CN104163590A - 一种玻化微珠保温砂浆及其制备方法 - Google Patents

一种玻化微珠保温砂浆及其制备方法 Download PDF

Info

Publication number
CN104163590A
CN104163590A CN201410332890.6A CN201410332890A CN104163590A CN 104163590 A CN104163590 A CN 104163590A CN 201410332890 A CN201410332890 A CN 201410332890A CN 104163590 A CN104163590 A CN 104163590A
Authority
CN
China
Prior art keywords
parts
component
vitrified small
preparation
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410332890.6A
Other languages
English (en)
Other versions
CN104163590B (zh
Inventor
汪宗来
杨晓峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd
Original Assignee
CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd filed Critical CHIZHOU CHONGYUAN ENERGY-SAVING BUILDING MATERIALS Co Ltd
Priority to CN201410332890.6A priority Critical patent/CN104163590B/zh
Publication of CN104163590A publication Critical patent/CN104163590A/zh
Application granted granted Critical
Publication of CN104163590B publication Critical patent/CN104163590B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种玻化微珠保温砂浆，其是由下述重量份的原料制得：水泥80-100，萤石矿渣5-10，碳酸氢钠1-5，木薯淀粉10-15，酒石酸1-3，菱苦土1-5，膨胀玻化微珠60-80，山梨糖醇酐油酸酯0.5-1，过磷酸钙0.5-1，甘油0.2-1，双氧水0.5-1.5，复合助剂2-6；本发明的保温砂浆具有优异的保温隔热性能和防火耐老化性能，且抗压强度高，吸水小。

Description

一种玻化微珠保温砂浆及其制备方法
技术领域
本发明涉及建筑材料领域，具体涉及一种玻化微珠保温砂浆及其制备方法。 
背景技术
玻化微珠保温砂浆是以玻化微珠为轻质骨料、与添加剂、胶粉、水泥等按照一定的比例搅拌均匀混合而成用于外墙内外保温的一种无机保温砂浆材料。玻化微珠保温砂浆具有优异的保温隔热性能和防火耐老化性能、不空鼓开裂、强度高、等优点，然而也存在易破碎、易吸水等问题。为提高玻化微珠保温砂浆的整体性能，需要改变相对单一的材料、配比，开发高性能的玻化微珠保温砂浆。 
发明内容
本发明的目的是提供一种玻化微珠保温砂浆。 
本发明是通过以下技术方案实现的： 
一种玻化微珠保温砂浆，其特征在于，其是由下述重量份的原料制得：
水泥80-100，萤石矿渣5-10，碳酸氢钠1-5，木薯淀粉10-15，酒石酸1-3，菱苦土1-5，膨胀玻化微珠60-80，山梨糖醇酐油酸酯0.5-1，过磷酸钙0.5-1，甘油0.2-1，双氧水0.5-1.5，复合助剂2-6；
所述复合助剂由下列重量份的原料制成：
壳聚糖3-8，高岭土4-10，二氧化硅2-4，氢氧化钠2-4，氯化铵1-3，椰油酰二乙醇胺0.5-1，三聚磷酸钠0.5-1，可再分散乳胶粉10-15，聚山梨酯-80 1-3，丙烯酸羟乙酯0.2-0.5；
所述复合助剂的制备方法是：
将壳聚糖溶解于适量4%的醋酸水溶液，加入高岭土、二氧化硅研磨30min，将pH调至中性后依次加入氢氧化钠、氯化铵，60℃搅拌30min，将pH调至中性，常温下加入其余原料，搅拌30min后喷雾干燥，即得。
所述的玻化微珠保温砂浆的制备方法，其特征在于，包括以下步骤： 
（1）将膨胀玻化微珠与甘油、山梨糖醇酐油酸酯混合后搅拌均匀，150℃保温2h，得组分A；
（2）将萤石矿渣、碳酸氢钠、酒石酸和木薯淀粉混合，加入适量的水60-80℃搅拌1h，干燥后研磨均匀，过250目筛，得组分B；
（3）将组分A、组分B与其余原料混合，搅拌均匀后即得。
本发明的优点是： 
1. 抗压强度高，吸水小，不空鼓开裂；
2. 具有优异的保温隔热性能和防火耐老化性能，与建筑同寿命；
3. 施工要求低，施工方便，降低成本。
具体实施方式
本发明非限定实施例如下： 
实施例1 保温砂浆的制备
一种玻化微珠保温砂浆，由下列重量(kg)的组分原料制备而成：
水泥90，萤石矿渣8，碳酸氢钠4，木薯淀粉12，酒石酸2，菱苦土4，膨胀玻化微珠70，山梨糖醇酐油酸酯0.8，过磷酸钙0.6，甘油0.5，双氧水1，复合助剂4；
其中，复合助剂由下列重量（kg）的原料制成：
壳聚糖5，高岭土6，二氧化硅3，氢氧化钠3，氯化铵2，椰油酰二乙醇胺0.8，三聚磷酸钠0.6，可再分散乳胶粉12，聚山梨酯-80 2，丙烯酸羟乙酯0.3；
复合助剂的制备方法：
将壳聚糖溶解于适量4%的醋酸水溶液，加入高岭土、二氧化硅研磨30min，将pH调至中性后依次加入氢氧化钠、氯化铵，60℃搅拌30min，将pH调至中性，常温下加入其余原料，搅拌30min后喷雾干燥，即得。
玻化微珠保温砂浆的制备方法包括以下步骤： 
（1）将膨胀玻化微珠与甘油、山梨糖醇酐油酸酯混合后搅拌均匀，150℃保温2h，得组分A；
（2）将萤石矿渣、碳酸氢钠、酒石酸和木薯淀粉混合，加入适量的水60-80℃搅拌1h，干燥后研磨均匀，过250目筛，得组分B；
（3）将组分A、组分B与其余原料混合，搅拌均匀后即得。
使用时，按重量比砂浆：水=1:1.35加入水，混合均匀即可。 
实施例2 保温砂浆的性能 
根据JG/T 283-2010测定实施例1保温砂浆的性能参数，具体见表1。
表1 保温砂浆的性能参数 

