CN104327932A - Graphite lubricant - Google Patents
Graphite lubricant Download PDFInfo
- Publication number
- CN104327932A CN104327932A CN201310306554.XA CN201310306554A CN104327932A CN 104327932 A CN104327932 A CN 104327932A CN 201310306554 A CN201310306554 A CN 201310306554A CN 104327932 A CN104327932 A CN 104327932A
- Authority
- CN
- China
- Prior art keywords
- parts
- oildag
- graphite
- water
- talcum powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a graphite lubricant. The graphite lubricant comprises the following compositions in parts by weight: 20 parts-30 parts of graphite micro powder, 3 parts-10 parts of nanometer copper borate, 3 parts-8 parts of talcum powder, 2 parts-5 parts of polyoxyethylene oleyl ether, 5 parts-10 parts of molybdenum disulfide, 1 part-5 parts of sodium alkylbenzenesulphonate, 5 parts-20 parts of methyl cellulose, 4 parts-8 parts of sodium borate, 5 parts-15 parts of propanol, and 20 parts-40 parts of water. The aqueous graphite lubricant is small in environmental pollution, green, environment-friendly, wide in application temperature, good in lubricity, high in stability and low in cost.
Description
Technical field
The present invention relates to field of lubricant, be specifically related to a kind of oildag.
Background technology
Graphite lubricating oil (GLO) is widely used in all kinds mechanically to reduce friction, protection machinery and workpiece, mainly play lubrication, cooling, antirust, clean, seal and the effect such as buffering.The oildag of current use be mostly solid or based on mineral oil medium, at high temperature unstable, easily burn Sum decomposition, also machinery can be sustained damage because of at high temperature losing lubrication simultaneously.
Summary of the invention
The object of the invention is for the problems referred to above, the colloidal graphite mixed with water that a kind of lubricity is good, stability is high, Applicable temperature scope is large is provided.
For achieving the above object, technical scheme provided by the invention is, a kind of oildag, and component and the formula of described oildag are as follows:
Graphite microparticles 20 parts-30 parts;
Nano boric acid copper 3 parts-10 parts;
Talcum powder 3 parts-8 parts;
Polyoxyethylene oleyl ether 2 parts-5 parts;
Molybdenumdisulphide 5 parts-10 parts;
Sodium alkyl benzene sulfonate 1 part-5 parts;
Methylcellulose gum 5 parts-20 parts;
Sodium Tetraborate 4 parts-8 parts;
Propyl alcohol 5 parts-15 parts;
20 parts-40 parts, water.
Wherein, described oildag component and formula as follows:
Graphite microparticles 25 parts;
Nano boric acid copper 5 parts;
Talcum powder 5 parts;
Polyoxyethylene oleyl ether 3 parts;
Molybdenumdisulphide 7 parts;
Sodium alkyl benzene sulfonate 3 parts;
Methylcellulose gum 10 parts;
Sodium Tetraborate 6 parts;
Propyl alcohol 10 parts;
26 parts, water.
Wherein, described oildag component and formula as follows:
Graphite microparticles 30 parts;
Nano boric acid copper 3 parts;
Talcum powder 8 parts;
Polyoxyethylene oleyl ether 2 parts;
Molybdenumdisulphide 5 parts;
Sodium alkyl benzene sulfonate 4 parts;
Methylcellulose gum 15 parts;
Sodium Tetraborate 4 parts;
Propyl alcohol 5 parts;
24 parts, water.
Wherein, described oildag component and formula as follows:
Graphite microparticles 20 parts;
Nano boric acid copper 10 parts;
Talcum powder 6 parts;
Polyoxyethylene oleyl ether 4 parts;
Molybdenumdisulphide 10 parts;
Sodium alkyl benzene sulfonate 1 part;
Methylcellulose gum 5 parts;
Sodium Tetraborate 8 parts;
Propyl alcohol 15 parts;
21 parts, water.
Aqueous graphite lubricating agent environmental pollution of the present invention is little, environmental protection, and Applicable temperature scope is wide, and lubrication usefulness is good, and stability is high, and cost is low.
Embodiment
Below in conjunction with specific embodiment, set forth the present invention further.Should be understood that these embodiments are only not used in for illustration of the present invention to limit the scope of the invention.In addition should be understood that those skilled in the art can make various changes or modifications the present invention after having read content of the present invention, these equivalent form of values fall within the application's limited range equally.
