CN103881477A - Anti-counterfeiting printing ink based on up-and-down conversion synergistic luminescence material - Google Patents
Anti-counterfeiting printing ink based on up-and-down conversion synergistic luminescence material Download PDFInfo
- Publication number
- CN103881477A CN103881477A CN201410138745.4A CN201410138745A CN103881477A CN 103881477 A CN103881477 A CN 103881477A CN 201410138745 A CN201410138745 A CN 201410138745A CN 103881477 A CN103881477 A CN 103881477A
- Authority
- CN
- China
- Prior art keywords
- parts
- counterfeiting
- light
- forgery ink
- printing ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses anti-counterfeiting printing ink based on an up-and-down conversion synergistic luminescence material. The anti-counterfeiting printing ink is composed of 27-28 parts of polyurethane acrylate resin, 27-28 parts of polyester acrylic resin, 22-23 parts of tripropylene glycol diacrylate, 17-18 parts of anti-counterfeiting material, 0.7-0.8 part of low molecular weight polyethylene wax, 0.3-0.4 part of polydimethylsiloxane, 1-2 parts of polyether polyester modified polysiloxane, 0.3-0.4 part of photoinitiator and 0.3-0.4 part of adhesion promoter, and the anti-counterfeiting material is a material with synergistic frequency light conversion properties. A mark printed by the anti-counterfeiting printing ink is high in display brightness and strong in identifiability; the anti-counterfeiting printing ink is strong in repeatability, varied in color, capable of greatly improving the anti-counterfeiting performance, strong in confidentiality, good in stability and excellent in physicochemical properties and printability.
Description
Technical field
The present invention relates to a kind of anti-forgery ink that possesses composite anti-fake function, especially adopt the photosensitive anti-forgery ink of rare earth luminescent material as photoactivation compound.
Background technology
Anti-forgery ink (anti-forgery ink) refers to that the ink changing a lot under special conditions is in order to be printed in ticket, product brand and packing, produce visible or sightless mark, by applying different ambient conditions, as forms such as illumination, heating, spectral detection, observe the color change of ink pull, be convenient to verification and prevent from forging, reaching false proof object.Anti-fraud functional compound be one of effective way of improving false proof barrier and factor of assurance.
Rare earth luminously mainly contain at present two kinds of up-conversion luminescence and lower conversion luminescences for false proof theory and method.The theoretical infrared excitation luminescent material corresponding to method of up-conversion luminescence, the theoretical corresponding burst of ultraviolel luminescent material of lower conversion luminescence and method.Infrared excitation luminescent material has the colors such as red, green, yellow, blue by the infrared ray excited visible light colors of sending.Burst of ultraviolel luminescent material divides 2 kinds, one is can send visible ray under short wave ultraviolet light excites, have or not-yellow, orange, red, yellowish green, emerald green, grass green, dark green, bright blue, reddish blue, black, red-orange, red-red, green-grass green, blue-grass green, orange-red, yellow-red, black-red, green-red, blue-red, orange-orange of glow color, indigo plant-green, yellow-yellow, indigo plant-blue, green-yellowish green; Another kind is under long wave ultraviolet light excites, and can send visible ray.It is colourless, yellow, orange, red, green that glow color has etc.Although the multi-selection of its glow color provides better approach for improving antiforge function.But current upper efficiency of conversion is extremely low, even best up-conversion NaYF4:2%Er3+, the upper efficiency of conversion of 18%Yb3+ just has 3%, and this has seriously restricted its application.Affect the display brightness of the mark of anti-forgery ink printing, reduced the identifiability of anti-counterfeiting mark.Chinese invention patent document CN1O1942306B discloses the patent of invention that name is called " having material of cooperative frequency light conversion performance and preparation method thereof and application ", the molecular formula of this material is: YxYby(∑ Ln) zF3,0≤x<1, O<y<1, O<Z≤0.50, Ln be in rare earth element ce, Tm, Er, Ho, Dy, Tb, Gd, Eu, Sm, Nd, Pr any one or several arbitrarily.The preparation method of this material adopts any one in conventional high temperature solid-state method, hydrothermal synthesis method or coprecipitation method.This material has been realized and under upper conversion and quantum-cutting, has been changed two kinds of machine-processed combinations, effectively UV-light and infrared light have been transformed into the visible ray of a certain frequency simultaneously, and have obtained the enhancing that the visible light intensity of this frequency is greater than 2 times, cost is low, simple synthetic method, can manufacture.What this invention was emphasized is this material is in the application of preparing in solar-energy photo-voltaic cell, to its objective is in order solving in the switching process that prior art exists and to produce heat effect, photovoltaic device produced to the problem of infringement; And improve solar-energy photo-voltaic cell efficiency.Can effectively improve anti-forgery ink performance if be applied to anti-forgery ink.But this solar-energy photo-voltaic cell type material is applied to the false proof field of ink, needs feasibility study, and will meet the requirement of physico-chemical property and the printability aspect of ink.
