CN104529360A - 一种外墙用不易开裂的复合保温砂浆 - Google Patents

一种外墙用不易开裂的复合保温砂浆 Download PDF

Info

Publication number
CN104529360A
CN104529360A CN201410746700.5A CN201410746700A CN104529360A CN 104529360 A CN104529360 A CN 104529360A CN 201410746700 A CN201410746700 A CN 201410746700A CN 104529360 A CN104529360 A CN 104529360A
Authority
CN
China
Prior art keywords
parts
sodium
composite thermal
insulation mortar
kaolin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410746700.5A
Other languages
English (en)
Inventor
李松涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410746700.5A priority Critical patent/CN104529360A/zh
Publication of CN104529360A publication Critical patent/CN104529360A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种外墙用不易开裂的复合保温砂浆，其是由下述重量份的原料制得：维生素C 0.1-0.2，蜂蜜0.5-1、包膜高岭土10-15、a-氰基丙烯酸酯 0.2-0.4、甜菜碱 0.1-0.2、硅酸盐水泥20-25、玻化微珠30-50、聚丙烯纤维0.05-0.2、大理石4-8、石膏1-3、富铝土 3-5、乙二醇2-3、醋酸钠1-3、硝酸铵1-3，三聚磷酸钠1-3、乙酸钠1-3、木质素磺酸钙1-3、三聚磷酸钾0.1-0.2、可再分散乳胶粉 10-20、草酸0.1-0.3。

Description

一种外墙用不易开裂的复合保温砂浆
技术领域
本发明涉及砂浆领域，确切地说是一种外墙用不易开裂的复合保温砂浆。
背景技术
无机外墙用不易开裂的复合保温砂浆是一种用于建筑物内外墙粉刷的新型保温节能砂浆材料，根据胶凝材料的不同分为水泥基无机外墙用不易开裂的复合保温砂浆和石膏基无机外墙用不易开裂的复合保温砂浆。
有机外墙用不易开裂的复合保温砂浆是一种用于建筑物内外墙的新型保温节能外墙用不易开裂的复合保温砂浆材料，以有机类的轻质保温颗粒作为轻骨料，加由胶凝材料、聚合物添加剂及其他填充料等组成的聚合物干粉砂浆保温材料。
发明内容
本发明的目的在于提供一种外墙用不易开裂的复合保温砂浆。
上述目的通过以下方案实现：
 一种外墙用不易开裂的复合保温砂浆，其特征在于：其是由下述重量份的原料制得：维生素C 0.1-0.2，蜂蜜0.5-1、包膜高岭土10-15、a-氰基丙烯酸酯 0.2-0.4、甜菜碱 0.1-0.2、硅酸盐水泥20-25、玻化微珠30-50、聚丙烯纤维0.05-0.2、大理石4-8、石膏1-3、富铝土 3-5、乙二醇2-3、醋酸钠1-3、硝酸铵1-3，三聚磷酸钠1-3、乙酸钠1-3、木质素磺酸钙1-3、三聚磷酸钾0.1-0.2、可再分散乳胶粉 10-20、草酸0.1-0.3；
所述的包膜高岭土由下述重量份的原料制得：高岭土80-110、六偏磷酸钠0.3-0.5、氨基磺酸0.3-0.6、纳米碳6-10、酒石酸0.01-0.03、氧化淀粉7-15、氟化钙0.3-0.5、乳糖0.1-0.2、羟甲基纤维素3-5、阴离子聚丙烯酰胺3-6、月桂酸钠0.1-0.2、十二烷基苯磺酸钠0.1-0.2、硬脂酸0.1-0.2、三乙醇胺油酸皂0.1-0.3；
所述的包膜高岭土的制备方法为：称取氧化淀粉于反应釜，并加水，于100-200转/分下配成浓度为10-20wt%的悬浮液，加入六偏磷酸钠、氨基磺酸、酒石酸、纳米碳、氟化钙、乳糖，再70-80转/分搅拌50-70min，再加入其余原料，40-50转/粉搅拌30-40min，调节pH值为8-9，静置浆料30-60分钟；将所得浆料进行抽滤、水洗，所得滤饼经烘干、粉碎得到包膜高岭土。
所述的一种外墙用不易开裂的复合保温砂浆，其特征在于：
制备方法包括以下步骤：
（1）a-氰基丙烯酸酯 、甜菜碱、乙二醇、醋酸钠、硝酸铵、三聚磷酸钠、乙酸钠混匀后，加适量水，于40-50℃下搅拌25-50min，得改性液；
（2）大理石破碎，过100-120目筛，与富铝土、包膜高岭土混匀得混合粉体；
（3)混合粉体放入改性液中，80-120转/分下搅拌20-40min，静置2-5小时后，过滤，烘干，得改性粉体备用；
（4）改性粉体再与剩余原料以及适量水混匀后，55-60℃下搅拌10-30min，即得。
本发明的有益效果为：本发明的优点是通过添加改性的填料，使得其具有较强的保温效果，施工结束后不易开鼓、脱落，不容易开裂。
具体实施方式
一种外墙用不易开裂的复合保温砂浆，其是由下述重量（kg)的原料制得：维生素C 0.2，蜂蜜0.5、包膜高岭土15、a-氰基丙烯酸酯0.4、甜菜碱 0.2、硅酸盐水泥25、玻化微珠40、聚丙烯纤维0.2、大理石8、石膏3、富铝土 5、乙二醇3、醋酸钠1、硝酸铵3，三聚磷酸钠1、乙酸钠3、木质素磺酸钙3、三聚磷酸钾0.2、可再分散乳胶粉20、草酸0.3；
所述的包膜高岭土由下述重量（kg)的原料制得：高岭土110、六偏磷酸钠0.5、氨基磺酸0.6、纳米碳10、酒石酸0.03、氧化淀粉15、氟化钙0.5、乳糖0.2、羟甲基纤维素5、阴离子聚丙烯酰胺6、月桂酸钠0.2、十二烷基苯磺酸钠0.2、硬脂酸0.2、三乙醇胺油酸皂0.3；
所述的包膜高岭土的制备方法为：称取氧化淀粉于反应釜，并加水，于140转/分下配成浓度为20wt%的悬浮液，加入六偏磷酸钠、氨基磺酸、酒石酸、纳米碳、氟化钙、乳糖，再80转/分搅拌60min，再加入其余原料，50转/粉搅拌40min，调节pH值为8.2，静置浆料50分钟；将所得浆料进行抽滤、水洗，所得滤饼经烘干、粉碎得到包膜高岭土。
所述的一种外墙用不易开裂的复合保温砂浆，
制备方法包括以下步骤：
（1）a-氰基丙烯酸酯 、甜菜碱、乙二醇、醋酸钠、硝酸铵、三聚磷酸钠、乙酸钠混匀后，加适量水，于50℃下搅拌50min，得改性液；
（2）大理石破碎，过100目筛，与富铝土、包膜高岭土混匀得混合粉体；
（3)混合粉体放入改性液中，120转/分下搅拌30min，静置4小时后，过滤，烘干，得改性粉体备用；
（4）改性粉体再与剩余原料以及适量水混匀后，60℃下搅拌30min，即得。
    本实施例涂墙后，测试其导热系数为0.052W/(m·K)，28天标准养护下拉伸粘结强度为0.94MPa,28天标准养护下泡于水中七天拉伸粘结强度为0.59MPa，不透水性（0.3MPa,30min)：不透水。

