CN104292442B - 吸湿导电聚酯纤维切片及其制备方法 - Google Patents
吸湿导电聚酯纤维切片及其制备方法 Download PDFInfo
- Publication number
- CN104292442B CN104292442B CN201410484974.1A CN201410484974A CN104292442B CN 104292442 B CN104292442 B CN 104292442B CN 201410484974 A CN201410484974 A CN 201410484974A CN 104292442 B CN104292442 B CN 104292442B
- Authority
- CN
- China
- Prior art keywords
- antioxidant
- moisture absorption
- polyester fibre
- conductive polyester
- fibre section
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及纤维改性领域,尤其涉及一种吸湿导电聚酯纤维切片,它由PTA、EG、炭黑、聚甘油、催化剂乙二醇锑和抗氧化剂组成,其制备方法为:(1)按照质量比称取配方量的PTA和?EG加入到聚合反应釜内,启动搅拌在0.2MPa压力下升温至260°C进行酯化反应,待出水量达到理论出水量的95%以上时,加入配方量的炭黑、抗氧化剂和聚甘油,在真空度为250Pa、温度为265°C条件下缩聚0.5h,逐步转入真空度为60Pa,温度升至280°C缩聚反应3h;(2)当熔体特性粘度在0.624dl/g时出料、冷却、切粒、干燥,即得所述的吸湿导电聚酯纤维切片。该吸湿导电聚酯纤维切片电阻率有了较大的提高。将切片熔融纺丝进行吸湿率测定,吸湿率为5.2%,常规PET纤维最高吸湿率为0.5%。
Description
技术领域
本发明涉及纤维改性领域,尤其涉及一种吸湿导电聚酯纤维切片及其制备方法。
背景技术
PET纤维自1941年由英国Whinfield和Dickson首次合成以来,由于其具有强度高、弹性好、耐热性好、耐光、耐磨和耐腐蚀等优异性能,得到了迅速发展,已成为最主要的聚酯纤维品种。然而PET纤维电阻大、导电率小、含水率低、透气性差、染色性差、易起球起毛、易沾污等缺点已不能满足人们对衣物日益增加的多功能需求。
近年来,功能性PET纤维已称为人们研究的重点,如阻燃、导电、吸湿、抗起球等新型改性聚酯纤维得到开发和应用,改性手段如共聚、共混、表面接枝、填充、结晶改性及玻璃纤维增强改性等手段也不断得到运用。目前,已有报道的制备吸湿导电聚酯纤维的方法很多,基本上可以分为类:一类是物理改性:如改变喷丝板微孔形状或对纤维进行特殊处理,纺制得到表面具有沟槽的异形纤维,利用纤维表面沟槽产生的毛细现象,使汗水得到扩散和芯吸。此种方法的缺点是喷丝板设计比较麻烦,且纺丝工艺条件要求较高。也有利用双组分复合共纺的方法,将亲水材料作为共纺复合纤维的芯层,将具有异形截面的常规聚酯作为复合共纺纤维的皮层,制得吸湿排汗纤维,但此种方法成本高、操作麻烦。也有采用共混的方法,将另一类是化学改性,在聚酯高分子链上引入亲水基团,提高聚酯纤维的吸湿排汗性能。此种方法虽然可以获得永久的亲水性聚酯纤维,但生产工艺复杂,操作麻烦,且成本较高。还有用亲水性高分子物质对聚酯纤维进行表面覆盖,此法由于操作复杂,生产条件控制严格,难以实现工业化大规模生产。
