CN104387672A - Regenerated polypropylene flame-retardant modified material and preparation method thereof - Google Patents
Regenerated polypropylene flame-retardant modified material and preparation method thereof Download PDFInfo
- Publication number
- CN104387672A CN104387672A CN201410754859.1A CN201410754859A CN104387672A CN 104387672 A CN104387672 A CN 104387672A CN 201410754859 A CN201410754859 A CN 201410754859A CN 104387672 A CN104387672 A CN 104387672A
- Authority
- CN
- China
- Prior art keywords
- polypropylene
- parts
- retardant
- flame
- modified material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of recycling of polypropylene regenerated materials, and particularly relates to a regenerated polypropylene flame-retardant modified material and a preparation method thereof. The regenerated polypropylene flame-retardant modified material comprises the following substances in parts by weight: 100 parts of polypropylene recovered materials, 10-15 parts of glass fibers, 40-45 parts of flame retardants, 1-2 parts of flame-retardant synergists, 10-15 parts of anti-impact modifying agents, 1-2 parts of antioxidants, 0.1-0.5 part of coupling agents and 0.3-0.8 part of reinforcing agents, wherein the flame retardants are compound flame retardants formed by compounding magnesium hydroxide and encapsulated red phosphorus, and the flame-retardant synergists are diatomite. The regenerated polypropylene has the advantages of low toxicity, low smoke and no melting drop, and achieves the oxygen index as high as 38% and the char yield as high as 35. The regenerated polypropylene flame-retardant modified material disclosed by the invention is high in mechanical property and excellent in flame-retardant effect. The preparation method disclosed by the invention has the advantages of high polypropylene purity and few impurities of an obtained polypropylene recovered material, simple preparation process and easiness for industrialization realization.
Description
Technical field
The present invention relates to the recovery and utilization technology field of polypropene recycled materials, be specifically related to a kind of regenerating polypropylene anti-flaming modified material and preparation method thereof.
Background technology
China Today has entered household electrical appliance and has discarded peak period, scraps household appliances every year by generation more than 3,000 ten thousand, and so huge waste household appliances certainly leads to a large amount of waste or used plastics.The recycling of waste or used plastics has sanitary landfill, burns heat-obtaining, and resource recycling three kinds of modes, and wherein landfill easily causes the wasting of resources and secondary pollution with burning, and this runs counter to the themes of the times of environmental protection.
Nowadays, the mode of regeneration is mainly taked in the recycling of waste or used plastics, mainly comprises Direct Regeneration, modification regeneration, gasification and oiling process.But the Mechanical Properties of Products of Direct Regeneration declines comparatively large, should not make high-grade goods; Plastics high-temperature gasification, oiling are high with the technical difficulty reclaiming the low component product such as monomer, fuel oil, equipment scale is large; And some mechanical property of the goods of modification regeneration can meet or exceed the performance of unmodified resin goods, there is very high added value.Therefore, the modification regeneration of waste or used plastics is the developing direction of resource utilization recycling.
Polypropylene (PP material) is a kind of thermoplastic resin material obtained by propylene polymerization, is an important kind in five large general synthetic resins.PP is that all synthetic resins Midst density are minimum, is only 0.90 ~ 0.91g/cm3, in five large general-purpose plastics, the excellent heat resistance of PP, PP belongs to non-polar polymer, has good electrical insulating property, and PP water-absorbent is extremely low, electrical insulating property can not be subject to the impact of humidity.
Therefore, polypropylene by injection moulding, extrude, the method such as blowing and thermoforming makes various product, be widely used in fields such as packaging, automobile, household electrical appliances, building materials, chemical industry.In electronic enterprises, used polypropylene can carry out recovery modification regeneration, but polypropylene own belongs to inflammable material, its oxygen index is only 17%-18.5%, and charring rate is low, easy propagating flame causes fire, produce during burning to melt and drip, therefore the modification of its flame retardant properties is a significant problem.
