CN107119405A - A kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics - Google Patents
A kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics Download PDFInfo
- Publication number
- CN107119405A CN107119405A CN201710532394.9A CN201710532394A CN107119405A CN 107119405 A CN107119405 A CN 107119405A CN 201710532394 A CN201710532394 A CN 201710532394A CN 107119405 A CN107119405 A CN 107119405A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- ultraviolet resistance
- preparation
- desizing
- dyestuff
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics, comprise the following steps：By in fabric debatching to cloth car, 20D woven fabrics are prepared；The 20D woven fabrics are subjected to desizing and washing, washer wrinkle fabric is obtained；Cloth dyeing will be washed using KN600 types overflow dye vat, stained clot-h is obtained；Stained clot-h is shaped, 20D sizing woven fabrics are obtained；20D sizing woven fabrics are carried out, coating clot carries out press polish processing, packed afterwards, prepares for improving ultraviolet resistance 20D woven fabrics.Compared with traditional handicraft, the 20D woven fabric protective values that the present invention is worked it out are obviously improved.
Description
Technical field
The invention belongs to Textile Engineering field, specifically, it is related to a kind of for improving ultraviolet resistance 20D woven fabrics
Preparation method.
Background technology
Sunproof clothes, also referred to as " skin clothing ", are first begin to prevalence in 2007 in the U.S., subsequently enter China, start big
It is applied among outdoor products more, is then transferred to march " tidal current limit " by the favor of women.
The main function of sunproof clothes is to prevent the direct irradiation of solar ultraviolet, and function is identical with parasols.Its principle
It is that sun-proof auxiliary agent is with the addition of in cloth --- uvioresistant finishing agent, the ultraviolet that it can be absorbed to clothes is transformed into separately
A kind of outer material, reaches anti-sunlight function；Also it is to be combined using ceramic with fiber to have some sun-proof clothes, increases garment surface
Reflection and scattering process to ultraviolet, prevent ultraviolet from passing through fibre damage human body skin.
Good sun-proof cloth can not only antiultraviolet, moreover it is possible to sweat is directed at rapidly to fabric face, and dried quickly；And
Cloth inferior then moisture absorption, poor air permeability, wear easily allow people not feel well or even seal out prickly heat for a long time.Product quality on the market
Very different, the situation that businessman is turned on the common fabric clothes of sun-proof banner sale is even more of common occurrence, most of injection knowledge
Sunproof clothes amusement is much larger than actual utility.
Theoretically, the color of clothes is deeper, and its ultraviolet protection performance is higher, but dark clothes are more easy to heat absorption,
It should not wear long.Preferable sun-proof clothes promote mainly peony or navy chemical fibre quality, can be big because red visible ripple is most long
Amount absorbs the ultraviolet in daylight, and protection skin preserves from, and this effect of the clothes of other colors is substantially weaker.With regard to quality
For, in chemical fibre, terylene>Polyamide fibre>Synthetic cotton, silk：In natural fiber, flax>Hemp>Staple.
A research report of the radiation protection committee of Britain is pointed out：Anti-sunlight function it is worst be lurid cotton goods,
Its SPF is only 7, soaks rear sun-proof result and drops to 4.In addition, the SPF of cream-coloured cotton goods is 9, white cotton
Although SPF up to 33-57, the clothes being made of this material, in this case it is still possible to shone the people of sensitive
Wound.
The ultraviolet resistance effect that traditional handicraft is processed is poor, it is difficult to up to the requirement of consumer.
The content of the invention
In view of this, the problem of present invention is directed to above-mentioned is used to improve ultraviolet resistance 20D woven fabrics there is provided one kind
Preparation method, UPF >=40+ of the 20D woven fabrics prepared, UVA≤5%, with this good outside line protection effect.
