CN104045272A - 一种耐火高强度混凝土及其制备方法 - Google Patents

一种耐火高强度混凝土及其制备方法 Download PDF

Info

Publication number
CN104045272A
CN104045272A CN201410178393.5A CN201410178393A CN104045272A CN 104045272 A CN104045272 A CN 104045272A CN 201410178393 A CN201410178393 A CN 201410178393A CN 104045272 A CN104045272 A CN 104045272A
Authority
CN
China
Prior art keywords
parts
concrete
water
stir
plant ash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410178393.5A
Other languages
English (en)
Inventor
方明珠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zongyang County Tian Zhu New Building Materials Co Ltd
Original Assignee
Zongyang County Tian Zhu New Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zongyang County Tian Zhu New Building Materials Co Ltd filed Critical Zongyang County Tian Zhu New Building Materials Co Ltd
Priority to CN201410178393.5A priority Critical patent/CN104045272A/zh
Publication of CN104045272A publication Critical patent/CN104045272A/zh
Pending legal-status Critical Current

Abstract

一种耐火高强度混凝土，由下列重量份的原料制成：水泥290-310、超细矿粉20-30、粉煤灰60-70、石子900-920、砂210-230、水120-130、改性草木灰80-100、方镁石粉100-130、氟硅酸镁3-4、氢氧化铝3-4、氯化亚铁2-3、钢渣60-70、植酸钠2-3、磷酸三苯酯5-8、柠檬酸钠2-4、聚羧酸高效减水剂7-8、聚苯乙烯微球4-6、蒙脱土20-30、十六烷基三甲基氯化铵2-3；本发明混凝土通过使用方镁石粉，具有优异的耐火性能；通过添加超细矿粉和蒙脱土，增加了混凝土密实性，抗压抗折强度高、抗裂性能好、抗冲击能力强，耐久性好；通过使用改性草木灰，增加了混凝土的防水性，可塑性和可泵送效果好。

Description

一种耐火高强度混凝土及其制备方法
技术领域
本发明属于建筑材料领域，特别涉及一种耐火高强度混凝土及其制备方法。 
背景技术
混凝土作为建筑材料已有一百多年历史，具有很多无法比拟的优点，例如抗压强度高，取材容易，易成型，价格低廉，可与其他材料结合制成各种沉重固件。 
随着混凝土组成材料的不断发展，人们对混凝土的性能要求不仅仅局限于抗压强度，而是在立足强度的基础上，更加注重混凝土的耐久性、变形性能、防火抗爆性能、防渗水性能、韧性、耐腐蚀性、保温性、健康环保性以及降低成本等等综合指标的平衡和协调。混凝土各项性能指标的要求比以前更明确、细化和具体。同时，建筑设备水平的提升，新型施工工艺的不断涌现和推广，使混凝土技术适应了不同的设计、施工和使用要求，发展很快。因此，研制性能更加优异、功能更加强大、更适应新工艺的混凝土就显得尤为重要。 
发明内容
本发明的目的在于提供一种耐火高强度混凝土及其制备方法，该混凝土具有优异的耐火性能，密实性好，抗压抗折强度高、抗裂性能好、抗冲击能力强，耐久性好，可泵送效果好。 
本发明的技术方案如下： 
一种耐火高强度混凝土,其特征在于由下列重量份的原料制成：水泥290-310、超细矿粉20-30、粉煤灰60-70、石子900-920、砂210-230、水120-130、改性草木灰80-100、方镁石粉100-130、氟硅酸镁3-4、氢氧化铝3-4、氯化亚铁2-3、钢渣60-70、植酸钠2-3、磷酸三苯酯5-8、柠檬酸钠2-4、聚羧酸高效减水剂7-8、聚苯乙烯微球4-6、蒙脱土20-30、十六烷基三甲基氯化铵2-3；
所述改性草木灰由下列重量份的原料制成：草木灰80-90、十三氟辛基三甲氧基硅烷5-7、聚葡萄糖1-2、木钙1-2、玻璃粉10-20、微孔硅酸钙8-10、丙烯酸甲酯3-4、石蜡乳液3-4、超细矿粉10-15、环氧丙烯酸酯6-7、碳酸钙3-4、过硫酸铵0.4-0.5、羟丙基淀粉0.7-1、磷酸酯0.6-0.9、水40-50；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1-2天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至80-90℃，搅拌30-40分钟，搅拌烘干粉碎成100-200目颗粒，再与其他剩余成分混合，分散研磨10-15分钟，即得。
所述的耐火高强度混凝土的制备方法，其特征在于包括以下步骤： 
（1）将钢渣、磷酸三苯酯、氢氧化铝、蒙脱土混合，加入十六烷基三甲基氯化铵搅拌均匀，分散研磨20-30分钟，得到混合物；
（2）将植酸钠、聚羧酸高效减水剂、聚苯乙烯微球、氟硅酸镁、氯化亚铁与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌2-6分钟，然后浇注；
（4）浇筑后在 5-25℃的潮湿环境中进行养护，养护时间不少于 7d。
本发明的有益效果 
本发明混凝土通过使用方镁石粉，具有优异的耐火性能；通过添加超细矿粉和蒙脱土，增加了混凝土密实性，抗压抗折强度高、抗裂性能好、抗冲击能力强，耐久性好；通过使用改性草木灰，增加了混凝土的防水性，可塑性和可泵送效果好。
具体实施方式
一种耐火高强度混凝土,由下列重量份(公斤)的原料制成：水泥300、超细矿粉25、粉煤灰65、石子910、砂220、水125、改性草木灰90、方镁石粉120、氟硅酸镁3.5、氢氧化铝3.5、氯化亚铁2.5、钢渣65、植酸钠2.5、磷酸三苯酯7、柠檬酸钠3、聚羧酸高效减水剂7.5、聚苯乙烯微球5、蒙脱土25、十六烷基三甲基氯化铵2.5； 
所述改性草木灰由下列重量份（公斤）的原料制成：草木灰85、十三氟辛基三甲氧基硅烷6、聚葡萄糖1.5、木钙1.5、玻璃粉15、微孔硅酸钙9、丙烯酸甲酯3.5、石蜡乳液3.5、超细矿粉13、环氧丙烯酸酯6.5、碳酸钙3.5、过硫酸铵0.5、羟丙基淀粉0.8、磷酸酯0.7、水45；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至85℃，搅拌35分钟，搅拌烘干粉碎成160目颗粒，再与其他剩余成分混合，分散研磨14分钟，即得。
所述的耐火高强度混凝土的制备方法，包括以下步骤： 
（1）将钢渣、磷酸三苯酯、氢氧化铝、蒙脱土混合，加入十六烷基三甲基氯化铵搅拌均匀，分散研磨25分钟，得到混合物；
（2）将植酸钠、聚羧酸高效减水剂、聚苯乙烯微球、氟硅酸镁、氯化亚铁与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌5分钟，然后浇注；
（4）浇筑后在 10-15℃的潮湿环境中进行养护，养护7d。
实验数据： 
该实施例的混凝土坍落度为12cm,强度等级为C45，抗压强度46MPa，抗折强度19.6Mpa。

