CN104452324A - Leather-imitation polyurethane shoe upper leather and production method thereof - Google Patents

Leather-imitation polyurethane shoe upper leather and production method thereof Download PDF

Info

Publication number
CN104452324A
CN104452324A CN201410572305.XA CN201410572305A CN104452324A CN 104452324 A CN104452324 A CN 104452324A CN 201410572305 A CN201410572305 A CN 201410572305A CN 104452324 A CN104452324 A CN 104452324A
Authority
CN
China
Prior art keywords
add
leather
surface layer
parts
ground
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410572305.XA
Other languages
Chinese (zh)
Inventor
金佐跃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI JINLINGLI CLOTHING Co Ltd
Original Assignee
HEFEI JINLINGLI CLOTHING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI JINLINGLI CLOTHING Co Ltd filed Critical HEFEI JINLINGLI CLOTHING Co Ltd
Priority to CN201410572305.XA priority Critical patent/CN104452324A/en
Publication of CN104452324A publication Critical patent/CN104452324A/en
Pending legal-status Critical Current

Abstract

The invention discloses a leather-imitation polyurethane shoe upper leather which comprises a base cloth layer, a foaming layer and a surface layer, wherein the surface layer is prepared from the following raw materials in parts by weight: 60-80 parts of waterborne polyurethane resin, 0.01-0.02 part of disodium stannous citrate, 0.5-1 part of calcium gluconate, 3-6 parts of bone meal, 2-4 parts of shell powder, 0.5-1 part of magnesium chloride, 0.5-1 part of polyethylene glycol tert-octylphenyl ether, 0.5-1 part of pentaerythrityl oleate, 0.5-1 part of carboxymethyl chitosan, 0.5-1 part of maltitol, 2-4 parts of color paste and 2-6 parts of a compound additive. The synthetic leather is close to real leather in the aspects of appearance and texture, is good in moisture permeability and air permeability as well as soft in hand feeling, and has the physical properties reaching the standard, thus being suitable for manufacturing shoe upper leather products.

