CN108033768A - Ceramic whiteware pot and preparation method thereof with high temperature resistant, explosion-proof glaze paint - Google Patents
Ceramic whiteware pot and preparation method thereof with high temperature resistant, explosion-proof glaze paint Download PDFInfo
- Publication number
- CN108033768A CN108033768A CN201711292554.3A CN201711292554A CN108033768A CN 108033768 A CN108033768 A CN 108033768A CN 201711292554 A CN201711292554 A CN 201711292554A CN 108033768 A CN108033768 A CN 108033768A
- Authority
- CN
- China
- Prior art keywords
- parts
- ceramic whiteware
- pot
- kettle body
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to ceramic field, more particularly to a kind of ceramic whiteware pot with high temperature resistant, explosion-proof glaze paint and preparation method thereof.This kind has high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, including ceramic whiteware kettle body, the ceramic whiteware kettle body include base substrate, glaze layer and nano heat-conductive silver coating, and nano heat-conductive silver coating is arranged at ceramic whiteware kettle body bottom, and is arranged on glaze layer.Ceramic whiteware pot with high temperature resistant, explosion-proof glaze paint provided by the invention and preparation method thereof, ceramic whiteware pot can directly heat food in electric furnace, safe and healthy;Nano composite powder is added in ceramic whiteware glaze, the toughness, intensity, heat resistance of ceramic whiteware glaze layer can be strengthened, and small gap is formed in glaze layer, so that glaze layer shrinking percentage reduces, high temperature is met water and is not split, this kind has high temperature resistant, its manufacture craft of the ceramic whiteware pot of explosion-proof glaze paint simple, has filled up the blank that can be directly used for the ceramic whiteware pot on electric circuit stove at present on the market not, has had a vast market prospect.
Description
Technical field
The invention belongs to ceramic field, specifically, the present invention relates to it is a kind of with high temperature resistant, explosion-proof glaze paint it is white
Porcelain pot and preparation method thereof.
Background technology
At present, in the streets most universal common electric stove should " electric ceramic heaters " and " electromagnetic oven " both electric furnaces at last
Tool;Wherein, the principle of heating of electric ceramic heaters converts electrical energy into thermal energy using internal heat generating component, and passes through glass-ceramic (stove
Face) by thermal energy transmit heat to top utensil or food materials.
Since electric stove is easy to use, popularization degree is high, and existing teapot, which is all pursued, to be used in electric furnace, such as patent
Number can utilize the direct-fired ceramic pan of electromagnetic oven for one kind disclosed in 201310450676.6, by quartz, calcite, potassium length
Stone, zinc oxide, boric acid, zirconium English powder, raw talcum and strontium carbonate are made.In use, it is circular in one piece of cookware bottom insertion, with pot
Have the identical ferromagnetic plate sheet of floor space, ceramic pan is placed directly within electromagnetic oven, it is thin to ferromagnetism using vortex principle
Plate is heated.This kind is inconvenient for use using the direct-fired ceramic pan of electromagnetic oven.This kind of ceramic pan is embedded in one in pot body bottom surface
Block ferromagnetic sheet,
Ceramic whiteware imposes pure clear frit firing and forms, due in the glaze of ceramic whiteware and glaze with the low porcelain billet of iron-holder
Without or the only photoghraphic coupler of denier, green compact rest, enter kiln and pass through the white porcelain that thermal-flame is burnt till.White for high temperature
Porcelain, is mainly fired with kaolin, has that physical stability is good, nontoxic, content of beary metal is low, the benefit of Low emissivity.But ceramic whiteware
The teapot that vessel are used in electric furnace is in use, the water in pot overflows and ceramic whiteware can be caused to burst, therefore existing ceramic whiteware can not be straight
Connect and be used for electric stove, therefore, if existing production can be overcome difficult, production one by the improvement of ceramic whiteware raw material and technique
The problem of planting the ceramic whiteware product suitable for electric stove, being ceramic whiteware manufacturing enterprise urgent need to resolve.
The content of the invention
To solve the above-mentioned problems, the present invention provides a kind of ceramic whiteware pot with high temperature resistant, explosion-proof glaze paint.