Claims (2)

1.一种耐火高强度混凝土,其特征在于由下列重量份的原料制成：水泥290-310、超细矿粉20-30、粉煤灰60-70、石子900-920、砂210-230、水120-130、改性草木灰80-100、方镁石粉100-130、氟硅酸镁3-4、氢氧化铝3-4、氯化亚铁2-3、钢渣60-70、植酸钠2-3、磷酸三苯酯5-8、柠檬酸钠2-4、聚羧酸高效减水剂7-8、聚苯乙烯微球4-6、蒙脱土20-30、十六烷基三甲基氯化铵2-3；
所述改性草木灰由下列重量份的原料制成：草木灰80-90、十三氟辛基三甲氧基硅烷5-7、聚葡萄糖1-2、木钙1-2、玻璃粉10-20、微孔硅酸钙8-10、丙烯酸甲酯3-4、石蜡乳液3-4、超细矿粉10-15、环氧丙烯酸酯6-7、碳酸钙3-4、过硫酸铵0.4-0.5、羟丙基淀粉0.7-1、磷酸酯0.6-0.9、水40-50；制作方法为：将草木灰与石蜡乳液、十三氟辛基三甲氧基硅烷混合均匀，放置1-2天，再与微孔硅酸钙、丙烯酸甲酯、超细矿粉、环氧丙烯酸酯、过硫酸铵、水混合，搅拌成泥状，加热至80-90℃，搅拌30-40分钟，搅拌烘干粉碎成100-200目颗粒，再与其他剩余成分混合，分散研磨10-15分钟，即得。
2.根据权利要求1所述的耐火高强度混凝土的制备方法，其特征在于包括以下步骤：
（1）将钢渣、磷酸三苯酯、氢氧化铝、蒙脱土混合，加入十六烷基三甲基氯化铵搅拌均匀，分散研磨20-30分钟，得到混合物；
（2）将植酸钠、聚羧酸高效减水剂、聚苯乙烯微球、氟硅酸镁、氯化亚铁与水混合，搅拌均匀，得到混合物；
（3）将其他剩余成分与第一步和第二步得到的混合物混合，搅拌2-6分钟，然后浇注；
（4）浇筑后在 5-25℃的潮湿环境中进行养护，养护时间不少于 7d。
CN201410178393.5A 2014-04-30 2014-04-30 一种耐火高强度混凝土及其制备方法 Pending CN104045272A (zh)