CN104401067B - Aluminum carbon plate production technology - Google Patents
Aluminum carbon plate production technology Download PDFInfo
- Publication number
- CN104401067B CN104401067B CN201410608276.8A CN201410608276A CN104401067B CN 104401067 B CN104401067 B CN 104401067B CN 201410608276 A CN201410608276 A CN 201410608276A CN 104401067 B CN104401067 B CN 104401067B
- Authority
- CN
- China
- Prior art keywords
- film
- hot
- aluminium base
- fusible high
- molecular film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses an aluminum carbon plate production technology, a material comprises a decoration membrane, an aluminium substrate, an active carbon cloth and a high-molecular hot melt membrane, the material is placed according to an order of the decoration membrane, the high-molecular hot melt membrane, the aluminium substrate, the high-molecular hot melt membrane and the active carbon cloth from down to top; the material enables physical thermal penetration through a high-frequency heating machine, so that high-molecular hot melt membrane can be softened to generate adhesion, then the synthetic material is rolled and reinforced by a rolling machine, so that the highly bonding between the materials can be reached, finally the synthetic material is cut according to certain size by a cutting machine to produce the finished product and then the finished product is packaged. The aluminum carbon plate production technology can be used for producing the aluminium carbon plates with different specification, the aluminium carbon plate has good moulding characteristic, abundant selection can be realized for surface material and pattern, and the aluminum carbon plate has the advantages of firm structure, durable performance, long service life, simple process, and low production cost.
Description
[technical field]
The present invention relates to the technical field of sheet material, the technical field of a kind of aluminum carbon slab production technology.
[background technology]
The kind of sheet material is the most, and widely, material and the characteristic of composition sheet material have the biggest purposes
Difference, but existing sheet material can not take into account multiple excellent characteristic, often can only have indivedual prominent good
Advantage, existing sheet material versatility is strong, and some sheet material plasticity ability is poor, some plate surface vision
Weak effect, means and the expression way of mountable decorations are less, and market demand one takes into account multiple superperformance
Sheet material, sheet material needs good moulding ability, Facing material and pattern can be the abundantest, ties simultaneously
Structure is firm, durable in use, and manufacturing process is simple as far as possible simultaneously, reduces manufacturing cost, reduces the valency of material
Lattice.
[summary of the invention]
The purpose of the present invention solves the problems of the prior art exactly, proposes a kind of aluminum carbon slab production technology, energy
Enough making the aluminum carbon slab of different size, aluminum carbon slab has good moulding characteristic, and Facing material and pattern can
Realizing very abundant selection, the most firm in structure, durable in use, the life-span is long, and technical process is simple, system
Cause relatively low.
For achieving the above object, the present invention proposes a kind of aluminum carbon slab production technology, material include decorating film,
Aluminium base, active carbon cloth and hot-fusible high-molecular film, from top to bottom by material according to decorating film-hot-fusible high-molecular film
The order of-aluminium base-hot-fusible high-molecular film-active carbon cloth is placed；Material is carried out physics by high frequency heating machine
Heat leak so that hot-fusible high-molecular film softens generation gluing；Then synthetic material is carried out by rolling machine
The bonding making to reach height between material is reinforced in rolling；Finally utilize cutting machine by synthetic material according to necessarily
Size is cut, and makes finished product；Finally pack.
As preferably, described material includes decorating film, aluminium base, active carbon cloth and hot-fusible high-molecular film, institute
State material from top to bottom according to decorating film-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-aluminium base-height
The order of molecule hot melt film-active carbon cloth is placed.
As preferably, described material includes decorating film, aluminium base, active carbon cloth and hot-fusible high-molecular film, from
Under on by material according to decorating film-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-aluminium base-high score
The order of sub-hot melt film-aluminium base-hot-fusible high-molecular film-active carbon cloth is placed.
As preferably, described material includes decorating film, aluminium base, active carbon cloth and hot-fusible high-molecular film, from
Under on by material according to decorating film-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-aluminium base-high score
The order of sub-hot melt film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-active carbon cloth is placed.
