CN104452149A - Two-step finishing process of jacquard fabric fibers - Google Patents
Two-step finishing process of jacquard fabric fibers Download PDFInfo
- Publication number
- CN104452149A CN104452149A CN201310415800.5A CN201310415800A CN104452149A CN 104452149 A CN104452149 A CN 104452149A CN 201310415800 A CN201310415800 A CN 201310415800A CN 104452149 A CN104452149 A CN 104452149A
- Authority
- CN
- China
- Prior art keywords
- fabric
- jacquard fabric
- drying
- step method
- jacquard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a two-step finishing process of jacquard fabric fibers. The finishing process jacquard fabric obtained by spinning on a loom is directly fed to a hot air tenter, temperature is controlled to be 150-200 DEG C, speed is controlled to be 20-60m/minute, thermal processing is performed on the fabric, the fabric is put into clean water in a material tank and then dried by a padder, an infrared weft straightener is used to straighten wefts, softener solution padding is performed through the padder, the fabric is placed on full-loosening drying equipment for drying and loosening, the temperature is controlled to be 20-4-140 DEG C, the speed is controlled to be 15-30m/minute, and fabric discharge is performed by hot air constantly beating and drying the fabric so as to complete fabric drying and loosening. Compared with the prior art, the two-step finishing process has the advantages that the fabric processed by process is good in softness, good in elasticity and drapability, and good in shrinkage rate.
Description
Technical field
The present invention relates to a kind of material treatment method, especially relate to a kind of two-step method finishing technique of jacquard fabric fiber.
Background technology
Suitable vast scale is had to belong to synthetic fiber and natural fabric intertexture in jacquard fabric, the modal warp that is combined as adopts synthetic fiber filament (mainly polyester polyamide), parallel many employings natural fabric, or synthesis, regenerated fiber short fiber yarn.Traditional Final finishing mode is mainly pads softener one-step building at hot blast framing shaping machine, frequent produced problem is that feel is hardened, style is stiff, drapability is poor, setting temperature usually higher (more than 180 DEG C) simultaneously, the migration of the surfactant aggravation dyestuff in softener, colour-change phenomena often occurs, causes client's color not confirm.Also cause color fastness decreased simultaneously, mutually cut marks between yarn.Color-woven fabric, once form finished product, is be difficult to adjustment color.
Application number be 200910155495.4 Chinese patent disclose a kind of method for sorting of weaving face fabric, get green compact cloth HEAT SETTING wipe oil, be washed to grey cloth pH and remain on 6-7,90-110 DEG C of oven dry, then arrange through dressing liquid feed liquor, containing soil release finishing agent and anti-soil agent in dressing liquid, eventually pass oven dry calendering, obtain the fabric after finished product arrangement.
Summary of the invention
Object of the present invention be exactly in order to overcome above-mentioned prior art exist defect and provide one to guarantee fabric pliability is good, elasticity and hang down feel, have the two-step method finishing technique of the jacquard fabric fiber of good shrinkage simultaneously.
Object of the present invention can be achieved through the following technical solutions:
A two-step method finishing technique for jacquard fabric fiber, comprises the following steps:
(1) sizing arranges: weave the jacquard fabric that obtains except direct upper hot blast framing shaping machine after degreasing from loom, control temperature is at 150-200 DEG C, speed is 20-60 m/min, heat treated is carried out to fabric, then fabric is placed in after hopper crosses clear water and dries through padding machine, utilize infrared weft straightener to arrange weft yarn, after sizing, enter next operation;
(2) dry bat pine to arrange: the fabric after sizing is padded soft additive solution through padding machine, then be placed on complete loose formula drying plant and carry out the arrangement of drying bat pine, control temperature is 120-140 DEG C, speed is 15-30 m/min, do not stop row by hot blast to beat drying and go out cloth, complete and pine arrangement is clapped to the oven dry of fabric.
Hot blast framing shaping machine control temperature described in step (1) preferably 180 DEG C.
The pick-up of the padding machine described in step (1) controls to be 80%.
Soft additive described in step (2) is film formation at low temp soft additive.
Described film formation at low temp soft additive is albumen film forming agent, acrylic resin film forming agent, butadiene resin film forming agent, polyurethane finishing agent or cellulose nitrate film forming agent.
The concentration of the soft additive solution described in step (2) is 10-30g/l.