Description

A kind of skin-imitated polyurethane upper leather and production method thereof
Technical field
The present invention relates to synthetic leather processing technique field, be specifically related to a kind of skin-imitated polyurethane upper leather and production method thereof.
Background technology
Polyurethane (PU) synthetic leather, because it has excellent ABRASION RESISTANCE, good tearing toughness and percentage elongation, advantages such as there is smooth, the good hand feeling in surface simultaneously, comfortable, recovery is good, be moderate, become the best substitute of expensive natural leathercraft, and be widely used in the industries such as clothes, shoemaking, case and bag, furniture.Meet the requirements of Synthetic Leather and not only need good physical property, also need the style and the outward appearance that there is good moisture-inhibiting, permeability, softness, plentiful, slim and graceful feel and be more imbued with natural leather.
Summary of the invention
The object of this invention is to provide a kind of skin-imitated polyurethane upper leather.
The present invention is achieved by the following technical solutions:
A kind of skin-imitated polyurethane upper leather, comprises base cloth layer, foaming layer and surface layer, wherein:
Surface layer is obtained by the raw material of following weight parts:
Waterborne polyurethane resin 60-80, distannous citrate 0.01-0.02, calcium gluconae 0.5-1, bone meal 3-6, oyster shell whiting 2-4, magnesium chloride 0.5-1, OPEO 0.5-1, PETO 0.5-1, cm-chitosan 0.5-1, maltitol 0.5-1, color 2-4, composite assistant 2-6;
Foaming layer is obtained by the raw material of following weight parts:
Waterborne polyurethane resin 60-80, precipitated calcium carbonate 2-4, white carbon 1-2, polyethylene glycol 2-6, triethanolamine 1-2, aluminium oxide 0.1-0.3, diatomite 1-2, cocamidopropyl betaine 1-2, pull open powder 0.5-1, sodium bicarbonate 1-3, boric acid 1-2, guar gum 1-3;
Wherein composite assistant is made up of the raw material of following weight portion:
Tannic acid 0.5-1, oxalic acid 0.5-1, sorbierite 4-8, ramee 4-8, tossa 2-4, wheat stalk 2-4, Silane coupling agent KH550 0.2-0.5, triisopropanolamine 3-6, glycerine 25-50;
The preparation method of composite assistant is:
Add triisopropanolamine after ramee, tossa and wheat stalk being mixed and be tentatively ground to 50-100 order, add Silane coupling agent KH550 again, 60-80 DEG C, 600-800r/min stirs 10-30min, 500-800 order is ground to after drying, add oxalic acid, tannic acid, sorbierite and glycerine, 140-180 DEG C, 400-600r/min stirs 5-10h, after cooling and get final product;
A production method for skin-imitated polyurethane upper leather, comprises the following steps:
(1) face stock is taken, 200-300 order is ground to by after bone meal and oyster shell whiting mixing, add the acetum 40-50 DEG C of process 6-8h of appropriate 2-6%, add maltitol and shitosan, 400-600r/min stirs 15-30min, be ground to 500-600 order after freeze drying, add all the other raw materials 600-800r/min, 40-60 DEG C and stir 30-60min, obtain surface layer slurry; Surface layer slurry is evenly coated in release liners, after 100-120 DEG C of drying, forms surface layer;
(2) foaming layer raw material is taken, by 800-1000 DEG C of calcining 2-4h after aluminium oxide and diatomite mixing, cool the temperature to 400-600 DEG C, add white carbon and precipitated calcium carbonate post processing 1-2h, triethanolamine, sodium bicarbonate and boric acid is added after cooling, be ground to 500-800 order, add all the other raw materials 60-80 DEG C, 600-800r/min stirs 3-6h, obtain foaming layer slurry; Evenly be coated in after the foaming layer slurry mechanical foaming prepared on surface layer, 100-140 DEG C of oven dry;
(3) in foaming layer, apply aqueous polyurethane binding paste, rear 120-140 bonding with base cloth layer DEG C is dried;
(4) release liners peeled off, trimming rolling, obtains synthetic leather finished product.
Advantage of the present invention is:
Synthetic leather outward appearance of the present invention, texture are close to corium, moisture-inhibiting, permeability are excellent, soft, physical property is up to standard, has both had natural leather institute inherent advantages, possesses again excellent in chemical resistance, waterproof, anti-mildew etc. that natural leather does not possess simultaneously; Raw material sources are extensive, and price is cheaper relative to natural leather, effectively cost-saving; Manufacturing technique safety and environmental protection, reduces the discharge of noxious pollutant, meets industrial policy.Be applicable to manufacture upper leather.
Detailed description of the invention
Non-limiting examples of the present invention is as follows:
Embodiment 1
A kind of skin-imitated polyurethane upper leather, comprises base cloth layer, surface layer and foaming layer, wherein:
Surface layer is obtained by the raw material of following weight parts:
Waterborne polyurethane resin 70, distannous citrate 0.15, calcium gluconae 0.6, bone meal 5, oyster shell whiting 3, magnesium chloride 0.8, OPEO 0.6, PETO 0.8, cm-chitosan 0.6, maltitol 0.8, color 3, composite assistant 4;
Foaming layer is obtained by the raw material of following weight parts:
Waterborne polyurethane resin 70, precipitated calcium carbonate 3, white carbon 1.5, polyethylene glycol 4, triethanolamine 1.5, aluminium oxide 0.2, diatomite 1.5, cocamidopropyl betaine 1.5, pulls open powder 0.8, sodium bicarbonate 2, boric acid 1.5, guar gum 2;
Wherein composite assistant is made up of the raw material of following weight portion:
Tannic acid 0.8, oxalic acid 0.8, sorbierite 6, ramee 6, tossa 3, wheat stalk 3, Silane coupling agent KH550 0.4, triisopropanolamine 5, glycerine 40;
The preparation method of composite assistant is:
Add triisopropanolamine after ramee, tossa and wheat stalk being mixed and be tentatively ground to 100 orders, add Silane coupling agent KH550 again, 60 DEG C, 600r/min stirs 15min, 500 orders are ground to after drying, add oxalic acid, tannic acid, sorbierite and glycerine, 160 DEG C, 400r/min stirs 5h, after cooling and get final product;
Waterborne polyurethane resin used is Bayer Impranil LP RSC 1380(60% solid content).
A production method for skin-imitated polyurethane upper leather, comprises the following steps:
(1) face stock is taken, 200 orders are ground to by after bone meal and oyster shell whiting mixing, add the acetum 40 DEG C process 6h of appropriate 2-6%, add maltitol and shitosan, 400r/min stirs 15min, be ground to 500 orders after freeze drying, add all the other raw materials 600r/min, 60 DEG C of stirring 30min, obtain surface layer slurry; Surface layer slurry is evenly coated in release liners, after 110 DEG C of dryings, forms surface layer;
(2) foaming layer raw material is taken, by aluminium oxide and the rear 800 DEG C of calcining 2h of diatomite mixing, cool the temperature to 400 DEG C, add white carbon and precipitated calcium carbonate post processing 2h, triethanolamine, sodium bicarbonate and boric acid is added after cooling, be ground to 500 orders, add all the other raw materials 80 DEG C, 600r/min stirs 3h, obtain foaming layer slurry; Evenly be coated in after the foaming layer slurry mechanical foaming prepared on surface layer, 120 DEG C of oven dry;
(3) in foaming layer, apply aqueous polyurethane binding paste, dry for bonding with base cloth layer latter 140 DEG C;
(4) release liners peeled off, trimming rolling, obtains synthetic leather finished product.
Properties of product test result:
Tensile load 59N/cm, tears load 38N;
Folding fastness 23 DEG C, 200,000 flawlesses.