Summary of the invention
The object of the invention is for deficiency of the prior art, a kind of regenerating polypropylene anti-flaming modified material is provided, it has good flame retardation effect, greatly improve containing oxygen index, after burning, charring rate is high, drip without melting, and material is excellent in cushion effect, while not affecting its mechanical property, greatly strengthen its flame retardant resistance.
Another goal of the invention of the present invention is to provide a kind of preparation method of regenerating polypropylene anti-flaming modified material, and its polypropylene purity with the polypropylene reclaimed material obtained is high, and impurity is few, and preparation technology is easy, easily realizes the feature of industrialization.
Object of the present invention is achieved through the following technical solutions:
A kind of regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
Glass fibre 10-15 part
Fire retardant 40-45 part
Retardant synergist 1-2 part
Anti-impact modifier 10-15 part
Oxidation inhibitor 1-2 part
Coupling agent 0.1-0.5 part
Strengthening agent 0.3-0.8 part,
Wherein, described fire retardant is the composite composite flame-retardant agent of magnesium hydroxide and encapsulated red phosphorus; Described retardant synergist is diatomite, and described anti-impact modifier is SBS, SEBS, POE, EPDM, and the particle diameter of described recovery rubber grain is 3-8 μm, and described coupling agent is titanate coupling agent.
The retardant synergist of diatomite as magnesium hydroxide and encapsulated red phosphorus composite flame-retardant agent is with the addition of in the present invention, the oxygen index of flame-retardant system can reach 38%, carbon left is increased to 36%, total thermal discharge significantly reduces, and diatomite can improve the thermostability of regenerating polypropylene material and residual quality rate, reduce Thermal release speed, to preventing propagation of flame from having good effect, therefore diatomite has obvious cooperative flame retardant effect to fire retardant of the present invention.
Glass fibre can promote tensile strength and the shock resistance of regenerating polypropylene, and the comprehensive mechanical property of regenerating polypropylene is effectively promoted.
Diatomaceous addition is not The more the better, and too much diatomite can reduce the material property of regenerating polypropylene on the contrary.Diatomaceous addition is preferably 1.5 parts, and its fire resistance is the highest, and is significantly improved to the material property of regenerating polypropylene.
Described anti-impact modifier is that SBS, SEBS, POE, EPDM reclaim granulation material, and the particle diameter of described recovery rubber grain is 3-8 μm.
POE plastics are the thermoplastic elastomers adopting the ethene of metallocene catalyst and octene to realize in-situ polymerization, be characterized in: the flexible chain coiled structure of (1) octene and the ethylene chain of crystallization, as physical crosslinking point, make the toughness of its existing excellence have again good processibility.(2) there is no unsaturated double-bond in POE plastic molecules structure, there is excellent ageing-resistant performance.(3) POE plastic molecules amount narrowly distributing, has good mobility, good with compatible polyolefin.(4) good mobility can improve the dispersion effect of filler, also can improve the weld mark strength of goods simultaneously.
SEBS take polystyrene as end segment, and the ethylene-butene copolymer obtained with polyhutadiene hydrogenation is the linear three embedding multipolymers of middle spring block.SEBS containing unsaturated double-bond, does not therefore have satisfactory stability and ageing resistance.
EPDM Chinese name: terpolymer EP rubber, the present invention uses and refers to that raw material had used twice or repeatedly, the epdm particle processed, its elasticity, all respects such as toughness are not all fine.
Styrene series thermoplastic elastomer (SBS) is maximum, the most similar to the rubber performance a kind of thermoplastic elastomer of world wide production, and adding angle clout can repeatedly recycle, and saving resource, is conducive to environment protection.
Further, a kind of regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
Glass fibre 10-12 part
Fire retardant 41-43 part
Retardant synergist 1-1.5 part
Anti-impact modifier 11-13 part
Oxidation inhibitor 1-2 part
Coupling agent 0.2-0.4 part
Strengthening agent 0.3-0.8 part.
