CN104312467A - 一种cnt热效快速反应粘接型自粘防水卷材 - Google Patents
一种cnt热效快速反应粘接型自粘防水卷材 Download PDFInfo
- Publication number
- CN104312467A CN104312467A CN201410587746.7A CN201410587746A CN104312467A CN 104312467 A CN104312467 A CN 104312467A CN 201410587746 A CN201410587746 A CN 201410587746A CN 104312467 A CN104312467 A CN 104312467A
- Authority
- CN
- China
- Prior art keywords
- adhesive waterproof
- rapid reaction
- adhesion type
- effect rapid
- coiled material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及建筑防水技术领域,具体涉及一种CNT热效快速反应粘接型自粘防水卷材,它采用如下的技术方案:步骤一:取100#沥青60-80%、SBR20-22%、橡胶粉末8-12%、萜烯树脂3-5%、表面活性剂2-4.5%、高效热活催化剂4.3-5.8%、填充料8-15%备用;步骤二:将上述的100#沥青、SBR、橡胶粉末、萜烯树脂氧化改性得预混合物;步骤三:在预混合物内按步骤一中的比例添加高效热活催化剂和填充料,形成物料混合物;步骤四:将物料混合物研磨,形成半成品混合物料;它具有能快速反应,牢靠粘接的强度、不受气温变化影响,增加厚度,兼具SBS和自粘、反应粘特性等优点。
Description
【技术领域】
本发明涉及建筑防水技术领域,具体涉及一种CNT热效快速反应粘接型自粘防水卷材。
【背景技术】
现有广西金雨伞CPS反应粘通过与水泥发生物理交联反应技术,但原有技术反应时效很长,需时72小时,而且在气温变化大时,很容易被剥离,在施工过程中发现并没有达到反应设计要求,在多次样板制作对比中CPS反应发生失败,现行技术均为无胎体自粘。本发明含括PY类,是反应粘的技术突破。本设计原理源自生活,将热沥青铺洒在水泥基面上时,沥青瞬间与水泥基面反应,沥青与水泥间不可能存在剥离情况,且与水泥粘接强度牢靠,不论气温怎么变化,经过热效反应后,是不会剥离,从而达到彻底解决满粘问题。
【发明内容】
本发明的目的在于针对现有技术的缺陷和不足,提供一种结构简单,设计合理、使用方便的一种CNT热效快速反应粘接型自粘防水卷材,它具有能快速反应,牢靠粘接的强度、不受气温变化影响,增加厚度,兼具SBS和自粘、反应粘特性等优点。
本发明所述的一种CNT热效快速反应粘接型自粘防水卷材,它采用如下的技术方案:
步骤一:取100#沥青60-80%、SBR20-22%、橡胶粉末8-12%、萜烯树脂3-5%、表面活性剂2-4.5%、高效热活催化剂4.3-5.8%、填充料8-15%备用;
步骤二:将上述的100#沥青、SBR、橡胶粉末、萜烯树脂氧化改性得预混合物;
步骤三:在预混合物内按步骤一中的比例添加高效热活催化剂和填充料,形成物料混合物;
步骤四:将物料混合物研磨,形成半成品混合物料;
步骤五:在半成品混合物料中添加表面活性剂搅拌均匀出料,形成成品混料合物料;
步骤六:按自粘卷材生产或SBS生产办法实施,形成产成品自粘防水卷材。
较优的,所述高效热活催化剂为试剂型GaO生石灰粉末。
采用上述结构后,本发明有益效果为:本发明所述的一种CNT热效快速反应粘接型自粘防水卷材,它具有能快速反应,牢靠粘接的强度、不受气温变化影响,增加厚度,兼具SBS和自粘、反应粘特性等优点。
【具体实施方式】
下面就具体实施例来详细说明本发明,其中的示意性实施例以及说明仅用来解释本发明,但并不作为对本发明的限定。
本具体实施方式所述的一种CNT热效快速反应粘接型自粘防水卷材,它采用如下的技术方案:
步骤一:取100#沥青60-80%、SBR20-22%、橡胶粉末8-12%、萜烯树脂3-5%、表面活性剂2-4.5%、高效热活催化剂4.3-5.8%、填充料8-15%备用;
步骤二:将上述的100#沥青、SBR、橡胶粉末、萜烯树脂氧化改性得预混合物;
步骤三:在预混合物内按步骤一中的比例添加高效热活催化剂和填充料,形成物料混合物;
步骤四:将物料混合物研磨,形成半成品混合物料;
步骤五:在半成品混合物料中添加表面活性剂搅拌均匀出料,形成成品混料合物料;
步骤六:按自粘卷材生产或SBS生产办法实施,形成产成品自粘防水卷材。
较优的,所述高效热活催化剂为试剂型GaO生石灰粉末。
本发明中,分为两个类型:其一是外敷型,其二是内聚型;
外敷型技术方案如下:外敷型反应粘***配套专用粘接砂浆,达到时效需4h,在原有改性沥青胶膜层物理交联反应技术基础上,通过专用砂浆与水化合放出大量的热催化湿铺达到满粘快速反应的目的。专用砂浆是缓凝型高标号水泥制品。
内聚型技术方案如下:内聚型反应粘***配套普通325水泥,达到时效需时36h,牢靠粘接不受气温变化,在原有改性沥青胶膜层物理交联反应技术基础上,在自粘胶膜层添加高效热活催化剂,达到快速反应的目的。其中,高效热活催化剂:试剂型GaO生石灰粉末。
本发明具有如下特点:
1)、兼具SBS和自粘、反应粘特性,较之前技术,厚度增加了:3mm、4mm,PY类,技术指标符合GB18242-2008和GB23441-2009。
2)、彻底解决防水施工窜水引发的渗漏问题,特别是长期以来由于窜水造成的地下室、车库渗漏,大家几乎都应该经历过注浆、堵漏维修,治表不治本。
3)、解决了反应粘卷材长期由于厚度薄、可溶物含量低、拉伸强度低引发的耐久性差所造成的困扰。
4)、反应型和快速反应型2种,反应型达到效果需时36h,快速反应型达到效果需时3h立等。
5)、经济成本等同于平时的SBS改性沥青防水卷材,提高了产品的可操作性、市场推广性。
本发明所述的一种CNT热效快速反应粘接型自粘防水卷材,它具有能快速反应,牢靠粘接的强度、不受气温变化影响,增加厚度,兼具SBS和自粘、反应粘特性等优点。
以上所述仅是本发明的较佳实施方式,故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰,均包括于本发明专利申请范围内。
Claims (2)
1.一种CNT热效快速反应粘接型自粘防水卷材,其特征在于:它采用如下的技术方案:
步骤一:取100#沥青60-80%、SBR20-22%、橡胶粉末8-12%、萜烯树脂3-5%、表面活性剂2-4.5%、高效热活催化剂4.3-5.8%、填充料8-15%备用;
步骤二:将上述的100#沥青、SBR、橡胶粉末、萜烯树脂氧化改性得预混合物;
步骤三:在预混合物内按步骤一中的比例添加高效热活催化剂和填充料,形成物料混合物;
步骤四:将物料混合物研磨,形成半成品混合物料;
步骤五:在半成品混合物料中添加表面活性剂搅拌均匀出料,形成成品混料合物料;
步骤六:按自粘卷材生产或SBS生产办法实施,形成产成品自粘防水卷材。
2.根据权利要求1所述的一种CNT热效快速反应粘接型自粘防水卷材,其特征在于:所述高效热活催化剂为试剂型GaO生石灰粉末。