CN104550908A - 一种阀门用防开裂铁基粉末冶金材料及其制备方法 - Google Patents

一种阀门用防开裂铁基粉末冶金材料及其制备方法 Download PDF

Info

Publication number
CN104550908A
CN104550908A CN201410818824.XA CN201410818824A CN104550908A CN 104550908 A CN104550908 A CN 104550908A CN 201410818824 A CN201410818824 A CN 201410818824A CN 104550908 A CN104550908 A CN 104550908A
Authority
CN
China
Prior art keywords
parts
powder
valve
minute
iron
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410818824.XA
Other languages
English (en)
Inventor
吴寿涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Jingwei Fluid Technology Co Ltd
Original Assignee
Tongling Jingwei Fluid Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Jingwei Fluid Technology Co Ltd filed Critical Tongling Jingwei Fluid Technology Co Ltd
Priority to CN201410818824.XA priority Critical patent/CN104550908A/zh
Publication of CN104550908A publication Critical patent/CN104550908A/zh
Pending legal-status Critical Current

Abstract

一种阀门用防开裂铁基粉末冶金材料，由下列重量份的原料制成：硬脂酸硼0.2-0.4、铝镍合金粉3-4、镀镍碳化硅晶须3-4、TiO2？3-4、气相二氧化硅1-1.5？、棕榈蜡0.4-0.6、纳米硼纤维1-2.6、堇青石粉1-1.5、钛酸铝2-2.6、硅烷偶联剂kh-550？0.3-0.4、1%碳酸钠溶液适量、水适量、次亚磷酸钠2.5-3.5、聚乙二醇0.4-0.6、2Mol/L硫酸铜溶液30-35、润湿助剂2-3、铁粉77-82；本发明阀门材料添加了纳米硼纤维、镀镍碳化硅晶须，增加了阀门材料韧性、耐热性和耐冲击强度的同时，也增加了相容性，防止开裂。

