CN104030565A - 一种高热稳定的暖瓶瓶坯材料 - Google Patents

一种高热稳定的暖瓶瓶坯材料 Download PDF

Info

Publication number
CN104030565A
CN104030565A CN201410190345.8A CN201410190345A CN104030565A CN 104030565 A CN104030565 A CN 104030565A CN 201410190345 A CN201410190345 A CN 201410190345A CN 104030565 A CN104030565 A CN 104030565A
Authority
CN
China
Prior art keywords
parts
oxide
raw material
stabilizer
mixed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410190345.8A
Other languages
English (en)
Other versions
CN104030565B (zh
Inventor
薛宗洪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Hengde Fire Equipment Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410190345.8A priority Critical patent/CN104030565B/zh
Publication of CN104030565A publication Critical patent/CN104030565A/zh
Application granted granted Critical
Publication of CN104030565B publication Critical patent/CN104030565B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高热稳定的暖瓶瓶坯材料，它是由下述重量份的原料组成的：硅石粉50-60、黏土5-7、食盐2-3、氟化钠2-3、碳酸钙7-9、氧化锂1-2、纯碱10-15、磷酸二氢铵0.5-1、氯化镁1-2、氟化钙3-4、氧化铝4-6、热稳定剂2-3、复合澄清助剂1-2。本发明加入的热稳定剂中将氧化钆、氧化镧很好的复合，可以起到更好的热稳定效果，锂云母能够改善玻璃体的流动性和粘着力，降低产品的热膨胀系数，氧化钡和碲酸钠也都可以提高玻璃的热稳定性。

Description

一种高热稳定的暖瓶瓶坯材料
技术领域
本发明主要涉及一种高热稳定的暖瓶瓶坯材料，属于玻璃材料领域。
背景技术
传统的暖瓶瓶坯是以二氧化硅为主料，加入几种氧化物混合制成，机械强度不高，导致在使用、运输的过程中比较容易破裂、造成资源的浪费，有的热稳定性不强，无法长期适应沸水环境，不仅容易破裂，还有可能会损害到人身安全。
发明内容
本发明目的就是提供一种高热稳定的暖瓶瓶坯材料。
本发明是通过以下技术方案实现的：
一种高热稳定的暖瓶瓶坯材料，它是由下述重量份的原料组成的：
硅石粉50-60、黏土5-7、食盐2-3、氟化钠2-3、碳酸钙7-9、氧化锂1-2、纯碱10-15、磷酸二氢铵0.5-1、氯化镁1-2、氟化钙3-4、氧化铝4-6、热稳定剂2-3、复合澄清助剂1-2；
所述的热稳定剂是由下述重量份的原料组成的：
锂云母60-75、氧化钡20-30、氧化钆1-2、氧化镧1-2、碲酸钠0.1-0.2、聚乙烯醇1-2、硅烷偶联剂kh550 1-2；
所述的热稳定剂的制备方法包括以下步骤：
将上述锂云母在500-600℃下煅烧1-2小时，冷却后与氧化钡混合研碎成粉，加入聚乙烯醇，在60-80℃下搅拌混合均匀，加入剩余各原料，1000-1600转/分搅拌分散30-50分钟，烘干，磨成细粉，得粒径为1-2μm；
所述的复合澄清助剂是由下述重量份的原料组成的：
粉煤灰25-30、碳酸钠8-14、骨炭1-2、硝酸钡4-7、50-60%的硫酸100、氧化锌0.8-1；
（1）将粉煤灰经过高温煅烧后除铁，使得所选粉煤灰中的成分含量为
50%≤SiO2≤70%、30%≤AL2O3≤40%，余量为氧化钙、氧化镁、氧化钠、氧化钾等；
（2）将上述粉煤灰与碳酸钠混合研磨，放入马弗炉内800-850℃煅烧1-2小时，取出后与骨炭混合研磨，加入上述硫酸，搅拌混合，置于90-100℃水浴中加热1-2小时，出料冷却，放入烘箱内120-130℃下烘干，研磨至细度为1-2μm；
（3）将上述硝酸钡、氧化锌混合，球磨，过筛，得粒径0.5-1.5mm；
（4）将上述处理后的各原料混合，球磨充分，即得所述复合澄清助剂。
一种高热稳定的暖瓶瓶坯材料的制备方法，包括以下步骤：
（1）将上述除了热稳定剂以外的各原料混合，送入熔化池，加热到1600-1650℃，熔化成玻璃液；
（2）将热稳定剂加入到玻璃液中，搅拌加热至完全溶解；
（3）将溶解完全的玻璃液挑出，置于滚料板或滚料碗中滚压成软化的玻璃料团；
（4）用吹杆的一端吹气于软化状态的玻璃料团内，在不停的转动和吹气下，使料泡不断胀大，吹泡成型；
（5）退火，即得所述成品。
本发明的优点是：
本发明加入的热稳定剂中将氧化钆、氧化镧很好的复合，可以起到更好的热稳定效果，锂云母能够改善玻璃体的流动性和粘着力，降低产品的热膨胀系数，氧化钡和碲酸钠也都可以提高玻璃的热稳定性。
本发明使用的复合澄清助剂，通过粉煤灰与碳酸钠和硫酸的反应处理，使得烘干后的物料中含有硫酸铝、硅酸铝等，其中硅酸铝可以增强玻璃的热稳定性，满足暖瓶的热需求，硫酸铝在770℃下加热可分解出三氧化硫，未反应完全的粉煤灰中的各成分可以作为玻璃的基料，氧化锌与硝酸钡混合使用，放氧能力强，各气体可以在不同的时期进入熔融玻璃液的气泡中，使气泡体积不断增大上浮排出液面，从而起到澄清作用。
具体实施方式
实施例1
一种高热稳定的暖瓶瓶坯材料，它是由下述重量份（公斤）的原料组成的：
硅石粉60、黏土5、食盐2、氟化钠2、碳酸钙7、氧化锂2、纯碱15、磷酸二氢铵0.5、氯化镁1、氟化钙4、氧化铝4、热稳定剂2-3、复合澄清助剂2；
所述的热稳定剂是由下述重量份的原料组成的：
锂云母75、氧化钡30、氧化钆1、氧化镧2、碲酸钠0.2、聚乙烯醇2、硅烷偶联剂kh550 2；
所述的热稳定剂的制备方法包括以下步骤：
将上述锂云母在600℃下煅烧1小时，冷却后与氧化钡混合研碎成粉，加入聚乙烯醇，在80℃下搅拌混合均匀，加入剩余各原料，1600转/分搅拌分散50分钟，烘干，磨成细粉，得粒径为1μm；
所述的复合澄清助剂是由下述重量份的原料组成的：
粉煤灰30、碳酸钠14、骨炭1、硝酸钡7、60%的硫酸100、氧化锌0.8；
（1）将粉煤灰经过高温煅烧后除铁，使得所选粉煤灰中的成分含量为
50%≤SiO2≤70%、30%≤AL2O3≤40%，余量为氧化钙、氧化镁、氧化钠、氧化钾等；
（2）将上述粉煤灰与碳酸钠混合研磨，放入马弗炉内850℃煅烧2小时，取出后与骨炭混合研磨，加入上述硫酸，搅拌混合，置于100℃水浴中加热2小时，出料冷却，放入烘箱内130℃下烘干，研磨至细度为2μm；
（3）将上述硝酸钡、氧化锌混合，球磨，过筛，得粒径1.5mm；
（4）将上述处理后的各原料混合，球磨充分，即得所述复合澄清助剂。
一种高热稳定的暖瓶瓶坯材料的制备方法，包括以下步骤：
（1）将上述除了热稳定剂以外的各原料混合，送入熔化池，加热到1600-1650℃，熔化成玻璃液；
（2）将热稳定剂加入到玻璃液中，搅拌加热至完全溶解；
（3）将溶解完全的玻璃液挑出，置于滚料板或滚料碗中滚压成软化的玻璃料团；
（4）用吹杆的一端吹气于软化状态的玻璃料团内，在不停的转动和吹气下，使料泡不断胀大，吹泡成型；
（5）退火，即得所述成品。
耐热急变性能测试：
将用本发明的瓶坯材料制得的暖瓶启口在环境温度下保持30min以上，灌沸水至满溢，维持1min，在不多于10s的时间倒去热水，立刻灌入5℃的冷水，至满溢，放置30s，倒出冷水，检查瓶胆有无开裂：
结果，无开裂。