Realize above-mentioned purpose, present invention offer is a kind of to have high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, including ceramic whiteware kettle body,
The ceramic whiteware kettle body includes base substrate, glaze layer and nano heat-conductive silver coating;Its parts by weight of the base substrate of the ceramic whiteware kettle body are as follows:Longyan
35-40 parts of kaolin, kaolin 20-25 parts of New Zealand, Australian 10-15 parts of feldspar, 8-12 parts of cordierite powder, zirconium silicate 3-
8 parts, 1-5 parts of spodumene, Brazilian 1-5 parts of tourmaline;The glaze layer formula of the ceramic whiteware kettle body is as follows:Clear frit frit 75-80
Part, 8-12 parts of spodumene, kaolin 5-8 parts of New Zealand, 1-5 parts of high alumina, 1-3 parts of zirconium silicate, 0.8-1.2 parts of nano yttrium oxide,
0.6-1 parts of nano aluminium oxide, 0.5-1 parts of nano zircite, 0.5-0.8 parts of nano-titanium oxide;The nano heat-conductive silver coating is set
Ceramic whiteware kettle body bottom is placed in, and is arranged on glaze layer.
Further, the glaze layer of ceramic whiteware kettle body is arranged inside and outside ceramic whiteware kettle body, and the nano-silver layer is arranged at ceramic whiteware pot
In vivo and the thickness of the nano-silver layer is 1-5mm.
Further, its parts by weight of the base substrate of ceramic whiteware kettle body are as follows:38 parts of Longyan kaolin, 24 parts of New Zealand's kaolin,
Australian 13 parts of feldspar, 11 parts of cordierite powder, 6 parts of zirconium silicate, 4 parts of spodumene, Brazilian 4 parts of tourmaline.
Further, the glaze layer formula of ceramic whiteware kettle body is as follows:77 parts of clear frit frit, 11 parts of spodumene, New Zealand are high
5 parts of ridge soil, 2 parts of high alumina, 2 parts of zirconium silicate, 0.9 part of nano yttrium oxide, 0.8 part of nano aluminium oxide, 0.7 part of nano zircite, receive
0.6 part of titanium oxide of rice.
Further, its parts by weight of the base substrate of ceramic whiteware kettle body are as follows:38 parts of Longyan kaolin, 24 parts of New Zealand's kaolin,
Australian 13 parts of feldspar, 11 parts of cordierite powder, 7 parts of zirconium silicate, 3 parts of spodumene, Brazilian 4 parts of tourmaline.
Further, the glaze layer formula of ceramic whiteware kettle body is as follows:75 parts of clear frit frit, 9 parts of spodumene, New Zealand's kaolinite
6 parts of soil, 4 parts of high alumina, 2.3 parts of zirconium silicate, 1.1 parts of nano yttrium oxide, 0.9 part of nano aluminium oxide, nano zircite 1 part, nanometer
0.7 part of titanium oxide.
Preparation process with high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that preparing above-mentioned has resistance to height
The ceramic whiteware pot of warm, explosion-proof glaze paint, comprises the following steps that:
Step 1, by ceramic whiteware kettle body raw material components dispensing, raw material is put into wet grinding in ball mill, obtains ceramic whiteware kettle body
Base is starched;
Step 2, by the glaze layer material component dispensing of ceramic whiteware kettle body, ceramic whiteware kettle body glaze slip is prepared;
Step 3, pot base is made by slip casting or moulding process using ceramic whiteware kettle body base slurry made from step 1;
Step 4, wiping water, repaired biscuit, glazing are carried out after the drying of pot base;
Step 5, the pot base after glazing is put into kiln and formed by a firing, firing temperature is 1310-1320 degree, the firing time
For 20-30 it is small when, obtain ceramic whiteware kettle body;
Step 6, in ceramic whiteware kettle body bottom surface brush nano heat-conductive silver coating.
Optimization, in step 2 ceramic whiteware kettle body glaze slip make when, first by clear frit frit, spodumene, New Zealand's kaolin,
Raw material is put into wet grinding in ball mill by high alumina, zirconium silicate, is mixed into nano yttrium oxide, nano aluminium oxide, nano zircite, is received
Rice titanium oxide part, obtains ceramic whiteware kettle body glaze slip.
Optimization, the glazing process in step 4 is leaching glaze.
Optimization, the Baume Hydrometer concentration of glaze slip is 50-53 degree during step 4 glazing.
