CN104027261A - UV photocuring blue nail polish - Google Patents
UV photocuring blue nail polish Download PDFInfo
- Publication number
- CN104027261A CN104027261A CN201410253153.7A CN201410253153A CN104027261A CN 104027261 A CN104027261 A CN 104027261A CN 201410253153 A CN201410253153 A CN 201410253153A CN 104027261 A CN104027261 A CN 104027261A
- Authority
- CN
- China
- Prior art keywords
- photocuring
- nail polish
- blue
- blue nail
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of printing ink and particularly relates to UV photocuring blue nail polish. The UV photocuring blue nail polish comprises the following components in percentage by weight: 35-55% of polyurethane acrylate, 20-35% of trimethylolpropane triacrylate, 15-20% of epoxy acrylate, 3-5% of a photoinitiator, 1-5% of an indigo dye and 0.5-1% of a flatting agent. The UV photocuring blue nail polish provided by the invention is moderate in adhesive force, can satisfy the adhering effect on nails and can be easily stripped from the nails, and assistant stripping due to addition of an organic solvent is avoided, so that the damage of a stripping solution on the nails is effectively prevented.
Description
Technical field
The present invention relates to technical field of ink, especially relate to a kind of UV photocuring blue nail polish.
Background technology
Nial polish is the large series products belonging in color make-up series, has and beautifies the function of modifying fingernail.Common nial polish is that a kind of NC Nitroncellulose of ester dissolubility is dissolved in the fingernail film former in certain high activity ester group dicyandiamide solution, its also comparative maturity of filling a prescription, main component is 70%～80% volatile solvent, the nitrocellulose of 15% left and right, a small amount of oil-based solvent, Camphora, titanium dioxide and oily molten pigment etc.Nial polish is applied to the thin film forming after fingernail, strong and have the painted gloss of appropriateness, can protect fingernail, gives again fingernail a kind of aesthetic feeling.
UV photocuring nial polish product in the market has a lot, but its pliability is poor, easily causes the embrittlement of first sheet, and adhesive force is excessively firm, is not easy to take off from fingernail.
Summary of the invention
The present invention has overcome UV photocuring nial polish product in the market of the prior art to be had a lot, but its pliability is poor, easily cause the embrittlement of first sheet, and adhesive force is excessively firm, the problem that is not easy to take off from fingernail, a kind of UV photocuring blue nail polish is provided, adhesive force is moderate, can meet the adhesion effect on fingernail, and can peel off from fingernail easily, avoid with an organic solvent carrying out up-stripping, effectively prevented to peel off the injury of solvent to fingernail.
The technical solution adopted for the present invention to solve the technical problems is: a kind of UV photocuring blue nail polish, and each component and each component weight percent content are:
Urethane acrylate 35-55%
Trimethylolpropane triacrylate 20-35%
Epoxy acrylate 15-20
Light trigger 3-5%
Blue pigment 1-5%
Levelling agent 0.5-1%.
Particularly, described initiator is 1173 and/or 907.。
Particularly, described levelling agent be in organic silicon modified by polyether, polyester resin change properties of organic silicon, polyacrylate, acrylated polyurethane resin, polydimethylsiloxane, PSI, organic group modified polyorganosiloxane one or more.
The preparation method of UV photocuring blue nail polish, comprises the steps:
Step 1) take in proportion each component of UV photocuring blue nail polish,
Step 2) by step 1) in each component stir, blender rotating speed is 1000-1800 rev/min, can obtain UV photocuring blue nail polish;
Step 3) encapsulate, label.
The invention has the beneficial effects as follows: a kind of UV photocuring blue nail polish provided by the invention, adhesive force is moderate, can meet the adhesion effect on fingernail, and can peel off from fingernail easily, avoid with an organic solvent carrying out up-stripping, effectively prevented to peel off the injury of solvent to fingernail.
Detailed description of the invention
Below in conjunction with specific embodiment, further the present invention is set forth, should be understood that and quote embodiment only for the present invention is described, limit the scope of the invention and be not used in.
Embodiment 1
A kind of UV photocuring blue nail polish, in each component and each component weight percent content is:
Urethane acrylate 55%
Trimethylolpropane triacrylate 20%
Epoxy acrylate 15
Described initiator is 11734%
Blue pigment 5%
Organic silicon modified by polyether 1%.