Further, a kind of regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
11 parts, glass fibre
Fire retardant 42 parts
Retardant synergist 1.5 parts
Anti-impact modifier 11 parts
2 parts, oxidation inhibitor
Coupling agent 0.35 part
Strengthening agent 0.5 part.
Wherein, described coupling agent is titanate coupling agent, and preferably, described titanate coupling agent is sec.-propyl three (dioctylphyrophosphoric acid amide oxygen base) titanic acid ester.
Simple fire retardant and polypropylene have the defect that poor compatibility, the easily moisture absorption are moved.Major cause is easily reunited in polyacrylic surface, particle diameter is larger, disperse uneven, therefore fire retardant can only be exposed on surface, the present invention adds sec.-propyl three (dioctylphyrophosphoric acid amide oxygen base) titanic acid ester, and fire retardant can be evenly dispersed in polypropylene, and particle diameter diminishes, improve fire retardant and polyacrylic bonding force, therefore improve the flame retardant properties of material.Preferably, titanate coupling agent is 0.35 part, the flame retardant properties of material and mechanical property the best.
Wherein, in described fire retardant, the mass ratio of magnesium hydroxide and encapsulated red phosphorus is 2:1, and its flame retardant effect is best.
Wherein, described diatomite carries out modification through following methods: calcine 2 hours 600 DEG C of anoxics, obtain modified diatomite, can be that decolorizing carbon adsorbed close is in diatom soil cursting surface and inner micropore by organic matter transformation wherein, unbodied carbon improves diatomite and polyacrylic consistency, is conducive to improving polyacrylic mechanical property.
Diatomite and magnesium hydroxide and encapsulated red phosphorus composite flame-retardant agent system composite, can form a layer of charcoal at material surface during burning, this layer of charcoal has heat insulation, oxygen barrier, presses down cigarette and drip without melting, flame retardant effect excellent performance.
Recovery rubber grain is prepared into powdery or particulate state, be equivalent to functional elastomer-filled material, can improve the adherence of regenerating polypropylene material, hardness or elasticity when high temperature extruding pelletization, and the cost reclaiming rubber is lower, preparation technology is also simple.
Wherein, described strengthening agent is two water desulfurated plasters.Two water desulfurated plasters are generally the strengthening agents being used as rubber materials, the present invention, by adding two a small amount of water desulfurated plasters as filler, can promote the processing performance of regenerating polypropylene material, and reduce costs, improve the hardness of material, elasticity, resistance toheat, and reduce compression set.
Wherein, described oxidation inhibitor be irgasfos 168 or antioxidant 1010 oxidation inhibitor add the antioxidant property that can improve regenerating polypropylene, delay the aging of material.
A preparation method for regenerating polypropylene anti-flaming modified material, comprises the following steps:
Step one, take polypropylene reclaimed material by weight, by polypropylene reclaimed material good for fragmentation through single screw extrusion machine, temperature controls at 200-230 DEG C, melting, at the head place of single screw extrusion machine, filtration unit is set, melt is filtered, removing insoluble impurities, extrude polypropylene and reclaim bar;
Step 2: take leftover materials by weight, reclaims bar by polypropylene and leftover materials join in Banbury mixer, at 210-220 DEG C of mixing 18-20min;
Step 3, material step 2 mixed add extruding pelletization in twin screw extruder, and barrel temperature is 180-210 DEG C, and screw speed is 300-400rpm, extrudes, granulation.
Beneficial effect of the present invention: the regenerating polypropylene anti-flaming modified material prepared by the present invention, fire-retardant rank is high, can reach V-0 level, oxygen index is up to 38, charring rate is up to 35, and excellent in cushion effect, and processing fluidity is good, the glossiness of finished product is high, thermal deformation behavior is stablized, and after burning, charring rate is high, drips without melting, and material is excellent in cushion effect, while not affecting its mechanical property, greatly strengthen its flame retardant resistance.The polypropylene purity that this preparation method has the polypropylene reclaimed material obtained is high, and impurity is few, and preparation technology is simple and easy, easily realizes industrialization.
