CN104231763B - 一种纤维板用防火涂料及其制备方法 - Google Patents
一种纤维板用防火涂料及其制备方法 Download PDFInfo
- Publication number
- CN104231763B CN104231763B CN201410480886.4A CN201410480886A CN104231763B CN 104231763 B CN104231763 B CN 104231763B CN 201410480886 A CN201410480886 A CN 201410480886A CN 104231763 B CN104231763 B CN 104231763B
- Authority
- CN
- China
- Prior art keywords
- parts
- fibre board
- board use
- fireproof paint
- epoxychloropropane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种纤维板用防火涂料及其制备方法，该涂料以质量份计含有以下成分：聚氯乙烯树脂5～15份，聚异丁烯15～30份，氯化橡胶10～20份，磷酸三-(2,3-二溴丙基)酯10～20份，三聚氰胺焦磷酸盐1～5份，玻璃粉3～8份，十溴代联苯醚2～6份，六偏磷酸钠0.3～1.2份，环氧氯丙烷0.5～1份，氯化铜1～4份。本发明提供的涂料具有优异的耐火和耐水性能，对纤维板的附着力强，能够很好地保护纤维板，延长纤维板的使用寿命。
Description
技术领域
本发明涉及涂料领域，尤其涉及一种纤维板用防火涂料及其制备方法。
背景技术
纤维板是以木质纤维或其他植物素纤维为原料，施加脲醛树脂或其他适用的胶粘剂制成的人造板。纤维板具有材质均匀、纵横强度差小、不易开裂等优点，用途广泛。发展纤维板生产是木材资源综合利用的有效途径。
目前，纤维板表面涂覆的涂料种类有很多，但是它们的耐火和耐水性能较差，不能起到很好地保护作用。
发明内容
解决的技术问题：针对现有纤维板用涂料耐火和耐水性能较差的缺点，本发明提供一种纤维板用防火涂料及其制备方法。
技术方案：一种纤维板用防火涂料，以质量份计含有以下成分：聚氯乙烯树脂5～15份，聚异丁烯15～30份，氯化橡胶10～20份，磷酸三-(2,3-二溴丙基)酯10～20份，三聚氰胺焦磷酸盐1～5份，玻璃粉3～8份，十溴代联苯醚2～6份，六偏磷酸钠0.3～1.2份，环氧氯丙烷0.5～1份，氯化铜1～4份。
上述所述的一种纤维板用防火涂料，以质量份计含有以下成分：聚氯乙烯树脂7～12份，聚异丁烯20～25份，氯化橡胶13～17份，磷酸三-(2,3-二溴丙基)酯14～18份，三聚氰胺焦磷酸盐2～4份，玻璃粉4～6份，十溴代联苯醚3～5份，六偏磷酸钠0.5～0.8份，环氧氯丙烷0.6～0.9份，氯化铜1.5～3份。
上述所述的一种纤维板用防火涂料的制备步骤如下：先将聚氯乙烯树脂、聚异丁烯和氯化橡胶投入陶瓷釜中，搅拌混合均匀，得到树脂溶液；另将磷酸三-(2,3-二溴丙基)酯、三聚氰胺焦磷酸盐、玻璃粉、十溴代联苯醚、六偏磷酸钠、环氧氯丙烷和氯化铜混合均匀后进行研磨，研磨至细度≤50μm，接着与树脂溶液混合均匀，即得成品。
有益效果：本发明提供的一种纤维板用防火涂料及其制备方法，该涂料具有优异的耐火和耐水性能，对纤维板的附着力强，能够很好地保护纤维板，延长纤维板的使用寿命。
具体实施方式
