CN103938338B - A kind of thin red Buddhist nun's anti-ultraviolet fabric and production method thereof - Google Patents
A kind of thin red Buddhist nun's anti-ultraviolet fabric and production method thereof Download PDFInfo
- Publication number
- CN103938338B CN103938338B CN201410111481.3A CN201410111481A CN103938338B CN 103938338 B CN103938338 B CN 103938338B CN 201410111481 A CN201410111481 A CN 201410111481A CN 103938338 B CN103938338 B CN 103938338B
- Authority
- CN
- China
- Prior art keywords
- buddhist nun
- red buddhist
- fabric
- thin red
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of thin red Buddhist nun's anti-ultraviolet fabric and production method thereof, the production method of described thin red Buddhist nun's anti-ultraviolet fabric comprises the steps: the preparation of (1) yarn: all adopt thin red Buddhist nun's yarn through broadwise; (2) weaving grey cloth: ready yarn is woven into grey cloth by the equipment of weaving cotton cloth; (3) dye; Through oven for drying after grey cloth dyes in dyeing machine; (4) shape: by dyeing after cloth flood in the dipping tank that maceration extract is housed, post-drying; (5) press polish: the fabric after shaping and drying carries out press polish process through calender.Production method of the present invention, saves coating procedure, decreasing pollution, energy-saving and cost-reducing, environmental and reduce costs.Thin red Buddhist nun's anti-ultraviolet fabric of the present invention, obtain through special setting process, multiple color from shallow to deep can have light weight concurrently, expect thin and direct high ultraviolet resistance.Add thin dawn Buddhist nun yarn fabric especially the thin red Buddhist nun's fabric of 20D purposes and develop the efficient antiultraviolet field of cloister fabric.
Description
Technical field
The present invention relates to a kind of fabric and production method thereof, particularly relate to a kind of anti-ultraviolet fabric and production method thereof.
Background technology
On market, existing ultraviolet-resistant fabric need reach certain thickness usually, stops penetrability and the reflectivity of solar ultraviolet, but can increase fabric thickness, affect ready-made clothes weight, reduces wearing comfort.In recent years, although also there are some companies to release the cloister fabric with anti-ultraviolet function, but it reaches preventing ultraviolet effect by coating technology, coating procedure can produce certain pollution to environment on the one hand, increase cost, this technology of another aspect is produced its antiultraviolet index of fabric obtained and is also only had 30+, and color is generally dark system, namely belongs to general ultraviolet-resistant fabric.
Summary of the invention
Instant invention overcomes the deficiencies in the prior art, one of technical problem to be solved by this invention is to provide a kind of production method of thin red Buddhist nun's anti-ultraviolet fabric.
Two of technical problem to be solved by this invention is to provide a kind of thin red Buddhist nun's anti-ultraviolet fabric.
For achieving the above object, the technical solution used in the present invention is: a kind of production method of thin red Buddhist nun's anti-ultraviolet fabric, is characterized in that, comprise the steps:
(1) preparation of yarn: all adopt thin red Buddhist nun's yarn through broadwise;
(2) weaving grey cloth: ready yarn is woven into grey cloth by the equipment of weaving cotton cloth;
(3) dye; Through oven for drying after grey cloth dyes in dyeing machine;
(4) shape: by dyeing after cloth flood in the dipping tank that maceration extract is housed, post-drying;
(5) press polish: the fabric after shaping and drying carries out press polish process through calender;
Described maceration extract is made up of by weight following component:
Preferably, the specification of described yarn is 20D, single thread F number scope 10-30.
Preferably, select suitable organizational form during weaving grey cloth, make the coverage coefficient of described grey cloth reach 70-90%.
Preferably, during weaving grey cloth, control through close scope: 220T/inch-260T/inch, filling density scope: 160T/inch-200T/inch.
Preferably, in described fixating shape step, after dyeing, the dip time of cloth in maceration extract is 10-30 second, and stoving temperature is 150-180 DEG C, cures time 30-60s.
Preferably, in described calendaring step, control temperature: 150 DEG C-180 DEG C, pressure: 220N-290N.
In addition, present invention also offers a kind of thin red Buddhist nun's anti-ultraviolet fabric, adopt said method to be prepared from.
Preferably, the UPF value >=50+ of described thin red Buddhist nun's anti-ultraviolet fabric.
Preferably, UVA transmissivity≤5% of described thin red Buddhist nun's anti-ultraviolet fabric.
The invention solves the defect existed in background technology, there is following beneficial effect:
1. thin red Buddhist nun's anti-ultraviolet fabric of the present invention, obtain through special setting process, multiple color from shallow to deep can have light weight concurrently, expect thin and direct high ultraviolet resistance.Solve traditional technical barrier, add thin dawn Buddhist nun yarn fabric especially the thin red Buddhist nun's fabric of 20D purposes and develop the efficient antiultraviolet field of cloister fabric.
2. controlled in the selection of yams, organizational form, setting temperature and press polish parameter especially respectively, the antiultraviolet grade of fabric can be improved further.Tested by professional institution, by the antiultraviolet grade of fabric, >=50+ can be brought up to by existing common 30+.
3. production method of the present invention, owing to saving coating procedure, can decreasing pollution, energy-saving and cost-reducing, environmental and reduce costs.
Detailed description of the invention
In conjunction with detailed description of the invention, the present invention is further detailed explanation now.
Embodiment 1
A production method for thin red Buddhist nun's anti-ultraviolet fabric, comprises the steps:
(1) preparation of yarn: all adopt thin red Buddhist nun's yarn through broadwise, and the specification of yarn is 20D, single thread F number scope 10-30.Select above-mentioned yarn to be conducive to reducing gap between fabric yarn, fabric penetrability when Ultraviolet radiation is reduced.