Claims (2)

1. a skin-imitated polyurethane upper leather, comprises base cloth layer, foaming layer and surface layer, it is characterized in that:
Described surface layer is obtained by the raw material of following weight parts:
Waterborne polyurethane resin 60-80, distannous citrate 0.01-0.02, calcium gluconae 0.5-1, bone meal 3-6, oyster shell whiting 2-4, magnesium chloride 0.5-1, OPEO 0.5-1, PETO 0.5-1, cm-chitosan 0.5-1, maltitol 0.5-1, color 2-4, composite assistant 2-6;
Described foaming layer is obtained by the raw material of following weight parts:
Waterborne polyurethane resin 60-80, precipitated calcium carbonate 2-4, white carbon 1-2, polyethylene glycol 2-6, triethanolamine 1-2, aluminium oxide 0.1-0.3, diatomite 1-2, cocamidopropyl betaine 1-2, pull open powder 0.5-1, sodium bicarbonate 1-3, boric acid 1-2, guar gum 1-3;
Described composite assistant is made up of the raw material of following weight portion:
Tannic acid 0.5-1, oxalic acid 0.5-1, sorbierite 4-8, ramee 4-8, tossa 2-4, wheat stalk 2-4, Silane coupling agent KH550 0.2-0.5, triisopropanolamine 3-6, glycerine 25-50;
The preparation method of described composite assistant is:
Add triisopropanolamine after ramee, tossa and wheat stalk being mixed and be tentatively ground to 50-100 order, add Silane coupling agent KH550 again, 60-80 DEG C, 600-800r/min stirs 10-30min, 500-800 order is ground to after drying, add oxalic acid, tannic acid, sorbierite and glycerine, 140-180 DEG C, 400-600r/min stirs 5-10h, after cooling and get final product.
2. the preparation method of a kind of skin-imitated polyurethane upper leather according to claim 1, is characterized in that, comprise the following steps:
(1) face stock is taken, 200-300 order is ground to by after bone meal and oyster shell whiting mixing, add the acetum 40-50 DEG C of process 6-8h of appropriate 2-6%, add maltitol and shitosan, 400-600r/min stirs 15-30min, be ground to 500-600 order after freeze drying, add all the other raw materials 600-800r/min, 40-60 DEG C and stir 30-60min, obtain surface layer slurry; Surface layer slurry is evenly coated in release liners, after 100-120 DEG C of drying, forms surface layer;
(2) foaming layer raw material is taken, by 800-1000 DEG C of calcining 2-4h after aluminium oxide and diatomite mixing, cool the temperature to 400-600 DEG C, add white carbon and precipitated calcium carbonate post processing 1-2h, triethanolamine, sodium bicarbonate and boric acid is added after cooling, be ground to 500-800 order, add all the other raw materials 60-80 DEG C, 600-800r/min stirs 3-6h, obtain foaming layer slurry; Evenly be coated in after the foaming layer slurry mechanical foaming prepared on surface layer, 100-140 DEG C of oven dry;
(3) in foaming layer, apply aqueous polyurethane binding paste, rear 120-140 bonding with base cloth layer DEG C is dried;
(4) release liners peeled off, trimming rolling, obtains synthetic leather finished product.
CN201410572305.XA 2014-10-23 2014-10-23 Leather-imitation polyurethane shoe upper leather and production method thereof Pending CN104452324A (en)