Embodiment
The invention will be further described with the following Examples.
embodiment 1
A kind of regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
10 parts, glass fibre
Fire retardant 45 parts
Retardant synergist 1 part
Anti-impact modifier 15 parts
1 part, oxidation inhibitor
Coupling agent 0.5 part
Strengthening agent 0.3 part,
Wherein, described fire retardant is the composite composite flame-retardant agent of magnesium hydroxide and encapsulated red phosphorus; Described retardant synergist is diatomite, and described anti-impact modifier is that SBS reclaims granulation material, and the particle diameter of described recovery rubber grain is 3-8 μm, and described coupling agent is titanate coupling agent.In described fire retardant, the mass ratio of magnesium hydroxide and encapsulated red phosphorus is 2:1.
The retardant synergist of diatomite as magnesium hydroxide and encapsulated red phosphorus composite flame-retardant agent is with the addition of in the present invention, the oxygen index of flame-retardant system can reach 38%, carbon left is increased to 36%, total thermal discharge significantly reduces, and diatomite can improve the thermostability of regenerating polypropylene material and residual quality rate, reduce Thermal release speed, to preventing propagation of flame from having good effect, therefore diatomite has obvious cooperative flame retardant effect to fire retardant of the present invention.
Glass fibre can promote tensile strength and the shock resistance of regenerating polypropylene, and the comprehensive mechanical property of regenerating polypropylene is effectively promoted.
Recovery rubber grain is prepared into powdery or particulate state, be equivalent to functional elastomer-filled material, can improve the adherence of regenerating polypropylene material, hardness or elasticity when high temperature extruding pelletization, and the cost reclaiming rubber is lower, preparation technology is also simple.
Wherein, described strengthening agent is two water desulfurated plasters.Two water desulfurated plasters are generally the strengthening agents being used as rubber materials, the present invention, by adding two a small amount of water desulfurated plasters as filler, can promote the processing performance of regenerating polypropylene material, and reduce costs, improve the hardness of material, elasticity, resistance toheat, and reduce compression set.
Wherein, described oxidation inhibitor is irgasfos 168, oxidation inhibitor add the antioxidant property that can improve regenerating polypropylene, delay the aging of material.
A preparation method for regenerating polypropylene anti-flaming modified material, comprises the following steps:
Step one, take polypropylene reclaimed material by weight, by polypropylene reclaimed material good for fragmentation through single screw extrusion machine, temperature controls at 230 DEG C, melting, arranges filtration unit at the head place of single screw extrusion machine, filters melt, removing insoluble impurities, extrudes polypropylene and reclaims bar;
Step 2: take leftover materials by weight, reclaims bar by polypropylene and leftover materials join in Banbury mixer, at 2220 DEG C of mixing 20min;
Step 3, material step 2 mixed add extruding pelletization in twin screw extruder, and barrel temperature is 210 DEG C, and screw speed is 400rpm, extrudes, granulation.
embodiment 2
A kind of regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
15 parts, glass fibre
Fire retardant 40 parts
Retardant synergist 2 parts
Anti-impact modifier 10 parts
2 parts, oxidation inhibitor
Coupling agent 0.1 part
Strengthening agent 0.8 part,
Wherein, described fire retardant is the composite composite flame-retardant agent of magnesium hydroxide and encapsulated red phosphorus; Described retardant synergist is diatomite, and described anti-impact modifier is that SEBS reclaims granulation material, and the particle diameter of described recovery rubber grain is 3-8 μm, and described coupling agent is titanate coupling agent.In described fire retardant, the mass ratio of magnesium hydroxide and encapsulated red phosphorus is 2:1.
Glass fibre can promote tensile strength and the shock resistance of regenerating polypropylene, and the comprehensive mechanical property of regenerating polypropylene is effectively promoted.
