CN104497796A - High weather-resistant and anti-interference anticorrosive paint for power distribution cabinet - Google Patents
High weather-resistant and anti-interference anticorrosive paint for power distribution cabinet Download PDFInfo
- Publication number
- CN104497796A CN104497796A CN201410671640.5A CN201410671640A CN104497796A CN 104497796 A CN104497796 A CN 104497796A CN 201410671640 A CN201410671640 A CN 201410671640A CN 104497796 A CN104497796 A CN 104497796A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- power distribution
- distribution cabinet
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high weather-resistant and anti-interference anticorrosive paint for power distribution cabinets. The anticorrosive paint is characterized by comprising the following raw materials by weight: 22-25 parts of ethylene propylene terpolymer, 30-36 parts of bisphenol A type epoxy resin, 2-3 parts of chlorinated paraffin, 4-6 parts of glycol, 1-2 parts of dibutyl phthalate, 2-4 parts of vermiculite powder, 2-3 parts of celestite powder, 1-2 parts of triphenylmethyl ethylphenol polyoxyethylene ether, 2-3 parts of sodium benzoate, 5-7 parts of talcum powder, 2-3 parts of molybdenum pentachloride, 1-2 parts of vinyl tri(beta-methoxy ethoxy) silane, 1-2 parts of sulfonated lanolin calcium soap, 1-2 parts of carboxymethyl cellulose, 15-17 parts of butyl acetate, 6-9 parts of xylene and 4-7 parts of an aid. The paint provided by the invention has good decorative effect on the power distribution cabinet under natural conditions, and the paint film is smooth and flat, has good gloss and high weather resistance, and is not easy to turn yellowing or chalking; the added additive promotes the film forming ability of the paint, and also has anti-electromagnetic interference effect to prevent the interference on the electronic equipment in the power distribution cabinet, so as to avoid error signal.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly anti-interference power distribution cabinet antifouling paste of a kind of high durable and preparation method thereof.
Background technology
In recent years, along with the constant development of Chinese national economy, electricity needs presents a rapidly rising trend, and for meeting the household electricity needs of industrial or agricultural product and people, electrical network scale and electrical network general layout there occurs significant change.For meeting the continuous growth of power load, improving electrical network is the ability that load center transmits electric power, the substation of 110kV and above is progressively built at urban central zone, simultaneously because the geography in current city is expanded, the high voltage substation being arranged in outskirts of a town before many also includes city neighborhood in now, in addition due to the modernization restructuring construction in city, the power supply facilities such as the power traction substation of the modern transportation such as subway, light rail instrument are also progressively set up in city.Transforming plant primary equipment will produce various interfering source when running.Second set (as digital relay and monitoring equipment) is arranged on high-voltage switch gear cashier's office in a shop on the spot, near high-voltage power supply, is subject to strong electromagnetic.Various interference can be applied to electrical secondary system by different coupling paths; produce many junk information, likely cause communications management unit to crash, affect operations staff to the operation monitoring of station equipment and operation; to false protection be caused time serious, even cause structure deteriorate.Some substations happen occasionally because interference produces false protection, and the quality that anti-interference problem solves is directly connected to popularization and the development of Substation Automation System.Therefore, automation of transformation substations equipment anti-interference problem should cause the attention of design, operation, manufacturer, takes the necessary measures, and guarantees the safe operation of substation.The use of magnetic shielding coating be can yet be regarded as one safeguard procedures effectively.
Summary of the invention
The object of this invention is to provide anti-interference power distribution cabinet antifouling paste of a kind of high durable and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
The anti-interference power distribution cabinet antifouling paste of a kind of high durable, is made up of the raw material of following weight part: terpolymer EP rubber 22-25, bisphenol A type epoxy resin 30-36, clorafin 2-3, ethylene glycol 4-6, dibutyl phthalate 1-2, vermiculite power 2-4, celestite powder 2-3, triphen ethyl phenol Soxylat A 25-7 1-2, Sodium Benzoate 2-3, talcum powder 5-7, five boronation two molybdenum 2-3, vinyl three ('beta '-methoxy oxyethyl group) silane 1-2, sulphur forging Lanolin Calcium Soap 1-2, Walocel MT 20.000PV 1-2, N-BUTYL ACETATE 15-17, dimethylbenzene 6-9, auxiliary agent 4-7;
Described auxiliary agent is made up of the raw material of following weight part: calcium propionate 3-5, sulfuration oleic acid 1-2, hydrochloric acid wood oil 4-6, Silane coupling agent KH550 2-3, two ten four carbon alcohols ester 1-2, aluminum nitride powder 2-3, Sodium dehydroacetate 0.7-1.4, 2-amino-2-methyl-1-propanol 2-3, quaternary ammonium salt-modified organobentonite 2-3, tertbutyl peroxide 1-2, fatty alcohol-polyoxyethylene ether 1-2, vinyl acetate 5-8, vinylformic acid 3-5, ethanol 10-15, silver powder 3-4, expanded graphite 6-8, sheet cobalt powder 8-11, dilute sulphuric acid 0.4-0.8, preparation method is that sheet cobalt powder, silver powder, aluminum nitride powder, expanded graphite, ethanol, dilute sulphuric acid mix by (1), and temperature controls to react 20-30 minute at 70-80 ° of C, leaves standstill precipitation pressed powder for subsequent use, (2) product of hydrochloric acid wood oil, sulfuration oleic acid, vinyl acetate, vinylformic acid, fatty alcohol-polyoxyethylene ether and step (1) is mixed, carry out mechanical blending by high speed dispersion, then add tertbutyl peroxide stirring reaction 1-2 hour, (3) Silane coupling agent KH550 is added in the ethanol of 3-6 weight part, is sprayed onto after mixing on the product of step (2), then add all the other surplus materialss high speed dispersion 0.5-1 hour.
