CN104262830A - 环保pvc塑料胶粒配方 - Google Patents
环保pvc塑料胶粒配方 Download PDFInfo
- Publication number
- CN104262830A CN104262830A CN201410458082.4A CN201410458082A CN104262830A CN 104262830 A CN104262830 A CN 104262830A CN 201410458082 A CN201410458082 A CN 201410458082A CN 104262830 A CN104262830 A CN 104262830A
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly pvc
- agent
- parts
- pvc plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保PVC塑料胶粒配方,其包括以下重量份的成分:稳定剂1-2.2份、润滑剂0.2-0.4份、发泡剂0.1-0.3份、抗静电剂2-5份、树脂粉30-45份、纳米钙5-11份、活性钙6-18份、钛白粉0.4-0.8份、增塑剂30-40份。本发明价格便宜、成品率高、性能优良、粘性较好。
Description
技术领域
本发明涉及一种环保PVC塑料胶粒配方。
背景技术
PVC(聚氯乙烯)由氯乙烯在引发剂的作用下聚合而成的热塑性树脂,是氯乙的均聚物,氯乙烯均聚物和氯乙烯共聚物统称为氯乙烯树脂。PVC具有较好的机械性能,抗张强度60mpa左右,冲击强度5-10kj/m2,有优异的介电性能,但对光和热的稳定性差,在100℃以上或经长时间阳光暴晒就会分解而产生氯化氢,并进一步自动催化分解引起变色,物理性能也迅速下降。在实际应用中必须加入稳定剂以提高对热和光的稳定性。在具体应用方面,按照PVC产品的主要性状可分为硬质PVC和软质PVC,其中硬质PVC主要应用在管材、型材等建筑材料方面,而软质PVC主要应用在电缆、软管、电器等方面。我国PVC塑料胶粒的混合工艺已经比较成熟,特别是使用开放式炼胶机作为主要设备的混合工艺已相当完善,一般性能的PVC塑料胶粒配方亦基本成熟。随着人类环境保护意识的提高和对自身健康的关注,许多国家和组织纷纷制定严格的标准和法规,限制有害物质在各类产品上的使用。
发明内容
本发明目的是:提供一种价格便宜、成品率高、性能优良、符合客户不同要求且环保、防静电的环保PVC塑料胶粒配方。
本发明的一技术方案是:一种环保PVC塑料胶粒配方,其至少包括以下重量份的成分:稳定剂1-2.2份、润滑剂0.2-0.4份、发泡剂0.1-0.3份、抗静电剂2-5份、树脂粉30-45份、纳米钙5-11份、活性钙6-18份、钛白粉0.4-0.8份、增塑剂30-40份。
优选地,所述树脂粉的份数大于增塑剂的份数。
优选地,其进一步包括增白剂,且增白剂的份数是稳定剂的份数0.01倍。
本发明的另一技术方案是:一种环保PVC塑料胶粒配方的制备方法,先将稳定剂、润滑剂、发泡剂、抗静电剂、树脂粉、纳米钙、活性钙、增白剂、钛白粉、增塑剂按照上述技术方案进行配比之后再加入高速搅拌机內搅拌,然后通过弹簧加料机加入双螺旋杆挤出机內挤出造粒。
优选地,所述造粒所测的导电系数为10的8次方欧姆。
本发明优点是:
本发明的有益效果是:价格便宜、成品率高、性能优良、粘性较好。
具体实施方式
实施例:本发明提供了一种热塑性弹性体塑料配方的具体实施例,其包括以下重量份的成分:稳定剂1-2.2份、润滑剂0.2-0.4份、发泡剂0.1-0.3份、抗静电剂2-5份、树脂粉30-45份、纳米钙5-11份、活性钙6-18份、钛白粉0.4-0.8份、增塑剂30-40份。
稳定剂优选采用16A稳定剂,润滑剂采用ST润滑剂,以增加产品的流动性和润滑性,树脂粉为塑料胶粒的基础材料,本发明优选S-65型树脂粉作为基础树脂粉,增塑剂可以控制PVC软硬度,增加光泽,发泡剂的加入是为了改变产品的特性,如增加弹性、降低密度等,抗静电剂采用M-308可以有效控制产品的导电性,为了改善产品的光泽还加入了增白剂。
优选地,本发明先将2.6公斤稳定剂1-2.2份、0.6公斤润滑剂0.2-0.4份、0.25公斤发泡剂、5公斤抗静电剂、50公斤树脂粉、10公斤纳米钙、15公斤活性钙、0.035公斤增白剂、1.1公斤钛白粉、45公斤增塑剂加入高速搅拌机內搅拌,然后通过弹簧加料机加入双螺旋杆挤出机內挤出造粒。
由此在恒温条件下经导电测量仪所测的导电系数为10的8次方欧姆。
本发明的有益效果是:价格便宜、成品率高、性能优良、粘性较好。
当然上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明主要技术方案的精神实质所做的等效变换或修饰,都应涵盖在本发明的保护范围之内。
Claims (5)
1.一种环保PVC塑料胶粒配方,其特征在于其至少包括以下重量份的成分:稳定剂1-2.2份、润滑剂0.2-0.4份、发泡剂0.1-0.3份、抗静电剂2-5份、树脂粉30-45份、纳米钙5-11份、活性钙6-18份、钛白粉0.4-0.8份、增塑剂30-40份。
2.如权利要求1所述的一种环保PVC塑料胶粒配方,其特征在于:所述树脂粉的份数大于增塑剂的份数。
3.如权利要求1所述的一种环保PVC塑料胶粒配方,其特征在于:其进一步包括增白剂,且增白剂的份数是稳定剂的份数0.01倍。
4.一种采用如权利要求1所述环保PVC塑料胶粒配方的制备方法,其特征在于:先将稳定剂、润滑剂、发泡剂、抗静电剂、树脂粉、纳米钙、活性钙、增白剂、钛白粉、增塑剂加入高速搅拌机內搅拌,然后通过弹簧加料机加入双螺旋杆挤出机內挤出造粒。
5.根据权利要求4所述的制备方法,其特征在于:所述造粒所测的导电系数为10的8次方欧姆。