本发明采用嵌段共聚的方法将具有亲水性的聚甘油引入到PET分子链上,并加入炭黑导电粉,制得了具有良好导电性、吸湿性的PET切片,此法操作简单,成本低,适合工业化大规模生产。
发明内容
本发明的主要目的在于提出一种添加量少、成本较低、制备方法简单、不影响PET纤维固有物理性能的导电吸湿聚酯纤维切片及其制备方法。
本发明解决其技术问题所采用的技术方案是:一种导电吸湿聚脂纤维切片,它由PTA、EG、炭黑、聚甘油、催化剂乙二醇锑和抗氧化剂组成,其中PTA与EG的质量比为:60~65:35~40;其余辅料添加量按与PTA质量比:炭黑1~5%,聚甘油2~10%,催化剂乙二醇锑0.1%~0.2%,抗氧化剂0.05%~0.2%。
所述的炭黑为超导电炭黑,其粒径在15~25nm,pH值7~8,比表面积200~400m2/g,吸碘值650~750g/kg,加热减量≤0.5%。
所述的抗氧化剂为抗氧化剂1076与抗氧化剂168的混合物,二者按质量百分数配比为:45%~60%抗氧化剂1076,40~55%抗氧化剂168。
上述的制备方法包括以下步骤:
(1)按照质量比称取配方量的PTA和EG加入到聚合反应釜内,启动搅拌在0.2~0.4MPa压力下升温至260°C~265°C进行酯化反应,待出水量达到理论出水量的95%以上时,加入配方量的炭黑、抗氧化剂和聚甘油,在真空度为250~350Pa、温度为265°C~270°C条件下缩聚0.5h~1h,逐步转入真空度为20~60Pa,温度升至275°C~280°C缩聚反应2.5h~3h;
(2)当熔体特性粘度在0.624±0.003dl/g时出料、冷却、切粒、干燥,即得所述的吸湿导电聚酯纤维切片。
与现有技术相比,本发明的有益效果为:由本发明制备吸湿导电PET纤维切片,制备过程简单,操作方便,成本较低,制得的切片具有良好的导电和吸湿性能。对所得切片进行电阻率测定,与常规PET纤维切片相比,电阻率有了较大的提高,电阻率为8.3×104W/cm左右。将切片熔融纺丝进行吸湿率测定,吸湿率为3.8~5.2%,常规PET纤维最高吸湿率为0.4~0.5%。
具体实施方式
下面结合具体实施例来进一步说明本发明的技术方案。
实施例1:
一种吸湿导电聚酯纤维切片,它由PTA、EG、炭黑、聚甘油、催化剂乙二醇锑和抗氧化剂组成,其中PTA与EG的质量比为:60:40;其余辅料添加量按与PTA质量比:炭黑5%,聚甘油10%,催化剂乙二醇锑0.1%,抗氧化剂0.05%,抗氧化剂由质量比为1:1的抗氧化剂1076和抗氧化剂168混合物。
制备方法:(1)按上述质量比称取一定量的PTA和EG加入到5L聚合反应釜内,启动搅拌在0.2MPa压力下升温至260°C进行酯化反应,待理论出水量达到95%以上时,加入一定质量比的炭黑、抗氧化剂和聚甘油,在真空度为250Pa、温度为270°C条件下缩聚0.5h左右,逐步转入真空度为40Pa,温度升至280°C缩聚反应2.5h左右;
(2)待特性粘度为0.624dl/g时出料、冷却、切粒、干燥,即得所述的吸湿导电聚酯纤维切片。
对所得的聚酯纤维切片进行电阻率测定,结果为8.3×104W/cm,将切片熔融纺丝,测得吸湿率为5.1%。
实施例2:
一种吸湿导电聚酯纤维切片,它由PTA、EG、炭黑、聚甘油、催化剂乙二醇锑和抗氧化剂组成,其中PTA与EG的质量比为:65:35;其余辅料添加量按与PTA质量比:炭黑2%,聚甘油5%,催化剂乙二醇锑0.2%,抗氧化剂0.1%,抗氧化剂由质量比为3:2的抗氧化剂1076和抗氧化剂168混合物。