The anti-interference power distribution cabinet antifouling paste of a kind of high durable of the present invention, be made up of following concrete steps:
(1) vermiculite power, celestite powder, talcum powder, five boronation two molybdenums are added in the mixing solutions of dimethylbenzene and N-BUTYL ACETATE, ultrasonic disperse 20-30 minute, adds dibutyl phthalate, clorafin, auxiliary agent continuation stirring reaction 30-40 minute when being heated to 50-80 ° of C;
(2) product of step (1) is continued raised temperature to 80-90 ° of C, add terpolymer EP rubber, bisphenol A type epoxy resin, vinyl three ('beta '-methoxy oxyethyl group) silane, 1200-1400 rev/min of lower high-speed mixing stirring reaction 1-2 hour;
(3) surplus materials is added in the product of step (2), is added to grinding machine for grinding after mixing and is uniformly dispersed, filter and obtain the material that fineness is 20-40 μm, pack.
Advantage of the present invention is: paint of the present invention has good ornamental for place's power distribution cabinet under field conditions (factors), and paint film is smooth, glossiness is good, weathering resistance is high, inhibited from yellowing, efflorescence, the terpolymer EP rubber added has the characteristics such as good weathering resistance, ageing resistance, preservative property, resistance to salt water, the auxiliary agent added facilitates the film-forming properties of paint, and there is the effect of electromagnetism interference, prevent from disturbing the interference to electronic equipment in power distribution cabinet, the effect of signal in order not to make any any mistakes.
specific embodiments
Below by specific examples, the present invention is described in detail.
The anti-interference power distribution cabinet antifouling paste of a kind of high durable, is made up of the raw material of following weight part (kilogram): the forging of terpolymer EP rubber 23, bisphenol A type epoxy resin 35, clorafin 2, ethylene glycol 4, dibutyl phthalate 1, vermiculite power 3, celestite powder 2, triphen ethyl phenol Soxylat A 25-7 1, Sodium Benzoate 3, talcum powder 5, five boronation two molybdenum 3, vinyl three ('beta '-methoxy oxyethyl group) silane 1, sulphur Lanolin Calcium Soap 1, Walocel MT 20.000PV 1, N-BUTYL ACETATE 16, dimethylbenzene 7, auxiliary agent 5;
Described auxiliary agent is made up of the raw material of following weight part (kilogram): calcium propionate 5, sulfuration oleic acid 2, hydrochloric acid wood oil 4, Silane coupling agent KH550 2, two ten four carbon alcohols esters 1, aluminum nitride powder 3, Sodium dehydroacetate 0.9,2-amino-2-methyl-1-propanol 2, quaternary ammonium salt-modified organobentonite 2, tertbutyl peroxide 1, fatty alcohol-polyoxyethylene ether 1, vinyl acetate 8, vinylformic acid 4, ethanol 14, silver powder 3, expanded graphite 7, sheet cobalt powder 9, dilute sulphuric acid 0.6; Preparation method is that sheet cobalt powder, silver powder, aluminum nitride powder, expanded graphite, ethanol, dilute sulphuric acid mix by (1), and temperature controls to react 20-30 minute at 70-80 ° of C, leaves standstill precipitation pressed powder for subsequent use; (2) product of hydrochloric acid wood oil, sulfuration oleic acid, vinyl acetate, vinylformic acid, fatty alcohol-polyoxyethylene ether and step (1) is mixed, carry out mechanical blending by high speed dispersion, then add tertbutyl peroxide stirring reaction 1-2 hour; (3) Silane coupling agent KH550 is added in the ethanol of 3-6 weight part, is sprayed onto after mixing on the product of step (2), then add all the other surplus materialss high speed dispersion 0.5-1 hour.