In order to solve the above-mentioned technical problem, it is used to improve ultraviolet resistance 20D woven fabrics the invention discloses a kind of
Preparation method, comprises the following steps：
Step 1, debatching：By in fabric debatching to cloth car, 20D woven fabrics are prepared；
Step 2, desizing：The 20D woven fabrics are subjected to desizing and washing, washer wrinkle fabric is obtained；
Step 3, dyeing：Using KN600 types overflow dye vat by the washing cloth dyeing obtained by step 2, stained clot-h is obtained；
Step 4, sizing：Step 3 gained stained clot-h is shaped, 20D sizing woven fabrics are obtained；
Step 5, press polish：The 20D sizing woven fabrics that step 4 is prepared are carried out, and coating clot carries out press polish processing,
Packed, prepared for improving ultraviolet resistance 20D woven fabrics afterwards.
Further, the auxiliary agent used in the desizing processes in step 2 includes following component：NaOH6-10g/L, essence
Practice agent 1-3g/L, deoil clever 0.5-1.5g/L, bleeding agent 0.5-1.5g/L.
Further, the desizing condition in step 2 is：90-110 DEG C is warming up to 2 DEG C/min speed, 25-35 is incubated
Minute, 75-85 DEG C is then cooled to, is washed.
Further, the dyestuff in step 3 includes following component：Scattered orchid 0.1%-0.3%, disperse yellow 0.2%-
0.4%, Disperse Leveler 0.6-1g/L, glacial acetic acid 0.1-0.5g/L；Ultraviolet P liquid 1%-5%.
Further, the mass concentration of glacial acetic acid is 100%, and ultraviolet P liquid is the thunder mountain P liquid difficult to understand of Clariant.
Further, the dyeing condition in step 3 is：The dyestuff is first warming up to by 75- with 2 DEG C/min heating rate
85 DEG C, the dyestuff is then warming up to 125-135 DEG C with 1 DEG C/min heating rate, 25-35min is incubated, finally will be described
Dyestuff is cooled to 75-85 DEG C；Dyeing pressure is 1.0-1.4kg/cm2；Cloth speed is 280-320m/min；Torsion 65-75 ￠；Bath amount
1900-2100L；Bath raio 1:12-1:18.
Further, the setting temperature in step 4 is 155-165 DEG C, and shaping time is 25-35s.
Further, the press polish treatment conditions in step 5 are：With 15-25m/min speed, pressed under the conditions of 120 DEG C
Light processing.
Compared with prior art, the present invention can be obtained including following technique effect：
1) compared with traditional handicraft, the 20D woven fabric protective values that the present invention is worked it out are obviously improved.
2) present invention is used in KN600 type overflow dye vats plus ultraviolet, then carries out press polish processing；Clothes are made to compare simple stain
More preferable feel, and keep good airing function.
Certainly, any product for implementing the present invention it is not absolutely required to while reaching all the above technique effect.
Embodiment
Describe embodiments of the present invention in detail below in conjunction with embodiment, thereby to the present invention how application technology hand
Section can fully understand and implement according to this to solve technical problem and reach the implementation process of technology effect.
The invention discloses a kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics, comprise the following steps：
Step 1, debatching：By in fabric debatching to cloth car, 20D woven fabrics are prepared；
Step 2, desizing：The 20D woven fabrics are subjected to desizing and washing, washer wrinkle fabric is obtained；
Wherein, the auxiliary agent used in the desizing processes includes following component：NaOH 8g/L, scouring agent 2g/L, spirit of deoiling
1g/L, bleeding agent 1g/L；100 DEG C are warming up to 2 DEG C/min speed, 30 minutes is incubated, then cools to 80 DEG C and washed,
Prepare washer wrinkle fabric；
Step 3, dyeing：By the washing cloth dyeing obtained by step 2, stained clot-h is obtained；
Wherein, in the dyeing course, using KN600 type overflow dye vats, dyestuff includes following component：Scattered orchid 0.1%-
0.3% (o.w.f), disperse yellow 0.2%-0.4% (o.w.f), Disperse Leveler 0.6-1g/L, Hac (mass concentration is 100%)
0.1-0.5g/L；Ultraviolet P liquid 1%-5%, are first warming up to 75-85 DEG C, then with 2 DEG C/min heating rate by the dyestuff
The dyestuff is warming up to 125-135 DEG C with 1 DEG C/min heating rate, 30min is incubated, is finally cooled to the dyestuff
75-85℃；The ultraviolet P liquid is the thunder mountain P liquid difficult to understand of Clariant.