As preferably, described decorating film is leather or wallpaper.
As preferably, the thickness of described wallpaper is 3.5～5m.
As preferably, described leather according to immersion, depilation, defat, liming, deliming, pickling liquid, tanning,
Retanning, stuffing, be dried, stake technique makes.
As preferably, the kind of described wallpaper is plastic wallpaper or foaming wallpaper.
As preferably, described decorating film is cloth or cork.
Beneficial effects of the present invention: the present invention is by by decorating film, aluminium base, active carbon cloth and macromolecule heat
Melt film superposition in a certain order, by heating and pressurization, makes hot-fusible high-molecular film melt top and the bottom
Material is pasted together, it is possible to increases aluminium base and the number of plies of hot-fusible high-molecular film as required, makes difference
The aluminum carbon slab of thickness and intensity, technical process is relatively simple, and manufacturing cost is relatively low, and finished product aluminum carbon slab has very well
Moulding characteristic, Facing material and pattern are capable of enriching very much selection, the most firm in structure, prolonged resistance to
With.
Inventive feature and advantage will be described in detail by embodiment.
[detailed description of the invention]
Embodiment 1: one aluminum carbon slab production technology of the present invention, material includes decorating film, aluminium base, activated carbon
Cloth and hot-fusible high-molecular film, from top to bottom by material according to decorating film-hot-fusible high-molecular film-aluminium base-macromolecule
The order of hot melt film-active carbon cloth is placed；Material is carried out physical thermal infiltration by high frequency heating machine so that high
Molecule hot melt film softens generation gluing；Then synthetic material is carried out rolling reinforcing by rolling machine and make material
The bonding of height is reached between material；Finally utilize cutting machine to be cut according to certain size by synthetic material, make
Finished product；Finally pack.Described material includes decorating film, aluminium base, active carbon cloth and hot-fusible high-molecular film,
Described material from top to bottom according to decorating film-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-aluminium base-
The order of hot-fusible high-molecular film-active carbon cloth is placed.Described decorating film is leather or wallpaper.The thickness of described wallpaper
Degree is 3.5～5mm.Described leather according to immersion, depilation, defat, liming, deliming, pickling liquid, tanning,
Retanning, stuffing, be dried, stake technique makes.The kind of described wallpaper is plastic wallpaper or foaming wallpaper.
Described decorating film is cloth or cork.
Embodiment 2: one aluminum carbon slab production technology of the present invention, material includes decorating film, aluminium base, activated carbon
Cloth and hot-fusible high-molecular film, described material is from top to bottom according to decorating film-hot-fusible high-molecular film-aluminium base-high score
The order of sub-hot melt film-aluminium base-hot-fusible high-molecular film-active carbon cloth is placed；Material is passed through high frequency heating machine
Carry out physical thermal infiltration so that hot-fusible high-molecular film softens generation gluing；Then by synthetic material by rolling
Machine carries out rolling and reinforces the bonding making to reach height between material；Finally utilize cutting machine by synthetic material
Cut according to certain size, make finished product；Finally pack.Described decorating film is leather or wallpaper.Described wall
The thickness of paper is 3.5～5mm.Described leather according to immersion, depilation, defat, liming, deliming, pickling liquid,
Tanning, retanning, stuffing, be dried, stake technique makes.The kind of described wallpaper is plastic wallpaper or sends out
Bubble wallpaper.Described decorating film is cloth or cork.
Embodiment 3: one aluminum carbon slab production technology of the present invention, material includes decorating film, aluminium base, activated carbon
Cloth and hot-fusible high-molecular film, from top to bottom by material according to decorating film-hot-fusible high-molecular film-aluminium base-macromolecule
The order of hot melt film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-active carbon cloth is placed；Will
Material carries out physical thermal infiltration by high frequency heating machine so that hot-fusible high-molecular film softens generation gluing；Then
Synthetic material is carried out rolling by rolling machine and reinforces the bonding making to reach height between material；Last profit
With cutting machine, synthetic material is cut according to certain size, make finished product；Finally pack.Described decorating film is
Leather or wallpaper.The thickness of described wallpaper is 3.5～5mm.Described leather according to immersion, depilation, defat,
Liming, deliming, pickling liquid, tanning, retanning, stuffing, be dried, stake technique makes.Described wallpaper
Kind be plastic wallpaper or foaming wallpaper.Described decorating film is cloth or cork.
