CN104250090A - 一种发泡保温板及其制作方法 - Google Patents
一种发泡保温板及其制作方法 Download PDFInfo
- Publication number
- CN104250090A CN104250090A CN201310263903.4A CN201310263903A CN104250090A CN 104250090 A CN104250090 A CN 104250090A CN 201310263903 A CN201310263903 A CN 201310263903A CN 104250090 A CN104250090 A CN 104250090A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- insulation board
- foaming insulation
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于在建筑行业使用的发泡保温板,是一种利用工业废渣制作的发泡保温板及其制作方法,其特征在于是由以下按重量份配比的原料制成:矿渣粉、脱硫石膏、粉煤灰份、生石灰、水泥、聚丙烯纤维、双氧水、水玻璃、亚甲基二萘磺酸钠份、减水剂份、防水剂份和水份。按配比将原料放到搅拌机搅拌混合后,浇注到模具中,经固化湿热养护,即得发泡保温板成品本。发泡保温板主要采用了工业废渣,节能环保,产品保温性能好,抗压强度高,生产成本低廉,工艺简单。
Description
技术领域
本发明属于在建筑行业使用的发泡保温板,是一种利用工业废渣制作的发泡保温板及其制作方法。
背景技术
目前使用的聚苯乙烯和聚氨脂等塑料材质的挤塑板和发泡板,尽管轻质保温,但抗压强度低、易燃,严重威胁人民生命财产的安全。以珍珠岩等多孔轻质材料制成的颗粒胶粉砂浆,虽然解决了防火问题,但是吸水率高,容易开裂,保温效果欠佳。发泡水泥保温板轻质隔热效果较好,但大量使用水泥不利于节能环保。
发明内容
本发明的目的是提供一种由矿渣粉、粉煤灰、脱硫石膏、生石灰和外加剂制作的具有轻质高强、防火防水、隔热保温良好性能的发泡保温板及其制作方法。
实现上述的技术方案为:一种发泡保温板,其特征在于是由以下按重量份配比的原料制成:矿渣粉10-50份、脱硫石膏30-40份、粉煤灰10-20份、生石灰2-10份、水泥5-10份、聚丙烯纤维0.1-0.3份、双氧水0.1-0.6份、水玻璃1-10份、亚甲基二萘磺酸钠0.01-0.015份、减水剂0.5-1份、防水剂1-5份和水40-60份。
一种发泡保温板,其最佳方案,是由以下按重量份配比的原料制成:矿渣粉15份、脱硫石膏30份、粉煤灰15份、生石灰5份、水泥6份、聚丙烯纤维0.2份、双氧水0.4份、水玻璃5份、亚甲基二萘磺酸钠0.01份、减水剂0.5份、防水剂5份和水50份。
一种发泡保温板,其特征在于其制作方法是按下列步骤进行:
(1)按配比将矿渣粉、脱硫石膏、粉煤灰、生石灰、水泥、聚丙烯纤维干混备用成混合物A;
(2)按配比将水玻璃、亚甲基二萘磺酸钠、减水剂、防水剂和水搅拌均匀成混合物B;
(3)将混合物A和混合物B放到搅拌机搅拌,然后加入双氧水搅拌混合后,浇注到模具中,经固化湿热养护,即得发泡保温板成品。
使用本发明的有益效果是;发泡保温板主要采用了工业废渣,节能环保,产品保温性能好,抗压强度高,生产成本低廉,工艺简单。
具体实施方式
实施例1:
一种发泡保温板,是由以下按重量份配比的原料制成;矿渣粉40份、脱硫石膏30份、粉煤灰20份、生石灰4份、水泥6份、聚丙烯纤维0.1份、双氧水0.6份、水玻璃5份、亚甲基二萘磺酸钠0.01份、减水剂1份、防水剂3份和水50份。