Recovery rubber grain is prepared into powdery or particulate state, be equivalent to functional elastomer-filled material, can improve the adherence of regenerating polypropylene material, hardness or elasticity when high temperature extruding pelletization, and the cost reclaiming rubber is lower, preparation technology is also simple.
Wherein, described strengthening agent is two water desulfurated plasters.Two water desulfurated plasters are generally the strengthening agents being used as rubber materials, the present invention, by adding two a small amount of water desulfurated plasters as filler, can promote the processing performance of regenerating polypropylene material, and reduce costs, improve the hardness of material, elasticity, resistance toheat, and reduce compression set.
Wherein, described oxidation inhibitor is irgasfos 168, oxidation inhibitor add the antioxidant property that can improve regenerating polypropylene, delay the aging of material.
A preparation method for regenerating polypropylene anti-flaming modified material, comprises the following steps:
Step one, take polypropylene reclaimed material by weight, by polypropylene reclaimed material good for fragmentation through single screw extrusion machine, temperature controls at 200 DEG C, melting, arranges filtration unit at the head place of single screw extrusion machine, filters melt, removing insoluble impurities, extrudes polypropylene and reclaims bar;
Step 2: take leftover materials by weight, reclaims bar by polypropylene and leftover materials join in Banbury mixer, at 210 DEG C of mixing 18min;
Step 3, material step 2 mixed add extruding pelletization in twin screw extruder, and barrel temperature is 180 DEG C, and screw speed is 300rpm, extrudes, granulation.
embodiment 3
A kind of regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
12 parts, glass fibre
Fire retardant 41 parts
Retardant synergist 1 part
Anti-impact modifier 11 parts
2 parts, oxidation inhibitor
Coupling agent 0.2 part
Strengthening agent 0.8 part,
Wherein, described fire retardant is the composite composite flame-retardant agent of magnesium hydroxide and encapsulated red phosphorus; Described retardant synergist is diatomite, and described anti-impact modifier is that POE reclaims granulation material, and the particle diameter of described recovery rubber grain is 3-8 μm, and described coupling agent is titanate coupling agent.In described fire retardant, the mass ratio of magnesium hydroxide and encapsulated red phosphorus is 2:1.
Glass fibre can promote tensile strength and the shock resistance of regenerating polypropylene, and the comprehensive mechanical property of regenerating polypropylene is effectively promoted.
Recovery rubber grain is prepared into powdery or particulate state, be equivalent to functional elastomer-filled material, can improve the adherence of regenerating polypropylene material, hardness or elasticity when high temperature extruding pelletization, and the cost reclaiming rubber is lower, preparation technology is also simple.
Wherein, described strengthening agent is two water desulfurated plasters.Two water desulfurated plasters are generally the strengthening agents being used as rubber materials, the present invention, by adding two a small amount of water desulfurated plasters as filler, can promote the processing performance of regenerating polypropylene material, and reduce costs, improve the hardness of material, elasticity, resistance toheat, and reduce compression set.
Wherein, described oxidation inhibitor is antioxidant 1010, oxidation inhibitor add the antioxidant property that can improve regenerating polypropylene, delay the aging of material.
A preparation method for regenerating polypropylene anti-flaming modified material, comprises the following steps:
Step one, take polypropylene reclaimed material by weight, by polypropylene reclaimed material good for fragmentation through single screw extrusion machine, temperature controls at 230 DEG C, melting, arranges filtration unit at the head place of single screw extrusion machine, filters melt, removing insoluble impurities, extrudes polypropylene and reclaims bar;
Step 2: take leftover materials by weight, reclaims bar by polypropylene and leftover materials join in Banbury mixer, at 220 DEG C of mixing 18min;
Step 3, material step 2 mixed add extruding pelletization in twin screw extruder, and barrel temperature is 210 DEG C, and screw speed is 350rpm, extrudes, granulation.
embodiment 4
A kind of regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
12 parts, glass fibre
Fire retardant 43 parts
Retardant synergist 1.5 parts
Anti-impact modifier 13 parts
1 part, oxidation inhibitor
Coupling agent 0.4 part
Strengthening agent 0.5 part,
Wherein, described fire retardant is the composite composite flame-retardant agent of magnesium hydroxide and encapsulated red phosphorus; Described retardant synergist is diatomite, and described anti-impact modifier is that EPDM reclaims granulation material, and the particle diameter of described recovery rubber grain is 3-8 μm, and described coupling agent is titanate coupling agent.In described fire retardant, the mass ratio of magnesium hydroxide and encapsulated red phosphorus is 2:1.