下面结合具体实施方式对本发明作进一步详细说明。
实施例1
本实施例提供一种纤维板用防火涂料，以质量份计含有以下成分：聚氯乙烯树脂5份，聚异丁烯15份，氯化橡胶10份，磷酸三-(2,3-二溴丙基)酯10份，三聚氰胺焦磷酸盐1份，玻璃粉3份，十溴代联苯醚2份，六偏磷酸钠0.3份，环氧氯丙烷0.5份，氯化铜1份。
一种纤维板用防火涂料的制备步骤如下：先将聚氯乙烯树脂、聚异丁烯和氯化橡胶投入陶瓷釜中，搅拌混合均匀，得到树脂溶液；另将磷酸三-(2,3-二溴丙基)酯、三聚氰胺焦磷酸盐、玻璃粉、十溴代联苯醚、六偏磷酸钠、环氧氯丙烷和氯化铜混合均匀后进行研磨，研磨至细度≤50μm，接着与树脂溶液混合均匀，即得成品。
实施例2
本实施例提供一种纤维板用防火涂料，以质量份计含有以下成分：聚氯乙烯树脂7份，聚异丁烯20份，氯化橡胶13份，磷酸三-(2,3-二溴丙基)酯14份，三聚氰胺焦磷酸盐2份，玻璃粉4份，十溴代联苯醚3份，六偏磷酸钠0.5份，环氧氯丙烷0.6份，氯化铜1.5份。
一种纤维板用防火涂料的制备步骤如下：先将聚氯乙烯树脂、聚异丁烯和氯化橡胶投入陶瓷釜中，搅拌混合均匀，得到树脂溶液；另将磷酸三-(2,3-二溴丙基)酯、三聚氰胺焦磷酸盐、玻璃粉、十溴代联苯醚、六偏磷酸钠、环氧氯丙烷和氯化铜混合均匀后进行研磨，研磨至细度≤50μm，接着与树脂溶液混合均匀，即得成品。
实施例3
本实施例提供一种纤维板用防火涂料，以质量份计含有以下成分：聚氯乙烯树脂12份，聚异丁烯25份，氯化橡胶17份，磷酸三-(2,3-二溴丙基)酯18份，三聚氰胺焦磷酸盐4份，玻璃粉6份，十溴代联苯醚5份，六偏磷酸钠0.8份，环氧氯丙烷0.9份，氯化铜3份。
一种纤维板用防火涂料的制备步骤如下：先将聚氯乙烯树脂、聚异丁烯和氯化橡胶投入陶瓷釜中，搅拌混合均匀，得到树脂溶液；另将磷酸三-(2,3-二溴丙基)酯、三聚氰胺焦磷酸盐、玻璃粉、十溴代联苯醚、六偏磷酸钠、环氧氯丙烷和氯化铜混合均匀后进行研磨，研磨至细度≤50μm，接着与树脂溶液混合均匀，即得成品。
上述实施例1～实施例3的一种纤维板用防火涂料的技术性能指标，其检测结果如下：
检测结果
以上对本发明实施例进行了详细介绍，对于本领域的一般技术人员，依据本发明实施例的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。
Claims (2)
1.一种纤维板用防火涂料，其特征在于，以质量份计含有以下成分：聚氯乙烯树脂5～15份，聚异丁烯15～30份，氯化橡胶10～20份，磷酸三-(2,3-二溴丙基)酯10～20份，三聚氰胺焦磷酸盐1～5份，玻璃粉3～8份，十溴代联苯醚2～6份，六偏磷酸钠0.3～1.2份，环氧氯丙烷0.5～1份，氯化铜1～4份；
所述的一种纤维板用防火涂料的制备方法，该方法的制备步骤如下：先将聚氯乙烯树脂、聚异丁烯和氯化橡胶投入陶瓷釜中，搅拌混合均匀，得到树脂溶液；另将磷酸三-(2,3-二溴丙基)酯、三聚氰胺焦磷酸盐、玻璃粉、十溴代联苯醚、六偏磷酸钠、环氧氯丙烷和氯化铜混合均匀后进行研磨，研磨至细度≤50μm，接着与树脂溶液混合均匀，即得成品。
2.根据权利要求1所述的一种纤维板用防火涂料，其特征在于，以质量份计含有以下成分：聚氯乙烯树脂7～12份，聚异丁烯20～25份，氯化橡胶13～17份，磷酸三-(2,3-二溴丙基)酯14～18份，三聚氰胺焦磷酸盐2～4份，玻璃粉4～6份，十溴代联苯醚3～5份，六偏磷酸钠0.5～0.8份，环氧氯丙烷0.6～0.9份，氯化铜1.5～3份。