Key assistant is ultraviolet P liquid in this method, and the year-on-year general ultraviolet of this branch ultraviolet is with after conventional method operation
UPF (UPF) can slightly higher 5-10.
Dyeing pressure is 1.0-1.4kg/cm2；Cloth speed is 280-320m/min；Torsion 65-75 ￠；Bath amount 1900-
2100L；Bath raio 1:12-1:18；
Step 4, sizing：Step 3 gained stained clot-h is shaped, 20D sizing woven fabrics are obtained；Setting temperature is 155-
165 DEG C, shaping time is 25-35s；
Step 5, press polish：The 20D sizing woven fabrics that step 4 is prepared are carried out, coating clot, with 15-25m/min speed
Rate, press polish processing is carried out under the conditions of 115-125 DEG C, is packed afterwards, is prepared for improving ultraviolet resistance 20D
Woven fabric.Pass through the different final styles for determining 115-125 DEG C of temperature progress press polish to feel cloth of experiment, ultraviolet protection effect
Fruit is all optimal.Such as temperature is too low, and DeGrain, the too high cloth cover of temperature is too bright, and feel is partially hard.
Embodiment 1
A kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics, comprises the following steps：
Step 1, debatching：By in fabric debatching to cloth car, 20D woven fabrics are prepared；
Step 2, desizing：The 20D woven fabrics are subjected to desizing and washing, washer wrinkle fabric is obtained；
Wherein, the auxiliary agent used in the desizing processes includes following component：NaOH 6-10g/L, scouring agent 1-3g/L,
Deoil clever 0.5-1.5g/L, bleeding agent 0.5-1.5g/L；90-110 DEG C, 25-35 points of insulation are warming up to 2 DEG C/min speed
Clock, then cools to 75-85 DEG C and is washed, prepare washer wrinkle fabric；
Step 3, dyeing：By the washing cloth dyeing obtained by step 2, stained clot-h is obtained；
Wherein, in the dyeing course, using KN600 type overflow dye vats, dyestuff includes following component：Scattered orchid 0.2%
(o.w.f), disperse yellow 0.3% (o.w.f), Disperse Leveler 0.8g/L, HAC (100%) 0.3g/L；Ultraviolet P liquid 3%, first
The dyestuff is warming up to 80 DEG C with 2 DEG C/min heating rate, then the dyestuff heated up with 1 DEG C/min heating rate
To 130 DEG C, 30min is incubated, the dyestuff is finally cooled to 80 DEG C；
Dyeing pressure is 1.2kg/cm2；Cloth speed is 300m/min；The ￠ of torsion 70；Bath amount 2000L；Bath raio 1：15；
Step 4, sizing：Step 3 gained stained clot-h is shaped, 20D sizing woven fabrics are obtained；Setting temperature is 160 DEG C,
Shaping time is 30s；
Step 5, press polish：The 20D sizing woven fabrics that step 4 is prepared are carried out, coating clot, with 20m/min speed,
Press polish processing is carried out under the conditions of 120 DEG C, is packed afterwards, is prepared for improving ultraviolet resistance 20D woven fabrics.
