CN103880325B - Kieselguhr wall material and constructional method thereof - Google Patents
Kieselguhr wall material and constructional method thereof Download PDFInfo
- Publication number
- CN103880325B CN103880325B CN201410040013.1A CN201410040013A CN103880325B CN 103880325 B CN103880325 B CN 103880325B CN 201410040013 A CN201410040013 A CN 201410040013A CN 103880325 B CN103880325 B CN 103880325B
- Authority
- CN
- China
- Prior art keywords
- wall material
- weight parts
- kieselguhr
- kieselguhr wall
- wall body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of kieselguhr wall material and constructional method thereof, belong to building material field.Described kieselguhr wall material, component 250 ~ 500 order calcined diatomite containing, for example lower weight part: 20 ~ 52 weight parts; 35 ~ 825 order quartz sand powders: 24 ~ 48 weight parts; 325 ~ 1200 order natural colour sands: 10 ~ 30 weight parts; Nano titanium oxide: 3 ~ 10 weight parts; Methylcellulose gum: 0.4 ~ 1.2 weight part; Redispersible latex powder: 6 ~ 20 weight parts.After utilizing kieselguhr wall material provided by the invention and constructional method thereof to construct on wall body, finished product effect is attractive in appearance, and texture, close to the dreamlike decorated style of imperial noble, meets people to the ornamental requirement of kieselguhr wall material.
Description
Technical field
The present invention relates to building decoration field, particularly a kind of kieselguhr wall material and constructional method thereof.
Background technology
Diatomite is a kind of biogenic silicastone, and it formed primarily of the remains of diatom in ancient times, has the characteristics such as exquisiteness, loose, light weight, porous, water-absorbent and perviousness are strong.Along with the requirement of people to the living environment feature of environmental protection is more and more higher, diatomite becomes the very welcome new indoor decoration material of one gradually, with the addition of diatomaceous wall material and has and regulate the room temperature, eliminate peculiar smell, absorb the advantages such as Sum decomposition objectionable impurities.At present, although utilize kieselguhr wall material can produce certain texture on the surface at wall body, ornamental to increase it, still there is the space of improvement in this respect.
In human development history, because imperial noble is to the ascendancy of social life, the building decoration of imperial noble has embodied a concentrated reflection of the consummate technique of each epoch skillful craftsman, makes building decoration be provided with high aesthetic value.But, use traditional finishing pattern to reach the building decorative effect of imperial noble, there is long in time limit, costly distinct disadvantage, seriously limit the demand of general public.
Therefore, if a kind of kieselguhr wall material and the construction technology thereof with imperial noble's decorated style texture can be provided, then people must be met to a certain extent to the ornamental requirement of kieselguhr wall material.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of kieselguhr wall material and constructional method thereof.
For solving the problems of the technologies described above, technical scheme provided by the invention is as follows:
A kind of kieselguhr wall material, the component containing, for example lower weight part:
250 ~ 500 order calcined diatomites: 20 ~ 52 weight parts;
35 ~ 825 order quartz sand powders: 24 ~ 48 weight parts;
325 ~ 1200 order natural colour sands: 10 ~ 30 weight parts;
Nano titanium oxide: 3 ~ 10 weight parts;
Methylcellulose gum: 0.4 ~ 1.2 weight part;
Redispersible latex powder: 6 ~ 20 weight parts;
Further, described kieselguhr wall material is also containing, for example the component of lower weight part:
Mineral dye: 1 ~ 30 weight part.
Preferably, described kieselguhr wall material, the content of each component is as follows:
250 ~ 500 order calcined diatomites: 30 ~ 42 weight parts;
175 ~ 725 order quartz sand powders: 30 ~ 40 weight parts;
550 ~ 1150 order natural colour sands: 15 ~ 25 weight parts;
Nano titanium oxide: 5 ~ 7 weight parts;
Methylcellulose gum: 0.7 ~ 0.9 weight part;
Redispersible latex powder: 12 ~ 14 weight parts.
