CN103121825A - 以工业副产石膏采用免煅烧技术生产的轻质保温砂浆及其制备方法 - Google Patents
以工业副产石膏采用免煅烧技术生产的轻质保温砂浆及其制备方法 Download PDFInfo
- Publication number
- CN103121825A CN103121825A CN 201310082420 CN201310082420A CN103121825A CN 103121825 A CN103121825 A CN 103121825A CN 201310082420 CN201310082420 CN 201310082420 CN 201310082420 A CN201310082420 A CN 201310082420A CN 103121825 A CN103121825 A CN 103121825A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- industry
- gypsum
- aglite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了以工业副产石膏采用免煅烧技术生产的轻质保温砂浆及其制备方法。其中,制备轻质保温砂浆的方法包括以下步骤:(1)按重量份取工业副产石膏34~36份,高岭土10~15份、高分子微矿粉3~5份、半水石膏8~12份、钢渣20份,乳胶粉5~7份,羟丙基甲基纤维素2~4份,聚丙烯短纤维0.3-0.4份,水泥18~22份;(2)将上述原料通过雷蒙磨机磨到细度200目,再添加轻质骨料40~45份(重量)混合搅拌,装袋。本发明突破了传统的以水泥为主要原料添加粉煤灰矿渣等材料制成轻质保温砂浆的做法,让石膏作为胶凝材料应用到干粉砂浆技术当中。并且利用免煅烧技术简化了生产工艺,克服了传统煅烧工艺,投入大、成本高、耗能、污染的弊端。
Description
技术领域
本发明涉及一种以工业副产石膏采用免煅烧技术生产的轻质保温砂浆及其制备方法。
背景技术
国家***2011年12月10日2919号文件明确指出:工业副产石膏综合利用是战略性新兴产业,具有广阔的发展前景。固体废弃物综合利用是文件的指导思想核心,重点发展脱硫石膏,磷石膏生产建材制品。以工业副产石膏采用免煅烧技术生产轻质保温砂浆在建筑上用量非常大,其中用于聚苯板或挤塑板保温***表面局部找平,有时也用于窗口四周局部保温。南方地区则主要用于外墙整体保温抹灰。可广泛用于墙体保温和找平,按照热工计算,可降低外墙保温的设计厚度。
传统行业以水泥为主要原料添加粉煤灰矿渣等材料制成轻质保温砂浆,所用水泥基会因热胀冷缩容易产生开裂、起鼓等现象。
现有技术中,使用石膏多采用煅烧工艺,该工艺带来了投入大、成本高、耗能、污染的弊端,存在二次耗能、二次污染的问题。
发明内容
本发明要解决的技术问题是提供一种以工业副产石膏采用免煅烧技术生产的轻质保温砂浆。
本发明要解决的另外一个技术问题是提供一种以工业副产石膏免煅烧技术制备轻质保温砂浆的方法。
对于轻质保温砂浆,本发明采用的技术方案是:由下述重量配比的原料制成的:
工业副产石膏34~36份,高岭土10~15份、高分子微矿粉3~5份、半水石膏8~12份、钢渣20~22份,乳胶粉5~7份,羟丙基甲基纤维素2~4份,聚丙烯短纤维0.3-0.4份,水泥18~22份,轻质骨料40~45份。
作为优选,轻质保温砂浆由下述重量配比的原料制成的:
工业副产石膏34份,高岭土10份,高分子微矿粉3份、半水石膏8份、钢渣20份,乳胶粉5份,羟丙基甲基纤维素2份,聚丙烯短纤维0.3份,水泥18份,轻质骨料40份。
作为优选,工业副产石膏是指工业生产排出的以硫酸钙为主要成分的副产品,其包括脱硫石膏,磷石膏,柠檬酸石膏。
石膏:
1)具有A级防火,保温隔热性能:石膏硬化体是一种多孔质材料,导热系数小,保温隔热性能好。
2)具有呼吸功能:当室内环境湿度较大时,呼吸孔自动吸湿;在相反条件下,能自动释放储备的水份,反复循环,将室内湿度控制在适宜范围之内,为居住者创造有利舒适的生活环境。