Summary of the invention
In order to solve above-mentioned drawback, technical problem to be solved by this invention is, a kind of anti-forgery ink based on changing up and down collaborative luminescent material is provided, and can effectively improve the quality of anti-counterfeiting performance and anti-counterfeiting mark.In order to solve the problems of the technologies described above, the technical solution used in the present invention is, based on the anti-forgery ink of changing up and down collaborative luminescent material, to be made up of the raw material of following weight part:
27~28 parts of polyurethane acrylate resins, 27~28 parts of polyester acrylate resins, 22~23 parts of tri (propylene glycol) diacrylates, 17~18 parts of anti-fake materials, 0.7~0.8 part of polyethylene low-molecular-weight wax, 0.3~0.4 part of polydimethylsiloxane, 1~2 part, polyether polyester modified organic silicon oxygen alkane, 0.3~0.4 part of light trigger, 0.3~0.4 part of adhesion promoter;
Described anti-fake material adopts the material with cooperative frequency light conversion performance, the molecular formula of this material is: YxYby(∑ Ln) zF3,0≤x<1, O<y<1, O<Z≤0.50, Ln be in rare earth element ce, Tm, Er, Ho, Dy, Tb, Gd, Eu, Sm, Nd, Pr any one or several arbitrarily.
This patent quotes in full the patent of invention that the disclosed name of Chinese invention patent document CN1O1942306B is called " having material of cooperative frequency light conversion performance and preparation method thereof and application ".
Its preparation method comprises the steps:
The first step: by polyurethane acrylate resin and polyester acrylate resin mixing and stirring according to quantity;
Second step: anti-fake material was ground to 300~400 mesh sieves, add according to quantity anti-fake material and polyethylene low-molecular-weight wax under sieve, polydimethylsiloxane under whipped state, and continued to stir 30 minutes;
The 3rd step: under the condition of 65 ℃ of constant temperature, above-mentioned material is ground two to four times;
The 4th step: add according to quantity tri (propylene glycol) diacrylate and light trigger under whipped state, continue to stir 30 minutes;
The 5th step: add polyether polyester modified organic silicon oxygen alkane, adhesion promoter under whipped state, continue to stir 30 minutes, make anti-forgery ink.
The using method of described anti-forgery ink is, anti-forgery ink adopts silk-screen mode to be printed in and on anti-counterfeiting product, forms anti-counterfeiting mark, use UV-light and infrared light as excitaton source, anti-counterfeiting mark to be excited simultaneously, described UV-light is the UV-light of 340~400nm, and described infrared light is the infrared light of 970~l064nm or 1500~1600nm.
Further, the read value group of the spectrogram after exciting using anti-counterfeiting mark is as anti-forge cipher.As false proof means accurately and reliably, meet the final requirement of identifying.
Beneficial effect of the present invention is, 1. adopts the display brightness of mark of this anti-forgery ink printing high, and identifiability is strong; 2. circulation ratio is strong, variable color is various, greatly improved anti-counterfeiting performance, strong security; 3. there is satisfactory stability; 4. the physico-chemical property of ink is good, and its density, fineness, transparency, glossiness, photostabilization, thermotolerance and acid-and base-resisting, water, solvent (alcohol) property all meet the demands; 5. the printability of ink is good, and viscosity, tackiness, thixotropy, drying property etc. are suitable for presswork.
Below in conjunction with embodiment, the present invention will be further described.
Embodiment
The described anti-forgery ink based on changing up and down collaborative luminescent material, raw material by following weight part forms: 27 parts of polyurethane acrylate resins, 27 parts of polyester acrylate resins, 22 parts of tri (propylene glycol) diacrylates, 17 parts of anti-fake materials, 0.7 part of polyethylene low-molecular-weight wax, 0.3 part of polydimethylsiloxane, 1 part, polyether polyester modified organic silicon oxygen alkane, 0.3 part of light trigger, 0.3 part of adhesion promoter;
Its preparation method comprises the steps:
The first step: by polyurethane acrylate resin and polyester acrylate resin mixing and stirring according to quantity;
Second step: anti-fake material was ground to 300~400 mesh sieves, add according to quantity anti-fake material and polyethylene low-molecular-weight wax under sieve, polydimethylsiloxane under whipped state, and continued to stir 30 minutes;
The 3rd step: under the condition of 65 ℃ of constant temperature, above-mentioned material is ground two to four times;
The 4th step: add according to quantity tri (propylene glycol) diacrylate and light trigger under whipped state, continue to stir 30 minutes;
The 5th step: add polyether polyester modified organic silicon oxygen alkane, adhesion promoter under whipped state, continue to stir 30 minutes, make anti-forgery ink.