Compared with prior art, the present invention is by sizing and make the separately process of soft step, low temperature osmotic film forming softener is utilized in the soft link of system, pat finishing technique by a kind of complete loose formula drying and hot blast simultaneously, guarantee after have suffered in journey and reduce look as much as possible and become, guarantee and expect that pliability is good, elasticity is felt with hanging down, have good shrinkage simultaneously, make ready-made clothes indeformable, style is naturally soft.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1
A two-step method finishing technique for jacquard fabric fiber, comprises the following steps:
(1) sizing arranges: weave the jacquard fabric that obtains except direct upper hot blast framing shaping machine after degreasing from loom, control temperature is at 150 DEG C, speed is 20 ms/min, heat treated is carried out to fabric, then fabric is placed in after hopper crosses clear water and dries through padding machine, the pick-up of padding machine controls to be 80%, utilizes infrared weft straightener to arrange weft yarn, enters next operation after sizing;
(2) dry bat pine to arrange: the fabric after sizing is padded soft additive solution through padding machine, what the present embodiment adopted is albumen film forming agent, the concentration of soft additive solution is 10g/l, then be placed on complete loose formula drying plant and carry out the arrangement of drying bat pine, control temperature is 120 DEG C, speed is 15 ms/min, does not stop row beat drying and go out cloth by hot blast, completes and claps pine arrangement to the oven dry of fabric.
Embodiment 2
A two-step method finishing technique for jacquard fabric fiber, comprises the following steps:
(1) sizing arranges: weave the jacquard fabric that obtains except direct upper hot blast framing shaping machine after degreasing from loom, control temperature is at 180 DEG C, speed is 50 ms/min, heat treated is carried out to fabric, then fabric is placed in after hopper crosses clear water and dries through padding machine, the pick-up of padding machine controls to be 80%, utilizes infrared weft straightener to arrange weft yarn, enters next operation after sizing;
(2) dry bat pine to arrange: the fabric after sizing is padded soft additive solution through padding machine, what the present embodiment adopted is acrylic resin film forming agent, the concentration of soft additive solution is 20g/l, then be placed on complete loose formula drying plant and carry out the arrangement of drying bat pine, control temperature is 130 DEG C, speed is 20 ms/min, does not stop row beat drying and go out cloth by hot blast, completes and claps pine arrangement to the oven dry of fabric.
Embodiment 3
A two-step method finishing technique for jacquard fabric fiber, comprises the following steps:
(1) sizing arranges: weave the jacquard fabric that obtains except direct upper hot blast framing shaping machine after degreasing from loom, control temperature is at 200 DEG C, speed is 60 ms/min, heat treated is carried out to fabric, then fabric is placed in after hopper crosses clear water and dries through padding machine, the pick-up of padding machine controls to be 80%, utilizes infrared weft straightener to arrange weft yarn, enters next operation after sizing;
(2) dry bat pine to arrange: the fabric after sizing is padded soft additive solution through padding machine, what the present embodiment adopted is polyurethane finishing agent, the concentration of soft additive solution is 30g/l, then be placed on complete loose formula drying plant and carry out the arrangement of drying bat pine, control temperature is 140 DEG C, speed is 30 ms/min, does not stop row beat drying and go out cloth by hot blast, completes and claps pine arrangement to the oven dry of fabric.
Claims (6)
1. a two-step method finishing technique for jacquard fabric fiber, is characterized in that, this technique comprises the following steps:
(1) sizing arranges: weave the jacquard fabric that obtains except direct upper hot blast framing shaping machine after degreasing from loom, control temperature is at 150-200 DEG C, speed is 20-60 m/min, heat treated is carried out to fabric, then fabric is placed in after hopper crosses clear water and dries through padding machine, utilize infrared weft straightener to arrange weft yarn, after sizing, enter next operation;
(2) dry bat pine to arrange: the fabric after sizing is padded soft additive solution through padding machine, then be placed on complete loose formula drying plant and carry out the arrangement of drying bat pine, control temperature is 120-140 DEG C, speed is 15-30 m/min, do not stop row by hot blast to beat drying and go out cloth, complete and pine arrangement is clapped to the oven dry of fabric.
2. the two-step method finishing technique of a kind of jacquard fabric fiber according to claim 1, is characterized in that, the hot blast framing shaping machine control temperature described in step (1) preferably 180 DEG C.
3. the two-step method finishing technique of a kind of jacquard fabric fiber according to claim 1, is characterized in that, the pick-up of the padding machine described in step (1) controls to be 80%.
4. the two-step method finishing technique of a kind of jacquard fabric fiber according to claim 1, is characterized in that, the soft additive described in step (2) is film formation at low temp soft additive.
5. the two-step method finishing technique of a kind of jacquard fabric fiber according to claim 3, it is characterized in that, described film formation at low temp soft additive is albumen film forming agent, acrylic resin film forming agent, butadiene resin film forming agent, polyurethane finishing agent or cellulose nitrate film forming agent.
6. the two-step method finishing technique of a kind of jacquard fabric fiber according to claim 1, is characterized in that, the concentration of the soft additive solution described in step (2) is 10-30g/l.