CN103992528A - 一种耐油耐磨电源线护套料及其制备方法 - Google Patents

一种耐油耐磨电源线护套料及其制备方法 Download PDF

Info

Publication number
CN103992528A
CN103992528A CN201410163579.3A CN201410163579A CN103992528A CN 103992528 A CN103992528 A CN 103992528A CN 201410163579 A CN201410163579 A CN 201410163579A CN 103992528 A CN103992528 A CN 103992528A
Authority
CN
China
Prior art keywords
parts
wear
resistance
resistant
sheath material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201410163579.3A
Other languages
English (en)
Inventor
林文树
乔元朝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianchang Fuxin Electronic Co Ltd
Original Assignee
Tianchang Fuxin Electronic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianchang Fuxin Electronic Co Ltd filed Critical Tianchang Fuxin Electronic Co Ltd
Priority to CN201410163579.3A priority Critical patent/CN103992528A/zh
Publication of CN103992528A publication Critical patent/CN103992528A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种耐油耐磨电源线护套料及其制备方法，其由以下重量份的原料制成：丁腈橡胶40-60、顺丁橡胶20-30、乙烯-四氟乙烯共聚物15-25、磷酸三甲苯酯12-18、轻质氧化镁2-4、硬脂酸1-2、过氧化苯甲酰2.5-3.5、三烯丙基异氰脲酸酯2-3、单硬脂酸甘油酯4-8、环氧四氢邻苯二甲酸二辛酯10-15、氢氧化镁16-22、磷酸铝8-14、钼酸铵5-10、硼酸锌4-8、沉淀白炭黑22-28、煅烧陶土15-25、刚玉粉5-10、促进剂TMTM1-2、防老剂OD1-2、助剂10-15。本发明护套料具有耐油、耐磨、耐高低温、耐臭氧、耐酸碱，耐老化、耐辐射等特性，是耐油耐磨电源线最佳护套材料。

Description

一种耐油耐磨电源线护套料及其制备方法
技术领域
本发明涉及一种电源线护套料及其制备方法，具体涉及一种耐油耐磨电源线护套料及其制备方法。
背景技术
电源线是传输电流的电线，其中护套是电源线不可缺少的结构部分，起到防护绝缘的作用，保证电源线的通电安全，让导体和水、空气等介质隔绝，避免出现漏电现象。目前市场上电源线护套材料存在着耐油性差和耐磨性差的缺点，无法应用于环境恶劣防油等场合的电源线。因此，急需开发一种耐油耐磨电源线护套料。
发明内容
本发明的目的在于针对现有技术的不足，提供一种耐油耐磨电源线护套料及其制备方法。
为实现上述目的，本发明采用的技术方案如下：
一种耐油耐磨电源线护套料，由以下重量份的原料制成：丁腈橡胶40-60、顺丁橡胶20-30、乙烯-四氟乙烯共聚物15-25、磷酸三甲苯酯12-18、轻质氧化镁2-4、硬脂酸1-2、过氧化苯甲酰2.5-3.5、三烯丙基异氰脲酸酯2-3、单硬脂酸甘油酯4-8、环氧四氢邻苯二甲酸二辛酯10-15、氢氧化镁16-22、磷酸铝8-14、钼酸铵5-10、硼酸锌4-8、沉淀白炭黑22-28、煅烧陶土15-25、刚玉粉5-10、促进剂TMTM1-2、防老剂OD1-2、助剂10-15；
所述助剂的制备方法如下：a、取以下重量份的原料：钾长石18-24、重晶石16-22、火山岩10-15、纳米氧化锌2-3、氯化亚锡1-2、邻苯二甲酸二丁酯6-12、间苯二酚2-3、三氧化二铁1.5-2.5、防老剂4010NA2-3、促进剂CZ1-2、纳米碳纤维3-5、硬脂酸钙1-2、硬脂酸钡1-2、季戊四醇三丙烯酸酯5-10；b、将钾长石、重晶石、火山岩混合均匀，粉碎，然后放入浓度为10-15％的盐酸溶液中浸泡1-2h，取出用蒸馏水洗涤至中性，烘干，然后加水打浆制成浓度为45-55％的悬浮液，再加入相当于悬浮液重量25-35％的固含量为40％硅溶胶、5-8％的正硅酸丁酯和4-6％的双环戊二烯，水浴加热至40-50℃，高速球磨3-4h，过滤，烘干，780-860℃煅烧1-2h，自然冷却至室温后与其余原料混合，搅拌5-10min即可。
本发明耐油耐磨电源线护套料的制备方法，包括以下步骤：先将丁腈橡胶、顺丁橡胶和乙烯-四氟乙烯共聚物加入到开炼机内塑炼至料温为70-80℃，再加入其余原料，混炼10-15min后出料，胶料存放24-48h后在温度为170-190℃，压力为10-15MPa条件下硫化15-25min即可。
本发明有益效果：
本发明护套料具有耐油、耐磨、耐高低温、耐臭氧、耐酸碱，耐老化、耐辐射等特性，是耐油耐磨电源线最佳护套材料，可以广泛应用于工业机械设备、传输传送控制***、电子器械、家用电器、机电、厨房等设备电源线。
具体实施方式
一种耐油耐磨电源线护套料，由以下重量份的原料制成：丁腈橡胶50、顺丁橡胶25、乙烯-四氟乙烯共聚物25、磷酸三甲苯酯16、轻质氧化镁3、硬脂酸1.5、过氧化苯甲酰3、三烯丙基异氰脲酸酯2.5、单硬脂酸甘油酯6、环氧四氢邻苯二甲酸二辛酯12、氢氧化镁18、磷酸铝12、钼酸铵8、硼酸锌6、沉淀白炭黑25、煅烧陶土20、刚玉粉8、促进剂TMTM1.5、防老剂OD1、助剂12；
所述助剂的制备方法如下：a、取以下重量份的原料：钾长石22、重晶石18、火山岩12、纳米氧化锌2、氯化亚锡1.5、邻苯二甲酸二丁酯8、间苯二酚2.5、三氧化二铁2、防老剂4010NA2.5、促进剂CZ1.5、纳米碳纤维4、硬脂酸钙1、硬脂酸钡2、季戊四醇三丙烯酸酯7；b、将钾长石、重晶石、火山岩混合均匀，粉碎，然后放入浓度为15％的盐酸溶液中浸泡1h，取出用蒸馏水洗涤至中性，烘干，然后加水打浆制成浓度为50％的悬浮液，再加入相当于悬浮液重量30％的固含量为40％硅溶胶、6％的正硅酸丁酯和4％的双环戊二烯，水浴加热至45℃，高速球磨3h，过滤，烘干，820℃煅烧1.5h，自然冷却至室温后与其余原料混合，搅拌8min即可。
耐油耐磨电源线护套料的制备方法，包括以下步骤：先将丁腈橡胶、顺丁橡胶和乙烯-四氟乙烯共聚物加入到开炼机内塑炼至料温为70-80℃，再加入其余原料，混炼10-15min后出料，胶料存放24-48h后在温度为170-190℃，压力为10-15MPa条件下硫化15-25min即可。
制得的护套料的性能测试结果如下：

