CN103980568B - A kind of water swelling rubber material and preparation method thereof - Google Patents
A kind of water swelling rubber material and preparation method thereof Download PDFInfo
- Publication number
- CN103980568B CN103980568B CN201410243238.7A CN201410243238A CN103980568B CN 103980568 B CN103980568 B CN 103980568B CN 201410243238 A CN201410243238 A CN 201410243238A CN 103980568 B CN103980568 B CN 103980568B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- rubber material
- water swelling
- swelling rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of water swelling rubber material, it is characterized in that comprising following component: mark 98 ~ 102 parts, glue; Carbon black 18 ~ 22 parts; Nanometer strengthening agent 23 ~ 27 parts; Water-absorbing resin 18 ~ 22 parts; Rubber powder 18 ~ 22 parts; 3 ~ 7 parts, zinc oxide; Stearic acid 1.2 ~ 1.7 parts; Altax? 0.4 ~ 0.6 part; Accelerator NS? 0.7 ~ 0.9 part; Mould inhibitor 0.8 ~ 1.2 part; Anti-creme 1.3 ~ 1.7 parts; Solubilizing agent 2 ~ 5 parts; 1.3 ~ 1.7 parts, sulphur; With parts by weight.Excellent product performance of the present invention, expansion rate of water absorption is high, and tensile strength and elongation at break are all better than like product.
Description
Technical field
The present invention relates to a kind of elastomeric material and preparation method thereof, be specifically related to a kind of water swelling rubber material and preparation method thereof.
Background technology
Water swelling rubber is as a kind of watertight rubber material, and its great advantage is exactly have excellent sealing leak stopping function.Obtain at construction fields such as hydro project subway tunnel, underground foundation work dams at present and applied widely.
As everyone knows, on the whole, rubber is a kind of hydrophobic material, in its molecular chain except carbon, hydrogen segment, also containing a small amount of hydrophilic radical.Upon contact with water, by diffusion, knitting wool, the physical action such as thin and surface adsorption enters in rubber bodies water molecules, makes rubber rapid spatial expansion.Meanwhile, the hydrophilic radical of water molecules in rubber bodies is combined, and forms a kind of avidity.Like this, the water entered in rubber bodies makes hydrophilic radical dissolve or expands, inside and outside rubber bodies, form permeable pressure head.This pressure reduction also has promoter action to water to the infiltration in rubber bodies.Hydrophilic radical absorbs moisture continuously, makes rubber expand deformation.When anti deformational force is suitable with permeable pressure head, just reach balance, water-swelling effect can keep relative stability.
The performance of water swelling rubber has not only depended on formula and the component of material, has also depended on the preparation technology of material.Poor compatibility in existing water swelling rubber between rubber and resin, the cross-linking density of rubber is higher, and sealing performance is not good.
Summary of the invention
Goal of the invention: the object of the invention is for the deficiencies in the prior art, provides a kind of water swelling rubber material of excellent performance.
Another object of the present invention is to the preparation method that this water swelling rubber material is provided.
Technical scheme: water swelling rubber material of the present invention, comprises following component:
Mark 98 ~ 102 parts, glue;
Carbon black 18 ~ 22 parts;
Nanometer strengthening agent 23 ~ 27 parts;
Water-absorbing resin 18 ~ 22 parts;
Rubber powder 18 ~ 22 parts;
3 ~ 7 parts, zinc oxide;
Stearic acid 1.2 ~ 1.7 parts;
Altax 0.4 ~ 0.6 part;
Accelerator NS 0.7 ~ 0.9 part;
Mould inhibitor 0.8 ~ 1.2 part;
Anti-creme 1.3 ~ 1.7 parts;
Solubilizing agent 2 ~ 5 parts;
1.3 ~ 1.7 parts, sulphur;
With parts by weight.
Preferably, described water swelling rubber material comprises following component:
Mark 100 parts, glue;
Carbon black 20 parts;
Nanometer strengthening agent 25 parts;
Water-absorbing resin 20 parts;
Rubber powder 20 parts;
5 parts, zinc oxide;
Stearic acid 1.5 parts;
Altax 0.5 part;
Accelerator NS 0.8 part;
Mould inhibitor 1 part;
Anti-creme 1.5 parts;
Solubilizing agent 3 parts;
1.5 parts, sulphur.
The preparation method of water swelling rubber material of the present invention is, after all components is mixed, put into the container with agitator, repeatedly to pack stirring, vacuum defoamation, maturation, moulding, sulfuration is carried out after stirring, curing temperature is 150 ~ 160 DEG C, and the time is 10 ~ 14 minutes, and board pressure is 15Mpa.
Beneficial effect: excellent product performance of the present invention, expansion rate of water absorption is high, and tensile strength and elongation at break are all better than like product.
Embodiment
Below technical solution of the present invention is described in detail, but protection scope of the present invention is not limited to described embodiment.
