CN103862200A - 一种太阳能组件焊接专用助焊剂 - Google Patents
一种太阳能组件焊接专用助焊剂 Download PDFInfo
- Publication number
- CN103862200A CN103862200A CN201410110707.8A CN201410110707A CN103862200A CN 103862200 A CN103862200 A CN 103862200A CN 201410110707 A CN201410110707 A CN 201410110707A CN 103862200 A CN103862200 A CN 103862200A
- Authority
- CN
- China
- Prior art keywords
- scaling powder
- welding
- solar components
- acid
- high boiling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种太阳能组件焊接专用助焊剂,其特征是由下述重量百分比的原料制成:改性树脂0.2~0.4%,组合有机酸1.0~1.3%,氟碳表面活性剂0.1~0.2%,高沸点溶剂5~10%,余量为异丙醇。它具有刺激气味低,化锡流畅,锡面平整光滑,结合力高,虚焊率低,层压后无白斑发黄的优点,同时满足光伏行业双85及双95老化测试要求。
Description
技术领域
本发明属于焊接技术领域,具体涉及一种太阳能焊接组件专用助焊剂。
背景技术
光伏发电是可再生的清洁能源,值得大力发展,有可能成为未来最重要能源供应方式。电池片和光伏焊带焊接作为太阳能电池组件制造过程中重要的一环,其加工效果对太阳能电池组件的性能起到重要的影响。目前,国内外还没有相应的太阳能组件焊接专用助焊剂的专利,同时由于该行业的要求于普通电子行业要求不同,普通的电子行业助焊剂不能满足光伏焊带产品的性能要求,国内市场上现在的产品主要有新加坡ASAHI公司的ANX3012以及美国KESTER公司的952-S,这两款产品由于价格原因,大大增加了制造成本,众多中小型企业迫切需要找到一款性价比高的产品。满足该行业需要的助焊剂需要达到以下性能:
(1) 固体含量低,焊接后无残留;
(2) 焊接时助焊剂挥发气体无刺激性;
(3) 可焊性良好,化锡流畅,焊接后焊带和电池片结合强度高;
(4) 锡面均匀,光亮,无铺锡、锡珠、虚焊等不良;
(5) 焊接后的组件能够通过双85或双95老化测试;
(6) 组件层压后焊带无白斑及发黄现象。
发明内容
本发明的目的在于提供一种适用于太阳能组件焊接用的低固含量、低残留、低气味、均匀性好的助焊剂。
本发明是这样来实现的。一种太阳能组件焊接专用助焊剂,它由下述重量百分比的原料制成:改性树脂0.2~0.4%, 组合有机酸 1.0~1.3%, 氟碳表面活性剂 0.1~0.2%, 高沸点溶剂 5~10%,余量为异丙醇。
所述改性树脂采用聚醚改性树脂,主要作用为将助焊剂中的其他的有效成份吸附到基材表面,在320-350摄氏度的焊接温度范围内起到化锡作用,可以有效的提高化锡速率。
所述组合有机酸可以是丁二酸、戊二酸、己二酸、柠檬酸、草酸中的两种或以上组合物。主要作用是清洗基材表面的氧化物,起到活化基材的作用,在320-350摄氏度的焊接温度范围内可以完全分解无任何残留。
所述氟碳表面活性剂采用全氟类表面活性剂,具有良好的分散性、流平性,有效降低基材表面张力。
所述高沸点溶剂可以是醚类高沸点溶剂,乙二醇丁醚,乙二醇丙醚,主要作用降低体系的挥发速率,保证助焊剂有效成份的比重在工艺控制范围内。
本发明具有刺激气味低,化锡流畅,锡面平整光滑,结合力高,虚焊率低,层压后无白斑发黄的优点,同时满足光伏行业双85及双95老化测试要求,适用于太阳能电池片焊接及通用电子工业,可替代具有潜在腐蚀性的活化松脂焊剂以及性能不佳的纯松脂焊剂。
具体实施方式
为了便于理解,下面结合实施例对本发明予以进一步阐明。
实施例1
一种太阳能组件焊接专用助焊剂,它由下述重量百分比的原料混合制备而成:聚醚改性树脂0.2%, 丁二酸和草酸的组合物1.0%, 氟碳表面活性剂 0.1%,乙二醇丁醚5%,余量为异丙醇。
实施例2
一种太阳能组件焊接专用助焊剂,它由下述重量百分比的原料混合制备而成:聚醚改性树脂0.3%,戊二酸、己二酸和柠檬酸的组合物1.3%, 氟碳表面活性剂 0.2%,乙二醇丙醚10%,余量为异丙醇。
实施例3
一种太阳能组件焊接专用助焊剂,它由下述重量百分比的原料混合制备而成:聚醚改性树脂0.3%, 丁二酸、戊二酸、己二酸、柠檬酸和草酸的组合物1.2%, 氟碳表面活性剂 0.1%,乙二醇丙醚6%,余量为异丙醇。
实施例4
一种太阳能组件焊接专用助焊剂,它由下述重量百分比的原料混合制备而成:聚醚改性树脂0.4%, 丁二酸、柠檬酸和草酸的组合物1.0%, 全氟类表面活性剂 0.1%,乙二醇丙醚8%,余量为异丙醇。
实施例5
一种太阳能组件焊接专用助焊剂,它由下述重量百分比的原料混合制备而成:聚醚改性树脂0.3%, 丁二酸和戊二酸的组合物1.2%, 氟碳表面活性剂 0.2%,乙二醇丁醚10%,余量为异丙醇。
本发明的助焊剂按J-STD-004标准分类属于ORMO型助焊剂,其在20℃为无色透明的液体,按照GB/T4472-84测试20℃时比重为0.795±0.010,按照J-STD-004测试酸价位19.00±2.00mgKOH/g,气味小,焊后残余物少,残余物无腐蚀,不粘手,低缺陷率,免清洗,减少生产成本。
取实施例5的助焊剂作性能测试,所得实验结果如下表所示:
以上结合实施例对本发明的实施方式作了详细说明,但是本发明并不限于上述实施方式,在本领域技术人员所具备的知识范围内,还可以在不脱离本发明宗旨的前提下作出各种变化。
Claims (6)
1.一种太阳能组件焊接专用助焊剂,其特征是由下述重量百分比的原料制成:改性树脂0.2~0.4%, 组合有机酸 1.0~1.3%, 氟碳表面活性剂 0.1~0.2%, 高沸点溶剂 5~10%,余量为异丙醇。
2.根据权利要求1所述的太阳能组件焊接专用助焊剂,其特征是所述改性树脂为聚醚改性树脂。
3.根据权利要求1所述的太阳能组件焊接专用助焊剂,其特征是所述组合有机酸是丁二酸、戊二酸、己二酸、柠檬酸、草酸中的两种或以上组合物。
4.根据权利要求1所述的太阳能组件焊接专用助焊剂,其特征是所述氟碳表面活性剂是全氟类表面活性剂。
5.根据权利要求1所述的太阳能组件焊接专用助焊剂,其特征是所述高沸点溶剂是醚类高沸点溶剂。
6.根据权利要求1所述的太阳能组件焊接专用助焊剂,其特征是所述高沸点溶剂是乙二醇丁醚或乙二醇丙醚。