Description

一种阀门用防开裂铁基粉末冶金材料及其制备方法
技术领域
本发明涉及粉末冶金技术领域，尤其涉及一种阀门用防开裂铁基粉末冶金材料及其制备方法。
背景技术
阀门是在流体***中，用来控制流体的方向、压力、流量的装置，是使配管和设备内的介质（液体、气体、粉末）流动或停止并能控制其流量的装置。当阀门通过的介质和工况不一样时对阀门材质有着不同的要求，对材料的耐温性、耐腐蚀性、强度等性能有不同的要求。阀门的工作压力可从0.0013MPa到1000MPa 的超高压，工作温度从-270℃的超低温到1430℃的高温。
阀门材料可以用粉末冶金材料制作，但是普通铁粉末冶金材料耐热、耐腐蚀性较差，承重性差，强度、硬度、耐冲击性等力学性能不够高。在铁基粉末冶金材料中加入瓷粉等非金属相，可以改善材料的耐热性、耐腐蚀性，提高硬度，提高抗氧化性，提高抗蠕变性能。但是由于非金属相和金属相相容性差，易使成分出现偏析，组织均匀性差，强度不均匀，出现花斑，磨合性差，耐磨性差，不能承受较大的压力，热衰严重，抗裂纹性能差，抗冷热疲劳性能差，使用寿命短。
可以通过改变原料来改善铁基粉末冶金材料的性能，还可以通过改善非金属相和金属相的相容性来改善材料的性能。
发明内容
本发明的目的在于提供一种阀门用防开裂铁基粉末冶金材料及其制备方法，该阀门材料韧性、耐热性好，耐冲击强度高，相容性好，防止开裂。
本发明的技术方案如下：
一种阀门用防开裂铁基粉末冶金材料，其特征在于由下列重量份的原料制成：硬脂酸硼0.2-0.4、铝镍合金粉3-4、镀镍碳化硅晶须3-4、TiO2 3-4、气相二氧化硅1-1.5 、棕榈蜡0.4-0.6、纳米硼纤维1-2.6、堇青石粉1-1.5、钛酸铝2-2.6、硅烷偶联剂kh-550 0.3-0.4、1%碳酸钠溶液适量、水适量、次亚磷酸钠2.5-3.5、聚乙二醇0.4-0.6、2Mol/L硫酸铜溶液30-35、润湿助剂2-3、铁粉77-82；
所述润湿助剂由下列重量份的原料制成：K2ZrF6 1-2、V2O52-3、纳米银0.8-1.4、TiN0.4-0.6、MoO3 3-4、纳米云母粉0.6-0.9、水8-10、聚乙二醇0.1-0.2；制备方法为：将聚乙二醇加入水中，搅拌均匀后加入纳米银，搅拌20-30分钟，超声分散3-4分钟，再加入其它剩余成分，在7000-8000转/分下搅拌10-15分钟，超声分散4-5分钟，在120-130℃油浴中搅拌至绝干，粉碎，过80目筛，即得。
所述阀门用防开裂铁基粉末冶金材料的制备方法，其特征在于包括以下步骤：
（1）将TiO2、气相二氧化硅、纳米硼纤维、堇青石粉、钛酸铝混合，加入3-4倍重量份的1%碳酸钠溶液中，加热至40-50℃，搅拌10-15分钟，过滤，加入3-4倍重量份的水洗涤，重复洗涤2-3次，过滤，得到滤饼；
（2）将滤饼与润湿助剂混合，研磨30-40分钟，加入4-5倍重量份的水，加入硅烷偶联剂kh-550，搅拌10-15分钟，加热至60-70℃，再加入纳米铁，搅拌30-40分钟，过滤，在氢气氛围下喷雾干燥，粉碎，过130目筛，得到粉末；
（3）将第（2）步得到的粉末加入2Mol/L硫酸铜溶液中，加入聚乙二醇、次亚磷酸钠，加热至60-70℃，搅拌反应1-2个小时，过滤，用水洗涤至中性，通入氢气干燥，粉碎，得到粉末；
（4）将第（3）步得到的粉末与其他剩余成分混合、球磨、成形、烧结、精整加工，即得。
本发明的有益效果
本发明阀门材料添加了纳米硼纤维、镀镍碳化硅晶须，增加了阀门材料韧性、耐热性和耐冲击强度的同时，也增加了相容性，防止开裂，本发明制作工艺使得金属相与非金属相相互穿插，紧密结合，增加了非金属相与金属相的润湿性和粘结性，能够防止成分偏析，使得材料组织均匀，增加了强度和韧性；通过使用本发明的润湿助剂，能够增加金属对非金属相的润湿性能，增加阀门的疲劳强度和韧性。
具体实施方式
一种阀门用防开裂铁基粉末冶金材料，由下列重量（公斤）的原料制成：硬脂酸硼0.3、铝镍合金粉3.5、镀镍碳化硅晶须3.5、TiO2 3.5、气相二氧化硅1.3 、棕榈蜡0.5、纳米硼纤维1.8、堇青石粉1.4、钛酸铝2.4、硅烷偶联剂kh-550 0.3、1%碳酸钠溶液适量、水适量、次亚磷酸钠3、聚乙二醇0.5、2Mol/L硫酸铜溶液33、润湿助剂2.5、铁粉79；
所述润湿助剂由下列重量份（公斤）的原料制成：K2ZrF6 1.5、V2O52.5、纳米银1.1、TiN0.4-0.6、MoO3 3.5、纳米云母粉0.8、水9、聚乙二醇0.1；制备方法为：将聚乙二醇加入水中，搅拌均匀后加入纳米银，搅拌25分钟，超声分散3分钟，再加入其它剩余成分，在7500转/分下搅拌14分钟，超声分散5分钟，在125℃油浴中搅拌至绝干，粉碎，过80目筛，即得。
所述阀门用防开裂铁基粉末冶金材料的制备方法，包括以下步骤：
（1）将TiO2、气相二氧化硅、纳米硼纤维、堇青石粉、钛酸铝混合，加入3.5倍重量份的1%碳酸钠溶液中，加热至45℃，搅拌14分钟，过滤，加入3.5倍重量份的水洗涤，重复洗涤3次，过滤，得到滤饼；
（2）将滤饼与润湿助剂混合，研磨35分钟，加入4.5倍重量份的水，加入硅烷偶联剂kh-550，搅拌13分钟，加热至65℃，再加入纳米铁，搅拌35分钟，过滤，在氢气氛围下喷雾干燥，粉碎，过130目筛，得到粉末；
（3）将第（2）步得到的粉末加入2Mol/L硫酸铜溶液中，加入聚乙二醇、次亚磷酸钠，加热至65℃，搅拌反应1.5个小时，过滤，用水洗涤至中性，通入氢气干燥，粉碎，得到粉末；
（4）将第（3）步得到的粉末与其他剩余成分混合、球磨、成形、烧结、精整加工，即得。
实验数据：
经测试该实施例阀门材料的硬度HB为62，致密度为95.17%，空隙率9.11%，断裂韧性为12.6MPa·m1/2,抗压强度为155MPa，抗弯强度为496MPa。