Embodiment 1,
Raw material is taken in following ratio:
Graphite microparticles 25 parts;
Nano boric acid copper 5 parts;
Talcum powder 5 parts;
Polyoxyethylene oleyl ether 3 parts;
Molybdenumdisulphide 7 parts;
Sodium alkyl benzene sulfonate 3 parts;
Methylcellulose gum 10 parts;
Sodium Tetraborate 6 parts;
Propyl alcohol 10 parts;
26 parts, water.
Wherein, graphite microparticles selects content to be greater than 98%, and particle diameter is the Graphite Powder 99 of 2 ~ 3 microns.
Embodiment 2,
Raw material is taken in following ratio:
Graphite microparticles 25 parts;
Nano boric acid copper 5 parts;
Talcum powder 5 parts;
Polyoxyethylene oleyl ether 3 parts;
Molybdenumdisulphide 7 parts;
Sodium alkyl benzene sulfonate 3 parts;
Methylcellulose gum 10 parts;
Sodium Tetraborate 6 parts;
Propyl alcohol 10 parts;
26 parts, water.
Embodiment 3,
Raw material is taken in following ratio:
Graphite microparticles 30 parts;
Nano boric acid copper 3 parts;
Talcum powder 8 parts;
Polyoxyethylene oleyl ether 2 parts;
Molybdenumdisulphide 5 parts;
Sodium alkyl benzene sulfonate 4 parts;
Methylcellulose gum 15 parts;
Sodium Tetraborate 4 parts;
Propyl alcohol 5 parts;
24 parts, water.
The present invention is arbitrary combination in following scope:
A kind of oildag, calculate by weight percentage, the formula of described oildag is as follows:
Graphite microparticles 20 parts-30 parts;
Nano boric acid copper 3 parts-10 parts;
Talcum powder 3 parts-8 parts;
Polyoxyethylene oleyl ether 2 parts-5 parts;
Molybdenumdisulphide 5 parts-10 parts;
Sodium alkyl benzene sulfonate 1 part-5 parts;
Methylcellulose gum 5 parts-20 parts;
Sodium Tetraborate 4 parts-8 parts;
Propyl alcohol 5 parts-15 parts;
20 parts-40 parts, water.
Be more than the description to the embodiment of the present invention, by the above-mentioned explanation to the disclosed embodiments, professional and technical personnel in the field realized or uses the present invention.To be apparent for those skilled in the art to the multiple amendment of these embodiments, General Principle as defined herein can without departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention can not be restricted to these embodiments shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Claims (4)
1. an oildag, is characterized in that, calculates by weight percentage, and component and the formula of described oildag are as follows:
Graphite microparticles 20 parts-30 parts;
Nano boric acid copper 3 parts-10 parts;
Talcum powder 3 parts-8 parts;
Polyoxyethylene oleyl ether 2 parts-5 parts;
Molybdenumdisulphide 5 parts-10 parts;
Sodium alkyl benzene sulfonate 1 part-5 parts;
Methylcellulose gum 5 parts-20 parts;
Sodium Tetraborate 4 parts-8 parts;
Propyl alcohol 5 parts-15 parts;
20 parts-40 parts, water.
2. oildag as claimed in claim 1, is characterized in that, calculate by weight percentage, and component and the formula of described oildag are as follows:
Graphite microparticles 25 parts;
Nano boric acid copper 5 parts;
Talcum powder 5 parts;
Polyoxyethylene oleyl ether 3 parts;
Molybdenumdisulphide 7 parts;
Sodium alkyl benzene sulfonate 3 parts;
Methylcellulose gum 10 parts;
Sodium Tetraborate 6 parts;
Propyl alcohol 10 parts;
26 parts, water.
3. oildag as claimed in claim 1, is characterized in that, calculate by weight percentage, and component and the formula of described oildag are as follows:
Graphite microparticles 30 parts;
Nano boric acid copper 3 parts;
Talcum powder 8 parts;
Polyoxyethylene oleyl ether 2 parts;
Molybdenumdisulphide 5 parts;
Sodium alkyl benzene sulfonate 4 parts;
Methylcellulose gum 15 parts;
Sodium Tetraborate 4 parts;
Propyl alcohol 5 parts;
24 parts, water.
4. oildag as claimed in claim 1, is characterized in that, calculate by weight percentage, and component and the formula of described oildag are as follows:
Graphite microparticles 20 parts;
Nano boric acid copper 10 parts;
Talcum powder 6 parts;
Polyoxyethylene oleyl ether 4 parts;
Molybdenumdisulphide 10 parts;
Sodium alkyl benzene sulfonate 1 part;
Methylcellulose gum 5 parts;
Sodium Tetraborate 8 parts;
Propyl alcohol 15 parts;
21 parts, water.