Claims (2)

1.一种高热稳定的暖瓶瓶坯材料，其特征在于它是由下述重量份的原料组成的：
硅石粉50-60、黏土5-7、食盐2-3、氟化钠2-3、碳酸钙7-9、氧化锂1-2、纯碱10-15、磷酸二氢铵0.5-1、氯化镁1-2、氟化钙3-4、氧化铝4-6、热稳定剂2-3、复合澄清助剂1-2；
所述的热稳定剂是由下述重量份的原料组成的：
锂云母60-75、氧化钡20-30、氧化钆1-2、氧化镧1-2、碲酸钠0.1-0.2、聚乙烯醇1-2、硅烷偶联剂kh550 1-2；
所述的热稳定剂的制备方法包括以下步骤：
将上述锂云母在500-600℃下煅烧1-2小时，冷却后与氧化钡混合研碎成粉，加入聚乙烯醇，在60-80℃下搅拌混合均匀，加入剩余各原料，1000-1600转/分搅拌分散30-50分钟，烘干，磨成细粉，得粒径为1-2μm；
所述的复合澄清助剂是由下述重量份的原料组成的：
粉煤灰25-30、碳酸钠8-14、骨炭1-2、硝酸钡4-7、50-60%的硫酸100、氧化锌0.8-1；
（1）将粉煤灰经过高温煅烧后除铁，使得所选粉煤灰中的成分含量为
50%≤SiO2≤70%、30%≤AL2O3≤40%，余量为氧化钙、氧化镁、氧化钠、氧化钾等；
（2）将上述粉煤灰与碳酸钠混合研磨，放入马弗炉内800-850℃煅烧1-2小时，取出后与骨炭混合研磨，加入上述硫酸，搅拌混合，置于90-100℃水浴中加热1-2小时，出料冷却，放入烘箱内120-130℃下烘干，研磨至细度为1-2μm；
（3）将上述硝酸钡、氧化锌混合，球磨，过筛，得粒径0.5-1.5mm；
（4）将上述处理后的各原料混合，球磨充分，即得所述复合澄清助剂。
2.一种如权利要求1所述的高热稳定的暖瓶瓶坯材料的制备方法，其特征在于包括以下步骤：
（1）将上述除了热稳定剂以外的各原料混合，送入熔化池，加热到1600-1650℃，熔化成玻璃液；
（2）将热稳定剂加入到玻璃液中，搅拌加热至完全溶解；
（3）将溶解完全的玻璃液挑出，置于滚料板或滚料碗中滚压成软化的玻璃料团；
（4）用吹杆的一端吹气于软化状态的玻璃料团内，在不停的转动和吹气下，使料泡不断胀大，吹泡成型；
（5）退火，即得所述成品。
CN201410190345.8A 2014-05-07 2014-05-07 一种高热稳定的暖瓶瓶坯材料 Active CN104030565B (zh)