CN104312154A - 一种耐低温硅橡胶料及其制备方法 - Google Patents
一种耐低温硅橡胶料及其制备方法 Download PDFInfo
- Publication number
- CN104312154A CN104312154A CN201410481926.7A CN201410481926A CN104312154A CN 104312154 A CN104312154 A CN 104312154A CN 201410481926 A CN201410481926 A CN 201410481926A CN 104312154 A CN104312154 A CN 104312154A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicone rubber
- silicon rubber
- low temperature
- rubber material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐低温硅橡胶料及其制备方法。其由以下重量份的原料制成:低苯基硅橡胶90-110、二乙基硅橡胶40-60、三聚氰酸三烯丙酯5-10、三缩四乙二醇3-6、黄泥粉10-15、端羟基聚丁二烯5-10、二丁基二氯化锡2-3、聚碳化二亚胺1.5-2.5、三羟甲基丙烷椰油酸酯3-5、聚醚环氧共改性硅油4-8、芥酸酰胺2.5-4.5、尼龙酸二异丁酯5-10、三甘醇二异辛酸酯10-15、碱式硫酸镁晶须12-16、4,4-二苯乙烯化二苯胺2-3、二硫化四甲基秋兰姆1-2、助剂3.5-4.5。本发明硅橡胶料产品性能稳定,具有优异的耐低温性能,可以在严寒条件下长期工作,仍能保持较高的拉伸强度、撕裂强度和断裂伸长率,并具有良好的耐老化性、抗疲劳性、耐油性等性能,完全满足我国北方严寒地区的使用要求,应用前景广阔。
Description
技术领域
本发明涉及一种耐低温硅橡胶料及其制备方法,属于硅橡胶技术领域。
背景技术
硅橡胶是以聚硅烷为主链的高分子材料,由于主链硅氧链段的非极性和弱的分子间相互作用,具有良好的热稳定性、耐候性、耐老化性和电气性能,在很宽的温度内(-50~120℃)其力学性能相当稳定,在航天航空、电子电气工业等领域中得到广泛的应用。随着科学技术的发展,对硅橡胶的耐低温性能也提出了更高的要求,然而现有市场上的硅橡胶耐低温性能已无法满足特殊领域的需求。因此,需要对硅橡胶进行改性,以获得耐低温性能优异的硅橡胶料。
发明内容
本发明目的在于提供一种耐低温硅橡胶料及其制备方法,本发明提供的硅橡胶混炼胶具有很高的强度性能,较低的压缩永久变形,较好的力学性能。
为实现上述目的,本发明采用如下技术方案:
一种耐低温硅橡胶料,由以下重量份的原料制成:低苯基硅橡胶90-110、二乙基硅橡胶40-60、三聚氰酸三烯丙酯 5-10、三缩四乙二醇3-6、黄泥粉10-15、端羟基聚丁二烯5-10、二丁基二氯化锡2-3、聚碳化二亚胺1.5-2.5、三羟甲基丙烷椰油酸酯3-5、聚醚环氧共改性硅油4-8、芥酸酰胺2.5-4.5、尼龙酸二异丁酯5-10、三甘醇二异辛酸酯10-15、碱式硫酸镁晶须12-16、4,4-二苯乙烯化二苯胺2-3、二硫化四甲基秋兰姆1-2、助剂3.5-4.5;
所述助剂的制备方法如下:a、取以下重量份的原料:松香季戊四醇酯3-7、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯 2-5、氟化锆5-10、硫代磷酸三苯基异氰酸酯2-4、4 ,4′- 联苯二酚1-2、三异丙醇胺环硼酸酯3-5、2,2-二噻吩基乙醇酸甲酯2-3、骨胶粉4-8、碳化钨6-12、癸基十四醇鲸蜡硬脂酸酯2.5-4.5、2-(4-吗啉基二硫代)苯并噻唑 2-3;b、将氟化锆、碳化钨、骨胶粉、松香季戊四醇酯、癸基十四醇鲸蜡硬脂酸酯、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯加入高速搅拌机内,3000-4000rpm高速搅拌3-6min,然后加入余下原料,1000-1500rpm高速搅拌4-8min,即可。
本发明的耐低温硅橡胶料的制备方法,包括以下步骤:按配方配比将低苯基硅橡胶、二乙基硅橡胶、端羟基聚丁二烯、三甘醇二异辛酸酯、碱式硫酸镁晶须、芥酸酰胺一同投入到捏合机中,在75-85℃下混炼0.5-1h,加入尼龙酸二异丁酯、聚醚环氧共改性硅油、三羟甲基丙烷椰油酸酯、三聚氰酸三烯丙酯、黄泥粉、三缩四乙二醇,升温至80-100℃,混炼25-35min,再加入余下原料,升温至170-190℃,抽真空,真空度控制在0.08-0.10MPa,混炼15-20min,降温至60℃以下出胶;然后将胶料在开放式炼胶机上薄通4-6次,下片,停放24h以上;最后将胶料置于平板硫化机上进行硫化,硫化温度为150-170℃,硫化压力为15-20MPa,硫化时间为10-15min,即可得到本发明硅橡胶料。