Further, described kieselguhr wall material is also containing, for example the component of lower weight part:
Mineral dye: 1 ~ 30 weight part.
More preferably, described kieselguhr wall material, the content of each component is as follows:
250 ~ 500 order calcined diatomites: 36 weight parts;
225 ~ 675 order quartz sand powders: 36 weight parts;
625 ~ 925 order natural colour sands: 20 weight parts;
Nano titanium oxide: 6 weight parts;
Methylcellulose gum: 0.8 weight part;
Redispersible latex powder: 13 weight parts.
Further, described kieselguhr wall material is also containing, for example the component of lower weight part:
Mineral dye: 1 ~ 30 weight part.
The preparation method of above-mentioned kieselguhr wall material is: mixed according to corresponding parts by weight by mentioned component, stir.
A constructional method for above-mentioned kieselguhr wall material, comprising:
Step 1: base treatment is carried out to wall body;
Step 2: kieselguhr wall material and water are mixed according to the ratio of weight ratio 1:0.4 ~ 0.6;
Step 3: criticize and scrape two times constructions; First pass is criticized after the wall material scraped parches completely and is brushed one deck basement membrane, then criticizes and scrapes second time; To have scraped after second time immediately with Roller brush to the overall plucking of wall body, when wall material to 3 ~ 5 one-tenths is dry, be closed flat press polish with receipts light trowel, note during operation making the wall body surface irregular duck eye of appearance and duck eye is evenly distributed unanimously;
Step 4: after wall material complete drying, two times constructions of painting; Wherein first pass colouring dips in upper yellow ultramarine point gently with crash towel to wipe at wall material on the surface, notices that the duck eye do not clipped described in step 3 is inner; After the pigment of first pass colouring parches, the even some wiping second time pigment except yellow except on first pass yellow ultramarine, overall even, the shade of the pigment that second time point is wiped unanimously.
Wherein,
In step 1, described base treatment is carried out to wall body be: wall body entirety has been scraped water-proof putty and brushing basement membrane, has protected wall body corner with U.S. line paper; If wall body base material is different, also bandage or grid cloth process should be sticked in junction; Require wall body humidity to be less than 10% after being disposed, pH is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing;
In step 2, construction temperature is not less than 5 DEG C; Described kieselguhr wall material and the weight ratio of water are preferably 1:0.5; Described working method kieselguhr wall material and water mixed is as follows: the water first adding water consumption 80% in container, add described kieselguhr wall material again and leave standstill 3 ~ 5 minutes, then stir 8 ~ 10 minutes with electric mixer, the water of residue 20% is slowly added during stirring, leave standstill 3 ~ 5 minutes, then stir 8 ~ 10 minutes with electric mixer;
Preferably, 30 ~ 60 minutes are left standstill again after kieselguhr wall material and water being mixed;
In step 3, it is 0.7 ~ 0.9mm that described first pass criticizes the wall material thickness scraped, and the second time batch of wall material thickness scraped is 0.6 ~ 0.8mm; The operative body stainless steel of described receipts light trowel makes, and thickness is 0.03mm, and the plane set deformation volume of operative body is 0.03mm.
The present invention has following beneficial effect:
After utilizing kieselguhr wall material of the present invention and constructional method thereof to construct on wall body, finished product effect is attractive in appearance, and texture, close to dreamlike decorated style, meets people to the ornamental requirement of kieselguhr wall material.
Embodiment
For making the technical problem to be solved in the present invention, technical scheme and advantage clearly, be described in detail below in conjunction with specific embodiment.
The method used in following embodiment if no special instructions, is ordinary method.
Material used in following embodiment, reagent etc., if no special instructions, all can obtain from commercial channels.
On the one hand, the invention provides a kind of kieselguhr wall material, it is the powder body material allocated by various ingredients, and concrete component refers to following examples.
