CN104404677B - A kind of warming lightweight antistatic fabric and preparation method thereof - Google Patents
A kind of warming lightweight antistatic fabric and preparation method thereof Download PDFInfo
- Publication number
- CN104404677B CN104404677B CN201410616292.1A CN201410616292A CN104404677B CN 104404677 B CN104404677 B CN 104404677B CN 201410616292 A CN201410616292 A CN 201410616292A CN 104404677 B CN104404677 B CN 104404677B
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- sizing
- draining
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of warming lightweight antistatic fabric and preparation method thereof, belong to garment material processing technique field, wherein the weight portion of each component is wool fiber 50 ~ 90 parts, cotton fiber 20 ~ 40 parts, flax fiber 10 ~ 20 parts, bamboo fibre 1 ~ 10 part and mint fibers 1 ~ 10 part, and its preparation method includes pretreatment, weaving yarn, soft treatment, four steps of sizing；This fabric sense of touch comfortableness, warmth retention property is good, breathable moisture permeability good, and frivolous light refrigerant, possesses electrostatic-proof function, is suitable for process into the high-grade dress ornament such as Western-style clothes or jacket.
Description
Technical field
The present invention relates to a kind of fabric and preparation method thereof, particularly to a kind of warming lightweight antistatic fabric and preparation method thereof, belong to garment material processing technique field.
Background technology
Development along with dress culture, the functionalized design of dress materials is increasingly becoming the key content of Fabrics, refer to high-efficiency comfortable, health care, high security than more prominent function type, be prone to maintenance and complex function, as having moisture absorption (water suction) moisture-inhibiting, insulation is felt nice and cool, without the comfortableness fabric of the function such as scratchy；There is the health-care fabric fabric of the functions such as antibacterial, deodorant, physical therapy；There is the security protection fabric of the functions such as ray fire-retardant, anti-, antistatic；There is the specific use fabric of the functions such as non-ironing, the antipollution of anti-wrinkle shrink-proof；What have moisture-inhibiting and waterproof double effects concurrently easily maintains fabric.People are no longer single to the requirement of dress ornament.
The good natural characteristics such as wool fiber has softness, high resilience, strong hygroscopicity, not easily stains, gloss is soft have become as four seasons fashionable dress materials.But traditional wool fabric weight greatly, more abundant, make troubles to consumer to a certain extent, therefore, wool fabric lightweight is a development trend of wool textile industry in recent years.Patent CN200910134675.4 discloses a kind of wool knitting fabrics and manufacturing process thereof, described fabric is constituted by 100% ultra-fine wool top that wool fibre is 17.5 microns is knitting, in knitting fabric manufacture process, wool fabric is prepared through one-step building, cropping, secondary sizing, Buddhist nun's blanket machine four steps of shaping, although the product prepared is lighter relative to traditional wool fabric, but due to structure defective tightness so that it is the application on high-grade dress ornament is subject to certain restrictions.
After China's reform and opening-up, along with the raising of people's living standard, the demand of high-grade dress ornament is increasing, and especially on western-style clothes, the requirement of quality is more and more higher.Western-style clothes develops into today of 21 century, along with the transition in epoch and region, not only maintains that its outward appearance is well-pressed, the lines flow smoothly, traditional style comfortable and easy to wear, also more compatible times flavour in the use of fabric.Based on this feature, fabric (fabric) is not only had the performance requirement being different from other clothing fabrics by western-style clothes, and the functional novel fabric instantly constantly released to market also to meet these basic characteristics, is accepted by wide western-style clothes market.