(2) weaving grey cloth: ready yarn is woven into grey cloth by the equipment of weaving cotton cloth.This step is routine techniques, and special feature is: select suitable organizational form during weaving grey cloth, make the coverage coefficient of grey cloth reach 70-90%.The selection of organizational form can be any one in conventional organization form, such as plain weave, twill, jacquard weave.Increase fabric unit coverage rate, fabric penetrability when Ultraviolet radiation is reduced.In addition, special feature is also: during weaving grey cloth, control best density proportioning, through close scope: 200T/inch-240T/inch, filling density scope: 150T/inch-200T/inch, to reduce gap between yarn, makes fabric penetrability when Ultraviolet radiation reduce.
(3) dye; Through oven for drying after grey cloth dyes in dyeing machine.This step is routine techniques.Contaminate color for blue.
(4) shape: cloth after dyeing is flooded 10-30 second, 150-180 DEG C of oven-baked 30-60s afterwards in the dipping tank that maceration extract is housed.Wherein, maceration extract is made up of by weight following component:
Obviously, maceration extract, according to above-mentioned formula, can adopt industry universal method to be prepared from.
(5) press polish: the fabric after shaping and drying carries out press polish process through calender, calendering temperature: 150 DEG C-180 DEG C, pressure roll pressure: 220N-290N, obtains a kind of thin red Buddhist nun's anti-ultraviolet fabric.
Embodiment 2
A production method for thin red Buddhist nun's anti-ultraviolet fabric, is with the difference of embodiment 1: contaminate color for blue.Maceration extract is made up of by weight following component:
Obviously, maceration extract, according to above-mentioned formula, can adopt industry universal method to be prepared from.
The present embodiment method is adopted to obtain corresponding thin red Buddhist nun's anti-ultraviolet fabric.
Embodiment 3
A production method for thin red Buddhist nun's anti-ultraviolet fabric, is with the difference of embodiment 1: contaminate color for yellow.Maceration extract is made up of by weight following component:
Obviously, maceration extract, according to above-mentioned formula, can adopt industry universal method to be prepared from.
The present embodiment method is adopted to obtain corresponding thin red Buddhist nun's anti-ultraviolet fabric.
UPF numerical value and the transmissivity to UVA in sunshine thereof are tested respectively to thin red Buddhist nun's anti-ultraviolet fabric of embodiment 1-3.Method of testing and measurement result, see the following form 1:
Table 1
| Test event | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| UPF value (EN13758-1) | ≥50+ | ≥50+ | ≥50+ |
| UVA transmissivity % (EN13758-1) | ≤5％ | ≤5％ | ≤5％ |
It should be noted that, yarn material can select the corresponding material that the industry is general, concrete, and in embodiment 1-3, the yarn material that inventor selects is terylene.Water-proof aagent, drying bleeding agent, waterproof and oilproof anti-soil agent, defoamer and uvioresistant finishing agent also all can select the corresponding raw material that the industry is general.Concrete, in embodiment 1-3, what inventor selected is following raw material: described water-proof aagent is that Huntsman Corporation produces, the trade mark 2049037; Drying bleeding agent is that solar corona company produces, the trade mark 2049854; Waterproof and oilproof anti-soil agent is that Huntsman Corporation produces, the trade mark 2049036; Defoamer is that He Tai company produces, the trade mark 2059998; Uvioresistant finishing agent is that Huntsman Corporation produces, the trade mark 2980570.
Above according to desirable embodiment of the present invention for enlightenment, by above-mentioned description, related personnel in the scope not departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content on description, must determine technical scope according to right.
Claims (9)
1. a production method for thin red Buddhist nun's anti-ultraviolet fabric, is characterized in that, comprise the steps:
(1) preparation of yarn: all adopt thin red Buddhist nun's yarn through broadwise;
(2) weaving grey cloth: ready yarn is woven into grey cloth by the equipment of weaving cotton cloth;
(3) dye; Through oven for drying after grey cloth dyes in dyeing machine;
(4) shape: by dyeing after cloth flood in the dipping tank that maceration extract is housed, post-drying;
(5) press polish: the fabric after shaping and drying carries out press polish process through calender;
Described maceration extract is made up of by weight following component:
2. the production method of a kind of thin red Buddhist nun's anti-ultraviolet fabric according to claim 1, is characterized in that: the specification of described yarn is 20D, single thread F number scope 10-30.
3. the production method of a kind of thin red Buddhist nun's anti-ultraviolet fabric according to claim 1, is characterized in that: select suitable organizational form during weaving grey cloth, make the coverage coefficient of described grey cloth reach 70-90%.
4. the production method of a kind of thin red Buddhist nun's anti-ultraviolet fabric according to claim 1, is characterized in that: during weaving grey cloth, control through close scope: 220T/inch-260T/inch, filling density scope: 160T/inch-200T/inch.
5. the production method of a kind of thin red Buddhist nun's anti-ultraviolet fabric according to claim 1, is characterized in that: in described fixating shape step, and after dyeing, the dip time of cloth in maceration extract is 10-30 second, and stoving temperature is 150-180 DEG C, cures time 30-60s.
6. the production method of a kind of thin red Buddhist nun's anti-ultraviolet fabric according to claim 1, is characterized in that: in described calendaring step, control temperature: 150 DEG C-180 DEG C, pressure: 220N-290N.
7. thin red Buddhist nun's anti-ultraviolet fabric, is characterized in that: adopt the method described in any one of claim 1-6 produce and obtain.
8. the thin red Buddhist nun's anti-ultraviolet fabric of one according to claim 7, is characterized in that: UPF value >=50+.
9. the thin red Buddhist nun's anti-ultraviolet fabric of one according to claim 8, is characterized in that: UVA transmissivity≤5%.