CN103882596A - Elastic core-spun yarn and application thereof - Google Patents
Elastic core-spun yarn and application thereof Download PDFInfo
- Publication number
- CN103882596A CN103882596A CN201210556917.0A CN201210556917A CN103882596A CN 103882596 A CN103882596 A CN 103882596A CN 201210556917 A CN201210556917 A CN 201210556917A CN 103882596 A CN103882596 A CN 103882596A
- Authority
- CN
- China
- Prior art keywords
- fiber
- yarn
- core
- spun yarn
- elastic force
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an elastic core-spun yarn comprising an outer fiber layer and a fiber core wrapped by a covering process. The fiber core is made of spandex or other elastic fibers; the outer fiber layer is made of aramid short fiber or polyethylene short fiber, or made of mixture of aramid short fiber and polyethylene short fiber in any proportion, or made of fiber mixture including aramid short fiber and polyethylene short fiber. The invention further discloses application of the elastic core-spun yarn in textiles. The elastic core-spun yarn has excellent properties, excellent protective performance, better elasticity, and better comfort and flexibility.
Description
Technical field
The present invention relates to a kind of elastic force composite yarn line and application thereof.
Background technology
Often feel is stiff for the textiles that existing aramid fiber or high-strength high-modulus polyethylene (hppe) yarn is made, and comfort is poor, and malfunction causes the sense of user's body uncomfortable, and easily causes operate miss.
Summary of the invention
Technical problem to be solved by this invention is: a kind of elastic force composite yarn line and fabric thereof are provided, are ensureing, under the prerequisite of anti-cutting excellent quality, to ensure comfortable feel.
The technical solution adopted for the present invention to solve the technical problems is: a kind of elastic force composite yarn line, comprise core fiber and outer staple fibre, outer staple fibre is by cored technique parcel core fiber, (core fiber is spandex or other elastic fiberss); Outer layer fiber is aramid fiber short fiber or polyethylene short fiber, or is the blended fiber (arbitrary proportion) for aramid fiber short fiber and polyethylene short fiber or the blended fiber for containing aramid fiber short fiber and these two kinds of fibers of polyethylene short fiber.
The fineness of spandex or other elastic fiberss is 2～2500D, and drafting multiple is 5%-500%.
Average length 12～the 180mm of aramid fiber short fiber or polyethylene short fiber.
Cored technique is fiber in the process of stressed drawing-off twisting simultaneously, imports core fiber, and core fiber is wrapped in to the production process of outer layer fiber core by feed carrier.The twist of twisting is 20～1500 twists/m, twist with the fingers to be S to or Z-direction.
The application of elastic force composite yarn line in yarn, the cored that contains this elastic force composite yarn line, coated or close twisted yarn.
The application of elastic force composite yarn line in yarn fabric, thus composite yarn or there is the cored, coated and close twist yarn braiding and form of this composite yarn.
The invention has the beneficial effects as follows: protection excellent quality, the fabric of braiding is dressed comfortablely simultaneously, and the Protection Product user of order in hazardous environment can comfortable work freely, has greatly improved security and operating efficiency.
Brief description of the drawings
Fig. 1 is the structural representation of embodiments of the invention 1;
Fig. 2 is the structural representation of embodiments of the invention 2;
Fig. 3 is the structural representation of embodiments of the invention 3.
Detailed description of the invention
Embodiment 1
As shown in Figure 1, a kind of elastic force composite yarn line, comprises core fiber 1 and outer layer fiber 2, and outer layer fiber 2 is by cored technique parcel core fiber 1, and core fiber 1 is spandex or other elastic fiberss; Outer layer fiber 2 is aramid fiber short fiber or polyethylene short fiber, or be the blended fiber (arbitrary proportion) for aramid fiber short fiber and polyethylene short fiber, or for containing the blended fiber of a kind of or two kinds of fibers and other fibers in aramid fiber short fiber and these two kinds of fibers of polyethylene short fiber.
The fineness of spandex or other elastic fiberss is 2～2500D, and drafting multiple is 5%-500%.
Cored technique is fiber in the process of stressed drawing-off twisting simultaneously, imports core fiber, and core fiber is wrapped in to the production process of outer layer fiber core by feed carrier.The twist of twisting is 20～1500 twists/m.Twist with the fingers to be S to or Z-direction.
Aramid fiber 1313/spandex core-spun yarn: 1.5D aramid fiber 1313 staple fibre (average length 51mm) is passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is aramid fiber 1313/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
Aramid fiber 1313/Fanglun l414/spandex core-spun yarn: the mixing staple fibre of 1.5D aramid fiber 1313 staple fibre (average length 51mm) and 1.5D Fanglun l414 staple fibre (average length is 51mm) is passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is aramid fiber 1313/Fanglun l414/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
Aramid fiber 1313/anti-flaming viscose/spandex core-spun yarn: the mixing staple fibre of 1.5D aramid fiber 1313 staple fibre (average length 51mm) and 1.5D fire retardant viscose short filament (average length is 51mm) is passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is aramid fiber 1313/anti-flaming viscose/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
Aramid fiber 1313/flame-retardant acrylic fibre/cotton/spandex core-spun yarn: by 1.5D aramid fiber 1313 staple fibre (average length 51mm), the fire-retardant acrylic of 1.5D (average length is 51mm) and the mixing staple fibre of combed cotton pass through blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, changes into spun yarn from fiber, and in one-tenth spun yarn process, it is aramid fiber 1313/flame-retardant acrylic fibre/cotton/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
Aramid fiber 1313/wool/spandex core-spun yarn: the mixing staple fibre of 1.5D aramid fiber 1313 staple fibre (average length 51mm) and wool staple fibre is passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is aramid fiber 1313/wool/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
Fanglun l414/spandex core-spun yarn: 1.5D Fanglun l414 staple fibre (average length 51mm) is passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is Fanglun l414/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
Fanglun l414/polyester fibre/spandex cladded yarn: 1.5D Fanglun l414 staple fibre (average length 51mm) and 1.5D polyester staple fiber (average length 51mm) are passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is Fanglun l414/polyester fibre/spandex cladded yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
High-strength high-modulus polyethylene (hppe)/spandex core-spun yarn: the staple fibre of 1.5D high-strength high-modulus polyethylene (hppe) (average length 51mm) is passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is high-strength high-modulus polyethylene (hppe)/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
Fanglun l414/high-strength high-modulus polyethylene (hppe)/spandex core-spun yarn: the staple fibre (average length 51mm) of 1.5D Fanglun l414 staple fibre (average length 51mm) and 1.5D high-strength high-modulus polyethylene (hppe) is passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is Fanglun l414/high-strength high-modulus polyethylene (hppe)/spandex core-spun yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number.
