CN104513046A - 一种防静电水泥基自流平面层砂浆的制备方法 - Google Patents
一种防静电水泥基自流平面层砂浆的制备方法 Download PDFInfo
- Publication number
- CN104513046A CN104513046A CN201310452008.7A CN201310452008A CN104513046A CN 104513046 A CN104513046 A CN 104513046A CN 201310452008 A CN201310452008 A CN 201310452008A CN 104513046 A CN104513046 A CN 104513046A
- Authority
- CN
- China
- Prior art keywords
- cement
- water
- carbon fiber
- based self
- layer mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种防静电水泥基自流平面层砂浆的制备方法，本发明选用高铝水泥、铝水泥、硅酸盐水泥、粉煤灰、脱硫石膏、石英砂、尾矿砂、碳纤维、石墨粉、可再分散乳胶粉、纤维素醚、减水剂、消泡剂、速凝早强剂及缓凝剂为原料，并按比例配制，经转速60-200转／分钟的高速混合机混合8-10分钟至均匀制得。本发明通过大量添加粉煤灰等工业废渣，变废为宝，节约大量资源，带来可观的社会经济效益，原料中的碳纤维和石墨粉具有导电性，二者复合应用在砂浆水化物中形成立体的点线面交织的三维网状导电***，利于静电的排出和释放。另外，浇注后的自流平面层砂浆表面平整，同时也可降低车辆碾压走过地面的噪音，适用于需要防静电场所的地面找平与装饰。
Description
技术领域
本发明涉及到自流平面层砂浆的生产技术领域，具体地讲，涉及到一种防静电水泥基自流平面层砂浆的制备方法。
背景技术
自流平砂浆是一种由无机或者有机胶凝材料、细骨料、填料及外加剂组成，加水搅拌后具有流动性或稍加辅助性铺摊就能找平的地面材料，它具有流动度大、施工快表面光滑平整等优点，无机自流平砂浆包括水泥基自流平砂浆和石膏基自流平砂浆，其中水泥基自流平材料应用量最大，广泛应用在大型超市地面、生产车间、车库及仓库的地面上。
现有的水泥基自流平面层砂浆绝大部分在配方中是使用半水石膏和二水石膏，为节约资源和综合利用，人们开始研究利用粉煤灰和脱硫石膏这类工业固体废物生产自流平材料，但是这些材料的导电性能很差，众所周知，任何两个不同材质的物体接触后再分离，即可产生静电，最常见的就是摩擦生电，材料的绝缘性越好，越容易产生摩擦生电。静电放电造成电击将危及人身安全，静电发生在易燃易爆品或粉尘、油雾的生产场所极易引起***和火灾，尤其在电子、通讯、印刷、计算机房、光电车间、LED生产车间、精密机械、粉体、化学、兵工、航天等领域很难推广应用。静电对人类日常工作和生活所带来的危害由来已久，随着工业化发展及人们对生活质量的高度追求，因地面摩擦产生的静电对人体及器具等的损害越来越受到重视。
发明内容
本发明的目的就是在大量利用粉煤灰及脱硫石膏工业废弃物的条件下，提供一种防静电水泥基自流平面层砂浆的制备方法。
实现本发明的一种防静电水泥基自流平面层砂浆的制备方法是：
一、首先进行原料选取：
高铝水泥：CA50-G6型；
硅酸盐水泥：硅酸盐或普通硅酸盐水泥，强度等级42.5；
粉煤灰：I级；
脱硫石膏：二水硫酸钙的含量>93％且目数≥200；
石英砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
尾矿砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
碳纤维：长度2-5mm的聚丙烯腈基碳纤维；
石墨粉：300-800目鳞片石墨粉且碳含量≥99％；
可再分散乳胶粉：玻璃化转移温度为-10℃至-17℃的乳胶粉，醋酸乙烯酯、叔碳酸乙烯酯或丙烯酸酯的一种或几种的组合；
纤维素醚：粘度600-1000mPa·s的低粘度纤维醚；
减水剂：粉末状的聚羧酸减水剂，减水率≥20％；
消泡剂：具有流平性能的有机硅消泡剂；
速凝早强剂：工业级碳酸锂；
缓凝剂：柠檬酸、酒石酸或葡萄糖酸钠的一种或几种的组合。
二、原料选定后按下列重量(％)配制：
三、原料选定后其工艺步骤为：
按上述重量比例称量好物料，按下列先后顺序依次投入转速60-200转／分钟的高速混合机：高铝水泥、硅酸盐水泥、粉煤灰、脱硫石膏、碳纤维、石墨粉、可再分散乳胶粉、纤维素醚、减水剂、消泡剂、速凝早强剂、缓凝剂、石英砂、尾矿砂，混合8-10分钟至均匀，包装即得本发明的防静电水泥基自流平面层砂浆。
