CN104120002A - Cutting liquid with antibacterial and antimould effects and preparation method of cutting liquid - Google Patents
Cutting liquid with antibacterial and antimould effects and preparation method of cutting liquid Download PDFInfo
- Publication number
- CN104120002A CN104120002A CN201410290960.6A CN201410290960A CN104120002A CN 104120002 A CN104120002 A CN 104120002A CN 201410290960 A CN201410290960 A CN 201410290960A CN 104120002 A CN104120002 A CN 104120002A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting liquid
- sodium
- antibacterial
- auxiliary agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses cutting liquid with antibacterial and antimould effects. The cutting liquid is characterized by being prepared from the following raw materials in parts by weight: 2-3 parts of sodium ethylene diamine tetracetate, 2.5-3.5 parts of triethanolamine, 1-2 parts of sodium diacetate, 3-4 parts of garlic oil, 1-1.5 parts of 8-hydroxyquinoline, 3-4 parts of diethanol amine, 2-3 parts of salicylic acid, 4-5 parts of fatty alcohol-polyoxyethylene ether, 3-5 parts of inositol hexaphosphate, 3-5 parts of petroleum sodium sulfonate, 2-4 parts of borax, 5-7 parts of an assistant and 200 parts of de-ionized water. According to the cutting liquid, due to addition of 8-hydroxyquinoline and garlic oil which have antibacterial and antimould effects, the shortcomings of easy deterioration and difficulty in storage of the cutting liquid are overcome; due to addition of the assistant, the wear resistance, the dispersity, the lubricity and the film-forming property are improved; the cutting liquid contains various surfactants, and is good in permeability and cleanability, high in cooling speed, good in lubricity and rust resistance and suitable for processing various metals.
Description
Technical field
The present invention relates to cutting fluid field, particularly a kind of cutting fluid with antibacterial and mouldproof effect and preparation method thereof.
Background technology
Cutting fluid is that a kind of metal that is used in is cut, cuts, grinds in the course of processing, be used for the industrial type fluid of Cooling and Lubricator cutter and workpiece, cutting fluid is formed through the compound compatibility of science by multiple super strong functional auxiliary agent, possess good cooling performance, lubricity, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature simultaneously, but the traditional easily difficult dilution in smelly, winter in summer of soap base emulsion, rust-proof effect are poor, the present invention is directed to this shortcoming of cutting fluid, designed a kind of cutting fluid with good antibiosis and deodorization effects.
Summary of the invention
The object of this invention is to provide a kind of cutting fluid with antibacterial and mouldproof effect and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A cutting fluid with antibacterial and mouldproof effect, is made by the raw material of following weight part: sodium ethylene diamine tetracetate 2-3, trolamine 2.5-3.5, sodium Diacetate 1-2, Oleum Bulbus Allii 3-4, oxine 1-1.5, diethanolamine 3-4, Whitfield's ointment 2-3, fatty alcohol-polyoxyethylene ether 4-5, nucite six phosphoric acid fat 3-5, petroleum sodium sulfonate 3-5, borax 2-4, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made by the raw material of following weight part: nano aluminum nitride 3-4, graphite 2-3, Sodium dodecylbenzene sulfonate 1-2, borax 2-4, Lauryl Alcohol ester 2-3, xitix 1-2, Microcrystalline Wax 2-3, sodium stearate 3.5-4, water 50-54; First preparation method adds nano aluminum nitride, graphite, Microcrystalline Wax, sodium stearate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, be slowly heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
A kind of cutting fluid with antibacterial and mouldproof effect of the present invention, by following concrete steps, made:
(1) petroleum sodium sulfonate, borax, Oleum Bulbus Allii, oxine are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
Excellent effect of the present invention is: the present invention adds oxine, the Oleum Bulbus Allii with antibacterial and mouldproof effect, has improved the shortcoming that cutting fluid easily fouls, is difficult for preservation; Add auxiliary agent, strengthened wear-resistant, disperse, lubricated, film-forming properties; Cutting fluid of the present invention contains kinds of surface promoting agent, has good perviousness, cleaning, and speed of cooling is fast, oilness and good antirust property, is applicable to various metals processing.
Embodiment
Below by specific examples, the present invention is described in detail.
A cutting fluid with antibacterial and mouldproof effect, by following weight part (kilogram) raw material make: sodium ethylene diamine tetracetate 2, trolamine 2.5, sodium Diacetate 1, Oleum Bulbus Allii 3, oxine 1, diethanolamine 3, Whitfield's ointment 2, fatty alcohol-polyoxyethylene ether 4, nucite six phosphoric acid fat 3, petroleum sodium sulfonate 3, borax 2, auxiliary agent 5, deionized water 200;
Described auxiliary agent by following weight part (kilogram) raw material make: nano aluminum nitride 3, graphite 2, Sodium dodecylbenzene sulfonate 1, borax 2, Lauryl Alcohol ester 2, xitix 1, Microcrystalline Wax 2, sodium stearate 3.5, water 50; First preparation method adds nano aluminum nitride, graphite, Microcrystalline Wax, sodium stearate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, be slowly heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
A kind of cutting fluid with antibacterial and mouldproof effect of the present invention, by following concrete steps, made:
(1) petroleum sodium sulfonate, borax, Oleum Bulbus Allii, oxine are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.
After tested, cutting fluid of the present invention can reach following technical requirements:
Claims (2)
1. a cutting fluid with antibacterial and mouldproof effect, it is characterized in that, by the raw material of following weight part, made: sodium ethylene diamine tetracetate 2-3, trolamine 2.5-3.5, sodium Diacetate 1-2, Oleum Bulbus Allii 3-4, oxine 1-1.5, diethanolamine 3-4, Whitfield's ointment 2-3, fatty alcohol-polyoxyethylene ether 4-5, nucite six phosphoric acid fat 3-5, petroleum sodium sulfonate 3-5, borax 2-4, auxiliary agent 5-7, deionized water 200;
Described auxiliary agent is made by the raw material of following weight part: nano aluminum nitride 3-4, graphite 2-3, Sodium dodecylbenzene sulfonate 1-2, borax 2-4, Lauryl Alcohol ester 2-3, xitix 1-2, Microcrystalline Wax 2-3, sodium stearate 3.5-4, water 50-54; First preparation method adds nano aluminum nitride, graphite, Microcrystalline Wax, sodium stearate in the water of half amount, grind 1-2 hour, then slowly add all the other remaining components, be slowly heated to 70 ℃-80 ℃, stirring reaction 30-50 minute under 300-500 rev/min of condition, is cooled to room temperature and get final product.
2. a kind of cutting fluid with antibacterial and mouldproof effect according to claim 1, is characterized in that, by following concrete steps, is made:
(1) petroleum sodium sulfonate, borax, Oleum Bulbus Allii, oxine are mixed, add appropriate deionized water, be heated to 30 ℃-35 ℃, stirring reaction 30-40 minute, obtains mixing A material;
(2) all the other remaining components except auxiliary agent are joined in reactor, be uniformly mixed, be slowly heated to 55 ℃-65 ℃, insulation 1-1.5 hour, obtains mixing B material;
(3) the mixing B material of insulation is slowly joined while stirring and mixed in A material, after fully stirring, add auxiliary agent, 800-900 rev/min of lower stirring reaction 40-60 minute, is cooled to room temperature and get final product.