CN104532441A - Production method of shape memory cotton fabric - Google Patents
Production method of shape memory cotton fabric Download PDFInfo
- Publication number
- CN104532441A CN104532441A CN201410640050.6A CN201410640050A CN104532441A CN 104532441 A CN104532441 A CN 104532441A CN 201410640050 A CN201410640050 A CN 201410640050A CN 104532441 A CN104532441 A CN 104532441A
- Authority
- CN
- China
- Prior art keywords
- shape memory
- cotton
- production method
- cotton fabric
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a production method of a shape memory cotton fabric. The production method is that cotton fibers, polyurethane fibers and memory alloy wrapping wires are used as the raw materials and dyed and sized to prepare the shape memory cotton fabric through a plain structure. The production method comprises the steps of combining the cotton fibers, the polyurethane fibers and the memory alloy wrapping wires, and twisting to be used as wefts; treating cotton fibers as wraps; weaving the wefts and the warps through the plain structure to obtain a shape memory gray fabric; then preprocessing; dyeing; washing with soap water; drying and sizing to obtain the shape memory cotton fabric. The shape memory cotton fabric prepared by the method has the shape memory function, remains the characteristics of cotton fabrics, is hygroscopic, breathable and heat preserved, and particularly suitable for baby products, maternity dresses and bedding articles.
Description
Technical field:
The invention belongs to textile material technical field, particularly a kind of production method of COTTON FABRIC of shape memory.
Background technology:
Many notebooks all can use the keycap coating of backlight keyboard, its keycap takes three layers of coating way to be formed, as shown in Figure 1, its work flow is: sprayed layer undercoat light colour paint 60-solidification-spray black radium carving colored paint 40-solidification-radium carving character 41-sprays the strong UV photocuring of UV light-cured resin paint 50-; The process of repetition like this causes flow process very long, and cost is very high; In addition, cause environmental issue, need a large amount of solvent to cause a discharge difficult problem.Shape-memory material is a kind of novel functional material, and current shape-memory material is applied on the textile and mainly contained fancy yarn, fabric, clothes, drapery and functional fabric.Shape memory fabrics refers to the fabric with formative memory function, the clothes that this fabric is made do not need to support by external force just independently to keep form, when wrinkle appear in fabric, whip the form before can recovering completely gently, and can not leave a trace, there is the function of permanent conformal.
The shape conformal function of shape memory fabrics is can change environmentally by its functional fibre, and the shape of spontaneous adjustment self, maintains or return to the state preset.Marmem is a kind of special metal material, and it comprises Nitinol, nickel-titanium-copper alloy and cu-zn-al alloy etc., and normal and traditional fibre looping is prepared fancy yarns and weaves fabric.Conventional shape memory fabrics adopts the fiber with shape memory function, as poly-long filament, the woven frivolous highly dense fabric of polyurethane fiber to Benzenediol, it can record first time shaping time state, also secondary sizing can be carried out by low temperature or foreign compulsion, fiber after sizing and fabric just have the memory function of shape when shaping to fiber, make product have easily wrinkle easily flat, exempt from the characteristic pressed.
Shape memory fabrics feel is so soft, bright colors is gorgeous, have good tensility, recovery, antistatic behaviour and comfortableness, and anti-soil is durable, be aly integrate attractive in appearance, comfortable and multi-functional fabric, can be used for maternity dress, underwear, sportswear and bedding etc.
Summary of the invention:
The object of this invention is to provide a kind of production method of COTTON FABRIC of shape memory, the inventive method passes through cotton fiber, polyurethane fiber and memorial alloy looping silk as graticule, prepare shape memory grey cloth, again through preliminary treatment, dyeing, washing of soaping, drying and shaping obtains the COTTON FABRIC of shape memory, on the basis ensureing COTTON FABRIC moisture absorption air permeable humidity retaining, give shape memory function.
