CN107629837A - Mechanical lubrication agent with high lubricating property - Google Patents
Mechanical lubrication agent with high lubricating property Download PDFInfo
- Publication number
- CN107629837A CN107629837A CN201711019315.0A CN201711019315A CN107629837A CN 107629837 A CN107629837 A CN 107629837A CN 201711019315 A CN201711019315 A CN 201711019315A CN 107629837 A CN107629837 A CN 107629837A
- Authority
- CN
- China
- Prior art keywords
- parts
- stearic acid
- lubricating property
- borax
- lubrication agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the mechanical lubrication agent with high lubricating property, it it is 42~58 parts including 3~7 parts of acetate butyl, 5~10 parts of boric acid, 3~9 parts of zirconium manganese powder batch mixing, 2~7 parts of stearic acid, 4~11 parts of glycerine, 3~13 parts of sodium alkyl sulfate, 2~8 parts of Triton X-100,1~9 part of chlorinated paraffin, 5~12 parts of graphite, 5~10 parts of dispersant, stearic acid, 22~32 parts of base oil, sodium hydroxide is 3~7 parts, borax is 0.5~1 part, natrium nitrosum is 0.5~1 part, and odium stearate is 0.5~1 part.The present invention is using stearic acid, base oil as solvent, and using sodium hydroxide, borax, natrium nitrosum, odium stearate as additive, the lubricant of formation is inexpensive, pollution-free.
Description
Technical field
The present invention relates to promoter additive, and in particular to has the mechanical lubrication agent of high lubricating property.
Background technology
Lubricant to reduce the frictional resistance of friction pair, slow down its abrasion lubricant medium.Lubricant to friction pair also
Cooling can be played, clean and prevent pollution etc..In order to improve greasy property, suitable addition can be added in some lubricants
Agent.During from lubricant, motion conditions, material, surface roughness, working environment and the work bar of friction pair must be typically considered
Part, and many factors such as performance of lubricant.In plant equipment, lubricant gives each need by lubricating system transmission & distribution mostly
The position to be lubricated.Existing lubricant so increases cost, and pollute using catalyst etc..
The content of the invention
The technical problems to be solved by the invention are that existing lubricant uses catalyst etc., so increase cost, and cause
Pollution reduces pollution, and it is an object of the present invention to provide the mechanical lubrication agent with high lubricating property.
The present invention is achieved through the following technical solutions:
Mechanical lubrication agent with high lubricating property, including 3~7 parts of acetate butyl, 5~10 parts of boric acid, zirconium manganese powder batch mixing 3
~9 parts, 2~7 parts of stearic acid, 4~11 parts of glycerine, 3~13 parts of sodium alkyl sulfate, 2~8 parts of Triton X-100, chlorine
1~9 part of fossil waxes, 5~12 parts of graphite, 5~10 parts of dispersant, stearic acid are 42~58 parts, 22~32 parts of base oil, hydroxide
Sodium is 3~7 parts, and borax is 0.5~1 part, and natrium nitrosum is 0.5~1 part, and odium stearate is 0.5~1 part.
Further, there is the mechanical lubrication agent of high lubricating property, including 3 parts of acetate butyl, 5 parts of boric acid, zirconium manganese powder mix
3 parts of material, 2 parts of stearic acid, 4 parts of glycerine, 3 parts of sodium alkyl sulfate, 2 parts of Triton X-100,1 part of chlorinated paraffin, stone
5 parts of ink, 5 parts of dispersant, stearic acid are 42 parts, 22 parts of base oil, and sodium hydroxide is 3 parts, and borax is 0.5 part, and natrium nitrosum is
0.5 part, odium stearate is 0.5 part.
Further, there is the mechanical lubrication agent of high lubricating property, including 7 parts of acetate butyl, 10 parts of boric acid, zirconium manganese powder mix
9 parts of material, 7 parts of stearic acid, 11 parts of glycerine, 13 parts of sodium alkyl sulfate, 8 parts of Triton X-100,9 parts of chlorinated paraffin, stone
12 parts of ink, 10 parts of dispersant, stearic acid are 58 parts, 32 parts of base oil, and sodium hydroxide is 7 parts, and borax is 1 part, natrium nitrosum 1
Part, odium stearate is 1 part.
Further, there is the mechanical lubrication agent of high lubricating property, including 5 parts of acetate butyl, 5 parts of boric acid, zirconium manganese powder mix
6 parts of material, 7 parts of stearic acid, 5 parts of glycerine, 6 parts of sodium alkyl sulfate, 6 parts of Triton X-100,6 parts of chlorinated paraffin, stone
6 parts of ink, 8 parts of dispersant, stearic acid are 50 parts, 25 parts of base oil, and sodium hydroxide is 5 parts, and borax is 0.8 part, and natrium nitrosum is
0.8 part, odium stearate is 0.8 part.
The present invention compared with prior art, has the following advantages and advantages:The present invention is made with stearic acid, base oil
For solvent, using sodium hydroxide, borax, natrium nitrosum, odium stearate as additive, the lubricant of formation is inexpensive, pollution-free.
Embodiment
For the object, technical solutions and advantages of the present invention are more clearly understood, with reference to embodiment, the present invention is made
Further to describe in detail, exemplary embodiment of the invention and its explanation are only used for explaining the present invention, are not intended as to this
The restriction of invention.