制备方法:(1)按上述质量比称取一定量的PTA和EG加入到5L聚合反应釜内,启动搅拌在0.4MPa压力下升温至265°C进行酯化反应,待理论出水量达到95%以上时,加入一定质量比的炭黑、抗氧化剂和聚甘油,在真空度为300Pa、温度为265°C条件下缩聚0.5h左右,逐步转入真空度为30Pa,温度升至275°C缩聚反应2.5h左右;
(2)待特性粘度为0.624dl/g时出料、冷却、切粒、干燥,即得所述的吸湿导电聚酯纤维切片。
对所得的聚酯纤维切片进行电阻率测定,电阻率为7.8×104W/cm,将所得切片进行熔融纺丝,测得吸湿率为4.5%。
实施例3:
一种吸湿导电聚酯纤维切片,它由PTA、EG、炭黑、聚甘油、催化剂乙二醇锑和抗氧化剂组成,其中PTA与EG的质量比为:63:37;其余辅料添加量按与PTA质量比:炭黑1%,聚甘油3%,催化剂乙二醇锑0.2%,抗氧化剂0.2%,抗氧化剂由质量比为9:11的抗氧化剂1076和抗氧化剂168混合物。
制备方法:(1)按上述质量比称取一定量的PTA和EG加入到5L聚合反应釜内,启动搅拌在0.3MPa压力下升温至260°C进行酯化反应,待理论出水量达到95%以上时,加入一定质量比的炭黑、抗氧化剂和聚甘油,在真空度为350Pa、温度为265°C条件下缩聚0.5h左右,逐步转入真空度为35Pa,温度升至275°C缩聚反应2.5h左右;
(2)待特性粘度为0.624dl/g时出料、冷却、切粒、干燥,即得所述的吸湿导电聚酯纤维切片。
对所得的聚酯纤维切片进行电阻率测定,电阻率为7.2×104W/cm,将切片进行熔融纺丝,测得吸湿率为3.8%。
Claims (4)
1.一种吸湿导电聚酯纤维切片,其特征在于,它由PTA、EG、炭黑、聚甘油、催化剂乙二醇锑和抗氧化剂组成,其中PTA与EG的质量比为:60%~65%:35%~40%;其余辅料添加量按与PTA质量比:炭黑1~5%,聚甘油2~10%,催化剂乙二醇锑0.1%~0.2%,抗氧化剂0.05%~0.2%;吸湿导电聚酯纤维切片的制备方法为:包括以下步骤:
(1)按照质量比称取配方量的PTA和EG加入到聚合反应釜内,启动搅拌在0.2~0.4MPa压力下升温至260℃~265℃进行酯化反应,待出水量达到理论出水量的95%以上时,加入配方量的炭黑、抗氧化剂和聚甘油,在真空度为250~350Pa、温度为265℃~270℃条件下缩聚0.5h~1h,逐步转入真空度为20~60Pa,温度升至275℃~280℃缩聚反应2.5h~3h;
(2)当熔体特性粘度在0.624±0.003dl/g时出料、冷却、切粒、干燥,即得所述的吸湿导电聚酯纤维切片。
2.根据权利要求1所述的吸湿导电聚酯纤维切片,其特征在于,所述的炭黑的粒径在15~25nm,pH值7~8,比表面积200~400m2/g,吸碘值650~750g/kg,加热减量≤0.5%。
3.根据权利要求1所述的吸湿导电聚酯纤维切片,其特征在于,所述的抗氧化剂为抗氧化剂1076与抗氧化剂168的混合物,二者按质量百分数配比为:45%~60%的抗氧化剂1076,40%~55%抗氧化剂168。
4.一种如权利要求1所述的吸湿导电聚酯纤维切片的制备方法,其特征在于,所述的制备方法包括以下步骤:
(1)按照质量比称取配方量的PTA和EG加入到聚合反应釜内,启动搅拌在0.2~0.4MPa压力下升温至260℃~265℃进行酯化反应,待出水量达到理论出水量的95%以上时,加入配方量的炭黑、抗氧化剂和聚甘油,在真空度为250~350Pa、温度为265℃~270℃条件下缩聚0.5h~1h,逐步转入真空度为20~60Pa,温度升至275℃~280℃缩聚反应2.5h~3h;
(2)当熔体特性粘度在0.624±0.003dl/g时出料、冷却、切粒、干燥,即得所述的吸湿导电聚酯纤维切片。