CN104112488B - 一种草木灰/银粉复合的导电银浆及其制作方法 - Google Patents
一种草木灰/银粉复合的导电银浆及其制作方法 Download PDFInfo
- Publication number
- CN104112488B CN104112488B CN201410303711.6A CN201410303711A CN104112488B CN 104112488 B CN104112488 B CN 104112488B CN 201410303711 A CN201410303711 A CN 201410303711A CN 104112488 B CN104112488 B CN 104112488B
- Authority
- CN
- China
- Prior art keywords
- hour
- plant ash
- silver paste
- conductive silver
- argentum powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种草木灰/银粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉45‑50、氧化硅0.5‑1.1、硫酸锌0.3‑0.5、硅酸钠0.4‑0.7、甲基丙烯磺酸钠1.1‑2.3、二甘醇月桂酸酯2‑4、椰子油酰二乙醇胺1‑3、草木灰2.1‑3.4、松焦油4‑6、助剂30‑40、适量水；本发明通过对草木灰进行改性，添加到原料中，提高了导电银浆的抗压性以及基板的附着力。
Description
技术领域
本发明涉及导电银浆领域，具体涉及一种草木灰/银粉复合的导电银浆及其制作方法。
背景技术
导电银浆是指印刷于导电承印物上，使之具有传导电流和排除积累静电荷能力的银浆，一般是印在塑料、玻璃、陶瓷或纸板等非导电承印物上，它是由导电性填料、黏合剂、溶剂及添加剂组成。导电银浆时需要具备的特性有：导电性（抗静电性）佳、附着力强、印刷适应性好和耐溶剂性优等特性，而目前市场上现有的导电银浆有很多缺点，不仅含有铅、镉等且有毒，污染环境，而且使用在导电承印物上时附着力低、耐焊接性不佳，烧结性能差。
发明内容
本发明的目的就是提供一种草木灰/银粉复合的导电银浆及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种草木灰/银粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉45-50、氧化硅0.5-1.1、硫酸锌0.3-0.5、硅酸钠0.4-0.7、甲基丙烯磺酸钠1.1-2.3、二甘醇月桂酸酯2-4、椰子油酰二乙醇胺1-3、草木灰2.1-3.4、松焦油4-6、助剂30-40、适量水。
所述的助剂由下列重量份原料制成：氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
所述的一种草木灰/银粉复合的导电银浆的制备方法，其特征在于包括以下步骤：
（1）取草木灰送入煅烧炉中在540-630℃下烧结1-2小时，取出冷却至室温，放入3-5%的盐酸溶液中浸泡3-6小时，取出，用清水反复洗涤烘干，加适量水研磨2-3小时制得200-300目浆料，加入硫酸锌继续研磨3-4小时；
（2）取二甘醇月桂酸酯、椰子油酰二乙醇胺放入反应釜中加热到55-75℃搅拌混匀，加入松焦油，保持温度搅拌2-3小时，至完全溶解，再加入甲基丙烯磺酸钠，保温搅拌30-50分钟，研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
本发明有以下有益效果：本发明通过对草木灰进行改性，添加到原料中，提高了导电银浆的抗压性以及基板的附着力；本发明制得的银浆具有触变性良好、接触电阻低、无铅等优点，符合环保理念，可大批量持续生产。
具体实施方式
所述的一种草木灰/银粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉46、氧化硅0.5、硫酸锌0.4、硅酸钠0.5、甲基丙烯磺酸钠1.1、二甘醇月桂酸酯2、椰子油酰二乙醇胺3、草木灰2.1、松焦油6、助剂40、适量水。
所述的助剂由下列重量份原料制成：氧化铋2、氧化硼3、乙基纤维素0.9、十二烷基硫酸钠0.3、邻苯二甲酸二甲酯0.4、卵磷脂0.3、聚硅氧烷0.3、松油醇24，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
制作方法包括以下步骤：
（1）取草木灰送入煅烧炉中在540-630℃下烧结1-2小时，取出冷却至室温，放入3-5%的盐酸溶液中浸泡3-6小时，取出，用清水反复洗涤烘干，加适量水研磨2-3小时制得200-300目浆料，加入硫酸锌继续研磨3-4小时；
（2）取二甘醇月桂酸酯、椰子油酰二乙醇胺放入反应釜中加热到55-75℃搅拌混匀，加入松焦油，保持温度搅拌2-3小时，至完全溶解，再加入甲基丙烯磺酸钠，保温搅拌30-50分钟，研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
通过上述实施例加工得到的导电银浆的技术指标如下：
（1）黏度：50-100PaS（Brookfield，10RPM）；
（2）附着力：＞10N/mm2；
（3）方阻：＜5mΩ/c ；
（4）可焊性优、堆烧易分离、印刷适应性好和耐溶剂性优。
Claims (2)
1.一种草木灰/银粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉45-50、氧化硅0.5-1.1、硫酸锌0.3-0.5、硅酸钠0.4-0.7、甲基丙烯磺酸钠1.1-2.3、二甘醇月桂酸酯2-4、椰子油酰二乙醇胺1-3、草木灰2.1-3.4、松焦油4-6、助剂30-40、适量水；所述的助剂由下列重量份原料制成：氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25，所述助剂的制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
2.根据权利要求1所述的一种草木灰/银粉复合的导电银浆的制作方法，其特征在于包括以下步骤：
（1）取草木灰送入煅烧炉中在540-630℃下烧结1-2小时，取出冷却至室温，放入3-5%的盐酸溶液中浸泡3-6小时，取出，用清水反复洗涤烘干，加适量水研磨2-3小时制得200-300目浆料，加入硫酸锌继续研磨3-4小时；
（2）取二甘醇月桂酸酯、椰子油酰二乙醇胺放入反应釜中加热到55-75℃搅拌混匀，加入松焦油，保持温度搅拌2-3小时，至完全溶解，再加入甲基丙烯磺酸钠，保温搅拌30-50分钟，研磨成浆；
（3）将步骤（1）、（2）反应产物及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。