Embodiment 1
Mechanical lubrication agent with high lubricating property, including 3~7 parts of acetate butyl, 5~10 parts of boric acid, zirconium manganese powder batch mixing 3
~9 parts, 2~7 parts of stearic acid, 4~11 parts of glycerine, 3~13 parts of sodium alkyl sulfate, 2~8 parts of Triton X-100, chlorine
1~9 part of fossil waxes, 5~12 parts of graphite, 5~10 parts of dispersant, stearic acid are 42~58 parts, 22~32 parts of base oil, hydroxide
Sodium is 3~7 parts, and borax is 0.5~1 part, and natrium nitrosum is 0.5~1 part, and odium stearate is 0.5~1 part.
Embodiment 2
Mechanical lubrication agent with high lubricating property, including 3 parts of acetate butyl, 5 parts of boric acid, 3 parts of zirconium manganese powder batch mixing, tristearin
2 parts of acid, 4 parts of glycerine, 3 parts of sodium alkyl sulfate, 2 parts of Triton X-100,1 part of chlorinated paraffin, 5 parts of graphite, dispersant 5
Part, stearic acid are 42 parts, 22 parts of base oil, and sodium hydroxide is 3 parts, and borax is 0.5 part, and natrium nitrosum is 0.5 part, odium stearate
For 0.5 part.
Embodiment 3
Mechanical lubrication agent with high lubricating property, including it is 7 parts of acetate butyl, 10 parts of boric acid, 9 parts of zirconium manganese powder batch mixing, hard
7 parts of resin acid, 11 parts of glycerine, 13 parts of sodium alkyl sulfate, 8 parts of Triton X-100,9 parts of chlorinated paraffin, graphite 12 part, point
10 parts of powder, stearic acid are 58 parts, 32 parts of base oil, and sodium hydroxide is 7 parts, and borax is 1 part, and natrium nitrosum is 1 part, stearic acid
Sodium is 1 part.
Embodiment 4
Mechanical lubrication agent with high lubricating property, including 5 parts of acetate butyl, 5 parts of boric acid, 6 parts of zirconium manganese powder batch mixing, tristearin
7 parts of acid, 5 parts of glycerine, 6 parts of sodium alkyl sulfate, 6 parts of Triton X-100,6 parts of chlorinated paraffin, 6 parts of graphite, dispersant 8
Part, stearic acid are 50 parts, 25 parts of base oil, and sodium hydroxide is 5 parts, and borax is 0.8 part, and natrium nitrosum is 0.8 part, odium stearate
For 0.8 part.
Above-described embodiment, the purpose of the present invention, technical scheme and beneficial effect are carried out further
Describe in detail, should be understood that the embodiment that the foregoing is only the present invention, be not intended to limit the present invention
Protection domain, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc., all should include
Within protection scope of the present invention.
Claims (4)
1. the mechanical lubrication agent with high lubricating property, it is characterised in that including 3~7 parts of acetate butyl, 5~10 parts of boric acid, zirconium
3~9 parts of manganese powder batch mixing, 2~7 parts of stearic acid, 4~11 parts of glycerine, 3~13 parts of sodium alkyl sulfate, Triton X-100 2
~8 parts, 1~9 part of chlorinated paraffin, 5~12 parts of graphite, 5~10 parts of dispersant, stearic acid be 42~58 parts, base oil 22~32
Part, sodium hydroxide is 3~7 parts, and borax is 0.5~1 part, and natrium nitrosum is 0.5~1 part, and odium stearate is 0.5~1 part.
2. the mechanical lubrication agent according to claim 1 with high lubricating property, it is characterised in that including acetate butyl 3
Part, 5 parts of boric acid, 3 parts of zirconium manganese powder batch mixing, 2 parts of stearic acid, 4 parts of glycerine, 3 parts of sodium alkyl sulfate, Triton X-100 2
Part, 1 part of chlorinated paraffin, 5 parts of graphite, 5 parts of dispersant, stearic acid are 42 parts, and 22 parts of base oil, sodium hydroxide is 3 parts, and borax is
0.5 part, natrium nitrosum is 0.5 part, and odium stearate is 0.5 part.
3. the mechanical lubrication agent according to claim 1 with high lubricating property, it is characterised in that including acetate butyl 7
Part, 10 parts of boric acid, 9 parts of zirconium manganese powder batch mixing, 7 parts of stearic acid, 11 parts of glycerine, 13 parts of sodium alkyl sulfate, polyethylene glycol octyl phenyl
8 parts of ether, 9 parts of chlorinated paraffin, 12 parts of graphite, 10 parts of dispersant, stearic acid are 58 parts, 32 parts of base oil, and sodium hydroxide is 7 parts,
Borax is 1 part, and natrium nitrosum is 1 part, and odium stearate is 1 part.
4. the mechanical lubrication agent according to claim 1 with high lubricating property, it is characterised in that including acetate butyl 5
Part, 5 parts of boric acid, 6 parts of zirconium manganese powder batch mixing, 7 parts of stearic acid, 5 parts of glycerine, 6 parts of sodium alkyl sulfate, Triton X-100 6
Part, 6 parts of chlorinated paraffin, 6 parts of graphite, 8 parts of dispersant, stearic acid are 50 parts, and 25 parts of base oil, sodium hydroxide is 5 parts, and borax is
0.8 part, natrium nitrosum is 0.8 part, and odium stearate is 0.8 part.