CN103881143B - 一种莫来石复合型阻燃剂 - Google Patents

一种莫来石复合型阻燃剂 Download PDF

Info

Publication number
CN103881143B
CN103881143B CN201410057042.9A CN201410057042A CN103881143B CN 103881143 B CN103881143 B CN 103881143B CN 201410057042 A CN201410057042 A CN 201410057042A CN 103881143 B CN103881143 B CN 103881143B
Authority
CN
China
Prior art keywords
mullite
fire retardant
composite fire
parts
ammonium polyphosphate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410057042.9A
Other languages
English (en)
Other versions
CN103881143A (zh
Inventor
何益庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Super material technology (Shenzhen) Co., Ltd.
Original Assignee
Tongling Xiangyun Fire Fighting Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Xiangyun Fire Fighting Technology Co Ltd filed Critical Tongling Xiangyun Fire Fighting Technology Co Ltd
Priority to CN201410057042.9A priority Critical patent/CN103881143B/zh
Publication of CN103881143A publication Critical patent/CN103881143A/zh
Application granted granted Critical
Publication of CN103881143B publication Critical patent/CN103881143B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种莫来石复合型阻燃剂，其特征在于：由下列重量份的原料组成：莫来石10-15份、纳米钛白粉5-10份、硅藻土5-8份、氯化石蜡5-8份、季戊四醇50-60份、多聚磷酸铵20-30份、四硼酸钠3-5份、硼砂5-30份、空心微珠10-25份。本发明以纳米莫来石与季戊四醇、多聚磷酸铵混合制成复合型阻燃剂，莫来石具有耐高温、强度高、抗化学腐蚀性好、节能效果显著等特点，本发明的阻燃剂组分简单合理、低烟、使用量少、阻燃效果好、无毒、无污染。

