CN104005039A - Aluminum alloy die cleaning agent and preparation method thereof - Google Patents
Aluminum alloy die cleaning agent and preparation method thereof Download PDFInfo
- Publication number
- CN104005039A CN104005039A CN201410225673.7A CN201410225673A CN104005039A CN 104005039 A CN104005039 A CN 104005039A CN 201410225673 A CN201410225673 A CN 201410225673A CN 104005039 A CN104005039 A CN 104005039A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- agent
- tensio
- sanitising agent
- alloy mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an aluminum alloy die cleaning agent and a preparation method thereof. The cleaning agent comprises following components by mass percent: 6-12% of sodium dodecyl benzene sulfonate, 5-15% of surfactant, 40-50% of sodium hydroxide, 10-20% of anhydrous sodium carbonate, 8-15% of sodium citrate, 5-8% of sodium silicate, and 1-2% of defoaming agent. The aluminum alloy die cleaning agent is prepared through a scientific method, has strong capacity of washing oil membrane easy to pollute the aluminum alloy, has the oil membrane cleaning efficiency of 98%, is economic, meets the national environment protection requirements in indexes, has no harm to the skin of human body, does not corrode the aluminum alloy die, and can improve the quality of the product and prolong the service life of the die.
Description
Technical field
The invention belongs to clean-out system and manufacture field, be specifically related to a kind of aluminum alloy mould sanitising agent and preparation method thereof.
Background technology
In household electrical appliances, automobile industry Mould Machining enterprise, the material of most economical material benefit is aluminium alloy, aluminium, and aluminium alloy conducts heat, quality is light, be the good base material of processing mold, due to the optimization and upgrading of automobile industry inside in recent years, constantly stimulate the growth to mould demand.Automotive industry is for China; also in development, grow the stage; above-mentioned under the drive of above trend; the advantage that China's Die Industry is developed is very obvious; but aluminum alloy mould in use, often have pollution, particularly greasy dirt that greasy dirt, foreign material cause and in aluminum alloy surface, easily form oil film and be attached to surface and form colour film; time has been grown and can form irreversible erosion to aluminum alloy surface, has a strong impact on product quality and die life.
Summary of the invention
For addressing the above problem, the invention discloses a kind of aluminum alloy mould sanitising agent and preparation method thereof, the washing power of oil film is 98%, corrosion-free to aluminum alloy mould, price economy, environment-protecting asepsis.
For achieving the above object, technical scheme of the present invention is as follows:
A kind of aluminum alloy mould sanitising agent, it is characterized in that: described sanitising agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonate 6-12%, tensio-active agent 5-15%, sodium hydroxide 40-50%, anhydrous sodium carbonate 10-20%, Trisodium Citrate 8-15%, water glass 5-8%, defoamer 1-2%.
As a modification of the present invention, the component that described tensio-active agent is following mass percent is prepared from by chemical reaction: diethanolamine 60-80%; 4-chloromethyl pyridine hydrochloride 20-40%.
As a modification of the present invention, the making method of described tensio-active agent is: by after the diethanolamine of said components and the mixing of 4-chloromethyl pyridine hydrochloride, be under agitation heated to 60-80 ℃, then stir insulation 2 hours.
As a modification of the present invention, described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
A preparation method for aluminum alloy mould sanitising agent, is characterized in that: comprise the following steps:
(1) make tensio-active agent;
(2) tensio-active agent of making is added in reactor, then add ten disulfobenzene sodium sulfonates, sodium hydroxide, anhydrous sodium carbonate, Trisodium Citrate, water glass, closing presure still stirs 0.5-2 hour under 110Kpa air pressure, normal temperature;
(3) add under defoamer normal temperature and pressure and stir 10-20 minute;
(4) mixture is put into vaporizer, revolution distillation 3-6 hour, extracts supernatant liquor, puts into filtering centrifuge centrifugal under 1200 revolutions per seconds, obtains sanitising agent.
The invention has the beneficial effects as follows:
A kind of aluminum alloy mould sanitising agent of the present invention and preparation method, for the oil film easily causing on aluminium alloy, pollute and have powerful clean ability, to the washing power of oil film, be 98%, price economy, indices meets national requirements for environmental protection, without harm, corrosion-free to aluminum alloy mould to human body skin, can improving product quality and die life.
Embodiment
Embodiment 1
An aluminum alloy mould sanitising agent, described sanitising agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonates 9%, tensio-active agent 12%, sodium hydroxide 48%, anhydrous sodium carbonate 12%, Trisodium Citrate 12%, water glass 6%, defoamer 1%.
Tensio-active agent is that the component of following mass percent is prepared from by chemical reaction: diethanolamine 75%; 4-chloromethyl pyridine hydrochloride 25%, the making method of described tensio-active agent is: by after diethanolamine and the mixing of 4-chloromethyl pyridine hydrochloride, be under agitation heated to 75 ℃, then stir insulation 2 hours.