作为优选,轻质骨料为膨胀珍珠岩颗粒料或玻化微珠轻质骨料。
对于轻质保温砂浆的制备方法,本发明采用的技术方案是:包括以下步骤:
(1)按重量份取工业副产石膏34~36份,高岭土10~15份、高分子微矿粉3~5份、半水石膏8~12份、钢渣20~22份,乳胶粉5~7份,羟丙基甲基纤维素2~4份,聚丙烯短纤维0.3-0.4份,水泥18~22份;
(2)将上述原料通过雷蒙磨机磨到细度200目,再添加轻质骨料40~45重量份混合搅拌,装袋。
作为优选,轻质保温砂浆的制备方法包括以下步骤:
(1)按重量份取工业副产石膏34份,高岭土10份,高分子微矿粉3份、半水石膏8份、钢渣20份,乳胶粉5份,羟丙基甲基纤维素2份,聚丙烯短纤维0.3份,水泥18份;
(2)将上述原料通过雷蒙磨机磨到细度200目,再添加轻质骨料40重量份混合搅拌,装袋。
本发明的有益效果是:
1、利用免煅烧技术简化了生产工艺,克服传统煅烧工艺,投入大、成本高、耗能、污染的弊端;解决了二次耗能、二次污染的技术难题。
2、突破了传统的以水泥为主要原料添加粉煤灰矿渣等材料制成轻质保温砂浆的做法,让石膏作为一个全新的胶凝材料应用到干粉砂浆技术当中。以石膏基为主要原料不会象水泥基那样,因热胀冷缩产生开裂、起鼓等现象,用在外墙保温***中无需网格布。
具体实施方式
一种以工业副产石膏免煅烧技术制备轻质保温砂浆的方法,包括以下步骤:
(1)按重量份取工业副产石膏34份,高岭土10份,高分子微矿粉3份、半水石膏8份、钢渣20份,乳胶粉5份,羟丙基甲基纤维素2份,聚丙烯短纤维0.3份,水泥18份;
(2)将上述原料通过雷蒙磨机磨到细度200目,再添加轻质骨料40重量份混合搅拌,装袋。
本实施例的轻质砂浆,具有容重低,保温性能好,收缩值低等物理性能。
以上所述的本发明实施方式,并不构成对本发明保护范围的限定。任何在本发明的精神和原则之内所作的修改、等同替换和改进等,均应包含在本发明的权利要求保护范围之内。
Claims (9)
1.以工业副产石膏采用免煅烧技术生产的轻质保温砂浆,其特征在于,由下述重量配比的原料制成的:
工业副产石膏34~36份,高岭土10~15份、高分子微矿粉3~5份、半水石膏8~12份、钢渣20~22份,乳胶粉5~7份,羟丙基甲基纤维素2~4份,聚丙烯短纤维 0.3-0.4份,水泥18~22份,轻质骨料40~45份。
2.根据权利要求1所述的轻质保温砂浆,其特征在于,由下述重量配比的原料制成的:
工业副产石膏34份,高岭土10份,高分子微矿粉3份、半水石膏8份、钢渣20份,乳胶粉5份,羟丙基甲基纤维素2份,聚丙烯短纤维0.3份,水泥18份,轻质骨料40份。
3.根据权利要求1所述的轻质保温砂浆,其特征在于,所述工业副产石膏是指工业生产排出的以硫酸钙为主要成分的副产品,其包括脱硫石膏,磷石膏,柠檬酸石膏。
4.根据权利要求1所述的轻质保温砂浆,其特征在于,所述轻质骨料为膨胀珍珠岩颗粒料或玻化微珠轻质骨料。
5.一种以工业副产石膏免煅烧技术制备轻质保温砂浆的方法,其特征在于,包括以下步骤:
(1)按重量份取工业副产石膏34~36份,高岭土10~15份、高分子微矿粉3~5份、半水石膏8~12份、钢渣20~22份,乳胶粉5~7份,羟丙基甲基纤维素2~4份,聚丙烯短纤维0.3-0.4份,水泥18~22份;
(2)将上述原料通过雷蒙磨机磨到细度200目,再添加轻质骨料40~45重量份混合搅拌,装袋。
6.根据权利要求5所述的制备方法,其特征在于,包括以下步骤:
(1)按重量份取工业副产石膏34份,高岭土10份,高分子微矿粉3份、半水石膏8份、钢渣20份,乳胶粉5份,羟丙基甲基纤维素2份,聚丙烯短纤维0.3份,水泥18份;
(2)将上述原料通过雷蒙磨机磨到细度200目,再添加轻质骨料40重量份混合搅拌,装袋。
7.根据权利要求5所述的制备方法,其特征在于,所述轻质骨料为膨胀珍珠岩颗粒料或玻化微珠轻质骨料。
8.根据权利要求5所述的轻质保温砂浆,其特征在于,所述工业副产石膏是指工业生产排出的以硫酸钙为主要成分的副产品,其包括脱硫石膏,磷石膏,柠檬酸石膏。
9.根据权利要求5所述的轻质保温砂浆,其特征在于,所述轻质骨料为膨胀珍珠岩颗粒料或玻化微珠轻质骨料。