Embodiment 1:
Kieselguhr wall material is containing, for example the component of lower weight part: 250 ~ 500 order calcined diatomites: 20 weight parts; 35 ~ 825 order quartz sand powders: 48 weight parts; 325 ~ 1200 order natural colour sands: 10 weight parts; Nano titanium oxide: 10 weight parts; Methylcellulose gum: 0.4 weight part; Redispersible latex powder: 20 weight parts.
Embodiment 2:
Kieselguhr wall material is containing, for example the component of lower weight part: 250 ~ 500 order calcined diatomites: 52 weight parts; 35 ~ 825 order quartz sand powders: 24 weight parts; 325 ~ 1200 order natural colour sands: 30 weight parts; Nano titanium oxide: 3 weight parts; Methylcellulose gum: 1.2 weight parts; Redispersible latex powder: 6 weight parts.
Embodiment 3:
On the basis of embodiment 1, add mineral dye: 1 weight part.
Embodiment 4:
On the basis of embodiment 2, add mineral dye: 30 weight parts.
Embodiment 5:
Kieselguhr wall material is containing, for example the component of lower weight part: 250 ~ 500 order calcined diatomites: 42 weight parts; 175 ~ 725 order quartz sand powders: 30 weight parts; 550 ~ 1150 order natural colour sands: 25 weight parts; Nano titanium oxide: 5 weight parts; Methylcellulose gum: 0.9 weight part; Redispersible latex powder: 12 weight parts.
Embodiment 6:
Kieselguhr wall material is containing, for example the component of lower weight part: 250 ~ 500 order calcined diatomites: 30 weight parts; 175 ~ 725 order quartz sand powders: 40 weight parts; 550 ~ 1150 order natural colour sands: 15 weight parts; Nano titanium oxide: 7 weight parts; Methylcellulose gum: 0.7 weight part; Redispersible latex powder: 14 weight parts.
Embodiment 7:
On the basis of embodiment 5, add mineral dye: 1 weight part.
Embodiment 8:
On the basis of embodiment 6, add mineral dye: 30 weight parts.
Embodiment 9:
Kieselguhr wall material is containing, for example the component of lower weight part: 250 ~ 500 order calcined diatomites: 36 weight parts; 225 ~ 675 order quartz sand powders: 36 weight parts; 625 ~ 925 order natural colour sands: 20 weight parts; Nano titanium oxide: 6 weight parts; Methylcellulose gum: 0.8 weight part; Redispersible latex powder: 13 weight parts.
Embodiment 10:
On the basis of embodiment 9, add mineral dye: 1 weight part.
Embodiment 11:
On the basis of embodiment 9, add mineral dye: 30 weight parts.
The present invention utilizes natural colour sand and calcined diatomite meticulously to allocate, then adds a kind of novel environment friendly wall body finishing material that quartz sand powder, nano titanium oxide, methylcellulose gum and redispersible latex powder be prepared into.
Through actual verification, make by above-mentioned kieselguhr wall material provided by the invention the wall body decorative pattern obtained, there is dense dreamlike texture, meet people to the ornamental requirement of kieselguhr wall material.Further, the effect that the kieselguhr wall material wherein using embodiment 5 to 8 to provide obtains is better than embodiment 1 to 4, and the effect of embodiment 9 to 11 is better than embodiment 5 to 8.Meanwhile, in above-described embodiment, with the addition of the kieselguhr wall material of mineral dye relative to the kieselguhr wall material not adding mineral dye, the effect obtained is more attractive in appearance true to nature.