Claims (2)

1.一种玻化微珠保温砂浆，其特征在于，其是由下述重量份的原料制得：
水泥80-100，萤石矿渣5-10，碳酸氢钠1-5，木薯淀粉10-15，酒石酸1-3，菱苦土1-5，膨胀玻化微珠60-80，山梨糖醇酐油酸酯0.5-1，过磷酸钙0.5-1，甘油0.2-1，双氧水0.5-1.5，复合助剂2-6；
所述复合助剂由下列重量份的原料制成：
壳聚糖3-8，高岭土4-10，二氧化硅2-4，氢氧化钠2-4，氯化铵1-3，椰油酰二乙醇胺0.5-1，三聚磷酸钠0.5-1，可再分散乳胶粉10-15，聚山梨酯-80 1-3，丙烯酸羟乙酯0.2-0.5；
所述复合助剂的制备方法是：
将壳聚糖溶解于适量4%的醋酸水溶液，加入高岭土、二氧化硅研磨30min，将pH调至中性后依次加入氢氧化钠、氯化铵，60℃搅拌30min，将pH调至中性，常温下加入其余原料，搅拌30min后喷雾干燥，即得。
2.根据权利要求1所述的一种玻化微珠保温砂浆的制备方法，其特征在于，包括以下步骤：
（1）将膨胀玻化微珠与甘油、山梨糖醇酐油酸酯混合后搅拌均匀，150℃保温2h，得组分A；
（2）将萤石矿渣、碳酸氢钠、酒石酸和木薯淀粉混合，加入适量的水60-80℃搅拌1h，干燥后研磨均匀，过250目筛，得组分B；
（3）将组分A、组分B与其余原料混合，搅拌均匀后即得。
CN201410332890.6A 2014-07-14 2014-07-14 一种玻化微珠保温砂浆及其制备方法 Expired - Fee Related CN104163590B (zh)