Claims (2)

1.一种阀门用防开裂铁基粉末冶金材料，其特征在于由下列重量份的原料制成：硬脂酸硼0.2-0.4、铝镍合金粉3-4、镀镍碳化硅晶须3-4、TiO2 3-4、气相二氧化硅1-1.5 、棕榈蜡0.4-0.6、纳米硼纤维1-2.6、堇青石粉1-1.5、钛酸铝2-2.6、硅烷偶联剂kh-550 0.3-0.4、1%碳酸钠溶液适量、水适量、次亚磷酸钠2.5-3.5、聚乙二醇0.4-0.6、2Mol/L硫酸铜溶液30-35、润湿助剂2-3、铁粉77-82；
所述润湿助剂由下列重量份的原料制成：K2ZrF6 1-2、V2O52-3、纳米银0.8-1.4、TiN0.4-0.6、MoO3 3-4、纳米云母粉0.6-0.9、水8-10、聚乙二醇0.1-0.2；制备方法为：将聚乙二醇加入水中，搅拌均匀后加入纳米银，搅拌20-30分钟，超声分散3-4分钟，再加入其它剩余成分，在7000-8000转/分下搅拌10-15分钟，超声分散4-5分钟，在120-130℃油浴中搅拌至绝干，粉碎，过80目筛，即得。
2.根据权利要求1所述阀门用防开裂铁基粉末冶金材料的制备方法，其特征在于包括以下步骤：
（1）将TiO2、气相二氧化硅、纳米硼纤维、堇青石粉、钛酸铝混合，加入3-4倍重量份的1%碳酸钠溶液中，加热至40-50℃，搅拌10-15分钟，过滤，加入3-4倍重量份的水洗涤，重复洗涤2-3次，过滤，得到滤饼；
（2）将滤饼与润湿助剂混合，研磨30-40分钟，加入4-5倍重量份的水，加入硅烷偶联剂kh-550，搅拌10-15分钟，加热至60-70℃，再加入纳米铁，搅拌30-40分钟，过滤，在氢气氛围下喷雾干燥，粉碎，过130目筛，得到粉末；
（3）将第（2）步得到的粉末加入2Mol/L硫酸铜溶液中，加入聚乙二醇、次亚磷酸钠，加热至60-70℃，搅拌反应1-2个小时，过滤，用水洗涤至中性，通入氢气干燥，粉碎，得到粉末；
（4）将第（3）步得到的粉末与其他剩余成分混合、球磨、成形、烧结、精整加工，即得。
CN201410818824.XA 2014-12-25 2014-12-25 一种阀门用防开裂铁基粉末冶金材料及其制备方法 Pending CN104550908A (zh)