Object of the present invention is achieved through the following technical solutions:
A production method for the COTTON FABRIC of shape memory, comprises the following steps:
(1) cotton fiber, polyurethane fiber and memorial alloy looping silk are carried out doubling, add low twist, obtain shape memory blend fibre;
(2) shape memory blend fibre step (1) obtained is as parallel, and cotton fiber, as warp, adopts plain weave, on woven, weave shape memory grey cloth;
(3) after the shape memory grey cloth that step (2) obtains being carried out preliminary treatment, dye by REACTIVE DYES, a leaching one is rolled, and takes out the shape memory grey cloth obtaining dyeing;
(4) the shape memory grey cloth of dyeing step (3) obtained, soap after washing, 100-120 DEG C of drying and shaping, obtains the COTTON FABRIC of shape memory.
Preferred as technique scheme, the fiber number of the shape memory blend fibre described in step (1) is 45-156dtex.
Preferred as technique scheme, in the shape memory blend fibre described in step (1), the content of cotton fiber is 60-80%, and the content of polyurethane fiber is 10-20%, and the content of memorial alloy looping silk is 5-20%.
Preferred as technique scheme, the memorial alloy looping silk described in step (1) is the looping silk of Nitinol and cotton fiber.
Preferred as technique scheme, the twist of the low twist described in step (1) is 200-800 sth. made by twisting/m.
Preferred as technique scheme, the fiber number of step (1) and the cotton fiber described in step (2) is 10-40S.
Preferred as technique scheme, the shape memory grey cloth described in step (2) through close be 268-472 root/cm, filling density is 123-258 root/cm.
Preferred as technique scheme, the preliminary treatment described in step (3) is alkali treatment.
Preferred as technique scheme, the soaking temperature that the leaching one described in step (3) is rolled is 70-80 DEG C, and soak time is 30-60min, and pH value is 5-7.
Beneficial effect of the present invention is: polyurethane fiber is combined by the strand of the hard section of polymer and soft section, by controlling the degree of cross linking, make fiber except the mechanical performance possessing general fibre, temperature sensor can also be passed through, freely change in the intercropping of deformation states many bullets state and original form glassy state, show the intelligent characteristic of shape memory.Nitinol is the alloy with thermoelastic martensitic transformation, and it is by heat treatment, changes between austenite and martensite, returns to original shape.
The application of polyurethane fiber wrapped yarn and Nitinol looping silk makes fabric have the fixing of deformation and recovery capability, because of direction of warp and weft, fiber has reciprocation, fabric is when being subject to simple tension, by the effect of fibre-fibre friction power, fabric entirety all can deform, so all add polyurethane fiber and Nitinol looping silk in graticule, ensure the shape memory function of fabric entirety, and the memory performance of fabric and fabric tissue and tightness have close relationship, in order to memory performance optimization selection plain weave, and appropriate thread count.
Detailed description of the invention:
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment 1:
Cotton fiber, polyurethane fiber and Nitinol looping silk are carried out doubling, twist 200 sth. made by twisting/m, obtain the shape memory blend fibre of 156dtex, wherein the content of cotton fiber is 80%, the content of polyurethane fiber is 10%, the content of memorial alloy looping silk is 10%, and using shape memory blend fibre as parallel, the cotton fiber of 10S is as warp, adopt plain weave, by through close be 268/cm, filling density is 123/cm, on woven, weave shape memory grey cloth.
After shape memory grey cloth is carried out oxygenation pretreatment, dye by REACTIVE DYES, a leaching one is rolled, wherein the pH value of dye liquor is 5,70 DEG C of immersion 60min, takes out the shape memory grey cloth obtaining dyeing, soap after washing, 120 DEG C of drying and shaping, obtain the COTTON FABRIC of shape memory.
The elastic recovery angle utilizing the restorative analyzer of LFY-IA fabric folds to record fabric is 254 °, as calculated, the deformation fixed rate of the COTTON FABRIC of shape memory is 81%, shape recovery rate 78%.