Embodiment 2
A kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics, comprises the following steps：
Step 1, debatching：By in fabric debatching to cloth car, 20D woven fabrics are prepared；
Step 2, desizing：The 20D woven fabrics are subjected to desizing and washing, washer wrinkle fabric is obtained；
Wherein, the auxiliary agent used in the desizing processes includes following component：NaOH 6g/L, scouring agent 3g/L, spirit of deoiling
0.5g/L, bleeding agent 1.5g/L；90 DEG C are warming up to 2 DEG C/min speed, 35 minutes is incubated, then cools to 75 DEG C and enter water-filling
Wash, prepare washer wrinkle fabric；
Step 3, dyeing：By the washing cloth dyeing obtained by step 2, stained clot-h is obtained；
Wherein, in the dyeing course, using KN600 type overflow dye vats, dyestuff includes following component：Scattered orchid 0.1%
(o.w.f), disperse yellow 0.4% (o.w.f), Disperse Leveler 0.6g/L, HAC (100%) 0.5g/L；Ultraviolet P liquid 1%, first
The dyestuff is warming up to 85 DEG C with 2 DEG C/min heating rate, then the dyestuff heated up with 1 DEG C/min heating rate
To 125 DEG C, 30min is incubated, the dyestuff is finally cooled to 85 DEG C；
Dyeing pressure is 1.0kg/cm2；Cloth speed is 320m/min；The ￠ of torsion 65；Bath amount 2100L；Bath raio 1:12；
Step 4, sizing：Step 3 gained stained clot-h is shaped, 20D sizing woven fabrics are obtained；Setting temperature is 155 DEG C,
Shaping time is 35s；
Step 5, press polish：The 20D sizing woven fabrics that step 4 is prepared are carried out, coating clot, with 15m/min speed,
Press polish processing is carried out under the conditions of 125 DEG C, is packed afterwards, is prepared for improving ultraviolet resistance 20D woven fabrics.
Embodiment 3
A kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics, comprises the following steps：
Step 1, debatching：By in fabric debatching to cloth car, 20D woven fabrics are prepared；
Step 2, desizing：The 20D woven fabrics are subjected to desizing and washing, washer wrinkle fabric is obtained；
Wherein, the auxiliary agent used in the desizing processes includes following component：NaOH 10g/L, scouring agent 1g/L, deoil
Clever 1.5g/L, bleeding agent 0.5g/L；110 DEG C are warming up to 2 DEG C/min speed, 25 minutes is incubated, then cools to 85 DEG C and enter
Water-filling is washed, and prepares washer wrinkle fabric；
Step 3, dyeing：By the washing cloth dyeing obtained by step 2, stained clot-h is obtained；
Wherein, in the dyeing course, using KN600 type overflow dye vats, dyestuff includes following component：Scattered orchid 0.3%
(o.w.f), disperse yellow 0.2% (o.w.f), Disperse Leveler 1g/L, HAC (100%) 0.1g/L；Ultraviolet P liquid 5%, first with 2
DEG C/dyestuff is warming up to 75 DEG C by min heating rate, then the dyestuff is warming up to 1 DEG C/min heating rate
135 DEG C, 30min is incubated, the dyestuff is finally cooled to 75 DEG C；
Dyeing pressure is 1.4kg/cm2；Cloth speed is 280m/min；The ￠ of torsion 75；Bath amount 1900L；Bath raio 1:18；
Step 4, sizing：Step 3 gained stained clot-h is shaped, 20D sizing woven fabrics are obtained；Setting temperature is 165 DEG C,
Shaping time is 25s；
Step 5, press polish：The 20D sizing woven fabrics that step 4 is prepared are carried out, coating clot, with 25m/min speed,
Press polish processing is carried out under the conditions of 115 DEG C, is packed afterwards, is prepared for improving ultraviolet resistance 20D woven fabrics.