Claims (2)

1.一种外墙用不易开裂的复合保温砂浆，其特征在于：其是由下述重量份的原料制得：
维生素C 0.1-0.2，蜂蜜0.5-1、包膜高岭土10-15、a-氰基丙烯酸酯 0.2-0.4、甜菜碱 0.1-0.2、硅酸盐水泥20-25、玻化微珠30-50、聚丙烯纤维0.05-0.2、大理石4-8、石膏1-3、富铝土 3-5、乙二醇2-3、醋酸钠1-3、硝酸铵1-3，三聚磷酸钠1-3、乙酸钠1-3、木质素磺酸钙1-3、三聚磷酸钾0.1-0.2、可再分散乳胶粉 10-20、草酸0.1-0.3；
所述的包膜高岭土由下述重量份的原料制得：高岭土80-110、六偏磷酸钠0.3-0.5、氨基磺酸0.3-0.6、纳米碳6-10、酒石酸0.01-0.03、氧化淀粉7-15、氟化钙0.3-0.5、乳糖0.1-0.2、羟甲基纤维素3-5、阴离子聚丙烯酰胺3-6、月桂酸钠0.1-0.2、十二烷基苯磺酸钠0.1-0.2、硬脂酸0.1-0.2、三乙醇胺油酸皂0.1-0.3；
所述的包膜高岭土的制备方法为：称取氧化淀粉于反应釜，并加水，于100-200转/分下配成浓度为10-20wt%的悬浮液，加入六偏磷酸钠、氨基磺酸、酒石酸、纳米碳、氟化钙、乳糖，再70-80转/分搅拌50-70min，再加入其余原料，40-50转/粉搅拌30-40min，调节pH值为8-9，静置浆料30-60分钟；将所得浆料进行抽滤、水洗，所得滤饼经烘干、粉碎得到包膜高岭土。
2.根据权利要求1所述的一种外墙用不易开裂的复合保温砂浆，其特征在于：制备方法包括以下步骤：
（1）a-氰基丙烯酸酯 、甜菜碱、乙二醇、醋酸钠、硝酸铵、三聚磷酸钠、乙酸钠混匀后，加适量水，于40-50℃下搅拌25-50min，得改性液；
（2）大理石破碎，过100-120目筛，与富铝土、包膜高岭土混匀得混合粉体；
（3)混合粉体放入改性液中，80-120转/分下搅拌20-40min，静置2-5小时后，过滤，烘干，得改性粉体备用；
（4）改性粉体再与剩余原料以及适量水混匀后，55-60℃下搅拌10-30min，即得。
CN201410746700.5A 2014-12-09 2014-12-09 一种外墙用不易开裂的复合保温砂浆 Pending CN104529360A (zh)