CN104529419A - Ceramic cup containing tourmaline and six-ring rock and preparation method thereof - Google Patents
Ceramic cup containing tourmaline and six-ring rock and preparation method thereof Download PDFInfo
- Publication number
- CN104529419A CN104529419A CN201410793233.1A CN201410793233A CN104529419A CN 104529419 A CN104529419 A CN 104529419A CN 201410793233 A CN201410793233 A CN 201410793233A CN 104529419 A CN104529419 A CN 104529419A
- Authority
- CN
- China
- Prior art keywords
- parts
- tourmalinite
- ring
- ceramic cup
- ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a ceramic cup containing tourmaline and six-ring rock and a preparation method thereof, belonging to the technical field of domestic ceramics. The ceramic cup comprises the following raw material components in parts by weight: 1-5 parts of tourmaline, 1-5 parts of six-ring rock, 10-15 parts of potassium feldspar, 10-15 parts of albite, 1-3 parts of raw talc and 2-4 parts of magnesium oxide. The preparation method comprises the following steps: proportionally weighing the substances, performing ball milling for 30-35 minutes, adding deionized water which is 1-1.5 times the powder obtained by the ball milling in weight to obtain ceramic pug, and preparing a ceramic body from the ceramic pug; and firing for 7-7.5 hours at 1,100-1,150 DEG C, cooling to room temperature and polishing to obtain the product. The ceramic cup has good comprehensive properties and realizes a certain effect on promoting health of a human body after long-time use; and the process is simple and easy to implement, and the production cost is relatively low.
Description
Technical field
The present invention relates to a kind of ceramic cup, be specifically related to a kind of to there is ceramic cup containing tourmalinite, six ring stones and preparation method thereof, belong to domestic ceramics technical field.
Background technology
Pottery is the general name of pottery and porcelain.People has just invented pottery the Neolithic Age before about B.C. 8000.Stupalith is oxide compound, nitride, boride and carbide etc. mostly.Common stupalith has clay, aluminum oxide, kaolin etc.The general hardness of stupalith is higher, but plasticity-is poor.Except in the use of feeder, decoration, also play an important role in the development of science, technology.Ceramic raw material is that the original ample resources clay of the earth forms through quenching to get.And the character tool toughness of clay, it is plastic that normal temperature meets water, micro-ly dry can to carve, and absolutely dryly grinds; Burning can become pottery to fill water to 700 degree; Burn to 1230 degree of then porcelain, can almost not absorb water completely and corrosion-and high-temp-resistant.The elasticity of its usage, has the application of various intention in culture today science and technology.
Domestic ceramics (also referring to tableware or family's porcelain), as the term suggests refer to: requisite life porcelain in people's daily life.The generation of domestic ceramics can be described as because the demand of people to daily life produces, and in daily life, people contact at most, are also the most familiar porcelain, as tableware, tea set, coffee service, coffee set, drinking utensils, meal tool etc.
Domestic porcelain, for a long time by broad masses of the people are liked and use, because it has following advantage: the first, is easy to washing and keeps clean.Household china glaze paint light, fine and smooth, use after staiing and easily wash away; The second, better heat stability, heat transfer is slow.The performance that tableware for daily use not easily bursts when having the hot quenching of the urgency standing a fixed difference difference to change.It is more superior than glassware for this point, and it is the poor conductor of heat, and heat transfer slowly.Be used for splendid attire boiling water or boiling hot food, not too hot when end is taken; 3rd, stable chemical nature is durable in use.This point is as more superior in bronze, brass or copper ware, ironware, aluminium device etc. than metal products, and household china has the ability that certain acid-and base-resisting, salt and carbon in atmosphere acid gas corrode, and not easily with these material generation chemical reactions, non-corrosive is aging; 4th, the pore of porcelain is few, and water-intake rate is very low.Store food with domestic porcelain, after tight sealing, the infringement of moisture evaporation in food, infiltration and extraneous bacterium can be prevented; 5th, painted decoration is rich and varied, and especially high temperature muffle painting and underglaze blue decoration etc. are without lead poisoning harm, can courageously use, popular to people.