From the above-mentioned description of this invention, it is provided by the invention with high temperature resistant, explosion-proof glaze paint ceramic whiteware pot and its
Production method, is provided with nano heat-conductive silver coating in kettle body bottom and is used to coordinate with electric furnace, for heat conduction and be rapidly heated, make
Ceramic whiteware pot can directly heat food in electric furnace, safe and healthy;Added in ceramic whiteware glaze by nano yttrium oxide, nano oxygen
Change aluminium, nano zircite, the nano composite powder of nano-titanium oxide compounding composition, can strengthen the toughness of ceramic whiteware glaze layer, intensity,
Heat resistance, and small gap is formed in glaze layer so that glaze layer shrinking percentage reduces, and high temperature is met water and do not split, this kind has
High temperature resistant, its manufacture craft of the ceramic whiteware pot of explosion-proof glaze paint are simple, filled up at present on the market without can be directly used for electric circuit
The blank of ceramic whiteware pot on stove, has a vast market prospect.
Embodiment
Below by way of embodiment, the invention will be further described.
Ceramic whiteware pot with high temperature resistant, explosion-proof glaze paint, including ceramic whiteware kettle body, the ceramic whiteware kettle body include base substrate, be arranged at it is white
Glaze layer and nano heat-conductive silver coating inside and outside porcelain kettle body;
Its parts by weight of the base substrate of ceramic whiteware kettle body are as follows:Kaolin 35-40 parts of Longyan, kaolin 20-25 parts of New Zealand, Australia are big
10-15 parts of Leah feldspar, 8-12 parts of cordierite powder, 3-8 parts of zirconium silicate, 1-5 parts of spodumene, Brazilian 1-5 parts of tourmaline;
The glaze layer formula of ceramic whiteware kettle body is as follows:75-80 parts of clear frit frit, 8-12 parts of spodumene, New Zealand's kaolin
5-8 parts, 1-5 parts of high alumina, 1-3 parts of zirconium silicate, 0.8-1.2 parts of nano yttrium oxide, 0.6-1 parts of nano aluminium oxide, nano zircite
0.5-1 parts, 0.5-0.8 parts of nano-titanium oxide;
Nano heat-conductive silver coating is arranged at ceramic whiteware kettle body bottom, and is arranged on glaze layer, and nano-silver layer is arranged at ceramic whiteware
Kettle body is interior and the thickness of the nano-silver layer is 1-5mm.
A variety of nano composite powders are wherein added in the glaze layer of ceramic whiteware kettle body, wherein especially nano yttrium oxide
Add, the toughness of glaze layer can be strengthened, and small gap is formed in glaze layer so that glaze layer shrinking percentage reduces, high temperature
Water is met not split;The intensity and heat resistance of ceramic whiteware glaze layer can be strengthened by nano aluminium oxide, nano zircite, nano-titanium oxide,
Glaze layer is set to bear quick temperature change.
Wherein nano heat-conductive silver coating is arranged at ceramic whiteware kettle body bottom, and when electric furnace is electromagnetic oven, nano heat-conductive silver applies
Layer can be used as conductive media to heat kettle body, and when electric furnace is electric ceramic heaters, nano heat-conductive silver coating can make bottom of the pot thermally equivalent,
It is rapidly heated.
Specific embodiment one:
Ceramic whiteware pot with high temperature resistant, explosion-proof glaze paint, including ceramic whiteware kettle body, the ceramic whiteware kettle body include base substrate, be arranged at it is white
Glaze layer and nano heat-conductive silver coating inside and outside porcelain kettle body;
Its parts by weight of the base substrate of ceramic whiteware kettle body are as follows:38 parts of Longyan kaolin, 24 parts of New Zealand's kaolin, Australia are long
13 parts of stone, 11 parts of cordierite powder, 6 parts of zirconium silicate, 4 parts of spodumene, Brazilian 4 parts of tourmaline;
The glaze layer formula of ceramic whiteware kettle body is as follows:77 parts of clear frit frit, 11 parts of spodumene, 5 parts of New Zealand's kaolin, height
2 parts of aluminium, 2 parts of zirconium silicate, 0.9 part of nano yttrium oxide, 0.8 part of nano aluminium oxide, 0.7 part of nano zircite, nano-titanium oxide 0.6
Part;
Nano heat-conductive silver coating is arranged at ceramic whiteware kettle body bottom, and is arranged on glaze layer, and nano-silver layer is arranged at ceramic whiteware
Kettle body is interior and the thickness of the nano-silver layer is 2mm.