The raw material used in the embodiment of the present invention is commercially available prod, originates as follows: the large golden cup SVR-3L of Vietnam's AA level marks glue (Guan Hua rubber and plastic trade Co., Ltd of Shenzhen); Carbon black N550(Qingdao Zhong Xiangbokai Chemical Co., Ltd.); Nano-rubber strengthening agent (Hunan Yixiang Technology Corporation Ltd.); Water-absorbing resin is Mierocrystalline cellulose-acrylonitrile graft polymer (Dongguan City Su Zhan plastic cement company limited); Rubber powder (redispersable latex powder that Langfang Ying Shun Wanke produces); Zinc oxide (Linyi mayor woods Chemical Co., Ltd.); Stearic acid (reported in Tianhe district of Guangzhou grand sight intelligence industry Chemicals 1801 stearic acid); Rubber accelerator DM(Shijiazhuang City gathers hundred wide Chemical Industry Science Co., Ltd); Accelerator NS (Shijiazhuang City gathers hundred wide Chemical Industry Science Co., Ltd); Mould inhibitor (Bry Chemical Co., Ltd.); Anti-creme (Bry Chemical Co., Ltd.); Solubilizing agent (Shijiazhuang Fa Te Chemical Industry Science Co., Ltd); Sulphur (Linyi Jin Huang Chemical Co., Ltd.).
Embodiment 1: a kind of water swelling rubber material, comprises following component:
Mark 100 parts, glue;
Carbon black 20 parts;
Nanometer strengthening agent 25 parts;
Water-absorbing resin 20 parts;
Rubber powder 20 parts;
5 parts, zinc oxide;
Stearic acid 1.5 parts;
Altax 0.5 part;
Accelerator NS 0.8 part;
Mould inhibitor 1 part;
Anti-creme 1.5 parts;
Solubilizing agent 3 parts;
1.5 parts, sulphur.
Preparation method is: after being mixed by all components, put into the container with agitator, stirring of repeatedly packing, vacuum defoamation, maturation, moulding, sulfuration is carried out after stirring, curing temperature is 150 ~ 160 DEG C, and the time is 10 ~ 14 minutes, and board pressure is 15Mpa.
Embodiment 2: a kind of water swelling rubber material, comprises following component:
Mark 98 parts, glue;
Carbon black 18 parts;
Nanometer strengthening agent 27 parts;
Water-absorbing resin 22 parts;
Rubber powder 18 parts;
3 parts, zinc oxide;
Stearic acid 1.2 parts;
Altax 0.4 part;
Accelerator NS 0.9 part;
Mould inhibitor 0.8 part;
Anti-creme 1.3 parts;
Solubilizing agent 2 parts;
1.3 parts, sulphur.
Preparation method is: after being mixed by all components, put into the container with agitator, stirring of repeatedly packing, vacuum defoamation, maturation, moulding, sulfuration is carried out after stirring, curing temperature is 150 ~ 160 DEG C, and the time is 10 ~ 14 minutes, and board pressure is 15Mpa.
Embodiment 3: a kind of water swelling rubber material, comprises following component:
Mark 102 parts, glue;
Carbon black 22 parts;
Nanometer strengthening agent 23 parts;
Water-absorbing resin 18 parts;
Rubber powder 22 parts;
7 parts, zinc oxide;
Stearic acid 1.7 parts;
Altax 0.6 part;
Accelerator NS 0.7 part;
Mould inhibitor 1.2 parts;
Anti-creme 1.7 parts;
Solubilizing agent 5 parts;
1.7 parts, sulphur.
Preparation method is: after being mixed by all components, put into the container with agitator, stirring of repeatedly packing, vacuum defoamation, maturation, moulding, sulfuration is carried out after stirring, curing temperature is 150 ~ 160 DEG C, and the time is 10 ~ 14 minutes, and board pressure is 15Mpa.
The performance of water swelling rubber material of the present invention is in table 1.
Water swelling rubber material property in table 1 embodiment 1-3.
Embodiment | Tensile strength (Mpa) | Elongation at break (%) | Shore hardness | Expansion rate of water absorption (%) |
1 | 6.5 | 785 | 58 | 350 |
2 | 6.3 | 755 | 54 | 320 |
3 | 6.2 | 754 | 55 | 323 |
As mentioned above, although represented with reference to specific preferred embodiment and described the present invention, it shall not be construed as the restriction to the present invention self.Under the spirit and scope of the present invention prerequisite not departing from claims definition, various change can be made in the form and details to it.
Claims (3)
1. a water swelling rubber material, is characterized in that comprising following component:
With parts by weight.
2. water swelling rubber material according to claim 1, is characterized in that comprising following component:
3. the preparation method of water swelling rubber material according to claim 1 and 2, it is characterized in that: after all components is mixed, put into the container with agitator, repeatedly to pack stirring, vacuum defoamation, maturation, moulding, sulfuration is carried out after stirring, curing temperature is 150 ~ 160 DEG C, and the time is 10 ~ 14 minutes, and board pressure is 15MPa.