High-strength high-modulus polyethylene (hppe)/polyester fibre/spandex cladded yarn: the staple fibre of 1.5D high-strength high-modulus polyethylene (hppe) (average length 51mm) and 1.5D polyester staple fiber (average length 51mm) are passed through to blowing, comb and parallel cotton fibers prior to spinning, drafting, rove, the mode of spun yarn RING SPINNING, change into spun yarn from fiber, and in one-tenth spun yarn process, it is high-strength high-modulus polyethylene (hppe)/polyester fibre/spandex cladded yarn of 30Ne that the spandex filament cored of the calm and peaceful green wood in Yantai of diameter 50D is become to total number
Embodiment 2
As shown in Figure 2, a kind of coating cotton thread of elastic force composite yarn line, the coating cotton thread taking the elastic force composite yarn line that contains aramid fiber or high-strength high-modulus polyethylene (hppe) in embodiment 1 as core.Product, except the feature of cladded yarn described in having embodiment 1, more combines the diversity of cladding process, brings the superiority in more style/performance to product.
Core cladded yarn is the elastic force composite yarn that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1.
Outer coating cotton thread is short fiber yarn or the filament yarn of thickness 5-200tex, twist with the fingers to be S to or Z-direction.
The radical of outer coating cotton thread is 1-5 root, twist with the fingers to be respectively S to or Z-direction.
Embodiment 3
As shown in Figure 3, a kind of elastic force composite yarn line, to comprise the twisted yarn that closes of the elastic force composite yarn line that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1.Product, except the feature of cladded yarn described in having embodiment 1, more combines the feature of double twisting technique and the performance of other Split Down yarns, brings the superiority in more style/performance to product.
A yarn is the elastic force composite yarn that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1, twist with the fingers to be S to or Z-direction
B yarn is the resistance to elastic force composite yarn that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1, or other short fiber yarn or filament yarns, twists with the fingers to identical with A yarn.
Twine twists with the fingers contrary with B yarn to same A, and the twist is 20-1500 twist/m.
Strand single thread radical is 2-6 root.Described in example 1, contain the elastic force composite yarn of aramid fiber or high-strength high-modulus polyethylene (hppe), can be wherein 1-6 root, and every can be different.
Embodiment 4
A kind of knitted gloves, wherein comprises the elastic force composite yarn line that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1 or the cored that contains the elastic force composite yarn line that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1, wraps up or close twist yarn braiding and form.These gloves can be in providing excellent barrier propterty, and elasticity is better, more comfortable.
This knitted gloves knitting density is 7-18 pin/inch.
This knitted gloves is of a size of 6,7, and 8,9,10, No. 11, length is 100-350mm.
Embodiment 5
A kind of elastic force composite yarn woven fabric, wherein comprises the elastic force composite yarn line that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1 or the cored that contains the elastic force composite yarn line that contains aramid fiber or high-strength high-modulus polyethylene (hppe) described in embodiment 1, wraps up or close twist yarn braiding and form.This fabric can be in providing excellent barrier propterty, and elasticity is better, and comfort level and flexibility ratio are stronger.
The warp count of this woven fabric is 10-250 piece/inch, and weft count is 10-250 piece/inch.The structure of this fabric is plain weave, twill, satin weave, figured check etc.
Claims (5)
1. an elastic force composite yarn line, the core fiber that comprises outer layer fiber and wrap up by cored technique, is characterized in that:
Described core fiber is spandex or other elastic fiberss;
Described outer layer fiber is aramid fiber short fiber or polyethylene short fiber, or is the blended fiber that aramid fiber short fiber and polyethylene short fiber mix with arbitrary proportion, or is the blended fiber that contains aramid fiber short fiber and polyethylene short fiber.
2. a kind of elastic force composite yarn line according to claim 1, is characterized in that: the fineness of described core fiber is 2～2500D, drafting multiple is 5%～500%; Described aramid fiber short fiber or the average length of polyethylene short fiber are 12～180mm.
3. a kind of elastic force composite yarn line according to claim 1, it is characterized in that: described cored technique is that outer layer fiber is in the process of stressed drawing-off twisting simultaneously, import core fiber by feed carrier, and core fiber is wrapped in to outer layer fiber core, the twist of twisting is 20～1500 twists/m, twist with the fingers to be S to or Z-direction.
4. the application of a kind of elastic force composite yarn line claimed in claim 1 in yarn, is characterized in that: described yarn is the cored, coated or close twisted yarn of elastic force composite yarn line described in claim 1.
5. the application of a kind of elastic force composite yarn line claimed in claim 1 in yarn fabric, is characterized in that: described yarn fabric is that yarn braiding claimed in claim 4 forms.