Embodiment 2:
Cotton fiber, polyurethane fiber and Nitinol looping silk are carried out doubling, twist 800 sth. made by twisting/m, obtain the shape memory blend fibre of 45dtex, wherein the content of cotton fiber is 60%, the content of polyurethane fiber is 20%, the content of memorial alloy looping silk is 20%, and using shape memory blend fibre as parallel, the cotton fiber of 10S is as warp, adopt plain weave, by through close be 472/cm, filling density is 258/cm, on woven, weave shape memory grey cloth.
After shape memory grey cloth is carried out oxygenation pretreatment, dye by REACTIVE DYES, a leaching one is rolled, wherein the pH value of dye liquor is 7,80 DEG C of immersion 30min, takes out the shape memory grey cloth obtaining dyeing, soap after washing, 100 DEG C of drying and shaping, obtain the COTTON FABRIC of shape memory.
The elastic recovery angle utilizing the restorative analyzer of LFY-IA fabric folds to record fabric is 258 °, as calculated, the deformation fixed rate of the COTTON FABRIC of shape memory is 83%, shape recovery rate 79%.
Embodiment 3:
Cotton fiber, polyurethane fiber and Nitinol looping silk are carried out doubling, twist 600 sth. made by twisting/m, obtain the shape memory blend fibre of 98dtex, wherein the content of cotton fiber is 70%, the content of polyurethane fiber is 15%, the content of memorial alloy looping silk is 15%, and using shape memory blend fibre as parallel, the cotton fiber of 30S is as warp, adopt plain weave, by through close be 365/cm, filling density is 159/cm, on woven, weave shape memory grey cloth.
After shape memory grey cloth is carried out oxygenation pretreatment, dye by REACTIVE DYES, a leaching one is rolled, wherein the pH value of dye liquor is 6,75 DEG C of immersion 50min, takes out the shape memory grey cloth obtaining dyeing, soap after washing, 110 DEG C of drying and shaping, obtain the COTTON FABRIC of shape memory.
The elastic recovery angle utilizing the restorative analyzer of LFY-IA fabric folds to record fabric is 263 °, as calculated, the deformation fixed rate of the COTTON FABRIC of shape memory is 82%, shape recovery rate 81%.
Embodiment 4:
Cotton fiber, polyurethane fiber and Nitinol looping silk are carried out doubling, twist 700 sth. made by twisting/m, obtain the shape memory blend fibre of 132dtex, wherein the content of cotton fiber is 75%, the content of polyurethane fiber is 15%, the content of memorial alloy looping silk is 10%, and using shape memory blend fibre as parallel, the cotton fiber of 20S is as warp, adopt plain weave, by through close be 298/cm, filling density is 188/cm, on woven, weave shape memory grey cloth.
After shape memory grey cloth is carried out oxygenation pretreatment, dye by REACTIVE DYES, a leaching one is rolled, wherein the pH value of dye liquor is 5,80 DEG C of immersion 50min, takes out the shape memory grey cloth obtaining dyeing, soap after washing, 100 DEG C of drying and shaping, obtain the COTTON FABRIC of shape memory.
The elastic recovery angle utilizing the restorative analyzer of LFY-IA fabric folds to record fabric is 273 °, as calculated, the deformation fixed rate of the COTTON FABRIC of shape memory is 85%, shape recovery rate 81%.
Embodiment 5:
Cotton fiber, polyurethane fiber and Nitinol looping silk are carried out doubling, twisting 200-800 sth. made by twisting/m, obtain the shape memory blend fibre of 132dtex, wherein the content of cotton fiber is 80%, the content of polyurethane fiber is 10%, the content of memorial alloy looping silk is 10%, and using shape memory blend fibre as parallel, the cotton fiber of 30S is as warp, adopt plain weave, by through close be 312/cm, filling density is 178/cm, on woven, weave shape memory grey cloth.