The preparation method of UV photocuring blue nail polish, comprises the steps:
Step 1) take in proportion each component of UV photocuring blue nail polish,
Step 2) by step 1) in each component stir, blender rotating speed is 1000 revs/min, can obtain UV photocuring blue nail polish;
Step 3) encapsulate, label.
Embodiment 2
A kind of UV photocuring blue nail polish, in each component and each component weight percent content is:
Urethane acrylate 35%
Trimethylolpropane triacrylate 35%
Epoxy acrylate 20
9075％
Blue pigment 4%
Polyester resin change properties of organic silicon 1%.
The preparation method of UV photocuring blue nail polish, comprises the steps:
Step 1) take in proportion each component of UV photocuring blue nail polish,
Step 2) by step 1) in each component stir, blender rotating speed is 1800 revs/min, can obtain UV photocuring blue nail polish;
Step 3) encapsulate, label.
Embodiment 3
A kind of UV photocuring blue nail polish, in each component and each component weight percent content is:
Urethane acrylate 55%
Trimethylolpropane triacrylate 20%
Epoxy acrylate 20
1173 and 9073%
Blue pigment 1%
Polyacrylate 1%.
The preparation method of UV photocuring blue nail polish, comprises the steps:
Step 1) take in proportion each component of UV photocuring blue nail polish,
Step 2) by step 1) in each component stir, blender rotating speed is 1200 revs/min, can obtain UV photocuring blue nail polish;
Step 3) encapsulate, label.
Embodiment 4
A kind of UV photocuring blue nail polish, in each component and each component weight percent content is:
Urethane acrylate 50%
Trimethylolpropane triacrylate 30%
Epoxy acrylate 15.5%
11733％
Blue pigment 1%
Polydimethylsiloxane and PSI 0.5%.
The preparation method of UV photocuring blue nail polish, comprises the steps:
Step 1) take in proportion each component of UV photocuring blue nail polish,
Step 2) by step 1) in each component stir, blender rotating speed is 1000 revs/min, can obtain UV photocuring blue nail polish;
Step 3) encapsulate, label.
Embodiment 5
A kind of UV photocuring blue nail polish, in each component and each component weight percent content is:
Urethane acrylate 40%
Trimethylolpropane triacrylate 35%
Epoxy acrylate 20
9073％
Blue pigment 1.5%
PSI and organic group modified polyorganosiloxane 0.5%.
The preparation method of UV photocuring blue nail polish, comprises the steps:
Step 1) take in proportion each component of UV photocuring blue nail polish,
Step 2) by step 1) in each component stir, blender rotating speed is 1500 revs/min, can obtain UV photocuring blue nail polish;
Step 3) encapsulate, label.
Taking above-mentioned foundation desirable embodiment of the present invention as enlightenment, by above-mentioned description, relevant staff can, not departing from the scope of this invention technological thought, carry out various change and amendment completely.The technical scope of this invention is not limited to the content in description, must determine its technical scope according to claim scope.
Claims (4)
1. a UV photocuring blue nail polish, is characterized in that each component and each component weight percent content are:
Urethane acrylate 35-55%
Trimethylolpropane triacrylate 20-35%
Epoxy acrylate 15-20
Light trigger 3-5%
Bipseudoindoxyl dye 1-5%
Levelling agent 0.5-1%.
2. UV photocuring blue nail polish as claimed in claim 1, is characterized in that: described initiator is 1173 and/or 907.
3. UV photocuring blue nail polish as claimed in claim 1, is characterized in that: described levelling agent be in organic silicon modified by polyether, polyester resin change properties of organic silicon, polyacrylate, acrylated polyurethane resin, polydimethylsiloxane, PSI, organic group modified polyorganosiloxane one or more.
4. the preparation method of the UV photocuring blue nail polish as described in claim 1-3 any one, is characterized in that comprising the steps:
Step 1) take in proportion each component of UV photocuring blue nail polish,
Step 2) by step 1) in each component stir, blender rotating speed is 1000-1800 rev/min, can obtain UV photocuring blue nail polish;
Step 3) encapsulate, label.