Embodiment 12:
The constructional method of a kind of above-mentioned kieselguhr wall material provided by the invention, specific as follows:
Step 1: base treatment is carried out to wall body;
According to the usual way in this area, wall body is processed, make it be suitable for the construction of follow-up kieselguhr wall material.Want to obtain the decorative effect better with dreamlike effect, wall body entirety should scrape water-proof putty and brushing basement membrane, and the U.S. line paper in wall body corner protects; If wall body base material is different, also bandage or grid cloth process should be sticked in junction; Require wall body humidity to be less than 10% after being disposed, pH is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing;
Step 2: kieselguhr wall material and water are mixed according to the ratio of weight ratio 1:0.4 ~ 0.6;
In this step, the water yield can not too much can not be very few, and the weight ratio of kieselguhr wall material and water is preferably 1:0.5, otherwise all can be not easy to subsequent construction, even affects the texture effect of finished product.Stir even, the application property of material is better; In order to obtain the decorative effect better with dreamlike effect, optionally with the following method kieselguhr wall material and water to be mixed: the water first adding water consumption 80% in container, add kieselguhr wall material again and leave standstill 3 ~ 5 minutes, then stir 8 ~ 10 minutes with electric mixer, the water of residue 20% is slowly added during stirring, leave standstill 3 ~ 5 minutes, then within 8 ~ 10 minutes, make it mix with electric mixer stirring; 30 ~ 60 minutes better effects if are left standstill again after mixing;
Step 3: criticize and scrape two times constructions; First pass is criticized after the wall material scraped parches completely and is brushed one deck basement membrane, then criticizes and scrapes second time; To have scraped after second time immediately with Roller brush to the overall plucking of wall body, when wall material to 3 ~ 5 one-tenths is dry, be closed flat press polish with receipts light trowel, note during operation making the wall body surface irregular duck eye of appearance and duck eye is evenly distributed unanimously;
In this step, in order to obtain the decorative effect better with dreamlike effect, it is 0.7 ~ 0.9mm that first pass criticizes the wall material thickness scraped, and the second time batch of wall material thickness scraped is 0.6 ~ 0.8mm; The present invention adopts two times batches of modes of scraping to construct, and first pass is criticized after the wall material scraped parches completely and brushed one deck basement membrane, then criticizes and scrapes second time; To have scraped after second time immediately with Roller brush to the overall plucking of wall body, when wall material to 3 ~ 5 one-tenths is dry, be closed flat press polish with receipts light trowel, note during operation making the wall body surface irregular duck eye of appearance and duck eye is evenly distributed unanimously.
Meanwhile, the operative body stainless steel of the receipts light trowel used in this step makes, and thickness is 0.03mm, and the plane set deformation volume of operative body is 0.03mm.
Step 4: after wall material complete drying, two times constructions of painting; Wherein first pass colouring dips in upper yellow ultramarine point gently with crash towel to wipe at wall material on the surface, notices that the duck eye do not clipped described in step 3 is inner; After the pigment of first pass colouring parches, the even some wiping second time pigment except yellow except on first pass yellow ultramarine, overall even, the shade of the pigment that second time point is wiped unanimously.
In this step, in order to obtain the decorative effect better with dreamlike effect, going up twice pigment process again to criticizing the wall material surface of scraping completion, the method for painting during colouring, must be noted, pigment is not clipped duck eye inside, thus reach decorative effect true to nature.
Contriver is through concentrating on studies discovery, and in order to use the texture presenting dreamlike decorated style containing diatomaceous wall material, first key point is the formula of kieselguhr wall material; Second key point is then constructional method, the opportunity often all over construction when comprising the ratio of kieselguhr wall material and water, stirring means, two times constructions, the working method of colouring and other concrete working method etc.; 3rd key point is the material of the receipts light trowel used, thickness and elastic performance, and these factors all can have influence on the texture effect of the finished product after kieselguhr wall unit construction.
Through studying for many years, the talent is according to the texture feature of dreamlike decorated style in invention, have developed kieselguhr wall material and the constructional method thereof with dreamlike effect of the present invention, thus can make and obtain the wall body decorative pattern of texture close to dreamlike decorated style, meet people to the ornamental requirement of kieselguhr wall material.