After shape memory grey cloth is carried out oxygenation pretreatment, dye by REACTIVE DYES, a leaching one is rolled, wherein the pH value of dye liquor is 7,70 DEG C of immersion 40min, takes out the shape memory grey cloth obtaining dyeing, soap after washing, 120 DEG C of drying and shaping, obtain the COTTON FABRIC of shape memory.
The elastic recovery angle utilizing the restorative analyzer of LFY-IA fabric folds to record fabric is 273 °, as calculated, the deformation fixed rate of the COTTON FABRIC of shape memory is 82%, shape recovery rate 79%.
Embodiment 6:
Cotton fiber, polyurethane fiber and Nitinol looping silk are carried out doubling, twist 800 sth. made by twisting/m, obtain the shape memory blend fibre of 96dtex, wherein the content of cotton fiber is 70%, the content of polyurethane fiber is 20%, the content of memorial alloy looping silk is 10%, and using shape memory blend fibre as parallel, the cotton fiber of 40S is as warp, adopt plain weave, by through close be 372/cm, filling density is 258/cm, on woven, weave shape memory grey cloth.
After shape memory grey cloth is carried out oxygenation pretreatment, dye by REACTIVE DYES, a leaching one is rolled, wherein the pH value of dye liquor is 5,80 DEG C of immersion 40min, takes out the shape memory grey cloth obtaining dyeing, soap after washing, 110 DEG C of drying and shaping, obtain the COTTON FABRIC of shape memory.
The elastic recovery angle utilizing the restorative analyzer of LFY-IA fabric folds to record fabric is 272 °, as calculated, the deformation fixed rate of the COTTON FABRIC of shape memory is 86%, shape recovery rate 82%.
From above-described embodiment, the COTTON FABRIC of shape memory prepared by the method is on the basis ensureing COTTON FABRIC characteristic, and its shape memory function is good, and therefore fabric possesses the intelligent effect of shape memory.
Claims (9)
1. a production method for the COTTON FABRIC of shape memory, is characterized in that, the method comprises the following steps:
(1) cotton fiber, polyurethane fiber and memorial alloy looping silk are carried out doubling, add low twist, obtain shape memory blend fibre;
(2) shape memory blend fibre step (1) obtained is as parallel, and cotton fiber, as warp, adopts plain weave, on woven, weave shape memory grey cloth;
(3) after the shape memory grey cloth that step (2) obtains being carried out preliminary treatment, dye by REACTIVE DYES, a leaching one is rolled, and takes out the shape memory grey cloth obtaining dyeing;
(4) the shape memory grey cloth of dyeing step (3) obtained, soap after washing, 100-120 DEG C of drying and shaping, obtains the COTTON FABRIC of shape memory.
2. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, is characterized in that: the fiber number of the shape memory blend fibre described in step (1) is 45-156dtex.
3. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, it is characterized in that: in the shape memory blend fibre described in step (1), the content of cotton fiber is 60-80%, the content of polyurethane fiber is 10-20%, and the content of memorial alloy looping silk is 5-20%.
4. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, is characterized in that: the memorial alloy looping silk described in step (1) is the looping silk of Nitinol and cotton fiber.
5. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, is characterized in that: the twist of the low twist described in step (1) is 200-800 sth. made by twisting/m.
6. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, is characterized in that: the fiber number of step (1) and the cotton fiber described in step (2) is 10-40S.
7. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, is characterized in that: the shape memory grey cloth described in step (2) through close for 268-472 root/cm, filling density is 123-258 root/cm.
8. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, is characterized in that: the preliminary treatment described in step (3) is alkali treatment.
9. the production method of the COTTON FABRIC of a kind of shape memory according to claim 1, is characterized in that: the soaking temperature that the leaching one described in step (3) is rolled is 70-80 DEG C, and soak time is 30-60min, and pH value is 5-7.