Claims (2)

1.一种耐油耐磨电源线护套料，其特征在于，由以下重量份的原料制成：丁腈橡胶40-60、顺丁橡胶20-30、乙烯-四氟乙烯共聚物15-25、磷酸三甲苯酯12-18、轻质氧化镁2-4、硬脂酸1-2、过氧化苯甲酰2.5-3.5、三烯丙基异氰脲酸酯2-3、单硬脂酸甘油酯4-8、环氧四氢邻苯二甲酸二辛酯10-15、氢氧化镁16-22、磷酸铝 8-14、钼酸铵 5-10、硼酸锌 4-8、沉淀白炭黑 22-28、煅烧陶土 15-25、刚玉粉 5-10、促进剂TMTM 1-2、防老剂OD 1-2、助剂 10-15；
所述助剂的制备方法如下：a、取以下重量份的原料：钾长石18-24、重晶石 16-22、火山岩 10-15、纳米氧化锌 2-3、氯化亚锡 1-2、邻苯二甲酸二丁酯6-12、间苯二酚 2-3、三氧化二铁1.5-2.5、防老剂4010NA 2-3、促进剂CZ 1-2、纳米碳纤维 3-5、硬脂酸钙1-2、硬脂酸钡1-2、季戊四醇三丙烯酸酯 5-10；b、将钾长石、重晶石、火山岩混合均匀，粉碎，然后放入浓度为10-15%的盐酸溶液中浸泡1-2h，取出用蒸馏水洗涤至中性，烘干，然后加水打浆制成浓度为45-55%的悬浮液，再加入相当于悬浮液重量25-35%的固含量为40%硅溶胶、5-8%的正硅酸丁酯和4-6%的双环戊二烯，水浴加热至40-50℃，高速球磨3-4h，过滤，烘干，780-860℃煅烧1-2h，自然冷却至室温后与其余原料混合，搅拌5-10min即可。
2.如权利要求1所述的耐油耐磨电源线护套料的制备方法，其特征在于包括以下步骤：先将丁腈橡胶、顺丁橡胶和乙烯-四氟乙烯共聚物加入到开炼机内塑炼至料温为70-80℃，再加入其余原料，混炼10-15min后出料，胶料存放24-48h后在温度为170-190℃，压力为10-15MPa条件下硫化15-25min即可。
CN201410163579.3A 2014-04-22 2014-04-22 一种耐油耐磨电源线护套料及其制备方法 Withdrawn CN103992528A (zh)