Anti-fake material described in aforesaid method adopts the fluorochemical with cooperative frequency light conversion performance, and molecular formula is Yb
0.90er
0.10f
3.Polyether polyester modified organic silicon oxygen alkane adopts 1080,1090 series product of the energy chemical industry that rubs.Described light trigger adopts 11732-hydroxy-2-methyl-1-phenyl-acetone.Described adhesion promoter adopts Hangzhou Jesse to block the epoxy modified silicone polymerization compound that Chemical Co., Ltd. produces, product type JSC-1645.
The anti-forgery ink that makes adopts silk-screen mode to be printed in and on anti-counterfeiting product, forms anti-counterfeiting mark, use UV-light and infrared light as excitaton source, anti-counterfeiting mark to be excited simultaneously, described UV-light is the UV-light of 340~400nm, and described infrared light is the infrared light of 970~l064nm or 1500~1600nm.
The anti-forgery ink making prints the check of decoration quality of item Supervision Test Center through country, and test basis is " anti-counterfeiting technology products production license licensed licenser licence detailed rules for the implementation (two) (anti-fake material part) ", and check conclusion is " qualified ".Its Specifeca tion speeification is as shown in the table:
The above-mentioned implementation that the present invention describes is only for technical scheme of the present invention is clearly described, and can not be interpreted as the present invention is made to any restriction.The present invention has known multiple substituting or distortion in the art, not departing under the prerequisite of essential meaning of the present invention, all falls into protection scope of the present invention.
Claims (4)
1. the anti-forgery ink based on changing up and down collaborative luminescent material, is characterized in that, is made up of the raw material of following weight part:
27~28 parts of polyurethane acrylate resins, 27~28 parts of polyester acrylate resins, 22~23 parts of tri (propylene glycol) diacrylates, 17~18 parts of anti-fake materials, 0.7~0.8 part of polyethylene low-molecular-weight wax, 0.3~0.4 part of polydimethylsiloxane, 1~2 part, polyether polyester modified organic silicon oxygen alkane, 0.3~0.4 part of light trigger, 0.3~0.4 part of adhesion promoter;
Described anti-fake material adopts the material with cooperative frequency light conversion performance, the molecular formula of this material is: YxYby(∑ Ln) zF3,0≤x<1, O<y<1, O<Z≤0.50, Ln be in rare earth element ce, Tm, Er, Ho, Dy, Tb, Gd, Eu, Sm, Nd, Pr any one or several arbitrarily.
2. the preparation method based on changing up and down the anti-forgery ink of working in coordination with luminescent material, is characterized in that, comprises the steps:
The first step: by polyurethane acrylate resin and polyester acrylate resin mixing and stirring according to quantity;
Second step: anti-fake material was ground to 300~400 mesh sieves, add according to quantity anti-fake material and polyethylene low-molecular-weight wax under sieve, polydimethylsiloxane under whipped state, and continued to stir 30 minutes;
The 3rd step: under the condition of 65 ℃ of constant temperature, above-mentioned material is ground two to four times;
The 4th step: add according to quantity tri (propylene glycol) diacrylate and light trigger under whipped state, continue to stir 30 minutes;
The 5th step: add polyether polyester modified organic silicon oxygen alkane, adhesion promoter under whipped state, continue to stir 30 minutes, make anti-forgery ink.
3. the using method based on changing up and down the anti-forgery ink of working in coordination with luminescent material, it is characterized in that, anti-forgery ink adopts silk-screen mode to be printed in and on anti-counterfeiting product, forms anti-counterfeiting mark, use UV-light and infrared light as excitaton source, anti-counterfeiting mark to be excited simultaneously, described UV-light is the UV-light of 340~400nm, and described infrared light is the infrared light of 970~l064nm or 1500~1600nm.
4. the using method based on changing up and down the anti-forgery ink of working in coordination with luminescent material as claimed in claim 3, is characterized in that, the read value group of the spectrogram after exciting using anti-counterfeiting mark is as anti-forge cipher.