本发明的防静电水泥基自流平面层砂浆施工时，直接按粉料：水=1：0.22使用搅拌枪搅拌4-5分钟至均匀即可使用。
本发明的防静电水泥基自流平面层砂浆通过大量添加粉煤灰、脱硫石膏、尾矿砂等工业废渣，变废为宝，节约大量资源，带来可观的社会经济效益，原料中的碳纤维和石墨粉具有导电性，二者复合应用在砂浆水化物中形成立体的点线面交织的三维网状导电***，利于静电的排出和释放。另外本发明的防静电水泥基自流平面层砂浆还具有地面找平和终饰效果，浇注后的自流平整体表面平整，表面柔弹性使行人走路的舒适度提高，同时也可降低车辆碾压走过地面的噪音，适用于电子、通讯、印刷、计算机房、光电车间、LED生产车间、SMT车间、精密机械、粉体、化学、兵工、航天等领域需要防静电场所的地面找平与装饰。
工业废物利用是国家环保节能政策所大力提倡的，工业废物消极堆存占用大量土地，造成人力物力的浪费，根据工信部的测算，“十二五”期间，大宗工业固体废物预计总产生量将达150亿吨，堆存量将净增80亿吨，总堆存量将达到270亿吨，大宗工业固体废物堆存将新增占用土地40万亩。在不影响和改善产品性能的前提下，水泥基自流平面层材料中大量利用粉煤灰及脱硫石膏等工业废物将有利于保护环境、减少土地占用。
本发明的防静电水泥基自流平面层砂浆基本性能指标为：
表1防静电水泥基自流平面层砂浆基本性能
由表1可知，本发明提出的一种防静电水泥基自流平面层砂浆满足国家水泥基自流平建材行业标准JC／T985-2005要求，强度等级高达C35F10，同时具有优良的导电性能，压折比≤3及尺寸变化率为-0.15～+0.15的严格控制使水泥基自流平面层砂浆具有优异的抗裂性，从而保证防静电水泥基自流平面层砂浆材料的安全、耐久使用。
具体实施方式
实施例1
实现本发明的一种防静电水泥基自流平面层砂浆的制备方法的具体实施方式是：
一、首先进行原料选取：
高铝水泥：CA50-G6型；
硅酸盐水泥：硅酸盐水泥，强度等级42.5；
粉煤灰：I级；
脱硫石膏：二水硫酸钙的含量>93％且目数为200；
石英砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
尾矿砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
碳纤维：长度3mm的聚丙烯腈基碳纤维；
石墨粉：500目鳞片石墨粉且碳含量≥99％；
可再分散乳胶粉：玻璃化转移温度为-17℃的丙烯酸酯乳胶粉；
纤维素醚；粘度1000mPa·s的羟丙基甲基纤维素醚；
减水剂：粉末状的聚羧酸减水剂，减水率≥20％；
消泡剂：具有流平性能的有机硅消泡剂；
速凝早强剂：工业级碳酸锂；
缓凝剂：酒石酸。
二、原料选定后按下列重量(％)配制：
三、原料选定后其工艺步骤为：
按上述重量比例称量好物料，按下列先后顺序依次投入转速120转／分钟的高速混合机：高铝水泥、硅酸盐水泥、粉煤灰、脱硫石膏、碳纤维、石墨粉、可再分散乳胶粉、纤维素醚、减水剂、消泡剂、速凝早强剂、缓凝剂、石英砂、尾矿砂，混合8分钟至均匀，包装即得本发明的防静电水泥基自流平面层砂浆，其基本性能指标如表2所示。
本发明的防静电水泥基自流平面层砂浆施工时，按粉料：水=1：0.22使用搅拌枪搅拌4-5分钟至均匀，使用桶或泵送装置浇注均匀即可。
表2防静电水泥基自流平面层砂浆基本性能
实施例2
实现本发明的一种防静电水泥基自流平面层砂浆的制备方法的具体实施方式是：
一、首先进行原料选取：
高铝水泥：CA50-G6型；
硅酸盐水泥：硅酸盐水泥，强度等级42.5；
粉煤灰：I级；
脱硫石膏：二水硫酸钙的含量>93％且目数为200；
石英砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
尾矿砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
碳纤维：长度5mm的聚丙烯腈基碳纤维；
石墨粉：500目鳞片石墨粉且碳含量≥99％；
可再分散乳胶粉：玻璃化转移温度为-10℃的醋酸乙烯酯乳胶粉；
纤维素醚；粘度1000mPa·s的羟丙基甲基纤维素醚；
减水剂：粉末状的聚羧酸减水剂，减水率≥20％；
消泡剂：具有流平性能的有机硅消泡剂；
速凝早强剂：工业级碳酸锂；
缓凝剂：酒石酸。
二、原料选定后按下列重量(％)配制：
三、原料选定后其工艺步骤为：