CN201410179523.7 discloses a kind of multifunctional ceramic cup, comprise cup (1) and bowl cover (2), described cup (1) is double-layer ceramic cup, the bottom surface of described cup (1) has prosopyle (4) and venting hole (3), and described prosopyle (4) and venting hole (3) seal respectively by sealing member (5); Liner prepared by food grade materials is provided with in described bowl cover (2).Multifunctional ceramic cup can reuse, and uses, economizes on resources, energy-conserving and environment-protective as water tumbler or other utensils.Above patent provides ceramic cup and preparation method thereof, but along with growth in the living standard, the demand of people to multifunctional product is increasing.Some stones as tourmalinite, six ring stones are proved has certain health-care effect, more and more receive the concern of people.
Summary of the invention
The present invention is directed to prior art Problems existing, provide a kind of ceramic cup containing tourmalinite, six ring stones, this ceramic cup over-all properties is good, and life-time service can promote health and have certain effect, and simple for process, and production cost is lower.
In order to solve the problem, the technical solution adopted in the present invention is:
There is the ceramic cup containing tourmalinite, six ring stones, be made up of the weight part of following component:
1 ~ 5 part, tourmalinite, 1 ~ 5 part, six ring stone, potassium felspar sand 10 ~ 15 parts, albite 10 ~ 15 parts, raw 1 ~ 3 part, talcum, 2 ~ 4 parts, magnesium oxide;
1 ~ 3 part, tourmalinite, 1 ~ 3 part, six ring stone, potassium felspar sand 13 ~ 15 parts, albite 13 ~ 15 parts, raw 2 ~ 3 parts, talcum, 3 ~ 4 parts, magnesium oxide;
3 ~ 5 parts, tourmalinite, 3 ~ 5 parts, six ring stone, potassium felspar sand 10 ~ 13 parts, albite 13 ~ 15 parts, raw 2 ~ 3 parts, talcum, 3 ~ 4 parts, magnesium oxide;
3.5 ~ 4.5 parts, tourmalinite, 3 ~ 5 parts, six ring stone, potassium felspar sand 10 ~ 13 parts, albite 10 ~ 13 parts, raw 1 ~ 2 part, talcum, 2 ~ 3 parts, magnesium oxide;
3.5 parts, tourmalinite, 3 parts, six ring stone, potassium felspar sand 10 parts, albite 10 parts, raw 1 part, talcum, 2 parts, magnesium oxide;
4.5 parts, tourmalinite, 5 parts, six ring stone, potassium felspar sand 13 parts, albite 13 parts, raw 2 parts, talcum, 3 parts, magnesium oxide.
Another object of the present invention is to provide a kind of ceramic cup preparation method containing tourmalinite, six ring stones, comprises the following steps:
Take above-mentioned substance in described ratio, ball milling 30 ~ 35 minutes, the deionized water that the powder obtained by ball milling adds its weight 1 ~ 1.5 times makes ceramic material, makes ceramic body; Fire 7 ~ 7.5 hours at 1100 ~ 1150 DEG C again, after being cooled to normal temperature, polishing is scraped, and obtains product.
The present invention relative to the beneficial effect of prior art is:
Ceramic cup provided by the invention, over-all properties is good, life-time service, can promote health and have certain effect, and simple for process, and production cost is lower.
Embodiment
Be described in further details the present invention below by embodiment, these embodiments are only used for the present invention is described, do not limit the scope of the invention.
embodiment 1:
There is the ceramic cup containing tourmalinite, six ring stones, be made up of the weight part of following component:
4.5 parts, tourmalinite, 5 parts, six ring stone, potassium felspar sand 13 parts, albite 13 parts, raw 2 parts, talcum, 3 parts, magnesium oxide.
Its preparation method, comprises the following steps:
Take above-mentioned substance in described ratio, ball milling 30 minutes, the deionized water that the powder obtained by ball milling adds its weight 1 times makes ceramic material, makes ceramic body; Fire 7 hours at 1100 DEG C again, after being cooled to normal temperature, polishing is scraped, and obtains product.
embodiment 2:
There is the ceramic cup containing tourmalinite, six ring stones, be made up of the weight part of following component:
3.5 parts, tourmalinite, 3 parts, six ring stone, potassium felspar sand 10 parts, albite 10 parts, raw 1 part, talcum, 2 parts, magnesium oxide.