Glass fibre can promote tensile strength and the shock resistance of regenerating polypropylene, and the comprehensive mechanical property of regenerating polypropylene is effectively promoted.
Recovery rubber grain is prepared into powdery or particulate state, be equivalent to functional elastomer-filled material, can improve the adherence of regenerating polypropylene material, hardness or elasticity when high temperature extruding pelletization, and the cost reclaiming rubber is lower, preparation technology is also simple.
Wherein, described strengthening agent is two water desulfurated plasters.Two water desulfurated plasters are generally the strengthening agents being used as rubber materials, the present invention, by adding two a small amount of water desulfurated plasters as filler, can promote the processing performance of regenerating polypropylene material, and reduce costs, improve the hardness of material, elasticity, resistance toheat, and reduce compression set.
Wherein, described oxidation inhibitor is irgasfos 168, oxidation inhibitor add the antioxidant property that can improve regenerating polypropylene, delay the aging of material.
A preparation method for regenerating polypropylene anti-flaming modified material, comprises the following steps:
Step one, take polypropylene reclaimed material by weight, by polypropylene reclaimed material good for fragmentation through single screw extrusion machine, temperature controls at 200 DEG C, melting, arranges filtration unit at the head place of single screw extrusion machine, filters melt, removing insoluble impurities, extrudes polypropylene and reclaims bar;
Step 2: take leftover materials by weight, reclaims bar by polypropylene and leftover materials join in Banbury mixer, at 210 DEG C of mixing 20min;
Step 3, material step 2 mixed add extruding pelletization in twin screw extruder, and barrel temperature is 180 DEG C, and screw speed is 300rpm, extrudes, granulation.
embodiment 5
A preparation method for regenerating polypropylene anti-flaming modified material, is made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
11 parts, glass fibre
Fire retardant 42 parts
Retardant synergist 1.5 parts
Anti-impact modifier 11 parts
2 parts, oxidation inhibitor
Coupling agent 0.35 part
Strengthening agent 0.5 part.
Wherein, described fire retardant is the composite composite flame-retardant agent of magnesium hydroxide and encapsulated red phosphorus; Described retardant synergist is diatomite, and described anti-impact modifier is that SBS reclaims granulation material, and the particle diameter of described recovery rubber grain is 3-8 μm, and described coupling agent is titanate coupling agent.In described fire retardant, the mass ratio of magnesium hydroxide and encapsulated red phosphorus is 2:1.
Glass fibre can promote tensile strength and the shock resistance of regenerating polypropylene, and the comprehensive mechanical property of regenerating polypropylene is effectively promoted.
Recovery rubber grain is prepared into powdery or particulate state, be equivalent to functional elastomer-filled material, can improve the adherence of regenerating polypropylene material, hardness or elasticity when high temperature extruding pelletization, and the cost reclaiming rubber is lower, preparation technology is also simple.
Wherein, described strengthening agent is two water desulfurated plasters.Two water desulfurated plasters are generally the strengthening agents being used as rubber materials, the present invention, by adding two a small amount of water desulfurated plasters as filler, can promote the processing performance of regenerating polypropylene material, and reduce costs, improve the hardness of material, elasticity, resistance toheat, and reduce compression set.
Wherein, described oxidation inhibitor is antioxidant 1010, oxidation inhibitor add the antioxidant property that can improve regenerating polypropylene, delay the aging of material.