Description

一种莫来石复合型阻燃剂
技术领域
本发明涉及阻燃产品技术领域，尤其涉及一种莫来石复合型阻燃剂。
背景技术
防火剂又称阻燃剂和耐火剂，能保护塑料制品、纺织品、木材等使不着火或使火焰迟缓蔓延的药剂。主要由于药剂能生成较多量的不可燃气体或药剂薄膜不能燃烧而达到防火的目的。现实中，很多产品都需要具有阻燃性能，如阻燃塑料等产品，这就需要有阻燃剂。现有的阻燃剂组成复杂，价格高，使用量大，阻燃效果欠佳，而且大部分还有剧毒，有污染。因此，使用时要考虑防火效果、毒害性、安全性。
发明内容
本发明的目的是克服现有技术的不足，提供一种组分简单合理、低烟、使用量少、阻燃效果好、无毒、无污染的莫来石复合阻燃剂。
为了实现上述目的本发明采用如下技术方案：
一种莫来石复合型阻燃剂，由下列重量份的原料组成：莫来石10-15份、纳米钛白粉5-10份、硅藻土5-8份、氯化石蜡5-8份、季戊四醇50-60份、多聚磷酸铵20-30份、四硼酸钠3-5份、硼砂5-30份、空心微珠10-25份。
优选地，一种莫来石复合型阻燃剂，由下列重量份的原料组成：莫来石12份、纳米钛白粉8份、硅藻土2份、氯化石蜡6份、季戊四醇60份、多聚磷酸铵30份、四硼酸钠5份、硼砂10份、空心微珠15份。
所述的莫来石复合型阻燃剂的制备方法，包括以下制备步骤：
(1)将莫来石粉碎至100-200目，再将粉碎后的莫来石粉置于电炉加热装置中以5-20℃/min的升温速率加热至1000-1200℃保温2-4h后，制得纳米莫来石；
(2)按上述重量份比例将步骤(1)制备的纳米莫来石与纳米钛白粉、硅藻土、氯化石蜡、四硼酸钠、硼砂、空心微珠充分混合，100-115℃高速3000-4000转/分搅拌30-40min；
(3)将季戊四醇、多聚磷酸铵加入到步骤(2)混合物中，充分混合30-50min，冷却即得白云石复合型阻燃剂。
与已有技术相比，本发明的有益效果如下：
本发明以纳米莫来石与季戊四醇、多聚磷酸铵混合制成复合型阻燃剂，莫来石具有耐高温、强度高、抗化学腐蚀性好、节能效果显著等特点，本发明的阻燃剂组分简单合理、低烟、使用量少、阻燃效果好、无毒、无污染。
具体实施方式
下面结合实施例对本发明作进一步的描述。
实施例1：
一种莫来石复合型阻燃剂，由下列重量份的原料组成：莫来石12份、纳米钛白粉8份、硅藻土2份、氯化石蜡6份、季戊四醇60份、多聚磷酸铵30份、四硼酸钠5份、硼砂10份、空心微珠15份。
莫来石复合型阻燃剂的制备方法，包括以下制备步骤：
(1)将莫来石粉碎至200目，再将粉碎后的莫来石粉置于电炉加热装置中以15℃/min的升温速率加热至1000℃保温3h后，制得纳米莫来石；
(2)按上述重量份比例将步骤(1)制备的纳米莫来石与纳米钛白粉、硅藻土、氯化石蜡、四硼酸钠、硼砂、空心微珠充分混合，100℃高速3000转/分搅拌40min；
(3)将季戊四醇、多聚磷酸铵加入到步骤(2)混合物中，充分混合30min，冷却即得白云石复合型阻燃剂。
实施例2：
一种莫来石复合型阻燃剂，由下列重量份的原料组成：莫来石10份、纳米钛白粉5份、硅藻土5份、氯化石蜡5份、季戊四醇50份、多聚磷酸铵20份、四硼酸钠3份、硼砂5份、空心微珠10份。
莫来石复合型阻燃剂的制备方法，包括以下制备步骤：
(1)将莫来石粉碎至100目，再将粉碎后的莫来石粉置于电炉加热装置中以10℃/min的升温速率加热至1000℃保温4h后，制得纳米莫来石；
(2)按上述重量份比例将步骤(1)制备的纳米莫来石与纳米钛白粉、硅藻土、氯化石蜡、四硼酸钠、硼砂、空心微珠充分混合，115℃高速3000转/分搅拌30min；
(3)将季戊四醇、多聚磷酸铵加入到步骤(2)混合物中，充分混合50min，冷却即得白云石复合型阻燃剂。
实施例3：
一种莫来石复合型阻燃剂，由下列重量份的原料组成：莫来石15份、纳米钛白粉10份、硅藻土8份、氯化石蜡8份、季戊四醇60份、多聚磷酸铵30份、四硼酸钠5份、硼砂30份、空心微珠25份。
莫来石复合型阻燃剂的制备方法，包括以下制备步骤：
(1)将莫来石粉碎至200目，再将粉碎后的莫来石粉置于电炉加热装置中以20℃/min的升温速率加热至1200℃保温2h后，制得纳米莫来石；
(2)按上述重量份比例将步骤(1)制备的纳米莫来石与纳米钛白粉、硅藻土、氯化石蜡、四硼酸钠、硼砂、空心微珠充分混合，100℃高速4000转/分搅拌30min；
(3)将季戊四醇、多聚磷酸铵加入到步骤(2)混合物中，充分混合50min，冷却即得白云石复合型阻燃剂。
试验例：
将实施例1、实施例2、实施例3制备的白云石复合型阻燃剂分别于乙烯-醋酸乙烯共聚物以45％、55％的重量比充分混合，采用注塑工艺在注塑机上注塑成型，得到阻燃乙烯-醋酸乙烯共聚物复合材料。测定的性能如下：
氧指数 燃烧性能
实施例1 35 UL94-0级
实施例2 33 UL94-0级
实施例3 32 UL94-0级

Claims (2)

1.一种莫来石复合型阻燃剂，其特征在于：由下列重量份的原料组成：莫来石10-15份、纳米钛白粉5-10份、硅藻土5-8份、氯化石蜡5-8份、季戊四醇50-60份、多聚磷酸铵20-30份、四硼酸钠3-5份、硼砂5-30份、空心微珠10-25份。
2.一种如权利要求1所述的莫来石复合型阻燃剂的制备方法，其特征在于：包括以下制备步骤：
(1)将莫来石粉碎至100-200目，再将粉碎后的莫来石粉置于电炉加热装置中以5-20℃/min的升温速率加热至1000-1200℃保温2-4h后，制得纳米莫来石；
(2)按上述重量份比例将步骤(1)制备的纳米莫来石与纳米钛白粉、硅藻土、氯化石蜡、四硼酸钠、硼砂、空心微珠充分混合，100-115℃高速3000-4000转/分搅拌30-40min；
(3)将季戊四醇、多聚磷酸铵加入到步骤(2)混合物中，充分混合30-50min，冷却即得莫来石复合型阻燃剂。
CN201410057042.9A 2014-02-20 2014-02-20 一种莫来石复合型阻燃剂 Expired - Fee Related CN103881143B (zh)