Comparative example 1：
Step 1, debatching：By in fabric debatching to cloth car, cold dome 24 hours prepares 20D woven fabrics；
Step 2, desizing：The 20D woven fabrics are conventionally subjected to desizing and washing, washer wrinkle fabric is obtained；
Step 3, dyeing：By the washing cloth dyeing obtained by step 2, stained clot-h is obtained；
Wherein, in the dyeing course, using KN600 type overflow dye vats, dyestuff includes following component：Acid orchid 0.2%,
Indian yellow 0.3%, Disperse Leveler 0.8g/L, HAC (100%) 0.3g/L, 30min is dyed under 100 DEG C of temperature conditionss；
Dyeing pressure is 1.2kg/cm2；Cloth speed is 300m/min；The ￠ of torsion 70；Bath amount 2000L；Bath raio 1：15；
Step 4, sizing：Step 3 gained stained clot-h is shaped, 20D sizing woven fabrics are obtained；Setting temperature is 160 DEG C,
Shaping time is 30s, is prepared for improving ultraviolet resistance 20D woven fabrics.
The ultraviolet resistance for the 20D woven fabrics that embodiment 1-3 is prepared with comparative example 1 is shown in Table 1.
Table 1 (380T conventional nylon cloth is light blue) GB/T18830
Some preferred embodiments of invention have shown and described in described above, but as previously described, it should be understood that invention is not
Form disclosed herein is confined to, the exclusion to other embodiment is not to be taken as, and available for various other combinations, modification
And environment, and can be carried out in invention contemplated scope described herein by the technology or knowledge of above-mentioned teaching or association area
Change., then all should be in the appended power of invention and the change and change that those skilled in the art are carried out do not depart from the spirit and scope of invention
In the protection domain that profit is required.
Claims (8)
1. a kind of preparation method for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that comprise the following steps：
Step 1, debatching：By in fabric debatching to cloth car, 20D woven fabrics are prepared；
Step 2, desizing：The 20D woven fabrics are subjected to desizing and washing, washer wrinkle fabric is obtained；
Step 3, dyeing：Using KN600 types overflow dye vat by the washing cloth dyeing obtained by step 2, stained clot-h is obtained；
Step 4, sizing：Step 3 gained stained clot-h is shaped, 20D sizing woven fabrics are obtained；
Step 5, press polish：The 20D sizing woven fabrics that step 4 is prepared are carried out, and coating clot carries out press polish processing, afterwards
Packed, prepared for improving ultraviolet resistance 20D woven fabrics.
2. the preparation method according to claim 1 for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that
The auxiliary agent used in the desizing processes in step 2 includes following component：NaOH6-10g/L, scouring agent 1-3g/L, spirit of deoiling
0.5-1.5g/L, bleeding agent 0.5-1.5g/L.
3. the preparation method according to claim 1 for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that
Desizing condition in step 2 is：90-110 DEG C is warming up to 2 DEG C/min speed, 25-35 minutes is incubated, then cools to 75-
85 DEG C, washed.
4. the preparation method according to claim 1 for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that
Dyestuff in step 3 includes following component：Scattered orchid 0.1%-0.3%, disperse yellow 0.2%-0.4%, Disperse Leveler 0.6-
1g/L, glacial acetic acid 0.1-0.5g/L；Ultraviolet P liquid 1%-5%.
5. the preparation method according to claim 4 for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that
The mass concentration of glacial acetic acid is 100%, and ultraviolet P liquid is the thunder mountain P liquid difficult to understand of Clariant.
6. the preparation method according to claim 1 for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that
Dyeing condition in step 3 is：First the dyestuff is warming up to 75-85 DEG C with 2 DEG C/min heating rate, then with 1 DEG C/
The dyestuff is warming up to 125-135 DEG C by min heating rate, is incubated 25-35min, the dyestuff finally is cooled into 75-85
℃；Dyeing pressure is 1.0-1.4kg/cm2；Cloth speed is 280-320m/min；Torsion 65-75 ￠；Bath amount 1900-2100L；Bath raio
1:12-1:18。
7. the preparation method according to claim 1 for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that
Setting temperature in step 4 is 155-165 DEG C, and shaping time is 25-35s.
8. the preparation method according to claim 1 for being used to improve ultraviolet resistance 20D woven fabrics, it is characterised in that
Press polish treatment conditions in step 5 are：With 15-25m/min speed, press polish processing is carried out under the conditions of 120 DEG C.