Embodiment 4: one aluminum carbon slab production technology of the present invention, material includes decorating film, aluminium base, activated carbon
Cloth and hot-fusible high-molecular film, from top to bottom by material according to decorating film-hot-fusible high-molecular film-aluminium base-macromolecule
Hot melt film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-
The order of active carbon cloth is placed；Material is carried out physical thermal infiltration by high frequency heating machine so that macromolecule heat
Melt film softens generation gluing；Then by rolling machine, synthetic material is carried out roll reinforcing to make between material
Reach the bonding of height；Finally utilize cutting machine to be cut according to certain size by synthetic material, make finished product；
Finally pack.Described decorating film is leather or wallpaper.The thickness of described wallpaper is 3.5～5mm.Described leather
According to immersion, depilation, defat, liming, deliming, pickling liquid, tanning, retanning, stuffing, it is dried, draws
Soft technique is made.The kind of described wallpaper is plastic wallpaper or foaming wallpaper.Described decorating film is cloth or soft
Wood.
One aluminum carbon slab production technology of the present invention, by by decorating film, aluminium base, active carbon cloth and macromolecule
Hot melt film superposition in a certain order, by heating and pressurization, makes hot-fusible high-molecular film melt top and the bottom
Material be pasted together, it is possible to increase aluminium base and the number of plies of hot-fusible high-molecular film as required, make not
The aluminum carbon slab of stack pile and intensity, technical process is relatively simple, and manufacturing cost is relatively low, and finished product aluminum carbon slab has very
Good moulding characteristic, Facing material and pattern are capable of enriching very much selection, the most firm in structure, prolonged
Durable.
Above-described embodiment is the description of the invention, is not limitation of the invention, any simple to the present invention
Scheme after conversion belongs to protection scope of the present invention.
Claims (4)
1. an aluminum carbon slab production technology, it is characterised in that: material includes decorating film, aluminium base, active carbon cloth and
Hot-fusible high-molecular film, from top to bottom by material according to decorating film-hot-fusible high-molecular film-aluminium base-macromolecule heat
The order of melt film-active carbon cloth is placed；Material is carried out physical thermal infiltration by high frequency heating machine so that high
Molecule hot melt film softens generation gluing；Then by rolling machine, synthetic material is carried out roll reinforcing to make
The bonding of height is reached between material；Cutting machine is finally utilized to be cut according to certain size by synthetic material,
Make finished product；Finally packing, described decorating film is leather or wallpaper, described leather according to immersion, depilation,
Defat, liming, deliming, pickling liquid, tanning, retanning, stuffing, be dried, stake technique make,
The kind of described wallpaper is plastic wallpaper or foaming wallpaper, and the thickness of described wallpaper is 3.5～5mm.
2. a kind of aluminum carbon slab production technology as claimed in claim 1, it is characterised in that: described material includes decoration
Film, aluminium base, active carbon cloth and hot-fusible high-molecular film, described material is from top to bottom according to decorating film-high score
The order of sub-hot melt film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-active carbon cloth is put
Put.
3. a kind of aluminum carbon slab production technology as claimed in claim 1, it is characterised in that: described material includes decoration
Film, aluminium base, active carbon cloth and hot-fusible high-molecular film, from top to bottom by material according to decorating film-macromolecule
Hot melt film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film
The order of-active carbon cloth is placed.
4. a kind of aluminum carbon slab production technology as claimed in claim 1, it is characterised in that: described material includes decoration
Film, aluminium base, active carbon cloth and hot-fusible high-molecular film, from top to bottom by material according to decorating film-macromolecule
Hot melt film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film-aluminium base-hot-fusible high-molecular film
The order of-aluminium base-hot-fusible high-molecular film-active carbon cloth is placed.