按上述重量比例称量好物料，按下列先后顺序依次投入转速65转／分钟的高速混合机：高铝水泥、硅酸盐水泥、粉煤灰、脱硫石膏、碳纤维、石墨粉、可再分散乳胶粉、纤维素醚、减水剂、消泡剂、速凝早强剂、缓凝剂、石英砂、尾矿砂，混合10分钟至均匀，包装即得本发明的防静电水泥基自流平面层砂浆，其基本性能指标如表3所示。
本发明的防静电水泥基自流平面层砂浆施工时，按粉料：水=1：0.22使用搅拌枪搅拌4-5分钟至均匀，使用桶或泵送装置浇注均匀即可。
表3防静电水泥基自流平面层砂浆基本性能
Claims (3)
1.一种防静电水泥基自流平面层砂浆的制备方法，其特征在于：
一、首先进行原料选取：
高铝水泥：CA50-G6型；
硅酸盐水泥：硅酸盐或普通硅酸盐水泥，强度等级42.5；
粉煤灰：I级；
脱硫石膏：二水硫酸钙的含量>93％且目数≥200；
石英砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
尾矿砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
碳纤维：长度2-5mm的聚丙烯腈基碳纤维；
石墨粉：300-800目鳞片石墨粉且碳含量≥99％；
可再分散乳胶粉：玻璃化转移温度为-10℃至-17℃的乳胶粉，醋酸乙烯酯、叔碳酸乙烯酯或丙烯酸酯的一种或几种的组合；
纤维素醚：粘度600-1000mPa·s的低粘度纤维醚；
减水剂：粉末状的聚羧酸减水剂，减水率≥20％；
消泡剂：具有流平性能的有机硅消泡剂；
速凝早强剂：工业级碳酸锂；
缓凝剂：柠檬酸、酒石酸或葡萄糖酸钠的一种或几种的组合；
二、原料选定后按下列重量(％)配制：
三、原料选定后其工艺步骤为：
按上述重量比例称量好物料，按下列先后顺序依次投入转速60-200转／分钟的高速混合机：高铝水泥、硅酸盐水泥、粉煤灰、脱硫石膏、碳纤维、石墨粉、可再分散乳胶粉、纤维素醚、减水剂、消泡剂、速凝早强剂、缓凝剂、石英砂、尾矿砂，混合8-10分钟至均匀，包装即得本发明的防静电水泥基自流平面层砂浆。
2.根据权利要求1所述的一种防静电水泥基自流平面层砂浆的制备方法，其特征在于：
一、首先进行原料选取：
高铝水泥：CA50-G6型；
硅酸盐水泥：硅酸盐水泥，强度等级42.5；
粉煤灰：I级；
脱硫石膏：二水硫酸钙的含量>93％且目数为200；
石英砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
尾矿砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
碳纤维：长度3mm的聚丙烯腈基碳纤维；
石墨粉：500目鳞片石墨粉且碳含量≥99％；
可再分散乳胶粉：玻璃化转移温度为-17℃的丙烯酸酯乳胶粉；
纤维素醚；粘度1000mPa·s的羟丙基甲基纤维素醚；
减水剂：粉末状的聚羧酸减水剂，减水率≥20％；
消泡剂：具有流平性能的有机硅消泡剂；
速凝早强剂：工业级碳酸锂；
缓凝剂：酒石酸；
二、原料选定后按下列重量(％)配制：
三、原料选定后其工艺步骤为：
按上述重量比例称量好物料，按下列先后顺序依次投入转速120转／分钟的高速混合机：高铝水泥、硅酸盐水泥、粉煤灰、脱硫石膏、碳纤维、石墨粉、可再分散乳胶粉、纤维素醚、减水剂、消泡剂、速凝早强剂、缓凝剂、石英砂、尾矿砂，混合8分钟至均匀，包装即得本发明的防静电水泥基自流平面层砂浆。
3.根据权利要求1所述的一种防静电水泥基自流平面层砂浆的制备方法，其特征在于：
一、首先进行原料选取：
高铝水泥：CA50-G6型；
硅酸盐水泥：硅酸盐水泥，强度等级42.5；
粉煤灰：I级；
脱硫石膏：二水硫酸钙的含量>93％且目数为200；
石英砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
尾矿砂：目数为50-100，含泥量≤1％，含水率≤0.5％；
碳纤维：长度5mm的聚丙烯腈基碳纤维；
石墨粉：500目鳞片石墨粉且碳含量≥99％；
可再分散乳胶粉：玻璃化转移温度为-10℃的醋酸乙烯酯乳胶粉；
纤维素醚；粘度1000mPa·s的羟丙基甲基纤维素醚；
减水剂：粉末状的聚羧酸减水剂，减水率≥20％；
消泡剂：具有流平性能的有机硅消泡剂；
速凝早强剂：工业级碳酸锂；
缓凝剂：酒石酸；
二、原料选定后按下列重量(％)配制：
三、原料选定后其工艺步骤为：
按上述重量比例称量好物料，按下列先后顺序依次投入转速65转／分钟的高速混合机：高铝水泥、硅酸盐水泥、粉煤灰、脱硫石膏、碳纤维、石墨粉、可再分散乳胶粉、纤维素醚、减水剂、消泡剂、速凝早强剂、缓凝剂、石英砂、尾矿砂，混合10分钟至均匀，包装即得本发明的防静电水泥基自流平面层砂浆。