A preparation method for regenerating polypropylene anti-flaming modified material, comprises the following steps:
Step one, take polypropylene reclaimed material by weight, by polypropylene reclaimed material good for fragmentation through single screw extrusion machine, temperature controls at 200 DEG C, melting, arranges filtration unit at the head place of single screw extrusion machine, filters melt, removing insoluble impurities, extrudes polypropylene and reclaims bar;
Step 2: take leftover materials by weight, reclaims bar by polypropylene and leftover materials join in Banbury mixer, at 220 DEG C of mixing 20min;
Step 3, material step 2 mixed add extruding pelletization in twin screw extruder, and barrel temperature is 180 DEG C, and screw speed is 400rpm, extrudes, granulation.
Embodiment 1-5 is carried out aptitude test, and performance is as shown in the table:
Can find out according to upper table, the comprehensive mechanical property of regenerating polypropylene prepared by the present invention and excellent fireproof performance.
Finally should be noted that; above embodiment is only in order to illustrate technical scheme of the present invention; but not limiting the scope of the invention; although done to explain to the present invention with reference to preferred embodiment; those of ordinary skill in the art is to be understood that; can modify to technical scheme of the present invention or equivalent replacement, and not depart from essence and the scope of technical solution of the present invention.
Claims (10)
1. a regenerating polypropylene anti-flaming modified material, is characterized in that: be made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
Glass fibre 10-15 part
Fire retardant 40-45 part
Retardant synergist 1-2 part
Anti-impact modifier 10-15 part
Oxidation inhibitor 1-2 part
Coupling agent 0.1-0.5 part
Strengthening agent 0.3-0.8 part,
Wherein, described fire retardant is the composite composite flame-retardant agent of magnesium hydroxide and encapsulated red phosphorus; Described retardant synergist is diatomite, and described anti-impact modifier is that SBS, SEBS, POE, EPDM reclaim granulation material, and described coupling agent is titanate coupling agent.
2. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: be made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
Glass fibre 10-12 part
Fire retardant 41-43 part
Retardant synergist 1-1.5 part
Anti-impact modifier 11-13 part
Oxidation inhibitor 1-2 part
Coupling agent 0.2-0.4 part
Strengthening agent 0.3-0.8 part.
3. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: be made up of the material of following weight part:
Polypropylene reclaimed material 100 parts
11 parts, glass fibre
Fire retardant 42 parts
Retardant synergist 1.5 parts
Anti-impact modifier 11 parts
2 parts, oxidation inhibitor
Coupling agent 0.35 part
Strengthening agent 0.5 part.
4. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: described titanate coupling agent is sec.-propyl three (dioctylphyrophosphoric acid amide oxygen base) titanic acid ester.
5. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: in described fire retardant, the mass ratio of magnesium hydroxide and encapsulated red phosphorus is 2:1.
6. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: described diatomite carries out modification through following methods: calcine 2 hours 600 DEG C of anoxics, obtain modified diatomite.
7. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: the particle diameter of described recovery rubber grain is 3-8 μm.
8. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: described strengthening agent is two water desulfurated plasters.
9. a kind of regenerating polypropylene anti-flaming modified material according to claim 1, is characterized in that: described oxidation inhibitor is irgasfos 168 or antioxidant 1010.
10. the preparation method of a kind of regenerating polypropylene anti-flaming modified material described in any one of claim 1-9, is characterized in that: comprise the following steps:
Step one, take polypropylene reclaimed material by weight, by polypropylene reclaimed material good for fragmentation through single screw extrusion machine, temperature controls at 200-230 DEG C, melting, at the head place of single screw extrusion machine, filtration unit is set, melt is filtered, removing insoluble impurities, extrude polypropylene and reclaim bar;
Step 2: take leftover materials by weight, reclaims bar by polypropylene and leftover materials join in Banbury mixer, at 210-220 DEG C of mixing 18-20min;
Step 3, material step 2 mixed add extruding pelletization in twin screw extruder, and barrel temperature is 180-210 DEG C, and screw speed is 300-400rpm, extrudes, granulation.