The anti-interference power distribution cabinet antifouling paste of a kind of high durable of the present invention, be made up of following concrete steps:
(1) vermiculite power, celestite powder, talcum powder, five boronation two molybdenums are added in the mixing solutions of dimethylbenzene and N-BUTYL ACETATE, ultrasonic disperse 20-30 minute, adds dibutyl phthalate, clorafin, auxiliary agent continuation stirring reaction 30-40 minute when being heated to 50-80 ° of C;
(2) product of step (1) is continued raised temperature to 80-90 ° of C, add terpolymer EP rubber, bisphenol A type epoxy resin, vinyl three ('beta '-methoxy oxyethyl group) silane, 1200-1400 rev/min of lower high-speed mixing stirring reaction 1-2 hour;
(3) surplus materials is added in the product of step (2), is added to grinding machine for grinding after mixing and is uniformly dispersed, filter and obtain the material that fineness is 20-40 μm, pack.
Paint paint film of the present invention is smooth, without lump, and hardness: 3H, sticking power: 1 grade, thermotolerance experiment (300 ° of C, 120h): paint film is complete, do not come off, alkali resistance experiment (72h): non-foaming, wrinkle resistant, do not come off, acid resistance experiment (72h): non-foaming, wrinkle resistant, does not come off, artificial ageing resistance is tested: 1200h is non-foaming, do not peel off, flawless, and electromagnetic shielding rate is tested: 75dB.
Claims (2)
1. the anti-interference power distribution cabinet antifouling paste of high durable, it is characterized in that, be made up of the raw material of following weight part: terpolymer EP rubber 22-25, bisphenol A type epoxy resin 30-36, clorafin 2-3, ethylene glycol 4-6, dibutyl phthalate 1-2, vermiculite power 2-4, celestite powder 2-3, triphen ethyl phenol Soxylat A 25-7 1-2, Sodium Benzoate 2-3, talcum powder 5-7, five boronation two molybdenum 2-3, vinyl three ('beta '-methoxy oxyethyl group) silane 1-2, sulphur forging Lanolin Calcium Soap 1-2, Walocel MT 20.000PV 1-2, N-BUTYL ACETATE 15-17, dimethylbenzene 6-9, auxiliary agent 4-7,
Described auxiliary agent is made up of the raw material of following weight part: calcium propionate 3-5, sulfuration oleic acid 1-2, hydrochloric acid wood oil 4-6, Silane coupling agent KH550 2-3, two ten four carbon alcohols ester 1-2, aluminum nitride powder 2-3, Sodium dehydroacetate 0.7-1.4, 2-amino-2-methyl-1-propanol 2-3, quaternary ammonium salt-modified organobentonite 2-3, tertbutyl peroxide 1-2, fatty alcohol-polyoxyethylene ether 1-2, vinyl acetate 5-8, vinylformic acid 3-5, ethanol 10-15, silver powder 3-4, expanded graphite 6-8, sheet cobalt powder 8-11, dilute sulphuric acid 0.4-0.8, preparation method is that sheet cobalt powder, silver powder, aluminum nitride powder, expanded graphite, ethanol, dilute sulphuric acid mix by (1), and temperature controls to react 20-30 minute at 70-80 ° of C, leaves standstill precipitation pressed powder for subsequent use, (2) product of hydrochloric acid wood oil, sulfuration oleic acid, vinyl acetate, vinylformic acid, fatty alcohol-polyoxyethylene ether and step (1) is mixed, carry out mechanical blending by high speed dispersion, then add tertbutyl peroxide stirring reaction 1-2 hour, (3) Silane coupling agent KH550 is added in the ethanol of 3-6 weight part, is sprayed onto after mixing on the product of step (2), then add all the other surplus materialss high speed dispersion 0.5-1 hour.
2. the anti-interference power distribution cabinet antifouling paste of a kind of high durable according to claim 1, is characterized in that, be made up of following concrete steps:
(1) vermiculite power, celestite powder, talcum powder, five boronation two molybdenums are added in the mixing solutions of dimethylbenzene and N-BUTYL ACETATE, ultrasonic disperse 20-30 minute, adds dibutyl phthalate, clorafin, auxiliary agent continuation stirring reaction 30-40 minute when being heated to 50-80 ° of C;
(2) product of step (1) is continued raised temperature to 80-90 ° of C, add terpolymer EP rubber, bisphenol A type epoxy resin, vinyl three ('beta '-methoxy oxyethyl group) silane, 1200-1400 rev/min of lower high-speed mixing stirring reaction 1-2 hour;
(3) surplus materials is added in the product of step (2), is added to grinding machine for grinding after mixing and is uniformly dispersed, filter and obtain the material that fineness is 20-40 μm, pack.