Described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
A preparation method for aluminum alloy mould sanitising agent, comprises the following steps:
(1) make according to the method described above tensio-active agent;
(2) tensio-active agent of making is added in reactor, then add ten disulfobenzene sodium sulfonates, sodium hydroxide, anhydrous sodium carbonate, Trisodium Citrate, water glass, closing presure still stirs 1.5 hours under 110Kpa air pressure, normal temperature;
(3) add under defoamer normal temperature and pressure and stir 10 minutes;
(4) mixture is put into vaporizer, revolution distillation 5 hours, extracts supernatant liquor, puts into filtering centrifuge centrifugal under 1200 revolutions per seconds, obtains sanitising agent.
During use, sanitising agent and water are according to the dilution proportion of 1:30, and oil film is with serious pollution can be diluted according to 1:25, when used winter, the solution having diluted suitably can be heated to 10-20 ℃ of use, better effects if.
Using a kind of aluminum alloy mould sanitising agent described in the present embodiment, is 98% to the washing power of oil film, and aluminum alloy mould is corrosion-free, and indices meets national requirements for environmental protection, to human body skin without harm.
Embodiment 2
An aluminum alloy mould sanitising agent, described sanitising agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonates 10%, tensio-active agent 12%, sodium hydroxide 44%, anhydrous sodium carbonate 14%, Trisodium Citrate 10%, water glass 8%, defoamer 2%.
Tensio-active agent is that the component of following mass percent is prepared from by chemical reaction: diethanolamine 80%; 4-chloromethyl pyridine hydrochloride 20%, the making method of described tensio-active agent is: by after diethanolamine and the mixing of 4-chloromethyl pyridine hydrochloride, be under agitation heated to 70 ℃, then stir insulation 2 hours.
Described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
A preparation method for aluminum alloy mould sanitising agent, comprises the following steps:
(1) make according to the method described above tensio-active agent;
(2) tensio-active agent of making is added in reactor, then add ten disulfobenzene sodium sulfonates, sodium hydroxide, anhydrous sodium carbonate, Trisodium Citrate, water glass, closing presure still stirs 1 hour under 110Kpa air pressure, normal temperature;
(3) add under defoamer normal temperature and pressure and stir 15 minutes;
(4) mixture is put into vaporizer, revolution distillation 6 hours, extracts supernatant liquor, puts into filtering centrifuge centrifugal under 1200 revolutions per seconds, obtains sanitising agent.
During use, sanitising agent and water are according to the dilution proportion of 1:30, and oil film is with serious pollution can be diluted according to 1:25, when used winter, the solution having diluted suitably can be heated to 10-20 ℃ of use, better effects if.
Using a kind of aluminum alloy mould sanitising agent described in the present embodiment, is 97% to the washing power of oil film, and aluminum alloy mould is corrosion-free, and indices meets national requirements for environmental protection, to human body skin without harm.
The disclosed technique means of the present invention program is not limited only to the disclosed technique means of above-mentioned embodiment, also comprises the technical scheme being comprised of above technical characterictic arbitrary combination.
Claims (5)
1. an aluminum alloy mould sanitising agent, it is characterized in that: described sanitising agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonate 6-12%, tensio-active agent 5-15%, sodium hydroxide 40-50%, anhydrous sodium carbonate 10-20%, Trisodium Citrate 8-15%, water glass 5-8%, defoamer 1-2%.
2. a kind of aluminum alloy mould sanitising agent according to claim 1, is characterized in that: the component that described tensio-active agent is following mass percent is prepared from by chemical reaction: diethanolamine 60-80%; 4-chloromethyl pyridine hydrochloride 20-40%.
3. a kind of aluminum alloy mould sanitising agent according to claim 2, it is characterized in that: the making method of described tensio-active agent is: by after the diethanolamine of said components and the mixing of 4-chloromethyl pyridine hydrochloride, under agitation be heated to 60-80 ℃, then stir insulation 2 hours.
4. a kind of aluminum alloy mould sanitising agent according to claim 1, is characterized in that: described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
5. a preparation method for aluminum alloy mould sanitising agent, is characterized in that: comprise the following steps:
(1) make tensio-active agent;
(2) tensio-active agent of making is added in reactor, then add ten disulfobenzene sodium sulfonates, sodium hydroxide, anhydrous sodium carbonate, Trisodium Citrate, water glass, closing presure still stirs 0.5-2 hour under 110Kpa air pressure, normal temperature;
(3) add under defoamer normal temperature and pressure and stir 10-20 minute;
(4) mixture is put into vaporizer, revolution distillation 3-6 hour, extracts supernatant liquor, puts into filtering centrifuge centrifugal under 1200 revolutions per seconds, obtains sanitising agent.