CN104120011A - Stable-quality cutting fluid with bactericidal effect and preparation method thereof - Google Patents
Stable-quality cutting fluid with bactericidal effect and preparation method thereof Download PDFInfo
- Publication number
- CN104120011A CN104120011A CN201410304853.4A CN201410304853A CN104120011A CN 104120011 A CN104120011 A CN 104120011A CN 201410304853 A CN201410304853 A CN 201410304853A CN 104120011 A CN104120011 A CN 104120011A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting fluid
- auxiliary agent
- dodecylbenzene sulfonate
- slowly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stable-quality cutting fluid with bactericidal effect. The invention is characterized in that the cutting fluid is prepared from the following raw materials in parts by weight: 1-2 parts of lime sulfur, 5-7 parts of lime powder, 2-3 parts of nano diamond powder, 2-4 parts of epoxy soybean oil, 1-2 parts of sodium gluconate, 0.8-1.4 parts of chitosan, 3-4.5 parts of phenethyl alcohol oleate, 1-1.5 parts of sodium diacetate, 3-4 parts of sodium dodecyl benzene sulfonate, 5-7 parts of assistant and 200 parts of deionized water. The nano diamond powder and surfactant are mixed by grinding to enhance the dispersion effect, so that the quality is stable and uniform; by adding the lime sulfur, the cutting fluid has favorable bactericidal effect; and the assistant enhances the wear resistance, dispersity, lubricating property and film formation property of the cutting fluid. The cutting fluid has excellent lubricating property, cleaning property and rust resistance, can prevent the built-up edge from generation, effectively protects the cutter, and enhances the processing quality.
Description
Technical field
The present invention relates to cutting fluid field, particularly a kind of steady quality has cutting fluid of sterilization effect and preparation method thereof.
Background technology
Cutting fluid comprises the oil base cutting fluid that contains mineral oil and additive, contains polyoxyethylene glycol or the polypropylene glycol glycol-based cutting fluid as main ingredient, and the water-based cutting fluid of water phase surfactant mixture form.Oil base cutting fluid is poor at the cooling performance of cutting point, oil base cutting fluid can be polluted workpiece or instrument, need to further clean with organic solvent, unfriendly to environment, performance is poor aspect the dispersion stabilization of viscosity stability in cutting operation of glycol-based cutting fluid and water-based cutting fluid and abrasive material.And the traditional easily difficult dilution in smelly, winter in summer of soap base emulsion, rust-proof effect are poor, be just badly in need of now solving these shortcomings, invent be a kind ofly uniformly dispersed, all excellent cutting fluids of steady quality, various performance.
Summary of the invention
The object of this invention is to provide a kind of steady quality and there is cutting fluid of sterilization effect and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
Steady quality has a cutting fluid for sterilization effect, is made up of the raw material of following weight part: lime sulfur mixture 1-2, lime powder 5-7, nano-diamond powder 2-3, epoxy soybean oil 2-4, Sunmorl N 60S 1-2, chitosan 0.8-1.4, phenylethyl alcohol oleic acid ester 3-4.5, sodium Diacetate 1-1.5, Sodium dodecylbenzene sulfonate 3-4, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made up of the raw material of following weight part: artificial diamond's stone flour 2-3, corundum 1-2, vinyl cyanide 1-2, Oleum Bupleuri 3-4, Lauryl Alcohol ester 2-3, rosin alcohol 2-3, hexamethyldisiloxane 1-1.5, Sodium dodecylbenzene sulfonate 3.5-4, water 50-54; First preparation method adds artificial diamond's stone flour, corundum, Oleum Bupleuri, Sodium dodecylbenzene sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
A kind of steady quality of the present invention has the cutting fluid of sterilization effect, is made up of following concrete steps:
(1) lime powder, nano-diamond powder, epoxy soybean oil, Sodium dodecylbenzene sulfonate are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, grind 30-40 minute, obtain mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-2 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 50-60 minute, is cooled to room temperature and get final product.
Excellent effect of the present invention is: the present invention mixes nano-diamond powder by grinding with tensio-active agent, increased dispersion effect, steady quality homogeneous; Add lime sulfur mixture, there is good sterilization effect, add auxiliary agent, strengthened wear-resistant, disperse, lubricated, film-forming properties; The present invention has excellent lubricated, cleaning and rustless property, can avoid the generation of BUE, has effectively protected cutter, has improved processing quality.
Embodiment
Below by specific examples, the present invention is described in detail.
Steady quality has a cutting fluid for sterilization effect, by following weight part (kilogram) raw material make: lime sulfur mixture 1, lime powder 5, nano-diamond powder 2, epoxy soybean oil 2, Sunmorl N 60S 1, chitosan 0.8, phenylethyl alcohol oleic acid ester 3, sodium Diacetate 1, Sodium dodecylbenzene sulfonate 3, auxiliary agent 5, deionized water 200;
Described auxiliary agent by following weight part (kilogram) raw material make: artificial diamond's stone flour 2, corundum 1, vinyl cyanide 1, Oleum Bupleuri 3, Lauryl Alcohol ester 2, rosin alcohol 2, hexamethyldisiloxane 1, Sodium dodecylbenzene sulfonate 3.5, water 50; First preparation method adds artificial diamond's stone flour, corundum, Oleum Bupleuri, Sodium dodecylbenzene sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
A kind of steady quality of the present invention has the cutting fluid of sterilization effect, is made up of following concrete steps:
(1) lime powder, nano-diamond powder, epoxy soybean oil, Sodium dodecylbenzene sulfonate are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, grind 30-40 minute, obtain mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-2 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 50-60 minute, is cooled to room temperature and get final product.
After tested, cutting fluid of the present invention can reach following technical requirements:
Claims (2)
1. a steady quality has the cutting fluid of sterilization effect, it is characterized in that, made by the raw material of following weight part: lime sulfur mixture 1-2, lime powder 5-7, nano-diamond powder 2-3, epoxy soybean oil 2-4, Sunmorl N 60S 1-2, chitosan 0.8-1.4, phenylethyl alcohol oleic acid ester 3-4.5, sodium Diacetate 1-1.5, Sodium dodecylbenzene sulfonate 3-4, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made up of the raw material of following weight part: artificial diamond's stone flour 2-3, corundum 1-2, vinyl cyanide 1-2, Oleum Bupleuri 3-4, Lauryl Alcohol ester 2-3, rosin alcohol 2-3, hexamethyldisiloxane 1-1.5, Sodium dodecylbenzene sulfonate 3.5-4, water 50-54; First preparation method adds artificial diamond's stone flour, corundum, Oleum Bupleuri, Sodium dodecylbenzene sulfonate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, slowly be heated to 70 DEG C-80 DEG C, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
2. a kind of steady quality has the cutting fluid of sterilization effect according to claim 1, it is characterized in that, is made up of following concrete steps:
(1) lime powder, nano-diamond powder, epoxy soybean oil, Sodium dodecylbenzene sulfonate are mixed, add appropriate deionized water, be heated to 30 DEG C-35 DEG C, grind 30-40 minute, obtain mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 DEG C-65 DEG C, insulation 1-2 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 50-60 minute, is cooled to room temperature and get final product.