CN104177061A - 一种空心砖的制造方法 - Google Patents
一种空心砖的制造方法 Download PDFInfo
- Publication number
- CN104177061A CN104177061A CN201410390707.8A CN201410390707A CN104177061A CN 104177061 A CN104177061 A CN 104177061A CN 201410390707 A CN201410390707 A CN 201410390707A CN 104177061 A CN104177061 A CN 104177061A
- Authority
- CN
- China
- Prior art keywords
- hollow brick
- manufacture method
- shale
- ageing
- roasting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种空心砖的制造方法,所述空心砖的制造方法包括以下步骤:步骤一:将页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板经机械粉碎,按35-45︰20-30︰5-10︰16-20︰13-18︰9-14︰5-10的配方比例搅拌均匀,然后加水搅拌均匀,形成混合物料;步骤二:陈化混合物料,陈化后再搅拌;步骤三:将陈化后的混合物料挤出成型,然后经切条机切成砖坯;步骤四:将砖坯送至干燥窑中干燥;步骤五:将干燥后的砖坯送至焙烧窑中焙烧。采用了页岩、煤矸石、粉煤灰、改性黄土、生石灰粉和矿石尾砂、合理的组分配比及合理的制早方法,易于烧结,烧结后粘结强度高,进而使得双联转的强度高,而纸屑在烧制过程中烧毁,则减轻了砖体的重量。
Description
技术领域
本发明涉及一种空心砖的制造方法。
背景技术
以前建筑使用的材料主要为红砖,是一种用粘土烧制的实心砖。这种砖需要使用的粘土非常多,占用了大量的土地资源,对当今的社会来说,这是一种资源的浪费。近些年,人们开始利用粉煤灰和粘合剂制造砖,同时,开发出了空心砖。这种砖砖体较轻,而且,不会造成土地资源的大量使用,可以充分利用废弃的材料,节能环保,但是砖体的强度和重量难以达到一个平衡的状态。
发明内容
本发明所要解决的问题是提供一种空心砖的制造方法,制成的空心砖强度高、重量轻。
为了解决上述技术问题,本发明采用如下技术方案:一种空心砖的制造方法,所述空心砖包括以下原料:页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板,所述页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板的质量比为:35-45︰20-30︰5-10︰16-20︰13-18︰9-14︰5-10,所述空心砖的制造方法包括以下步骤:
步骤一:将页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板经机械粉碎,按配方比例搅拌均匀,然后加水搅拌均匀,形成混合物料;
步骤二:陈化混合物料,陈化后再搅拌;
步骤三:将陈化后的混合物料挤出成型,然后经切条机切成砖坯;
步骤四:将砖坯送至干燥窑中干燥;
步骤五:将干燥后的砖坯送至焙烧窑中焙烧。
改进的,所述水和原料的体积比为16-20︰105-110。
改进的,所述纸板粉碎成纸屑的尺寸范围为4-6mm。
改进的,陈化时间为36h,陈化后混合物料中的含水率为14-21%。
改进的,焙烧温度为1200-1250℃,焙烧时间为11h。
有益效果:
采用上述技术方案后,该发明一种空心砖的制造方法,采用了页岩、煤矸石、粉煤灰、改性黄土、生石灰粉和矿石尾砂、合理的组分配比及合理的制早方法,易于烧结,烧结后粘结强度高,进而使得双联转的强度高,而纸屑在烧制过程中烧毁,则减轻了砖体的重量。
具体实施方式
实施例一:
一种空心砖的制造方法,包括以下步骤:
步骤一:将页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板经机械粉碎,按35︰30︰10︰20︰18︰14︰10的质量比混合搅拌均匀,然后加水搅拌均匀,形成混合物料;
步骤二:陈化混合物料36h,陈化后再搅拌,使混合物料中的含水率为14-21%;
步骤三:将陈化后的混合物料挤出成型,然后经切条机切成砖坯;
步骤四:将砖坯送至干燥窑中干燥;
步骤五:将干燥后的砖坯送至焙烧窑中于1200-1250℃下焙烧11h。
实施例二:
本实施例与实施例一的区别在于,所述页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸屑按45︰20︰6︰16︰13︰9︰5的质量比混合。
实施例三:
本实施例与实施例一的区别在于,所述页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸屑按40︰25︰8︰18︰15︰12︰7的质量比混合。
除上述优选实施例外,本发明还有其他的实施方式,本领域技术人员可以根据本发明作出各种改变和变形,只要不脱离本发明的精神,均应属于本发明所附权利要求所定义的范围。
Claims (5)
1.一种空心砖的制造方法,其特征在于:所述空心砖包括以下原料:页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板,所述页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板的质量比为:35-45︰20-30︰5-10︰16-20︰13-18︰9-14︰5-10,所述空心砖的制造方法包括以下步骤:
步骤一:将页岩、煤矸石、粉煤灰、改性黄土、生石灰粉、矿石尾砂和纸板经机械粉碎,按配方比例混合搅拌均匀,然后加水搅拌均匀,形成混合物料;
步骤二:陈化混合物料,陈化后再搅拌;
步骤三:将陈化后的混合物料挤出成型,然后经切条机切成砖坯;
步骤四:将砖坯送至干燥窑中干燥;
步骤五:将干燥后的砖坯送至焙烧窑中焙烧。
2.根据权利要求1所述的一种空心砖的制造方法,其特征在于:所述水和原料的体积比为16-20︰105-110。
3.根据权利要求1所述的一种空心砖的制造方法,其特征在于:所述纸板粉碎成纸屑的尺寸范围为4-6mm。
4.根据权利要求1或2或3所述的一种空心砖的制造方法,其特征在于:陈化时间为36h,陈化后混合物料中的含水率为14-21%。
5.根据权利要求1或2或3所述的一种空心砖的制造方法,其特征在于:焙烧温度为1200-1250℃,焙烧时间为11h。