一种发泡保温板的制作方法按下列步骤进行:
(1)按配比将矿渣粉、脱硫石膏、粉煤灰、生石灰、水泥、聚丙烯纤维干混搅拌成混合物A;
(2)按配比将水玻璃、亚甲基二萘磺酸钠、减水剂、防水剂与水搅拌均匀成混合物B;
(3)将混合物A和混合物B放到搅拌机搅拌,然后加入双氧水搅拌混合后,浇注到模具中,经固化湿热养护,即得发泡保温板成品。
实施例2:
一种发泡保温板,是由以下按重量份组成的原料制成:矿渣粉50份、脱硫石膏40份、粉煤灰20份、生石灰4份、水泥6份、聚丙烯纤维0.1份、双氧水0.6份、水玻璃5份、亚甲基二萘磺酸钠0.01份、减水剂1份、防水剂3份和水50份。
一种发泡保温板的制作方法按下列步骤进行:
(1)按配比将矿渣粉、脱硫石膏、粉煤灰、生石灰、水泥、聚丙烯纤维干混搅拌成混合物A;
(2)按配比将水玻璃、亚甲基二萘磺酸钠、减水剂、防水剂与水搅拌均匀成混合物B;
(3)将混合物A和混合物B放到搅拌机搅拌,然后加入双氧水搅拌混合后,浇注到模具中,经固化湿热养护,即得发泡保温板成品。
实施例3:
一种发泡保温板,是由以下按重量份组成的原料制成:矿渣粉50份、脱硫石膏30份、粉煤灰10份、生石灰4份、水泥6份、聚丙烯纤维0.1份、双氧水0.6份、水玻璃8份、亚甲基二萘磺酸钠0.015份、减水剂0.5份、防水剂2份和水50份。
一种发泡保温板的制作方法按下列步骤进行:
(1)按配比将矿渣粉、脱硫石膏、粉煤灰、生石灰、水泥、聚丙烯纤维干混搅拌成混合物A;
(2)按配比将水玻璃、亚甲基二萘磺酸钠、减水剂、防水剂与水搅拌均匀成混合物B;
(3)将混合物A和混合物B放到搅拌机搅拌,然后加入双氧水搅拌混合后,浇注到模具中,经固化湿热养护,即得发泡保温板成品。
实施例4
一种发泡保温板,是由以下按重量份配比的原料制成:矿渣粉15份、脱硫石膏30份、粉煤灰15份、生石灰5份、水泥6份、聚丙烯纤维0.2份、双氧水0.4份、水玻璃5份、亚甲基二萘磺酸钠0.01份、减水剂0.5份、防水剂5份和水50份。
一种发泡保温板的制作方法按下列步骤进行:
(1)按配比将矿渣粉、脱硫石膏、粉煤灰、生石灰、水泥、聚丙烯纤维干混搅拌成混合物A;
(2)按配比将水玻璃、亚甲基二萘磺酸钠、减水剂、防水剂与水搅拌均匀成混合物B;
(3)将混合物A和混合物B放到搅拌机搅拌,然后加入双氧水搅拌混合后,浇注到模具中,经固化湿热养护,即得发泡保温板成品。
Claims (3)
1.一种发泡保温板,其特征在于是由以下按重量份配比的原料制成:矿渣粉10-50份、脱硫石膏30-40份、粉煤灰10-20份、生石灰2-10份、水泥5-10份、聚丙烯纤维0.1-0.3份、双氧水0.1-0.6份、水玻璃1-10份、亚甲基二萘磺酸钠0.01-0.015份、减水剂0.5-1份、防水剂1-5份和水40-60份。
2.根据权利要求1所述的一种发泡保温板,其特征在于:是由以下按重量份配比的原料制成:矿渣粉15份、脱硫石膏30份、粉煤灰15份、生石灰5份、水泥6份、聚丙烯纤维0.2份、双氧水0.4份、水玻璃5份、亚甲基二萘磺酸钠0.01份、减水剂0.5份、防水剂5份和水50份。
3. 根据权利要求1所述的一种发泡保温板,其特征在于其制作方法是按下列步骤进行:
(1)按配比将矿渣粉、脱硫石膏、粉煤灰、生石灰、水泥、聚丙烯纤维干混备用成混合物A;
(2)按配比将水玻璃、亚甲基二萘磺酸钠、减水剂、防水剂和水搅拌均匀成混合物B;
(3)将混合物A和混合物B放到搅拌机搅拌,然后加入双氧水搅拌混合后,浇注到模具中,经固化湿热养护,即得发泡保温板成品。