Current domestic wool knitting fabrics is generally used to processing underwear, T-shirt, the fabric such as sweater knitted, and owing to wool knitting fabrics is by the restriction of its conventional machining process, make current most wool knitting fabrics cannot be used to processing overcoat, such as western-style clothes, jacket etc., cause that its use field is restricted.There is the processing method that patent (CN201110068674.1) discloses a kind of wool knitting fabrics, be characterized as being in the finishing process of the conventional machining process of wool knitting fabrics to increase fulling, dry, calendering and shrinking processes, so that the wool knitting fabrics body bone processed is well-pressed, close structure and high resilience, cloth cover is smooth and gloss is simple and elegant, feel is smooth full, which overcome that the wool knitting fabrics organizational structure produced by conventional machining process is lax, the shortcoming of defective tightness, be especially suitable for overcoats such as makeing high-grade leisure Western-style clothes or jacket.But the comfortableness of the fabric processed need to improve, and is easily generated electrostatic.
Summary of the invention
It is an object of the invention to provide a kind of warming lightweight antistatic fabric, this fabric sense of touch comfortableness, warmth retention property is good, breathable moisture permeability good, and frivolous light refrigerant, possesses electrostatic-proof function, is suitable for process into the high-grade dress ornament such as Western-style clothes or jacket.
In order to solve the problems referred to above, the technical solution adopted in the present invention is:
A kind of warming lightweight antistatic fabric, the weight portion of each component is:
Wool fiber 50 ~ 90 parts, cotton fiber 20 ~ 40 parts, flax fiber 10 ~ 20 parts, bamboo fibre 1 ~ 10 part and mint fibers 1 ~ 10 part.
The preparation method that another object of the present invention is to provide a kind of warming lightweight antistatic fabric, its technical scheme is as follows:
The preparation method of a kind of warming lightweight antistatic fabric, comprises the following steps:
A. pretreatment: above-mentioned raw materials is put in the water of its gross weight 20 ~ 100 times, adding degreaser is 0.1 ~ 1g/(100g raw material), controlling temperature is after 40 ~ 70 DEG C of process 2 ~ 3h, and draining, 50 ~ 60 DEG C are dried 20 ~ 24h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 70 ~ 100Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:1 ~ 1:10, adding softening agent is 0.1 ~ 1g/(100g raw material), controlling temperature is after 40 ~ 50 DEG C of process 1 ~ 3h, and draining, 50 ~ 60 DEG C are dried 10 ~ 20h；
D. sizing: wet cloth framing shaping machine sizing, temperature 90 ~ 100 DEG C, sizing speed is 10 ~ 20m/min, overfeeding 40% ~ 50%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
The present invention provides the benefit that relative to prior art:
(1) fabric provided by the invention, it is formed by weaving with wool fiber, cotton fiber, flax fiber, bamboo fibre and mint fibers, not only sense of touch comfortableness, warmth retention property is good, breathable moisture permeability good, and it is frivolous light refrigerant, possesses electrostatic-proof function, so as to play maximum effect, to meet many-sided demand of people.
(2) fabric provided by the invention, overcomes tradition wool knitting fabrics structural relaxation, tight not and have the shortcoming such as prodding and itching feeling, viscous body-sensing when wear, is suitable for process into the top grade dress ornament such as Western-style clothes or jacket.
(3) method preparing fabric provided by the invention, technique is simple, is suitable in technologic large-scale production.
Detailed description of the invention
By the examples below the present invention being described in further details, these embodiments are only used for the present invention is described, do not limit the scope of the invention.