To sum up, after utilizing kieselguhr wall material of the present invention and constructional method thereof to construct on wall body, finished product effect is attractive in appearance, and texture, close to dreamlike decorated style, meets people to the ornamental requirement of kieselguhr wall material.And, not containing any harmful material in kieselguhr wall material provided by the invention, not only can not the obnoxious flavour such as emitting formaldehyde, benzene, ammonia, radon, but also there is absorption, the function of resolving harmful gas, and there is certain equilibrium temperature function, possess transport, simple feature of constructing simultaneously.
Invention increases the utilization of diatomite in finishing material, for life brings selection that is more healthy, environmental protection at home.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from principle of the present invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (6)
1. a kieselguhr wall material, is characterized in that, is made up of the component of following weight part:
250 ~ 500 order calcined diatomites: 30 ~ 42 weight parts;
175 ~ 725 order quartz sand powders: 30 ~ 40 weight parts;
550 ~ 1150 order natural colour sands: 15 ~ 25 weight parts;
Nano titanium oxide: 5 ~ 7 weight parts;
Methylcellulose gum: 0.7 ~ 0.9 weight part;
Redispersible latex powder: 12 ~ 14 weight parts;
The constructional method of above-mentioned kieselguhr wall material, comprises the steps:
Step 1: base treatment is carried out to wall body;
Step 2: kieselguhr wall material and water are mixed according to the ratio of weight ratio 1:0.4 ~ 0.6;
Step 3: criticize and scrape two times constructions; First pass is criticized after the wall material scraped parches completely and is brushed one deck basement membrane, then criticizes and scrapes second time; To have scraped after second time immediately with Roller brush to the overall plucking of wall body, when wall material to 3 ~ 5 one-tenths is dry, be closed flat press polish with receipts light trowel, note during operation making the wall body surface irregular duck eye of appearance and duck eye is evenly distributed unanimously;
Step 4: after wall material complete drying, two times constructions of painting; Wherein first pass colouring dips in upper yellow ultramarine with crash towel to wipe at wall material on the surface in place gently, notices that the duck eye do not clipped described in step 3 is inner; After the pigment of first pass colouring parches, the even some wiping second time pigment except yellow except on first pass yellow ultramarine, overall even, the shade of the pigment that second time point is wiped unanimously.
2. kieselguhr wall material according to claim 1, is characterized in that, is made up of the component of following weight part:
250 ~ 500 order calcined diatomites: 36 weight parts;
225 ~ 675 order quartz sand powders: 36 weight parts;
625 ~ 925 order natural colour sands: 20 weight parts;
Nano titanium oxide: 6 weight parts;
Methylcellulose gum: 0.8 weight part;
Redispersible latex powder: 13 weight parts.
3. kieselguhr wall material according to claim 1, is characterized in that, in step 3, it is 0.7 ~ 0.9mm that described first pass criticizes the wall material thickness scraped, and the second time batch of wall material thickness scraped is 0.6 ~ 0.8mm.
4. kieselguhr wall material according to claim 1, is characterized in that, in step 1, described carry out base treatment to wall body and is: wall body entirety has been scraped water-proof putty and brushing basement membrane, has protected wall body corner with U.S. line paper; If wall body base material is different, also bandage or grid cloth process should be sticked in junction; Require wall body humidity to be less than 10% after being disposed, pH is less than 10, wall body overall leveling, closely knit, clean without floating dust, without cracking hollowing.
5. kieselguhr wall material according to claim 1, is characterized in that, in step 2, described kieselguhr wall material and the weight ratio of water are 1:0.5.
6. kieselguhr wall material according to claim 1, is characterized in that, in step 2, construction temperature is not less than 5 DEG C; Described working method kieselguhr wall material and water mixed is as follows: the water first adding water consumption 80% in container, add described kieselguhr wall material again and leave standstill 3 ~ 5 minutes, then stir 8 ~ 10 minutes with electric mixer, the water of residue 20% is slowly added during stirring, leave standstill 3 ~ 5 minutes, then stir 8 ~ 10 minutes with electric mixer; 30 ~ 60 minutes are left standstill again after kieselguhr wall material and water being mixed.