CN104355658B - 生产防火保温板方法 - Google Patents

生产防火保温板方法 Download PDF

Info

Publication number
CN104355658B
CN104355658B CN201410526458.0A CN201410526458A CN104355658B CN 104355658 B CN104355658 B CN 104355658B CN 201410526458 A CN201410526458 A CN 201410526458A CN 104355658 B CN104355658 B CN 104355658B
Authority
CN
China
Prior art keywords
temperature
dry
slurry
heated board
fireproof heated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410526458.0A
Other languages
English (en)
Other versions
CN104355658A (zh
Inventor
陈万国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Sheng Du Energy Saving Technology Co., Ltd.
Original Assignee
HEFEI XIANGRONG ENVIRONMENTAL PROTECTION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI XIANGRONG ENVIRONMENTAL PROTECTION TECHNOLOGY Co Ltd filed Critical HEFEI XIANGRONG ENVIRONMENTAL PROTECTION TECHNOLOGY Co Ltd
Priority to CN201410526458.0A priority Critical patent/CN104355658B/zh
Publication of CN104355658A publication Critical patent/CN104355658A/zh
Application granted granted Critical
Publication of CN104355658B publication Critical patent/CN104355658B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种生产防火保温板方法，该方法包括有以下步骤：取5-8份可发性聚苯乙烯母料颗粒经蒸汽预发泡，再将预制好的阻燃剂浆料与预发泡的聚苯乙烯颗粒按照重量比1∶2-4的比例混合均匀，再与5-8份浒苔纤维和25-35份泡花碱、12-15份膨胀珍珠岩充分混合后，一同放入球磨机中细磨，混合物的粒度控制在5-10mm；本发明的铁矿尾渣用量大、节能环保，缓解铁矿尾渣堆存处理带来的环境污染问题，同时为空心砖提供了新的原料。

Description

生产防火保温板方法
技术领域
本发明涉及新型建材领域，具体属于一种生产防火保温板方法。
背景技术
长期以来，铁矿尾渣的综合利用一直是个世界性难题，尽管国内外对萤铁矿尾渣的综合利用进行了大量的研究，但是由于技术上和经济上的种种原因，大多数未付诸工业实现。
综合所述，用铁矿尾渣为辅助原料生产水泥、墙体砖、道路材料已有报道，以铁矿尾渣作为主要原料用于加气砌块的生产还未见报道。
发明内容
本发明的目的是提供一种生产防火保温板方法，工艺简单，原料成本低，对环境影响小。
本发明的技术方案如下：
一种生产防火保温板方法，该方法包括有以下步骤：
1）、取5-8份可发性聚苯乙烯母料颗粒经蒸汽预发泡，再将预制好的阻燃剂浆料与预发泡的聚苯乙烯颗粒按照重量比1∶2-4的比例混合均匀，再与5-8份浒苔纤维和25-35份泡花碱、12-15份膨胀珍珠岩充分混合后，一同放入球磨机中细磨，混合物的粒度控制在5-10mm；
2）、将上述步骤（1）混合物干料与50-60份的水和5-7份的发泡剂混合搅拌后形成，浆料在65-75℃温度下，发泡时间30-40min；
3）、将发泡浆料注入到成型模具内压制形成生坯，压强为40-60Mpa；
4）、进行烘干，烘干分为低温区和高温区，首先进入低温区进行烘干，烘干温度为40-100℃，烘干时间6-8分钟；再进入高温区进行烘干，烘干温度为200-400℃，烘干时间20-40分钟。
所述步骤（1）混合物干料与55份的水和6份的发泡剂混合搅拌后形成，浆料在70℃温度下，发泡时间35min。
本发明与现有技术相比具有如下优点：
总之，本发明结合我国铁矿尾渣量大、利用率低的实际情况，充分利用了各种物料的组成结构和化学特性，形成了以硅铝酸钙、水化硅酸钙等为主体的矿物结构，其产品性能符合建筑用承重和非承重墙体材料质量要求。砌块主要原材料为铁矿尾渣，使用量大，有利于解决铁矿尾渣堆存处理而带来的环境污染问题，为铁矿尾渣的资源化利用开辟了一条新的利用途径。
具体实施方式
一种生产防火保温板方法，该方法包括有以下步骤：
1）、取5-8份可发性聚苯乙烯母料颗粒经蒸汽预发泡，再将预制好的阻燃剂浆料与预发泡的聚苯乙烯颗粒按照重量比1∶2-4的比例混合均匀，再与5-8份浒苔纤维和25-35份泡花碱、12-15份膨胀珍珠岩充分混合后，一同放入球磨机中细磨，混合物的粒度控制在5-10mm；
2）、将上述步骤（1）混合物干料与50-60份的水和5-7份的发泡剂混合搅拌后形成，浆料在65-75℃温度下，发泡时间30-40min；
3）、将发泡浆料注入到成型模具内压制形成生坯，压强为40-60Mpa；
4）、进行烘干，烘干分为低温区和高温区，首先进入低温区进行烘干，烘干温度为40-100℃，烘干时间6-8分钟；再进入高温区进行烘干，烘干温度为200-400℃，烘干时间20-40分钟。
所述步骤（1）混合物干料与55份的水和6份的发泡剂混合搅拌后形成，浆料在70℃温度下，发泡时间35min。

Claims (2)

1.一种生产防火保温板方法，其特征在于，该方法包括有以下步骤：
1）、取5-8份可发性聚苯乙烯母料颗粒经蒸汽预发泡，再将预制好的阻燃剂浆料与预发泡的聚苯乙烯颗粒按照重量比1∶2-4的比例混合均匀，再与5-8份浒苔纤维和25-35份泡花碱、12-15份膨胀珍珠岩充分混合后，一同放入球磨机中细磨，混合物的粒度控制在5-10mm；
2）、将上述步骤1）混合物干料与50-60份的水和5-7份的发泡剂混合搅拌后形成浆料，浆料在65-75℃温度下发泡，发泡时间30-40min；
3）、将发泡浆料注入到成型模具内压制形成生坯，压强为40-60MPa；
4）、进行烘干，烘干分为低温区和高温区，首先进入低温区进行烘干，烘干温度为40-100℃，烘干时间6-8分钟；再进入高温区进行烘干，烘干温度为200-400℃，烘干时间20-40分钟。
2.根据权利要求1所述的生产防火保温板方法，其特征在于，所述步骤1）混合物干料与55份的水和6份的发泡剂混合搅拌后形成浆料，浆料在70℃温度下发泡，发泡时间35min。
CN201410526458.0A 2014-10-09 2014-10-09 生产防火保温板方法 Active CN104355658B (zh)