Its preparation method, comprises the following steps:
Take above-mentioned substance in described ratio, ball milling 35 minutes, the deionized water that the powder obtained by ball milling adds its weight 1.5 times makes ceramic material, makes ceramic body; Fire 7.5 hours at 1150 DEG C again, after being cooled to normal temperature, polishing is scraped, and obtains product.
embodiment 3:
There is the ceramic cup containing tourmalinite, six ring stones, be made up of the weight part of following component:
3 parts, tourmalinite, 3 parts, six ring stone, potassium felspar sand 10 parts, albite 13 parts, raw 2 parts, talcum, 3 parts, magnesium oxide;
Its preparation method, comprises the following steps:
Take above-mentioned substance in described ratio, ball milling 33 minutes, the deionized water that the powder obtained by ball milling adds its weight 1.3 times makes ceramic material, makes ceramic body; Fire 7.3 hours at 1125 DEG C again, after being cooled to normal temperature, polishing is scraped, and obtains product.
embodiment 4:
There is the ceramic cup containing tourmalinite, six ring stones, be made up of the weight part of following component:
5 parts, tourmalinite, 5 parts, six ring stone, potassium felspar sand 13 parts, albite 15 parts, raw 3 parts, talcum, 4 parts, magnesium oxide;
Its preparation method, comprises the following steps:
Take above-mentioned substance in described ratio, ball milling 31 minutes, the deionized water that the powder obtained by ball milling adds its weight 1.1 times makes ceramic material, makes ceramic body; Fire 7 hours at 1100 DEG C again, after being cooled to normal temperature, polishing is scraped, and obtains product.
embodiment 5:
There is the ceramic cup containing tourmalinite, six ring stones, be made up of the weight part of following component:
1 part, tourmalinite, 1 part, six ring stone, potassium felspar sand 10 parts, albite 10 parts, raw 1 part, talcum, 2 parts, magnesium oxide.
Its preparation method, comprises the following steps:
Take above-mentioned substance in described ratio, ball milling 34 minutes, the deionized water that the powder obtained by ball milling adds its weight 1.35 times makes ceramic material, makes ceramic body; Fire 7.5 hours at 1150 DEG C again, after being cooled to normal temperature, polishing is scraped, and obtains product.
Claims (7)
1. the ceramic cup containing tourmalinite, six ring stones, is characterized in that: the weight part of each component of raw material is:
1 ~ 5 part, tourmalinite, 1 ~ 5 part, six ring stone, potassium felspar sand 10 ~ 15 parts, albite 10 ~ 15 parts, raw 1 ~ 3 part, talcum, 2 ~ 4 parts, magnesium oxide.
2. the ceramic cup containing tourmalinite, six ring stones, is characterized in that: the weight part of each component of raw material is:
1 ~ 3 part, tourmalinite, 1 ~ 3 part, six ring stone, potassium felspar sand 13 ~ 15 parts, albite 13 ~ 15 parts, raw 2 ~ 3 parts, talcum, 3 ~ 4 parts, magnesium oxide.
3. the ceramic cup containing tourmalinite, six ring stones, is characterized in that: the weight part of each component of raw material is:
3 ~ 5 parts, tourmalinite, 3 ~ 5 parts, six ring stone, potassium felspar sand 10 ~ 13 parts, albite 13 ~ 15 parts, raw 2 ~ 3 parts, talcum, 3 ~ 4 parts, magnesium oxide.
4. the ceramic cup containing tourmalinite, six ring stones, is characterized in that: the weight part of each component of raw material is:
3.5 ~ 4.5 parts, tourmalinite, 3 ~ 5 parts, six ring stone, potassium felspar sand 10 ~ 13 parts, albite 10 ~ 13 parts, raw 1 ~ 2 part, talcum, 2 ~ 3 parts, magnesium oxide.
5. the ceramic cup containing tourmalinite, six ring stones, is characterized in that: the weight part of each component of raw material is:
3.5 parts, tourmalinite, 3 parts, six ring stone, potassium felspar sand 10 parts, albite 10 parts, raw 1 part, talcum, 2 parts, magnesium oxide.
6. the ceramic cup containing tourmalinite, six ring stones, is characterized in that: the weight part of each component of raw material is:
4.5 parts, tourmalinite, 5 parts, six ring stone, potassium felspar sand 13 parts, albite 13 parts, raw 2 parts, talcum, 3 parts, magnesium oxide.
7., according to a kind of ceramic cup containing tourmalinite, six ring stones described in claim 1 ~ 6, it is characterized in that: its preparation method, comprise the following steps:
Take above-mentioned substance in described ratio, ball milling 30 ~ 35 minutes, the deionized water that the powder obtained by ball milling adds its weight 1 ~ 1.5 times makes ceramic material, makes ceramic body; Fire 7 ~ 7.5 hours at 1100 ~ 1150 DEG C again, after being cooled to normal temperature, polishing is scraped, and obtains product.