Embodiment 1
A kind of warming lightweight antistatic fabric, the weight portion of each component is:
Wool fiber 50 parts, cotton fiber 20 parts, flax fiber 10 parts, bamboo fibre 1 part, mint fibers 10 parts；
Its preparation method, comprises the following steps:
A. pretreatment: above-mentioned raw materials is put in the water of its weight 20 times, adding degreaser is 0.1g/(100g raw material), controlling temperature is after 40 DEG C of process 2h, and draining, 50 DEG C are dried 20h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 70Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:1, adding softening agent is 0.1g/(100g raw material), controlling temperature is after 40 DEG C of process 1h, and draining, 50 DEG C are dried 10h；
D. sizing: wet cloth framing shaping machine sizing, temperature 90 DEG C, sizing speed is 10m/min, overfeeding 40%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
Embodiment 2
A kind of warming lightweight antistatic fabric, the weight portion of each component is:
Wool fiber 90 parts, cotton fiber 40 parts, flax fiber 20 parts, bamboo fibre 10 parts, mint fibers 1 part；
Its preparation method, comprises the following steps:
A. pretreatment: above-mentioned raw materials is put in the water of its weight 100 times, adding degreaser is 1g/(100g raw material), controlling temperature is after 70 DEG C of process 3h, and draining, 60 DEG C are dried 24h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 100Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:10, adding softening agent is 1g/(100g raw material), controlling temperature is after 50 DEG C of process 3h, and draining, 60 DEG C are dried 20h；
D. sizing: wet cloth framing shaping machine sizing, temperature 100 DEG C, sizing speed is 20m/min, overfeeding 50%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
Embodiment 3
A kind of warming lightweight antistatic fabric, the weight portion of each component is:
Wool fiber 65 parts, cotton fiber 30 parts, flax fiber 15 parts, bamboo fibre 5 parts, mint fibers 5 parts；
One its preparation method, comprises the following steps:
A. pretreatment: above-mentioned raw materials is put in the water of its weight 70 times, adding degreaser is 0.5g/(100g raw material), controlling temperature is after 55 DEG C of process 2.5h, and draining, 55 DEG C are dried 22h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 85Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:5, adding softening agent is 0.5g/(100g raw material), controlling temperature is after 45 DEG C of process 2h, and draining, 55 DEG C are dried 15h；
D. sizing: wet cloth framing shaping machine sizing, temperature 95 DEG C, sizing speed is 15m/min, overfeeding 45%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
Embodiment 4
A kind of warming lightweight antistatic fabric, the weight portion of each component is:
Wool fiber 55 parts, cotton fiber 23 parts, flax fiber 11 parts, bamboo fibre 3 parts, mint fibers 7 parts；
Its preparation method, comprises the following steps:
A. pretreatment: above-mentioned raw materials is put in the water of its weight 30 times, adding degreaser is 0.3g/(100g raw material), controlling temperature is after 45 DEG C of process 2.1h, and draining, 52 DEG C are dried 21h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 75Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:3.5, adding softening agent is 0.15g/(100g raw material), controlling temperature is after 42 DEG C of process 1.5h, and draining, 51 DEG C are dried 12h；
D. sizing: wet cloth framing shaping machine sizing, temperature 92 DEG C, sizing speed is 13m/min, overfeeding 43%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
Embodiment 5
A kind of warming lightweight antistatic fabric, the weight portion of each component is:
Wool fiber 75 parts, cotton fiber 37 parts, flax fiber 17 parts, bamboo fibre 8 parts, mint fibers 2 parts；
Its preparation method, comprises the following steps:
A. pretreatment: above-mentioned raw materials is put in the water of its weight 90 times, adding degreaser is 0.85g/(100g raw material), controlling temperature is after 65 DEG C of process 2.8h, and draining, 57 DEG C are dried 23h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 99Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:9, adding softening agent is 0.75g/(100g raw material), controlling temperature is after 48 DEG C of process 2.7h, and draining, 57 DEG C are dried 18h；
D. sizing: wet cloth framing shaping machine sizing, temperature 97 DEG C, sizing speed is 18.5m/min, overfeeding 48%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
Claims (5)
1. a warming lightweight antistatic fabric, it is characterised in that: the weight portion of each component is:
Wool fiber 50 parts, cotton fiber 20 parts, flax fiber 10 parts, bamboo fibre 1 part, mint fibers 10 parts；
Its preparation method, comprises the following steps:,
A. pretreatment: put into by above-mentioned raw materials in the water of its weight 20 times, adds the 0.1g degreaser of every 100g raw material, and controlling temperature is after 40 DEG C of process 2h, and draining, 50 DEG C are dried 20h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 70Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:1, adds the 0.1g softening agent of every 100g raw material, and controlling temperature is after 40 DEG C of process 1h, and draining, 50 DEG C are dried 10h；
D. sizing: wet cloth framing shaping machine sizing, temperature 90 DEG C, sizing speed is 10m/min, overfeeding 40%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
2. a warming lightweight antistatic fabric, it is characterised in that: the weight portion of each component is:
Wool fiber 90 parts, cotton fiber 40 parts, flax fiber 20 parts, bamboo fibre 10 parts, mint fibers 1 part；
Its preparation method, comprises the following steps:
A. pretreatment: put into by above-mentioned raw materials in the water of its weight 100 times, adds the 1g degreaser of every 100g raw material, and controlling temperature is after 70 DEG C of process 3h, and draining, 60 DEG C are dried 24h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 100Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:10, adds the 1g softening agent of every 100g raw material, and controlling temperature is after 50 DEG C of process 3h, and draining, 60 DEG C are dried 20h；
D. sizing: wet cloth framing shaping machine sizing, temperature 100 DEG C, sizing speed is 20m/min, overfeeding 50%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
3. a warming lightweight antistatic fabric, it is characterised in that: the weight portion of each component is:
Wool fiber 65 parts, cotton fiber 30 parts, flax fiber 15 parts, bamboo fibre 5 parts, mint fibers 5 parts；
One its preparation method, comprises the following steps:
A. pretreatment: put into by above-mentioned raw materials in the water of its weight 70 times, adds the 0.5g degreaser of every 100g raw material, and controlling temperature is after 55 DEG C of process 2.5h, and draining, 55 DEG C are dried 22h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 85Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:5, adds the 0.5g softening agent of every 100g raw material, and controlling temperature is after 45 DEG C of process 2h, and draining, 55 DEG C are dried 15h；
D. sizing: wet cloth framing shaping machine sizing, temperature 95 DEG C, sizing speed is 15m/min, overfeeding 45%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
4. a warming lightweight antistatic fabric, it is characterised in that: the weight portion of each component is:
Wool fiber 55 parts, cotton fiber 23 parts, flax fiber 11 parts, bamboo fibre 3 parts, mint fibers 7 parts；
Its preparation method, comprises the following steps:
A. pretreatment: put into by above-mentioned raw materials in the water of its weight 30 times, adds the 0.3g degreaser of every 100g raw material, and controlling temperature is after 45 DEG C of process 2.1h, and draining, 52 DEG C are dried 21h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 75Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:3.5, adds the 0.15g softening agent of every 100g raw material, and controlling temperature is after 42 DEG C of process 1.5h, and draining, 51 DEG C are dried 12h；
D. sizing: wet cloth framing shaping machine sizing, temperature 92 DEG C, sizing speed is 13m/min, overfeeding 43%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.
5. a warming lightweight antistatic fabric, it is characterised in that: the weight portion of each component is:
Wool fiber 75 parts, cotton fiber 37 parts, flax fiber 17 parts, bamboo fibre 8 parts, mint fibers 2 parts；
Its preparation method, comprises the following steps:
A. pretreatment: put into by above-mentioned raw materials in the water of its weight 90 times, adds the 0.85g degreaser of every 100g raw material, and controlling temperature is after 65 DEG C of process 2.8h, and draining, 57 DEG C are dried 23h；
B. weave yarn: by the raw material after processing of step A, carry out weaving process when 99Nm/2 strand；
C. soft treatment: the weight ratio controlling grey cloth and water is 1:9, adds the 0.75g softening agent of every 100g raw material, and controlling temperature is after 48 DEG C of process 2.7h, and draining, 57 DEG C are dried 18h；
D. sizing: wet cloth framing shaping machine sizing, temperature 97 DEG C, sizing speed is 18.5m/min, overfeeding 48%, it is ensured that lower machine shrinks within 7%, cloth is shaped, obtains product.