Specific embodiment two:
Ceramic whiteware pot with high temperature resistant, explosion-proof glaze paint, including ceramic whiteware kettle body, the ceramic whiteware kettle body include base substrate, be arranged at it is white
Glaze layer and nano heat-conductive silver coating inside and outside porcelain kettle body;
Its parts by weight of the base substrate of ceramic whiteware kettle body are as follows:38 parts of Longyan kaolin, 24 parts of New Zealand's kaolin, Australia are long
13 parts of stone, 11 parts of cordierite powder, 7 parts of zirconium silicate, 3 parts of spodumene, Brazilian 4 parts of tourmaline;
The glaze layer formula of ceramic whiteware kettle body is as follows:75 parts of clear frit frit, 9 parts of spodumene, 6 parts of New Zealand's kaolin, height
4 parts of aluminium, 2.3 parts of zirconium silicate, 1.1 parts of nano yttrium oxide, 0.9 part of nano aluminium oxide, 1 part of nano zircite, nano-titanium oxide 0.7
Part;
Nano heat-conductive silver coating is arranged at ceramic whiteware kettle body bottom, and is arranged on glaze layer, and nano-silver layer is arranged at ceramic whiteware
Kettle body is interior and the thickness of the nano-silver layer is 3mm.
Preparation process with high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that preparing above-mentioned has resistance to height
The ceramic whiteware pot of warm, explosion-proof glaze paint, comprises the following steps that:
Step 1, by ceramic whiteware kettle body raw material components dispensing, raw material is put into wet grinding in ball mill, obtains ceramic whiteware kettle body
Base is starched;
Step 2, by the glaze layer material component dispensing of ceramic whiteware kettle body, ceramic whiteware kettle body glaze slip, ceramic whiteware kettle body glaze slip system are prepared
When making, first raw material is put into wet method in ball mill and ground by clear frit frit, spodumene, New Zealand's kaolin, high alumina, zirconium silicate
Mill, is mixed into nano yttrium oxide, nano aluminium oxide, nano zircite, nano-titanium oxide part, obtains ceramic whiteware kettle body glaze slip;
Step 3, pot base is made by slip casting or moulding process using ceramic whiteware kettle body base slurry made from step 1;
Step 4, wiping water, repaired biscuit, glazing being carried out after the drying of pot base, the Baume Hydrometer concentration of glaze slip is 50-53 degree during glazing,
Glazing process is leaching glaze, can be arranged at when soaking glaze with the glaze layer to the inside and outside glazing at the same time of ceramic whiteware kettle body base slurry, ceramic whiteware kettle body white
Inside and outside porcelain kettle body, toughness, intensity, heat resistance inside and outside ceramic whiteware kettle body can be made consistent;
Step 5, the pot base after glazing is put into kiln and formed by a firing, firing temperature is 1310-1320 degree, the firing time
For 20-30 it is small when, obtain ceramic whiteware kettle body;
Step 6, in ceramic whiteware kettle body bottom surface brush nano heat-conductive silver coating.
From the above-mentioned description of this invention, it is provided by the invention with high temperature resistant, explosion-proof glaze paint ceramic whiteware pot and its
Production method, is provided with nano heat-conductive silver coating in kettle body bottom and is used to coordinate with electric furnace, for heat conduction and be rapidly heated, make
Ceramic whiteware pot can directly heat food in electric furnace, safe and healthy;Added in ceramic whiteware glaze by nano yttrium oxide, nano oxygen
Change aluminium, nano zircite, the nano composite powder of nano-titanium oxide compounding composition, can strengthen the toughness of ceramic whiteware glaze layer, intensity,
Heat resistance, and small gap is formed in glaze layer so that glaze layer shrinking percentage reduces, and high temperature is met water and do not split, this kind has
High temperature resistant, its manufacture craft of the ceramic whiteware pot of explosion-proof glaze paint are simple, filled up at present on the market without can be directly used for electric circuit
The blank of ceramic whiteware pot on stove, has a vast market prospect.
The embodiment of the present invention is above are only, but the design concept of the present invention is not limited thereto, it is all to utilize this
Conceive the change that unsubstantiality is carried out to the present invention, the behavior for invading the scope of the present invention should all be belonged to.
