12分钟,搅拌速度为500转/分;
(3)以加热速度为3℃/分加热到70℃后,加入离子光引发剂和着色剂反应7分钟;
(4)继续搅拌4分钟,研磨分散成浆料,即得。
实施例3
一种印刷油墨的制作方法,包括如下的步骤:
(1)按如下重量份数分别取得各组分:钛白粉3份、异丙醇4份、乙酸乙酯3份、树脂3份、无机微粒4份、聚烯烃蜡5份、阳离子光引发剂4份和着色剂3份;
(2)将钛白粉、异丙醇、乙酸乙酯、树脂、无机微粒、聚烯烃蜡混合搅拌15分钟,搅拌速度为800转/分;
(3)以加热速度为4℃/分加热到70℃后,加入离子光引发剂和着色剂反应10分钟;
(4)继续搅拌5分钟,研磨分散成浆料,即得。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (4)
1.一种印刷油墨,其特征在于,包括如下重量份数的组分:钛白粉1-3份、异丙醇2-4份、乙酸乙酯1-3份、树脂1-3份、无机微粒2-4份、聚烯烃蜡3-5份、阳离子光引发剂2-4份和着色剂1-3份。
2.一种印刷油墨的制作方法,其特征在于,包括如下的步骤:
(1)按如下重量份数分别取得各组分:钛白粉1-3份、异丙醇2-4份、乙酸乙酯1-3份、树脂1-3份、无机微粒2-4份、聚烯烃蜡3-5份、阳离子光引发剂2-4份和着色剂1-3份;
(2)将钛白粉、异丙醇、乙酸乙酯、树脂、无机微粒、聚烯烃蜡混合搅拌10-15分钟;
(3)加热到70℃后,加入离子光引发剂和着色剂反应5-10分钟;
(4)继续搅拌3-5分钟,研磨分散成浆料,即得。
3.根据权利要求2所述的一种印刷油墨的制作方法,其特征在于,步骤(2)的搅拌速度为400-800转/分。
4.根据权利要求2所述的一种印刷油墨的制作方法,其特征在于,步骤(3)的加热速度为2-4℃/分。