本发明的有益效果:
本发明硅橡胶料产品性能稳定,具有优异的耐低温性能,可以在严寒条件下长期工作,仍能保持较高的拉伸强度、撕裂强度和断裂伸长率,并具有良好的耐老化性、抗疲劳性、耐油性等性能,完全满足我国北方严寒地区的使用要求,应用前景广阔。
具体实施方式
一种耐低温硅橡胶料,由以下重量(kg)的原料制成:低苯基硅橡胶100、二乙基硅橡胶50、三聚氰酸三烯丙酯 8、三缩四乙二醇4、黄泥粉12、端羟基聚丁二烯8、二丁基二氯化锡2.5、聚碳化二亚胺2、三羟甲基丙烷椰油酸酯4、聚醚环氧共改性硅油6、芥酸酰胺3.5、尼龙酸二异丁酯8、三甘醇二异辛酸酯12、碱式硫酸镁晶须14、4,4-二苯乙烯化二苯胺2.5、二硫化四甲基秋兰姆1.5、助剂4;
所述助剂的制备方法如下:a、取以下重量(kg)的原料:松香季戊四醇酯5、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯 3、氟化锆8、硫代磷酸三苯基异氰酸酯3、4 ,4′- 联苯二酚1.5、三异丙醇胺环硼酸酯4、2,2-二噻吩基乙醇酸甲酯2.5、骨胶粉6、碳化钨8、癸基十四醇鲸蜡硬脂酸酯3.5、2-(4-吗啉基二硫代)苯并噻唑 3;b、将氟化锆、碳化钨、骨胶粉、松香季戊四醇酯、癸基十四醇鲸蜡硬脂酸酯、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯加入高速搅拌机内,3500rpm高速搅拌4min,然后加入余下原料,1500rpm高速搅拌6min,即可。
耐低温硅橡胶料的制备方法,包括以下步骤:按配方配比将低苯基硅橡胶、二乙基硅橡胶、端羟基聚丁二烯、三甘醇二异辛酸酯、碱式硫酸镁晶须、芥酸酰胺一同投入到捏合机中,在80℃下混炼1h,加入尼龙酸二异丁酯、聚醚环氧共改性硅油、三羟甲基丙烷椰油酸酯、三聚氰酸三烯丙酯、黄泥粉、三缩四乙二醇,升温至90℃,混炼30min,再加入余下原料,升温至180℃,抽真空,真空度控制在0.09MPa,混炼18min,降温至60℃以下出胶;然后将胶料在开放式炼胶机上薄通5次,下片,停放24h以上;最后将胶料置于平板硫化机上进行硫化,硫化温度为160℃,硫化压力为18MPa,硫化时间为10min,即可得到本发明硅橡胶料。
上述实施例制得的耐低温硅橡胶料的性能测试结果如下表所示:
表1 耐低温硅橡胶料的性能测试结果
Claims (2)
1.一种耐低温硅橡胶料,其特征在于,由以下重量份的原料制成:低苯基硅橡胶90-110、二乙基硅橡胶40-60、三聚氰酸三烯丙酯 5-10、三缩四乙二醇3-6、黄泥粉10-15、端羟基聚丁二烯5-10、二丁基二氯化锡2-3、聚碳化二亚胺1.5-2.5、三羟甲基丙烷椰油酸酯3-5、聚醚环氧共改性硅油4-8、芥酸酰胺2.5-4.5、尼龙酸二异丁酯5-10、三甘醇二异辛酸酯10-15、碱式硫酸镁晶须12-16、4,4-二苯乙烯化二苯胺2-3、二硫化四甲基秋兰姆1-2、助剂3.5-4.5;
所述助剂的制备方法如下:a、取以下重量份的原料:松香季戊四醇酯3-7、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯 2-5、氟化锆5-10、硫代磷酸三苯基异氰酸酯2-4、4 ,4′- 联苯二酚1-2、三异丙醇胺环硼酸酯3-5、2,2-二噻吩基乙醇酸甲酯2-3、骨胶粉4-8、碳化钨6-12、癸基十四醇鲸蜡硬脂酸酯2.5-4.5、2-(4-吗啉基二硫代)苯并噻唑 2-3;b、将氟化锆、碳化钨、骨胶粉、松香季戊四醇酯、癸基十四醇鲸蜡硬脂酸酯、4,5-环氧环己烷-1,2-二甲酸二缩水甘油酯加入高速搅拌机内,3000-4000rpm高速搅拌3-6min,然后加入余下原料,1000-1500rpm高速搅拌4-8min,即可。
2.一种如权利要求1所述的耐低温硅橡胶料的制备方法,其特征在于包括以下步骤:按配方配比将低苯基硅橡胶、二乙基硅橡胶、端羟基聚丁二烯、三甘醇二异辛酸酯、碱式硫酸镁晶须、芥酸酰胺一同投入到捏合机中,在75-85℃下混炼0.5-1h,加入尼龙酸二异丁酯、聚醚环氧共改性硅油、三羟甲基丙烷椰油酸酯、三聚氰酸三烯丙酯、黄泥粉、三缩四乙二醇,升温至80-100℃,混炼25-35min,再加入余下原料,升温至170-190℃,抽真空,真空度控制在0.08-0.10MPa,混炼15-20min,降温至60℃以下出胶;然后将胶料在开放式炼胶机上薄通4-6次,下片,停放24h以上;最后将胶料置于平板硫化机上进行硫化,硫化温度为150-170℃,硫化压力为15-20MPa,硫化时间为10-15min,即可得到本发明硅橡胶料。