Claims (10)
1. with high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that:Including ceramic whiteware kettle body, the ceramic whiteware kettle body include base substrate,
Glaze layer and nano heat-conductive silver coating;
Its parts by weight of the base substrate of the ceramic whiteware kettle body are as follows:Kaolin 35-40 parts of Longyan, kaolin 20-25 parts of New Zealand, Australia are big
10-15 parts of Leah feldspar, 8-12 parts of cordierite powder, 3-8 parts of zirconium silicate, 1-5 parts of spodumene, Brazilian 1-5 parts of tourmaline;
The glaze layer formula of the ceramic whiteware kettle body is as follows:75-80 parts of clear frit frit, 8-12 parts of spodumene, New Zealand's kaolin
5-8 parts, 1-5 parts of high alumina, 1-3 parts of zirconium silicate, 0.8-1.2 parts of nano yttrium oxide, 0.6-1 parts of nano aluminium oxide, nano zircite
0.5-1 parts, 0.5-0.8 parts of nano-titanium oxide;
The nano heat-conductive silver coating is arranged at ceramic whiteware kettle body bottom, and is arranged on glaze layer.
2. according to claim 4 have high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that:The ceramic whiteware kettle body
Glaze layer be arranged inside and outside ceramic whiteware kettle body, the nano-silver layer is arranged in ceramic whiteware kettle body and the thickness of the nano-silver layer is
1-5mm。
3. according to claim 1 have high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that the ceramic whiteware kettle body
Base substrate its parts by weight it is as follows:38 parts of Longyan kaolin, 24 parts of New Zealand's kaolin, Australian 13 parts of feldspar, cordierite powder
11 parts, 6 parts of zirconium silicate, 4 parts of spodumene, Brazilian 4 parts of tourmaline.
4. there is high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint according to claim 1 or 3, it is characterised in that the ceramic whiteware pot
The glaze layer formula of body is as follows:77 parts of clear frit frit, 11 parts of spodumene, 5 parts of New Zealand's kaolin, 2 parts of high alumina, zirconium silicate 2
Part, 0.9 part of nano yttrium oxide, 0.8 part of nano aluminium oxide, 0.7 part of nano zircite, 0.6 part of nano-titanium oxide.
5. according to claim 1 have high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that the ceramic whiteware kettle body
Base substrate its parts by weight it is as follows:38 parts of Longyan kaolin, 24 parts of New Zealand's kaolin, Australian 13 parts of feldspar, cordierite powder
11 parts, 7 parts of zirconium silicate, 3 parts of spodumene, Brazilian 4 parts of tourmaline.
6. there is high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint according to claim 1 or 5, it is characterised in that the ceramic whiteware pot
The glaze layer formula of body is as follows:75 parts of clear frit frit, 9 parts of spodumene, 6 parts of New Zealand's kaolin, 4 parts of high alumina, zirconium silicate 2.3
Part, 1.1 parts of nano yttrium oxide, 0.9 part of nano aluminium oxide, 1 part of nano zircite, 0.7 part of nano-titanium oxide.
7. the preparation process with high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that prepare described in claim 1-6
Ceramic whiteware pot with high temperature resistant, explosion-proof glaze paint, comprises the following steps that:
Step 1, by ceramic whiteware kettle body raw material components dispensing, raw material is put into wet grinding in ball mill, obtains ceramic whiteware kettle body base slurry;
Step 2, by the glaze layer material component dispensing of ceramic whiteware kettle body, ceramic whiteware kettle body glaze slip is prepared;
Step 3, pot base is made by slip casting or moulding process using ceramic whiteware kettle body base slurry made from step 1;
Step 4, wiping water, repaired biscuit, glazing are carried out after the drying of pot base;
Step 5, the pot base after glazing is put into kiln and formed by a firing, firing temperature is 1310-1320 degree, and the firing time is
When 20-30 is small, ceramic whiteware kettle body is obtained;
Step 6, in ceramic whiteware kettle body bottom surface brush nano heat-conductive silver coating.
8. the preparation process according to claim 7 with high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that:Institute
When stating ceramic whiteware kettle body glaze slip making in step 2, first clear frit frit, spodumene, New Zealand's kaolin, high alumina, zirconium silicate are incited somebody to action
Raw material is put into wet grinding in ball mill, is mixed into nano yttrium oxide, nano aluminium oxide, nano zircite, nano-titanium oxide part, obtains
Obtain ceramic whiteware kettle body glaze slip.
9. the preparation process with high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint according to claim 7 or 8, it is characterised in that:
Glazing process in the step 4 is leaching glaze.
10. the preparation process according to claim 9 with high temperature resistant, the ceramic whiteware pot of explosion-proof glaze paint, it is characterised in that:Institute
The Baume Hydrometer concentration of glaze slip is 50-53 degree when stating step 4 glazing.