CN104496349A - 一种防水混凝土 - Google Patents

一种防水混凝土 Download PDF

Info

Publication number
CN104496349A
CN104496349A CN201410717046.5A CN201410717046A CN104496349A CN 104496349 A CN104496349 A CN 104496349A CN 201410717046 A CN201410717046 A CN 201410717046A CN 104496349 A CN104496349 A CN 104496349A
Authority
CN
China
Prior art keywords
parts
water
clay
tai
ace
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410717046.5A
Other languages
English (en)
Inventor
王新荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410717046.5A priority Critical patent/CN104496349A/zh
Publication of CN104496349A publication Critical patent/CN104496349A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防水混凝土，其是由下述重量份的原料制得：聚丙烯腈纤维2-4、氯化钙0.03-0.06,氯化钠0.03-0.06,三异丙醇胺1-2、磷石膏5-8、聚磷酸铵1-2、硼酸0.4-0.7、硫酸铝0.2-0.3、珍珠岩60-80，二丙二醇甲醚0.1-0.8、蔗糖2.5-4、改性包覆陶土4-5、白水泥30-40、四羟乙基乙二胺1-2,乳化沥青1-3。

Description

一种防水混凝土
技术领域
本发明涉及混凝土领域，确切地说是一种防水混凝土。
背景技术
     混凝土具有原料丰富，价格低廉，生产工艺简单的特点，因而使其用量越来越大。同时混凝土还具有抗压强度高，耐久性好，强度等级范围宽等特点。这些特点使其使用范围十分广泛，不仅在各种土木工程中使用，就是造船业，机械工业，海洋的开发，地热工程等，混凝土也是重要的材料。
发明内容
本发明的目的在于提供一种防水混凝土。
上述目的通过以下方案实现：
一种防水混凝土，其特征在于：其是由下述重量份的原料制得：
聚丙烯腈纤维2-4、氯化钙0.03-0.06,氯化钠0.03-0.06,三异丙醇胺1-2、磷石膏5-8、聚磷酸铵1-2、硼酸0.4-0.7、硫酸铝0.2-0.3、珍珠岩60-80，二丙二醇甲醚0.1-0.8、蔗糖2.5-4、改性包覆陶土4-5、白水泥30-40、四羟乙基乙二胺1-2,乳化沥青1-3；
所述的改性包覆陶土由下述重量份的原料制得：陶土40-50、海藻酸钠0.1-0.3,玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇 1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，再40-45℃下100-180转/分搅拌50-70min，再加入其余原料，搅拌均匀，静置浆料30-60分钟、干燥，粉碎即得。
所述的一种防水混凝土，其特征在于：
制备方法包括以下步骤：
（1）氯化钙、氯化钠、三异丙醇胺、磷石膏、聚磷酸铵、硼酸、硫酸铝混匀后，加适量水，搅拌均匀，搅拌成悬浮液，备用；
 （2）珍珠岩破碎，于900-920℃下闪烧窑中闪烧4-6秒钟，取出，去离子水洗涤后烘干，研磨成纳米粉末，得纳米珍珠岩粉末备用；
 （3)悬浮液与纳米珍珠岩粉末混匀后，20-30转/分搅拌10-30min,静置5-7小时后，抽滤干燥，得改性粉料备用；
 （4）改性粉料再与剩余原料混匀后，即得。
    本发明的有益效果为：本发明添加了改性的纳米珍珠岩粉末，以及蔗糖等物料，纳米粉料相容性好，孔隙好，防水性能好。
具体实施方式
一种防水混凝土，其是由下述重量（kg)的原料制得：
聚丙烯腈纤维4、氯化钙0.03,氯化钠0.06,三异丙醇胺1、磷石膏5、聚磷酸铵2、硼酸0.4、硫酸铝0.2、珍珠岩60，二丙二醇甲醚0.4、蔗糖2.5、改性包覆陶土5、白水泥30、四羟乙基乙二胺1,乳化沥青3；
所述的改性包覆陶土由下述重量（kg)的原料制得：陶土40、海藻酸钠0.1,玉米淀粉3、硅酸钠0.4、硫酸铝0.2、硬脂酰胺0.4、硬脂酸钙1.8、聚乙二醇 1、柠檬酸0.2、二异氰酸酯0.2；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，再43℃下140转/分搅拌70min，再加入其余原料，搅拌均匀，静置浆料40分钟、干燥，粉碎即得。
所述的一种防水混凝土，
制备方法包括以下步骤：
（1）氯化钙、氯化钠、三异丙醇胺、磷石膏、聚磷酸铵、硼酸、硫酸铝混匀后，加适量水，搅拌均匀，搅拌成悬浮液，备用；
 （2）珍珠岩破碎，于920℃下闪烧窑中闪烧5秒钟，取出，去离子水洗涤后烘干，研磨成纳米粉末，得纳米珍珠岩粉末备用；
 （3)悬浮液与纳米珍珠岩粉末混匀后，30转/分搅拌30min,静置7小时后，抽滤干燥，得改性粉料备用；
 （4）改性粉料再与剩余原料混匀后，即得。
    将所有原料加适量水搅拌均匀，通过筑模、压实振捣、表面弄平整 8 小时后脱模， 再标准自然养护5天，每天洒水两次得混凝土样品，制得混凝土样品执行 GB/T50081-2002标准， 三次试验的平均强度为 26.9Mpa。

Claims (2)

1.一种防水混凝土，其特征在于：其是由下述重量份的原料制得：
聚丙烯腈纤维2-4、氯化钙0.03-0.06,氯化钠0.03-0.06,三异丙醇胺1-2、磷石膏5-8、聚磷酸铵1-2、硼酸0.4-0.7、硫酸铝0.2-0.3、珍珠岩60-80，二丙二醇甲醚0.1-0.8、蔗糖2.5-4、改性包覆陶土4-5、白水泥30-40、四羟乙基乙二胺1-2,乳化沥青1-3；
所述的改性包覆陶土由下述重量份的原料制得：陶土40-50、海藻酸钠0.1-0.3,玉米淀粉3-5、硅酸钠0.4-0.6、硫酸铝0.2-0.4、硬脂酰胺0.4-0.7、硬脂酸钙1.8-2.2、聚乙二醇 1-2、柠檬酸0.2-0.4、二异氰酸酯0.1-0.6；
所述的改性包覆陶土的制备方法为：取玉米淀粉加水搅拌均匀得悬浮液，再加入硅酸钠、硫酸铝、硬脂酰胺，再40-45℃下100-180转/分搅拌50-70min，再加入其余原料，搅拌均匀，静置浆料30-60分钟、干燥，粉碎即得。
2.根据权利要求1所述的一种防水混凝土，其特征在于：
制备方法包括以下步骤：
（1）氯化钙、氯化钠、三异丙醇胺、磷石膏、聚磷酸铵、硼酸、硫酸铝混匀后，加适量水，搅拌均匀，搅拌成悬浮液，备用；
 （2）珍珠岩破碎，于900-920℃下闪烧窑中闪烧4-6秒钟，取出，去离子水洗涤后烘干，研磨成纳米粉末，得纳米珍珠岩粉末备用；
 （3)悬浮液与纳米珍珠岩粉末混匀后，20-30转/分搅拌10-30min,静置5-7小时后，抽滤干燥，得改性粉料备用；
 （4）改性粉料再与剩余原料混匀后，即得。
CN201410717046.5A 2014-12-03 2014-12-03 一种防水混凝土 Pending CN104496349A (zh)